Functionality of optical systems requires optical coatings of
high quality which have to be adapted to the application in
terms of the performance of optical parameters such as
reflectivity (AR, low, defined, high), the substrate material of
interest (polymers, ceramics, and glass), the environmental
conditions (such as temperature or humidity), and the service
conditions (such spectral range and power density). Moreover,
in many cases, additional non-optical requirements have
to be met, including mechanical features such as scratch
resistance, hardness and modulus.
Consequently, thickness and overall uniformity requirements
are steadily increasing. In general, these demands can usually
not be achieved by a single film or coating. Instead, films with
specific design features (such as gradients), layer stacks and
multilayers are a prerequisite for high quality layers and their
reliability. For the development of such layer systems, a
versatile cluster deposition system consisting of three clusters
and a cluster-to-cluster handler has been designed. Besides a
PECVD cluster for DLC coatings, two PVD clusters implement
ion assisted electron beam evaporation and plasmabased
sputter technology. In addition to metallic films, preparation
of oxide and nitride optical coatings (SiO2, TiO2, Ta2O5,
ITO, Al2O3, TiN, AlN) in various process modifications (nonreactive,
partially reactive, full-reactive; rf-, dc-, mf- mode;
PEM control) has been carried out.
Within this paper, the effect of several process parameters on
layer quality (optical constants, density, and uniformity) is
discussed for selected applications examples (AR- and HR
coatings, applications at elevated temperatures and applications
of enhanced mechanical performance).
It has been shown that specific features of ion and plasma
assisted PVD processes, including ion-beam and plasma preand
post-treatment of substrates and layer systems, may
widen the application range and improve functionality features
of given coating/substrate systems.
Public, hidden, and forensic features either encoded or directly legible are used for authentication. Fabry-Perot layer stacks as information carriers in combination with imaging ellipsometry as optical read-out system provide all-in-one anti-counterfeiting capability that may establish the new security level 'encoded forensic'. Different layer designs are described with regard to all three security levels: public features (e.g. color and tilt effect) perceptible by the human eye, hidden features (e.g. spectroscopic response in the UV or IR), and forensic features (ellipsometric quantities Ψ and Δ as a function of wavelength λ and angle of incidence AOI). Physically uncloneable functions (PUF) could be realized as a result of a multi-material and a multi-parameter deposition approach as well as by means of specific design features of the Fabry-Perot layer stack. Hence, they are not subject to any reverse engineering strategies. Examples of stratified, micro-structured, and laser-modified Fabry-Perot layer systems are considered that may be used at all perception levels (e.g. human eye, bar code reader, and imaging ellipsometry) for authentication against product counterfeiting and related areas. --------------------------------------------------------------------------------------------------------------------
Zur Authentifizierung werden offene, versteckte und forensische Merkmale entweder codiert oder direkt auslesbar verwendet. Mit Fabry-Perot Schichtsystemen als Informationsträger in Kombination mit der abbildenden Ellipsometrie als optischem Auslesesystem steht ein 'all-in-one' Fälschungsschutz-System zur Verfügung, das ein neues Sicherheitsniveau 'kodiert-forensisch' darstellt. Es werden unterschiedliche Schichtdesigns beschrieben, mit denen alle drei Sicherheitsniveaus realisiert werden können: offene Merkmale (z.B. Farbe und Kippeffekt), die mit dem menschlichen Auge wahrnehmbar sind, versteckte Merkmale (z.B. die spektrale Antwort im Sichtbaren oder im IR) sowie forensische Merkmale (ellipsometrische Größen Ψ und Δ als Funktion der Wellenlänge λ und des Einfallswinkels AOI).
Physikalisch nicht klonbare Funktionen (PUF) können im Ergebnis einer Multi-Material- und Multi-Parameter Beschichtungsstrategie sowie durch spezifische Design-Merkmale des Fabry-Perot Schichtsystems realisiert werden. Folglich sind solche Schichtsysteme dem 'reverse engineering' nicht zugänglich. Es werden Beispiele für lateral ausgedehnte, mikrostrukturierte und Laser modifizierte Schichtsysteme auf verschiedenen Ausleseniveaus (menschliches Auge, Barcode-Lesegerät, abbildendes Ellipsometer) vorgestellt, die zur Authentifizierung von Produkten und verwandte Gebiete geeignet sind.
The irradiation of ~0.9-µm-thick hydrogenated amorphous carbon (a-C:H) layers deposited on silicon substrates with single femtosecond (fs) laser pulses (35 fs pulse duration, 790 nm centre wavelength) in air is studied experimentally. Irradiation spots have been generated with different peak fluences and subsequently investigated by optical topometry, micro Raman spectroscopy and microscale mechanical indentation in order to evaluate their microscopic, topographical, structural and mechanical properties (e.g. elastic modulus). By this multi-method approach, a clear separation of different effects (delamination and graphitisation) becomes possible. The joint application of mechanical and spectroscopic techniques provides unique insights into the effects of the fs-laser radiation on the carbon layer.
In this contribution we present a novel thermo-acoustic approach for the generation of broad band airborne ultrasound and investigate the applicability of resonance-free thermo-acoustic emitters for very short high pressure airborne ultrasound pulses. We report on measurements of thermo-acoustic emitter consisting of a 30 nm thin metallic film on a usual soda-lime glass substrate, generating sound pressure values of more than 140 dB at 60 mm distance from the transducer and compare the results with conventional piezoelectric airborne ultrasound transducers. Our experimental investigations show that such thermo-acoustic devices can be used as broad band emitters using pulse excitation.
The new promoted ignition combustion test apparatus at BAM matches the requirements of ASTM test method G 124 [ASTM G 124, Standard Test Method for Determining the Combustion Behavior of Metallic Materials in Oxygen-Enriched Atmospheres, 2003] and of EIGA publication, IGC Doc 13/02/E [EIGA Gas Association Document IGC Doc 13/02/E, Oxygen Pipeline Systems, 2003]. The test apparatus is most likely the only one in Europe. The test chamber allows investigations with pure oxygen or oxygen mixtures at pressures up to 500 bar and at temperatures up to 400°C at static or flowing gas conditions. The ignition device consists of an electrical ignition wire and a promoter. IR-sensors, distributed over the whole length of the rod, measure and record the burning temperature and allow measurement of the burn rate. A video system records the experiment for visual characterization of the burning behavior. BAM test results are compared with published data. Results on investigations with coated rods are presented. Ceramic coatings seem to be a solution for the use of certain less compatible metallic materials at higher oxygen pressures.
Two different test apparatuses are used at BAM to evaluate the safety of oxygen components: First, the promoted ignition combustion test according to ASTM G 124 [1] and to EIGA IGC Doc 13/02/E [2], and second, the new metallic disk ignition test that has not been standardized yet. The standard test method ASTM G 124 allows a ranking of metallic materials for use at high pressure oxygen. However, the transfer of those test results to valves and fittings in real-life situations is rather complex. The metallic disk ignition test, developed at BAM, is more practice oriented and uses metallic disks of different thicknesses of the investigated material. A commonly used nonmetallic sealing ring is placed in front of this disk and serves as an igniter. This test array is then exposed to high pressure gaseous oxygen impacts in a standardized pneumatic impact tester according to DIN EN 1797 [3].
Hydrogen-Containing Amorphous Carbon Layers as Optical Materials in the Near-IR Spectral Range
(2007)
Hydrogenated amorphous carbon layers were deposited on various substrates by means of a plasma CVD process with a RF substrate bias as well as an ECR plasma source. The optical properties of the a-C:H layers were obtained via spectroscopic ellipsometry and correlated with their mechanical and chemical properties. The layers from pure RF plasma exhibit a higher absorption constant in the visible spectral range and a higher refractive index. All layers are nearly transparent in the NIR spectral range making them candidates for optical thin layer systems. The laser damage behaviour of the a-C:H layers was investigated with ultrashort pulses. The damage thresholds were consistent with the absorption constants of the layers. Interesting damage morphologies were observed indicating a sensitivity of this experiment to sub-structures in the layer.
Embedding of information on surfaces is state of the art for identification testing in which public, hidden and forensic features are used. In many instances, the legal authentication of a product, a material or a document is required. Among the surface-based encoded labels, bar codes and data matrices are most frequently applied. They are publicly visible. The material itself is irrelevant, only a sufficient optical contrast is required.
However, a strong material dependence of the label can be achieved by means of Fabry-Perot layer stacks. Stack designs are described with regard to all three security levels: public features (e.g. color and tilt effect) perceptible by the human eye, hidden features (e.g. optical response in a given spectral range) detectable by commonly available instruments and forensic features (ellipsometric quantities Ψ and Δ as a function of wavelength λ and angle of incidence AOI) only detectable by sophisticated instruments.
Regarding material-correlated authentication, ellipsometric quantities Ψ and Δ are used as encoded forensic features for the first time. Hence, Fabry-Perot layer stacks as information carriers in combination with imaging ellipsometry as optical read-out system provide all-in-one anti-counterfeiting capabilities.
Standardised conventional adhesion tests are time-consuming single-sample tests. Moreover, except for the pull-off test, all these tests provide only qualitative or semi-quantitative (ranking, respectively measurement of an adhesion-correlated quantity) information on adhesion. Sometimes, adhesion is evaluated even under compressive stress conditions (e.g. cross-cut and scratch test), which itself is a contradiction to adhesive strength as defined in terms of tensile force per area.
For optical coatings it has been shown that the pull-off test in a centrifuge is definitely a promising alternative with respect to the reliable, fast and quantitative determination of adhesive strength in N/mm2. The force-controlled centrifuge test is the only multiple-sample test which provides reliable quantitative information on the adhesive strength in agreement with DIN EN 15870 and DIN EN ISO 4624 on a statistical basis for up to eight samples simultaneously tested under identical testing conditions.
Reinigung wird in der Lebensmittel- und Pharmaindustrie aufgrund des stetig steigenden Kosten- und Zeitdrucks sowie der hohen Verbrauchererwartungen hinsichtlich Produktsicherheit und -haltbarkeit ein immer zentraleres Thema. Eine verbesserte Reinigbarkeit bedeutet für die produzierende Industrie eine Steigerung der Effizienz der Produktionsanlage. Besonders in der heutigen medienintensiven Zeit kommt ein "Lebensmittelskandal" durch ein unsicheres Produkt einem finanziellen Desaster und immensem Imageverlust gleich. Aus diesem Grund ist die Reinigbarkeit der produktberührenden Oberflächen stets ein wichtiges Kriterium für die Werkstoffauswahl.
Basierend auf den Theorien zu Schmutzhaftung und -entfernung wurde im Rahmen dieser Arbeit überprüft, ob und wie die theoretisch relevanten Parameter auch in den Experimenten den Reinigungserfolg beeinflussen. Der Schwerpunkt wurde auf die Einflussgrößen des Werkstoffes gelegt, um herauszufinden, wie stark eine Oberfläche selbst zu ihrer Reinigbarkeit beitragen kann (self-cleaning).
In den durchgeführten Versuchen hat sich gezeigt, dass die Oberflächenrauheit lediglich bei der Reinigung von kohäsiven Schmutzfilmen eine entscheidende Rolle gespielt hat. Hingegen ist ihr Einfluss auf das Reinigungsergebnis von sich auflösenden Schmutzfilmen und Partikeln nur begrenzt bis gar nicht zur Geltung gekommen. Das Oberflächenmaterial hatte keinen starken, aber dennoch signifikanten Einfluss auf die Reinigbarkeit der untersuchten Oberflächen. Dass die Reinigbarkeit einer Oberfläche keine Materialkonstante sein kann, wurde unter Verwendung spezieller Oberflächen mit definiert geätzten Rauheitsstrukturen nachgewiesen. Der Reinigungserfolg hängt immer auch von der Verunreinigungsart ab, was sich auch in vergleichbaren Versuchen der Einzelpartikelablösung mittels AFM in dem Einfluss der Elastizität bzw. Plastizität der Partikeln geäußert hat.
Praxistaugliche Empfehlungen gehören mit zu den wichtigsten Zielen dieser Arbeit gewesen. Mit Fokus auf die Oberflächenparameter und auf Basis der durchgeführten Untersuchungen wurde zur Optimierung der Reinigung produktberührender Oberflächen für bekannte Kontaminationen eine Checkliste als Orientierungshilfe erarbeitet. Ist die Verunreinigungsart dennoch unbekannt, so sollte der "Grenzwert" von Ra = 1 µm unterschritten werden, um bei Vorhandensein filmartiger Verschmutzungen keine negativen Auswirkungen auf die Reinigbarkeit zu haben. Die Notwendigkeit nach hochpolierten Oberflächen (Ra < 0,3 µm) aus Reinigbarkeitsgründen kann aufgrund der Untersuchungen nicht nachvollzogen werden.
Das Ziel des Vorhabens wurde erreicht.
The extremely low acoustic impedance of polypropylene ferroelectret combined with its piezoelectric properties makes this material suitable for construction of aircoupled ultrasonic transducers for non-destructive testing. For the fabrication of transducers with a stable quality, the reproducibility of their key parameters is of interest.
The reproducibility was evaluated by means of (i) impedance spectroscopy and (ii) pulse-echo measurements. (i) Impedance spectroscopy was applied to identify the resonance frequency, the coupling factor and the acoustic impedance of several nominally identical transducers. (ii) Pulse-echo measurements yielded the signal form of these transducers.
The variation of the signal amplitude measured with pulseecho technique was about 10 dB. A part of this variation Comes from the deposition of transducer electrodes and another part from local variations of ferroelectret properties. The variation of the signal amplitude was caused by the observed variation of the coupling factor, which was also about 10 dB. The variation of the acoustic impedance was only about 1 dB, thus having no effect on the variation of the signal amplitude.
These results indicate that the variability can be reduced by improving the control of electrode deposition and by optimizing the production technology affecting the reproducibility of material properties.
A novel approach for the generation of broadband airborne ultrasound by using the thermo-acoustic effect is presented in this contribution. We investigate the applicability of resonance-free thermo-acoustic emitters for generation of very short high pressure airborne ultrasound pulses. A thermoacoustic emitter consisting of a 30 nm thin metallic film on a usual soda-lime glass substrate generates sound pressure values of more than 140 dB at 60 mm distance. The results are compared with conventional piezoelectric airborne ultrasound transducers. Our investigations show the applicability of the thermo-acoustic devices for broadband and high pressure ultrasound emitters using pulse excitation.
Novel air-coupled ultrasonic transducer combining the thermoacoustic with the piezoelectric effect
(2016)
In recent years, there has been an increasing industrial demand for one-sided inspection of various structures by means of air-coupled ultrasonic technique. Lightweight structures based on carbon-fibre-reinforced polymers may have very complex shapes, making air-coupled transmission difficult or even impossible. The inspection of concrete structures is another example where one-sided inspection is required.
To address these challenges a new type of transducer for air-coupled pulse-echo inspection was developed, which unites two principles: thermoacoustic emission and piezoelectric reception. The thermoacoustic emitter is a titanium electrode with a thickness of several tens of nanometer. This electrode was deposited onto charged cellular polypropylene, which serves as a piezoelectric receiver. The thermoacoustic transmission is based on a transformation of the thermal energy of an electrically heated electrode into the acoustic energy of an ultrasonic wave. Thermoacoustic emitters provide resonance-free behaviour and thus extremely broadband pulses. Charged cellular polypropylene is piezoelectric due to the polarization of its cells and it is well matched to air, with a Young modulus in the order of magnitude of MPa. In this contribution we present some pulse-echo measurements with the first prototypes of the combined thermoacoustic-piezoelectric transducer.
Multiple-sample approach: reliable ranking and validated statistics of bonding and adhesive strength
(2014)
Bonding strength of adhesive-bonded joints and adhesive strength of coatings have been exclusively determined in
single-sample tests using a tensile testing machine. Necessarily, the single-sample approach was also applied to the
corresponding bonding procedure. As a consequence, reliability and reproducibility of results were restricted. By
applying the newly introduced centrifuge technology, the multiple-sample approach was realized for simultaneous
tensile testing of up to eight samples under identical conditions without any disturbing shear-force effects. In order to
introduce the multiple-sample approach into the bonding procedure, a hydraulic bonding set-up was developed which
enables identical bonding pressure also for slightly different heights of sample assemblies. Both sample approaches
were compared for various application examples: ranking of different classes of adhesives, validated statistics of
adhesive-bonded joints using one particular adhesive and effects of cleaning and plasma-treatment on the adhesive
strength of coatings. The investigated systems included glass, metals and polymer substrates, different adhesives,
metallic and dielectric coatings on polymers.
Multiple-sample approach: reliable ranking and validated statistics of bonding and adhesive strength
(2014)
Bonding strength of adhesive-bonded joints and adhesive strength of coatings have been exclusively determined in single-sample tests using a tensile testing machine. Necessarily, the single-sample approach was also applied to the corresponding bonding procedure. As a consequence, reliability and reproducibility of results were restricted. By applying the newly introduced centrifuge technology, the multiple-sample approach was realized for simultaneous tensile testing of up to eight samples under identical conditions without any disturbing shear-force effects. In order to introduce the multiple-sample approach into the bonding procedure, a hydraulic bonding set-up was developed which enables identical bonding pressure also for slightly different heights of sample assemblies. Both sample approaches were compared for various application examples: ranking of different classes of adhesives, validated statistics of adhesive-bonded joints using one particular adhesive and effects of cleaning and plasma-treatment on the adhesive strength of coatings. The investigated systems included glass, metals and polymer substrates, different adhesives, metallic and dielectric coatings on polymers.
Hydrogenated amorphous carbon layers were deposited on BK7 glass in a plasma-assisted chemical vapor deposition
process. Low and high refracting films with thicknesses d ranging from 11 nm to 5.8 µm were produced having refractive
indices n between 1.68 and 2.41 and linear absorption coefficients of α~100 cm-1 and α~20000 cm-1 at 800 nm wavelength as a result of different plasma modes. Laser ablation thresholds Fth in dependence on d were determined using 30-fs laser pulses. Low absorbing layers show a constant Fth while Fth increases with rising d up to the optical penetration depth of light α-1 for high absorbing films.
The synthesis of polymerlike amorphous carbon (a-C:H) thin-films by microwave excited collisional hydrocarbon plasma process is reported. Stable and highly aromatic a-C:H were obtained containing significant inclusions of poly(p-phenylene vinylene) (PPV). PPV confers universal optoelectronic properties to the synthesized material. That is a-C:H with tailor-made refractive index are capable of becoming absorption-free in visible (red)-near infrared wavelength range. Production of large aromatic hydrocarbon including phenyl clusters and/or particles is attributed to enhanced coagulation of elemental plasma species under collisional plasma conditions. Detailed structural and morphological changes that occur in a-C:H during the plasma synthesis are also described.
Die Oberflächentechnik ist eine Schlüsseltechnologie in nahezu zu allen industriellen Branchen. Mit Ausnahme der mechanischen Stabilität, die das Substrat bereitstellt, werden verschiedenartigste Funktionen materialsparend, zum Teil hochintegriert mit maßgeschneiderten Schichtdesigns unter Ausnutzung von Nano- und Quanteneffekten auf Oberflächen appliziert. Ein Großteil der Fertigungskosten in der Mikro- und Nanotechnik wird durch Reinräume und die Umsetzung ausgeklügelter Reinigungsstrategien zur Vermeidung von Restverschmutzungen und partikulären Belegungen
verursacht, da diese unweigerlich zum Bauteilversagen führen. Die Validierung des Reinigungszustandes ist somit von zentraler Bedeutung für die Schichtqualität und Produktfunktionalität. Dies gilt in Abhängigkeit von der Applikation und den vertikalen Schicht- bzw. lateralen Strukturdimensionen sowohl für Fertigungsprozesse im Reinraum als auch für solche in robuster Umgebung. In der Praxis kommt es häufig vor, dass man mikroskopisch scheinbar saubere Substrate erst durch die Beschichtung „enttarnt" und dann Defekte oft mit bloßem Auge sichtbar werden. Noch problematischer ist der Einbau von Verunreinigungen während der Schichtabscheidung, die zunächst nicht sichtbar sind, dann aber zum Bauteilversagen führen.
In Glasfasern eingeschriebene Bragg-Gitter (FBG: fibre-based Bragg gratings) sind über die Verschiebung der Bragg-Wellenlänge in der Lage, Stauchungen und Dehnungen von Glasfasern hochgenau zu erfassen. In Kompositwerkstoffe eingebettete faseroptische Sensoren können Bauteile bezüglich ihrer mechanischen Integrität überwachen und früh-zeitig Informationen über Materialveränderungen gewinnen.
Um die Zuverlässigkeit eines solchen Sensors zu gewährleisten, ist es wichtig, die korrekte Funktion des Sensors im Verbund mit der Werkstoff-Matrix on-line und in-situ sicherzu-stellen. Im Rahmen des DFG-Projekts FAMOS² (FAser-basierter Magneto-Optischer SchichtSensor) wurde ein selbstdiagnosefähiger Schichtsensor entwickelt, der mit Hilfe von magnetostriktiven Aktorschichten aus Nickel bzw. Eisen-Nickel validiert werden kann.
Der FAMOS²-Schichtsensor wird durch ein PVD (physical vapour deposition)/ECD (electro-chemical deposition) Hybridschichtsystem realisiert, das auf dem Fasermantel im Bereich des FBG haftfest, homogen und langzeitfunktional abzuscheiden ist. Dabei wird in einem ersten Schritt ein etwa 100 Nanometer dünnes PVD-Schichtsystem aus Chrom und Kupfer als Haftvermittler auf der Glasfaser bzw. als leitfähige Startschicht für den nachfolgenden ECD-Prozess abgeschieden. Um eine rotationssymmetrische Schich-tabscheidung zu gewährleisten, erfolgt während der PVD-Beschichtung eine Rotation der Glasfasern. In einem zweiten Schritt wird dann unter Verwendung eines klassischen Watts-Elektrolyten in einer speziell entwickelten ebenfalls rotationssymmetrisch aufgebau-ten ECD-Durchströmungszelle dann die etwa 30 Mikrometer dicke, magnetostriktive Ak-torschicht auf dem PVD-Schichtsystem abgeschieden, im Vergleich sowohl reine Nickel-Schichten als auch Nickel-Eisen-Schichten.
Ein äußeres Magnetfeld dehnt die magnetostriktive Aktorschicht und damit auch die Faser reversibel. Diese Dehnung führt zu einer Verschiebung der Bragg-Wellenlänge, welche direkt mit der Stärke eines zu messenden oder zu Validierungszwecken vorgegebenen Magnetfeldes korreliert. Die Anpassung der Beschichtungsverfahren an die Fasergeome-trie und die mechanischen Eigenschaften der Hybridschichten werden hinsichtlich der me-chanischen Integrität des faseroptischen Sensors diskutiert und der Nachweis der Selbst-diagnosefähigkeit erbracht.
Auf dem Weg zu Industrie 4.0: Bestimmung von Messunsicherheitsbudgets in der Oberflächentechnik
(2019)
Vorgestellt wurde die Bestimmung von Messunsicherheitsbudgets für sehr unterschiedliche physikalische Größen, die in der Oberflächentechnik von hoher Relevanz sind: Stufenhöhe h, Schichtdicke d, Eindringhärte HIT und Haftfestigkeit. Die Unterschiede betreffen die Art der Prüfmethodik (optisch zerstörungsfrei vs. mechanisch invasiv/zerstörend), die laterale Größe des Integrationsgebietes der Messung (lokal: nano bis sub-mikro vs. global: mikro bis makro) und die Art der Bestimmung von Messunsicherheitsbudgets (physikalische Größen: direkt rückführbar; Werkstoffkenngröße: genormt; Systemkenngröße: genormt).
Im Rahmen von Industrie 4.0 werden ausgehend der geforderten Spezifikation des beschichteten Produkts (Mittelwert mit Vertrauensbereich oder Mindestwert) durchgehende Toleranzbänder zur Oberflächenmodifizierung/Beschichtung des Substrats, einhergehend mit Prozessfenstern, die diese Toleranzbänder garantieren, erforderlich, die zuverlässig erfasst werden müssen. Die Frage der anzuwendenden Mess- und Prüftechnik und die damit notwendige Betrachtung von Messunsicherheitsbudgets ist für die Digitalisierung von Konditionierungs-, Zustands-, Regel- und Steuergrößen unverzichtbar. Mit Blick auf die Einhaltung von Prozessfenstern und die dafür notwendige Prozessführung wird technologisches Kern-Know-how digitalisiert, das es unbedingt zu schützen gilt. Nur lokale Netze können diese Sicherheit garantieren, in globalen Netzen ist die Datensicherheit bestenfalls maximierbar
Most of the polymeric materials used are easy to ignite and show extensive flame spread along their surfaces. Apart from extensive heat release rates, their short time to ignition (tig), in particular, is a key fire hazard. Preventing ignition eliminates fire hazards completely. Protection layers that shift tig by more than an order of magnitude are powerful flame retardancy approaches presenting an alternative to the usual flame retardancy concepts.
Coatings are proposed that consist of a three-layer system to ensure adhesion to the substrate, acting as an infrared (IR) mirror and protecting against oxidation. The IR-mirror layer stack is realised by physical vapour deposition in the sub-micrometre (<1 µm) range, reducing heat absorption by up to an order of magnitude. Not only is the ease of ignition diminished (tig is increased by several minutes), the flame spread and fire growth indices are also remarkably reduced to as little as 1/10 of the values of the uncoated polymers open for further optimization. Sub-micrometre thin IR-mirror coatings yielding surface absorptivity <0.1 are proposed as a novel and innovative flame retardancy approach.