Zeolitic Imidazolate Frameworks (ZIFs) are crystalline materials
that comprise of metal nodes and Imidazole derivatives as
linkers. ZIF-67 is often used in polymer composite materials
e. g. for gas separation membranes. Post-synthesis treatment of
ZIF-67 crystals with ultrasound leads to unforeseen plasticity
that resulted in sintered ZIF-67 and ZIF-67 nano-flakes.
Consequently, ultrasound increases the external surface area of
ZIF-67 which might improve e.g. blending with polymers in
composite materials. These new morphologies of ZIF-67 were
characterized by transmission electron, scanning electron, and
atomic force microscopy. The ultrasound treatment of ZIF-67
did not result in the formation of an amorphous framework or
a meta-stable crystal structure as indicated by powder x-ray
diffraction. In addition, ultra-sonicated ZIF-67 retained the high
gas adsorption capacity and pore size compared to synthesized
ZIF-67. The morphological changes are hard to detect with
standard analytical methods that are usually utilized for MOF
characterization. These findings also suggest that sonochemical
treatment of ZIFs leads to structural effects beyond increasing
the amount of nucleation clusters during sono-chemical synthesis,
which is currently not addressed in the field.
Equipping ZIF particles with a polyelectrolyte membrane provides functional groups at their interface, enabling further conjugations necessary for applications such as targeted drug delivery. Previous approaches to coat ZIF particles with polyelectrolytes led to surface corrosion of the template material. This work overcomes previous limitations by performing a Layer-by-Layer (LbL) polyelectrolyte coating onto ZIF-8 and ZIF-67 particles in nonaqueous environment. Using the 2-methylimidazolium salt of polystyrensulfonic acid instead of the acid itself and polyethyleneimine in methanol led to intact ZIF particles after polyelectrolyte coating. This was verified by electron microscopy. Further, zetapotential and atomic force microscopy measurements confirmed a continuous polyelectrolyte multilayer built up. The here reported adaption to the well-studied (LbL) polyelectrolyte selfassembly process provides a facile method to equip ZIF particles with a nanometer thin polyelectrolyte multilayer membrane.