The paper presents the damage model of German Research Unit 537 which was used as a working hypothesis for the development of a user-friendly design model. Excerpts from the laboratory experiments and numerical calculations processed in project A of the research unit are presented here. The excerpts include the quantification of self-corrosion, geometrical effects in the macrocell corrosion, development of corroding steel surface and pit depth as well as the quantification of the resistivity of the concrete and the corrosion of steel in cracked concrete.
Electrochemical noise measurements on unalloyed steel in chloride-containing alkaline environment
(2007)
The investigations discussed in this paper aim to clarify whether electrochemical noise measurements (ENM) are capable for application in concrete and mortar, particularly with regard to pitting initiation in such environment. For these purposes, the results of several different test series are compared and discussed. Based on investigations on passivity and pitting corrosion in alkaline solutions with different chloride contents further results in cement paste, mortar and concrete are evaluated.
Modelling of reinforcement corrosion - Influence of concrete technology on corrosion development
(2006)
Reinforcement corrosion is influenced by different parameters like resistivity of concrete, setting conditions and also by concrete technology. Moreover the presence of cathodic areas and the possibility of unhampered cathodic reaction influences the reinforcement corrosion. In this paper the development of corrosion without large cathodic areas, called self-corrosion, considering different concrete parameters, is studied.
Corrosion of steel reinforcement in concrete exposed to chloride containing environments is a serious problem in civil engineering practice. Electrochemical methods, e.g., potential mapping, provide information whether the steel reinforcement is still passive or depassivation has been initiated. By applying such techniques no information on the type of corrosion, its extent and distribution of corrosion products is available. Particular the corrosion progress is a significant problem. Especially in the case of macrocell corrosion in reinforced concrete structures, the development at the anode cannot be separated into corrosion damage resulting from macrocell corrosion or self-corrosion. Until now also in laboratory tests it is impossible to collect such information without destroying specimens after electrochemical testing was performed. To overcome this problem it was tried to study the steel surface within the mortar specimens by X-ray tomography (CT). Within the scope of these investigations it could be shown, that X-ray tomography is suitable to make corrosion pits and their development visible which are embedded in a mortar with a cover thickness of about 35 mm. In this publication the time-dependent corrosion damage of reinforced steel is documented by X-ray tomography.