Railway structures such as rails and axles are safety relevant components since any failure includes the risk of catastrophic derailment. This paper gives a brief overview on the most important potential failure scenarios driven by fatigue crack initiation and propagation and discusses the effects of important influencing factors such as vehicle weight and speed, track quality and environmental conditions. The present paper summarizes earlier work of the authors in this field.
Recently three of the authors of this paper presented analytical solutions for reference loads of plate geometries with semi-elliptical surface cracks subjected to tension, bending, combined tension-bending and biaxial tension. These solutions were shown to provide more accurate crack driving force estimates than the conventional limit load solutions available in the literature, and the method behind them allowed for a wider application range. Within the present paper a methodology for the fracture analysis of thick-wall pressurized pipes using the R6 assessment method and considering both, biaxial and combined tension-bending loading is developed and validated. The analyses are carried out analytically, and the comparison between the predicted critical loads and experimental burst test failure loads shows satisfying agreement, this way demonstrating the potential of the proposed method.
Rotor disks for gas turbines are heavy components and are usually designed following a safe-life approach, where the low-cycle fatigue analysis is carried out referring to design life curves with suitable probabilistic margins. However, in the case of such a heavy component there is the possibility of rare occurrence of undetected defects or, better, the need to identify the defect acceptability for the different rotor regions (considering stress, temperature, mission profile).In order to carry out such calculations for a turbine rotor disk a software named AStrID (Assessment of the Structural Integrity of Disks) has been developed in close cooperation between Politecnico di Milano and Ansaldo Energia (AEN). This paper summarizes its background and some of the relevant features.
In microelectronic packaging, wire bonding is the predominant method for making electrical connections. Copper is increasingly substituting gold as interconnection material since it is a much cheaper alternative and it also offers several physical advantages.
Adequate and reliable mechanical integrity of the connection is usually checked by process controls based onto 'wire pull' and 'ball bond shear' tests. In this paper the two methods are compared in terms of sensitiveness in detecting a latent weakness of the bond-pad structure, either induced by inappropriate wire bonding process or cumulated during reliability ageing. The failure modes (in terms of frequency and maximum test load) observed at the ball bond interface have been investigated on two different batches of a same chip, obtained from different wire-bonding recipes and including both unstressed and aged units. Cross-sections of the samples, submitted to pull and shear both in destructive and non-destructive tests, have allowed us to investigate the relationship between the bond morphological characteristics (metal deformation and potential micro-damages induced by copper bonding) and the weak points for fracture propagation inside the bond-pad inner layers and the silicon substrate.
Besides the experimental activities, fracture mechanics and the finite element method have been employed to model the pull and shear tests. The aims of the finite element modelling have been to predict the reduction of test maximum load in defective ball bonds and the crack growth angle adopting a mixed-mode criterion. Good results have been obtained by the numerical fracture analysis, which can then support the reliability characterization and mechanical improvement of the bond.
The burst of a disc in rotating machinery can cause catastrophic damage of the equipment and, more importantly, it can represent a mortal threat to anyone in the sphere of influence of the event. In order to minimize the danger associated to a rotating component failure, burst testing is required by the authorities in order to set safety margins to the normal operating speeds. Moreover more accurate predicting tools are required for designing the components. This paper presents the results of a numerical and analytical study on the assessment of the crack driving force for discs containing surface flaws. The aim is to provide a simple, though reliable, tool in order to be able to calculate the possible dangerous in-service speed for a rotating component and, therefore, to set burst margins above the normal operating conditions of the equipment. An R6-like flaw assessment procedure is adopted considering different assumptions in the definition of the critical speed and the analytical predictions are compared with the results of elastic-plastic finite element analysis of disc. In particular, the validity and potentiality of the method is proved for surface flaws in different positions in the disc.
The paper gives an overview on safe life and damage tolerance methods applied to railway axles. It describes failure scenarios due to fatigue crack initiation and propagation. Besides common aspects of design, specific features such as corrosion and impact damage from flying ballast are discussed which may reduce the fatigue strength of axles during service. Potential effects of non-metallic inclusions from the steel manufacturing process are addressed in the context of the very high number of loading cycles railway axles are designed for. With respect to damage tolerance general lines of fracture mechanics residual lifetime analyses are introduced. More specific discussion is provided on aspects such as the threshold value of fatigue crack propagation and reliability aspects of non-destructive inspection.
The aim of this paper is a collection of stress intensity factor solutions for cracks in railway axle geometries which the authors of the present special issue developed and/or used for damage tolerance analyses. These solutions comprise closed form analytical as well as tabled geometry functions and they refer to solid as well as hollow axles and various crack sites such as the T- and V-notch and the axle body.
The cyclic R-curve describes the resistance of a material to fatigue crack propagation fromthe short to the long crack regimes and it is therefore an essential ingredient in any fracturemechanics-based fatigue assessment procedure. This work presents different testing proceduresemployed in the experimental determination of the cyclic R-curve, especially focusing onthe comparison with long fatigue crack propagation thresholds obtained by means of thecompression precracking load reduction (CPLR) procedure. The tests were performed on theEA4T steel considering different stress ratios. The results show a good reproducibility of thecyclic R-curves at every stress ratio and for any testing procedure. In addition, the cyclicR-curves were used in a fracture mechanics-based assessment to predict the fatigue limits ofspecimens containing micro-notches.