The present study aims to investigate the use of geopolymer mortars as passive fire protection system for steel structures. Coal fly ashes were used as aluminosilicate source and perlite was employed as aggregate to obtain a lightweight system. In addition, a geopolymer mortar containing quartz aggregate was produced for comparison. The geopolymer mortars were applied on stainless steel plates and exposed to both, cellulosic and hydrocarbon standard fire curves, according to ISO 834-1 and EN 1363-2, respectively. Acoustic emission measurements were conducted to analyze cracking phenomena during the high temperature exposure. The resulting temperature-time curves showed that the investigated system is effective in retarding the temperature rise of the steel plates. When the cellulosic fire curve was applied, a 20 mm [0.79 in.] thick layer of lightweight geopolymer mortar protected the steel substrate from reaching the critical temperature of 500 °C [932 °F] for at least 30 minutes, avoiding the rapid decrease of its mechanical properties and thus representing an important safety measure against accidental fires. No spalling phenomena on heating were detected; however, significant cracking was observed on cooling.
This study aims at investigating the use of coal fly ash-based alkali activated mortars as passive fire protection system for steel structures. These systems are used to slow down the temperature rise of the steel substrate in case of fire. In addition, the protective system should guarantee the ability to prevent and/or mitigate steel corrosion phenomena. The behavior of a light-weight mortar was compared to that of a normal-weight mortar. Density and porosity were measured to better characterize the physical properties of the mortars. The degree of protection in case of fire was assessed by performing medium-scale fire tests. Acoustic emission measurements were conducted to analyze cracking phenomena during the high temperature exposure. The corrosion process was evaluated using an electrochemical approach in order to monitor the durability of the developed material. Preliminary results show that a 20 mm-thick layer of light-weight mortar is able to protect the steel substrate from reaching the critical temperature of 500 °C for 38 minutes in case of cellulosic fire. In addition, alkali activated mortars provide protection for carbon steel in presence of aggressive environment (i.e. presence of chlorides). The corrosion resistance is strictly related to the physical properties of the developed mortars.
Alkali-activated fly ashes have been proposed for various applications where resistance against high temperatures is required, yet several details regarding the response of these materials to heat-exposure need to be clarified. In the present study, heat-induced cracking in fly ash-based alkali-activated pastes and lightweight mortars was analyzed by in-situ acoustic emission (AE) detection during complete heating-cooling cycles (up to ∼1100 °C), augmented by thermogravimetry and ex-situ SEM and XRD analyses. The applicability of the lightweight mortars as passive fire protection coatings was assessed by recording temperature-time curves of mortar-coated steel plates. Cracking during heating was limited and associated exclusively with the dehydration of the materials in the temperature range ∼90–360 °C. However, samples heated to temperatures above ∼600 °C exhibited intense cracking on cooling. This was attributed to differential deformations caused by local sintering and partial melting at the glass transition temperature, and subsequent quenching on cooling.