High sensitivity is an important requirement for air-coupled ultrasonic sensors applied to materials testing. With a lower acoustic impedance than any piezoelectric material, charged cellular polypropylene (PP) offers better matching to air with a similar piezoelectric coefficient. The piezoelectric properties of charged cellular PP originate from their polarization, creating permanent internal voltage. The sensitivity of the sensor can be increased by applying additional dc bias voltage, as it has been done already for transmitters. This work presents the first ultrasonic sensor based on charged cellular PP including a high-voltage module providing dc bias voltage up to 2 kV. This bias voltage led to an increase in the signal-to-noise ratio of up to 15 ± 1 dB. The measurement of the received signal depending on the applied bias voltage is proposed as a new method of determining the internal voltage of ferroelectrets. The sensor combined with a cellular PP transmitter was applied to nondestructive testing of a rotor blade segment and glued-laminated timber, enabling imaging of the internal structure of these specimens with a thickness around 4 cm.
Air-coupled ultrasound has been applied increasingly as a non-destructive testing method for lightweight construction in recent years. It is particularly appropriate for composite materials being used in automotive and aviation industry. Air-coupled ultrasound transducers mostly consist of piezoelectric materials and matching layers. However, their fabrication is challenging and their signal-to-noise ratio often not sufficient for many testing requirements. To enhance the efficiency, air-coupled ultrasound transducers made of cellular polypropylene have been developed. Because of its small density and sound velocity, this piezoelectric ferroelectret matches the small acoustic impedance of air much better than matching layers applied in conventional transducers. In our contribution, we present two different methods of spherical focusing of ferroelectret transducers for the further enhancement of their performance in NDT applications. Measurements on carbon-fiber-reinforced polymer (CFRP) samples and on metal adhesive joints performed with commercially available focused air-coupled ultrasound transducers are compared to measurements executed with self-developed focused ferroelectret transducers.
Airborne ultrasonic inspection is performed in through transmission, where the test piece (e.g. adhesive joint or polymer-based composite plate) is placed between the transmitter and the receiver. However, many structures with difficult shapes allow only one-sided inspection. The strong reflection of the signal from the surface overshadows the signals from the inside, so that broadband pulses are required. Thermoacoustic transmission, where the thermal energy of an electrically heated electrode is transformed into the acoustic energy of an ultrasonic wave, opens the possibility to excite broadband pulses and thus to inspect objects with one-sided access.
We present various thermoacoustic transducers consisting of an electrically conductive film on a solid substrate. The first type of transducer is a transmitter with an indium-tin-oxide electrode on a glass substrate combined with a laser Doppler vibrometer as a receiver. The second type of transducer combines thermoacoustic transmission and piezoelectric reception, having a titanium electrode as a transmitter deposited onto charged cellular polypropylene serving as a piezoelectric receiver.
Using a focusing thermoacoustic transmitter and a separate cellular polypropylene receiver, a through-transmission inspection of a 4 mm thick CFRP test piece with inserts as small as 1 mm was performed. The same emitter and a laser vibrometer as a receiver were used for a one-sided inspection of a Plexiglas block with a cross hole at 15 mm depth. A twin probe consisting of a thermoacoustic transmitter on a cellular polypropylene receiver was applied to a profile measurement on a step wedge with flat bottom holes. The smallest detected diameter of a flat bottom hole was 1 mm. Sound pressure level above 140dB was achieved with each of these transmitters. Thermoacoustic transmitters enable a step towards one-sided air-coupled ultrasonic inspection.
Adhesively bonded aluminum components have been widely used in the aerospace industry for weight-efficient and damage-tolerant structures. Automated squirter jet immersion ultrasonic testing is a common inspection technique to assure the bond integrity of large, contoured assemblies. However, squirter jet inspection presents several limitations in scanning speed, related to water splash noise over protruding stiffeners and splash interference crosstalk in multi-channel inspection systems. Air-coupled ultrasonic testing has been evaluated as an alternative, possibly offering the benefits of increased throughput by enabling higher speeds, and eliminating the contamination concerns and maintenance issues of water couplant systems. Adhesive joints of multi-layer aluminum plates with artificial disbonds were inspected with novel air-coupled ultrasonic probes based on cellular polypropylene. Disbonds of various sizes were engineered in several multi-layer configurations and at various depths. Results were compared with squirter jet immersion and conventional piezoelectric transducer designs in terms of scan contrast, resolution and inspection time.
Ultrasonic testing of adhesively bonded joints using air-coupled cellular polypropylene transducers
(2014)
In air-coupled ultrasonic testing, the impedance mismatch between the transducer and the air is commonly being solved by adding matching layers to composite transducers. To avoid the difficult technological procedure regarding matching layers, some new piezoelectric materials have been proposed. Most promising are ferroelectrets, which are charged cellular polymers, having ferroelectric and consequently piezoelectric properties. In particular, the extreme softness of cellular polypropylene (cPP) leads to a high piezoelectric constant and to a good impedance match with the air, making matching layers redundant. Its elasticity modulus below 1 MPa causes an additional effect not observed with common piezoelectric materials: that is the electrostrictive effect, here defined as the thickness change due to the attractive force between the transducer electrodes. This effect exceeds the piezoelectric effect at excitation voltages over 1 kV. The extreme softness of cPP leads also to high flexibility, enabling easy focusing by bending the transducer.
We have developed air-coupled ultrasonic transducers based on cPP. This includes the electrical matching networks for the transmitter and for the receiver. The transmitter is excited with voltages up to 2.5 kV, so that the electrostrictive effect dominates, leading to sound pressure around 145dB at the transducer surface. These transducers have been applied for testing carbon-fiber-reinforced polymer plates, adhesive joints and other composite structures. Here we report about ultrasonic transmission of two types of adhesive joints. The first one is multi-layer aluminium components with some artificial disbonds, which are common in aerospace industry, and the second one is an aluminium-steel joint with polyurethane adhesive, which is used in automotive industry.
Polypropylene based ferroelectret films exhibit a strong electromechanical activity and provide a promising solution for the air coupled ultrasonic (ACUS) transducers. Ultrasonic transmission between two air coupled ferroelectret transducers in dependence on the amplitude and polarity of the high voltage exciting pulse revealed a strongly non-linear electromechanical response of the ferroelectret transmitter which provides an increase in the transmitter efficiency. The authors present a simple model describing both promotion and competition of the piezoelectric and electrostriction contributions, as well as increase in the transducer constant under high voltage excitation. Enlargement of the inverse transducer constant of the polypropylene ferroelectret film by a factor of 4 was demonstrated. The non-linear properties of the polypropylene ferroelectrets result in a strong increase in their ACUS figure of merit under the high voltage excitation, which exceeds the results of their technological optimisation. Consequently, enhancement of the ACUS system transmission by 12 dB and signal to noise ratio by 32 dB was achieved.
Ferroelectrets are promising materials for air-coupled ultrasonic transducers. A transducer made of polarized cellular polypropylene, including its electronic interface, was developed and compared with conventional air-coupled probes. Test pieces of fiber-reinforced polymer containing impact flaws and flat-bottom holes were inspected in transmission. The ferroelectret transducers achieved a considerably higher signal-to-noise ratio. The impacts were clearly visible with all transducers, but less noisy with ferroelectret transducers. The flat-bottom holes were better detectable than with a conventional probe with about the same focus size.
Für die luftgekoppelte Ultraschall-Prüfung wird der Prototyp eines neuartigen Prüfkopfes vorgestellt. Statt eines piezokeramischen Ultraschall-Wandlers mit einer λ/4-Anpassschicht wird eine Ferroelektret-Folie aus schaumförmigem Polypropylen eingesetzt. Durch die außerordentlich geringe akustische Impedanz der Folie reduzieren sich die Reflexionsverluste an den Grenzschichten zur Luft so stark, dass bei diesem Prüfkopf auf eine λ/4-Anpassschicht verzichtet werden kann. Außerdem ist die Folie hochspannungsfest. Sie konnte mit Spannungen von mehr als 3500 V angesteuert werden und erlaubte eine Vorspannung am Ultraschall-Wandler des Empfangsprüfkopfes von 2000 V. Mithilfe der hohen Anregungsspannung stieg die Amplitude des akustischen Prüfimpulses auf das 11,2-Fache. Die Empfindlichkeit des Empfängers erhöhte sich durch die Vorspannung weiter um den Faktor 4,3. Insgesamt steigt die Amplitude am Empfänger also auf das 48-Fache, bei gleichbleibendem Rauschpegel. Ein abschließender Vergleich mit kommerziellen Luftultraschall-Prüfköpfen belegt die Überlegenheit der Folien-Prüfköpfe. Damit rückt der Einsatz einer vollwertigen Impuls-Echo-Technik auch bei der luftgekoppelten Ultraschallprüfung deutlich näher.
Electromechanical response of polypropylene ferroelectret transducers under application of high-voltage pulses was measured by laser Doppler vibrometry and compared with results of ultrasonic through-air transmission between two ferroelectret transducers. The electromechanical response was completely explained by piezoelectric and electrostrictive effects. The electrostrictive effect dominates at high voltages and provides significant enlargement of the transducer constant, up to factor of 2.5. The induced strain of 1.7% was achieved at – 2000 V. The nonlinear ultrasonic transmission was shown to be well described by the piezoelectric and electrostrictive response of transmitter, except in the range of high negative exciting voltages where some limitation of the transmitted signal was observed. This limitation seems not to be a fundamental one and does not abolish the advantages of high-voltage excitation of polypropylene ferroelectret transducers.
The extremely low acoustic impedance of polypropylene ferroelectret combined with its piezoelectric properties makes this material suitable for construction of aircoupled ultrasonic transducers for non-destructive testing. For the fabrication of transducers with a stable quality, the reproducibility of their key parameters is of interest.
The reproducibility was evaluated by means of (i) impedance spectroscopy and (ii) pulse-echo measurements. (i) Impedance spectroscopy was applied to identify the resonance frequency, the coupling factor and the acoustic impedance of several nominally identical transducers. (ii) Pulse-echo measurements yielded the signal form of these transducers.
The variation of the signal amplitude measured with pulseecho technique was about 10 dB. A part of this variation Comes from the deposition of transducer electrodes and another part from local variations of ferroelectret properties. The variation of the signal amplitude was caused by the observed variation of the coupling factor, which was also about 10 dB. The variation of the acoustic impedance was only about 1 dB, thus having no effect on the variation of the signal amplitude.
These results indicate that the variability can be reduced by improving the control of electrode deposition and by optimizing the production technology affecting the reproducibility of material properties.