Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (43)
- Beitrag zu einem Tagungsband (31)
- Vortrag (27)
- Beitrag zu einem Sammelband (8)
- Posterpräsentation (5)
- Dissertation (1)
- Forschungsbericht (1)
Sprache
- Englisch (69)
- Deutsch (40)
- Mehrsprachig (6)
- Französisch (1)
Schlagworte
- Corrosion (21)
- Schadensanalyse (15)
- CCS (13)
- Fraktographie (11)
- Impurities (8)
- CCUS (7)
- Carbon steel (7)
- CO2 (6)
- Additive manufacturing (5)
- Datenbank (5)
Organisationseinheit der BAM
- 5 Werkstofftechnik (41)
- 5.1 Mikrostruktur Design und Degradation (41)
- 7 Bauwerkssicherheit (19)
- 7.6 Korrosion und Korrosionsschutz (19)
- 9 Komponentensicherheit (10)
- 9.0 Abteilungsleitung und andere (5)
- 9.4 Integrität von Schweißverbindungen (4)
- 9.6 Additive Fertigung metallischer Komponenten (4)
- 8 Zerstörungsfreie Prüfung (2)
- 8.0 Abteilungsleitung und andere (2)
Eingeladener Vortrag
- nein (27)
End of November 2005 strong south-west wind and heavy snowfall were predominant in the region Münsterland, north-western part of Germany. This led to accretion of a considerable quantity of wet snow to overhead electrical lines in form of snow rolls on the conductors. Eighty-two transmission towers failed catastrophically, most of them by buckling, however some by brittle fracture. As a consequence nearly 250,000 people have been cut off from electrical power supply for several days with major media attention.
This paper describes the forensic analysis in order to investigate the failure cause. Therefore extensive materials investigations, mechanical testing of original components and specimens thereof, estimations for the real wind and snow loads and their combinations, structural analyses as well as detailed evaluations on the basis of previous investigations, literature and regulations were conducted. It was revealed that some of the examined components were manufactured from Thomas steel which was partially in embrittled condition. The investigated towers fulfilled the design codes valid at the time of erection. However the present line loads of the wet snow rolls on the conductors exceeded by far the ones given in the design codes valid at that time.
The load case leading to failure was reconstructed by the derived positions of loads mainly caused by unequal and asymmetric distribution of snow rolls on left and right electrical system. The loads and corresponding stresses acting on the structure before failure were estimated. By comparison with the fracture forces from mechanical testing of original members of the collapsed tower the component that primarily failed was localised. The primary fracture occurred on a diagonal member under tension made of Thomas steel which was weakened by embrittlement. The failure cause was a combination of heavy weather conditions (storm, approx. 0 °C and wet snowfall leading to heavy snow rolls on conductors), asymmetric loading conditions and the usage of Thomas steel which was partially embrittled. Finally, recommendations for avoiding future failures are given.
Basic research on the corrosive effect of flue gases has been performed at the BAM Federal Institute for Materials Research and Testing (Germany). Conditions at both high and low temperatures were simulated in specially designed experiments. Carburization occured in flue gases with high CO2 content and temperatures higher than 500 °C. In SO2 containing flue gases sulphur was detected in the oxide scale. At lower temperatures no corrosion was observed when gases with low humidity were investigated. Humidity higher than 1500 ppm was corrosive and all steels with Cr contents lower than 12% revealed corroded surfaces. At low temperatures below 10 °C a mixture of sulphuric and nitric acid condensed on metal surfaces. Acid condensation caused severe corrosion. Humidity, CO2, O2, and SO2 contents are the important factors determining corrosion. Below 300 °C acid condensation is the primary reason for corrosion. Low humidity and low temperatures are conditions which can be expected in the CO2 separation and treatment process. This work includes major conditions of the flue gas and CO2 stream in CCS plants and CCS technology.
Am 9. Juli 2008 entgleiste ein Hochgeschwindigkeits-Triebzug der Baureihe 403, ICE3, bei der Ausfahrt aus dem Kölner Hauptbahnhof. Ursache dafür war der Schwingbruch einer Radsatzwelle. Im Auftrag der Staatsanwaltschaft Köln untersuchte die BAM die Schadensteile, insbesondere die gebrochene Treibradsatz-Hohlwelle.
Zunächst wurden das Drehgestell, der Antriebsstrang, die Räder, die Bremsen und die gebrochene Radsatzwelle visuell untersucht und deren Zustand dokumentiert.
Anschließend erfolgte die zerstörungsfreie Prüfung der beiden Bruchstücke der Hohlwelle mit teilmechanisierter Ultraschall-Handprüfung.
Vor der Zerlegung der Radsatzwelle wurden ausgewählte Maße kontrolliert und die Oberfläche eingehend untersucht. Nach der Probenahme und Präparation wurden die relevanten spezifizierten Eigenschaften des Wellenwerkstoffs überprüft.
Mittels Bruchflächenanalyse konnte die Startstelle des Schwingrisses lokalisiert, aufgrund der starken Sekundärschäden auf der Bruchfläche und an den Bruchkanten jedoch nicht direkt ausgewertet werden. Durch die Kombination von Mikro-Computertomographie und Ultraschall-Tauchtechnik wurden u. a. nahe der Schwingriss-Startstelle Inhomogenitäten erkannt, die durch metallographische Zielpräparation als nichtmetallische Einschlüsse identifiziert wurden. Die Größe dieser Einschlüsse ist gemäß gefordertem Reinheitsgrad unzulässig. Vergleichbare Einschlüsse in diesem hochbeanspruchten Bereich der Radsatzwelle haben vermutlich den Schwingriss initiiert.
COORAL Teilprojekt MINIRISK
(2011)