Selective Catalytic Reduction of Nitric Oxide by Ammonia over Egg-Shell MnOx/NaY Composite Catalysts
(2002)
A novel composite catalyst system for the selective catalytic reduction (SCR) of NOx by NH3 is described operating at temperatures lower than 470 K in the presence of water with NO conversions of 80100% at space velocities of 30,00050,000 h-1. The catalyst is prepared by egg-shell precipitation of MnO2 on the external surface of zeolite NaY. Structural and thermal stability of precipitated MnO2 as well as of the MnO2/NaY composite catalyst were characterized by N2 adsorption, X-ray diffraction, laser Raman spectroscopy, temperature-programmed reduction, and electron microscopy. MnO2 precipitated on zeolite NaY (15 wt% loading) retained its amorphous state up to calcination temperatures of 775 K. The zeolite component remained structurally intact. Calcination at higher temperatures destroyed the zeolite structure and transformed MnO2 into Mn3O4. DRIFT spectroscopic investigations revealed the presence of symmetric O=NON=O species formally corresponding to N2O3 on the composite catalyst after contact with NO. Catalytic measurements under integral flow conditions showed that the catalyst performance is associated with a close coupling of nitrite formation and its drain off from equilibria with NO/NO2 and nitrate by ammonia. Several results are in line with the diazotation mechanism, including NH3 protonation to NH4+, whereas prevailing Lewis acid sites should enable NH3 activation via amide species, thus leading to a parallel amide/nitrosamide SCR reaction route. The activity-temperature profile fulfills the requirements of a low-temperature NOx reduction catalyst for mobile diesel engines if an ammonia supply is implemented on board, e.g., by urea decomposition.
Composites containing 4-n-octyl-4?-cyanobiphenyl (8CB) either confined to nanopores of molecular sieves with very large pores or coating silica nanoparticles of aerosil type at high silica-to-8CB ratios are investigated by IR spectroscopy. Band shape analysis was performed in wavenumber regions in which the peaks due to CN stretching, CH stretching and CH out-of-plane vibrations appear. Some of molecules confined to molecular sieves show spectroscopic features characteristic to a bulk-like 8CB matter located in the centre of the pores or in the inter-grain space. Other features of the IR spectra are due to 8CB molecules located in the surface layer, mostly forming hydrogen bonds between their CN groups and surface OH groups. Another part of the 8CB molecules in the surface layer may also interact by ? electrons of the aromatic rings. Hydrogen bonding is less hindered for the molecules of the surface layers onto aerosil particles than inside pores of the molecular sieves. Comparison is also made with the case of composites based on molecular sieves with small pores.
As a model for spray drying the early stages of crystallization of complex molybdate catalyst precursors were monitored online in droplets levitated acoustically. Synchron X-ray scattering techniques were applied to study the drying process of a typical molybdate catalysts precursor prepared from Ni-,Fe-,Bi-nitrate, ammonium heptamolybdate and H3PO4. Comparison with diffraction patterns obtained from sessile droplets shows significant differences in the crystal growth, whereas the final crystal structure – including a Keggin-type anion – is identical in both cases. The levitated samples exhibit a decelerated growth with a large number of small crystallites at the beginning of the crystallization, whereas in case of the sessile droplets a small number of large crystallites were observed after a few minutes. The acoustic levitation using an ultrasonic trap proves to be an elegant tool to mimic spray drying and offers new possibilities in relation to the understanding of the drying process.
This work presents some results obtained by confining octylcyanobiphenyl (8CB) to the pores of two SBA-15 type host materials: a silica SBA-15 (pores of 10.2 nm) and an aluminum containing AlSBA-15 (pores of 7.5 nm). The LC molecules were loaded inside the pores from a solution in acetone, in a percentage higher than 70% from the maximum possible loading. It was observed that the 8CB molecules confined to molecular sieves may preserve the phase transitions characteristic for the bulk LC provided that the confining pores are sufficiently large, as offered by SBA materials. However, present guest-host interactions play an important role in these phase transitions. Such a behavior is at variance with the 8CB confined to Controlled Porous Glass with the same pore dimensions, for which the bulk-like phase transitions can be always observed.
A new setup is presented which enables simultaneous wide- and small-angle X-ray scattering (WAXS/SAXS) and Raman spectroscopic experiments during the synthesis of Mo-based mixed oxide catalyst precursors at the µ-spot beamline at the Berliner Elektronenspeicherring-Gesellschaft für Synchrotronstrahlung (BESSY). Furthermore, we report about the separate monitoring of the same reactions under comparable conditions by simultaneous combined ATR/UVvis/Raman spectroscopic measurements. For testing the performance of both experimental setups two syntheses were described comprising the precipitation of metal molybdates by mixing solutions of metal nitrates and ammonium heptamolybdate. Additionally, the effect of H3PO4 admixture on precipitation was investigated. The combined evaluation of spectroscopic and WAXS/SAXS data allows the discrimination between different molybdate species appearing in solution and precipitate. Furthermore, these molybdate species could be assigned to separate phases of different crystallinity.
Formation Mechanism of a Nano-Ring of Bismuth Cations and Mono-Lacunary Keggin-Type Phosphomolybdate
(2022)
A new hetero-bimetallic polyoxometalate (POM) nano-ring was synthesized in a one-pot procedure. The structure consists of tetrameric units containing four bismuth-substituted monolacunary Keggin anions including distorted [BiO8] cubes. The nano-ring is formed via self-assembly from metal precursors in aqueous acidic medium. The compound (NH4)16[(BiPMo11O39)4] ⋅ 22 H2O; (P4Bi4Mo44) was characterized by single-crystal X-ray diffraction, extended X-ray absorption fine structure spectroscopy (EXAFS), Raman spectroscopy, matrix-assisted laser desorption/ionisation-time of flight mass spectrometry (MALDI-TOF), and thermogravimetry/differential scanning calorimetry mass spectrometry (TG-DSC-MS). The formation of the nano-ring in solution was studied by time-resolved in situ small- and wide-angle X-ray scattering (SAXS/WAXS) and in situ EXAFS measurements at the Mo−K and the Bi−L3 edge indicating a two-step process consisting of condensation of Mo-anions and formation of Bi−Mo-units followed by a rapid self-assembly to yield the final tetrameric ring structure.