Multiple-sample approach: reliable ranking and validated statistics of bonding and adhesive strength
(2014)
Bonding strength of adhesive-bonded joints and adhesive strength of coatings have been exclusively determined in
single-sample tests using a tensile testing machine. Necessarily, the single-sample approach was also applied to the
corresponding bonding procedure. As a consequence, reliability and reproducibility of results were restricted. By
applying the newly introduced centrifuge technology, the multiple-sample approach was realized for simultaneous
tensile testing of up to eight samples under identical conditions without any disturbing shear-force effects. In order to
introduce the multiple-sample approach into the bonding procedure, a hydraulic bonding set-up was developed which
enables identical bonding pressure also for slightly different heights of sample assemblies. Both sample approaches
were compared for various application examples: ranking of different classes of adhesives, validated statistics of
adhesive-bonded joints using one particular adhesive and effects of cleaning and plasma-treatment on the adhesive
strength of coatings. The investigated systems included glass, metals and polymer substrates, different adhesives,
metallic and dielectric coatings on polymers.
Multiple-sample approach: reliable ranking and validated statistics of bonding and adhesive strength
(2014)
Bonding strength of adhesive-bonded joints and adhesive strength of coatings have been exclusively determined in single-sample tests using a tensile testing machine. Necessarily, the single-sample approach was also applied to the corresponding bonding procedure. As a consequence, reliability and reproducibility of results were restricted. By applying the newly introduced centrifuge technology, the multiple-sample approach was realized for simultaneous tensile testing of up to eight samples under identical conditions without any disturbing shear-force effects. In order to introduce the multiple-sample approach into the bonding procedure, a hydraulic bonding set-up was developed which enables identical bonding pressure also for slightly different heights of sample assemblies. Both sample approaches were compared for various application examples: ranking of different classes of adhesives, validated statistics of adhesive-bonded joints using one particular adhesive and effects of cleaning and plasma-treatment on the adhesive strength of coatings. The investigated systems included glass, metals and polymer substrates, different adhesives, metallic and dielectric coatings on polymers.
Standardised conventional adhesion tests are time-consuming single-sample tests. Moreover, except for the pull-off test, all these tests provide only qualitative or semi-quantitative (ranking, respectively measurement of an adhesion-correlated quantity) information on adhesion. Sometimes, adhesion is evaluated even under compressive stress conditions (e.g. cross-cut and scratch test), which itself is a contradiction to adhesive strength as defined in terms of tensile force per area.
For optical coatings it has been shown that the pull-off test in a centrifuge is definitely a promising alternative with respect to the reliable, fast and quantitative determination of adhesive strength in N/mm2. The force-controlled centrifuge test is the only multiple-sample test which provides reliable quantitative information on the adhesive strength in agreement with DIN EN 15870 and DIN EN ISO 4624 on a statistical basis for up to eight samples simultaneously tested under identical testing conditions.
The applicability of polymer-metal composites is mainly determined by the durability of the adhesive strength between both components. Aluminium (Al) deposited on polypropylene (PP) exemplifies different options of interface design. By deposition of plasma polymers on PP the effect of the type of the functionality was investigated. Spacer insertion was accomplished to position the functional group away from the topmost surface. A further kind of interface design involved a partial condensation of functional groups. Hydroxyl and carboxyl groups were most effective to improve adhesion in Al-PP systems. Approximately 7-10 carboxyl or 25-27 hydroxyl groups per 100 C atoms were necessary to increase the peel strength up to ~700 N/m. In this range, the failure of the composite propagated along the interface Al-tape (no peeling of the metal). Spacer molecules between surface and functional groups provoked the effect that the number of needed functional groups for maximum adhesion was strongly reduced. Linking of the functional groups resulted in non-peelable Al-PP laminates. Two adhesion tests were applied - the peel test and the centrifuge technology. For PP foils modified with chemically bonded and additionally linked silanol groups (no peeling) an adhesive strength of (2.5 ± 0.2) N/mm² was determined by centrifuge technology. XPS inspection of both fracture surfaces indicated a sub-surface failure in the polymer.