The cone calorimeter has become one of the most important and widely used instruments for the research and development of fire retarded polymeric materials. The paper addresses three important ways in which the principal setup influences the results factors which sometimes do not receive due consideration when drawing conclusions. The paper discusses in detail the impact on cone calorimeter results of the choice of external heat flux, the influence on the peak of heat release rate of sample thickness and thermal feedback from the back of the sample, and the influence on irradiance of the horizontal and vertical distances from the cone heater.
Barrier formation and increasing the melt viscosity are addressed as the two main general fire retardancy mechanisms of polymer nanocomposites. They result in specific impacts on fire properties that consequentially cause varying flame retardancy efficiency in different fire tests. The barrier formation retards mainly flame spread (peak of heat release rate) in developing fires, but does not reduce fire load (total heat evolved), ignitability or flammability (limiting oxygen index, UL 94). Furthermore, this flame retardancy effect increases with increasing irradiation and vanishes with decreasing irradiation. The increased melt viscosity prevents dripping, which is beneficial or disadvantageous depending on the fire test used. In some test, it become the dominant influence, transforming self-extinguishing samples into flammable materials or causing wicking. Advantages and the limits are sketched comprehensively for exploiting the main general fire retardancy mechanisms of polymer nanocomposites. It is concluded that barrier formation and changing the melt viscosity in nanocomposites are not sufficient for most applications, but must be accompanied by additional mechanisms in special systems or in combination with other flame retardants.
Nanocomposites of bisphenol A polycarbonate with 2, 4, 6, and 15 wt% multiwall carbon nanotubes (MWNT) and their use in fire retardancy are investigated. Their thermal behavior and pyrolysis are characterized using thermogravimetry, differential scanning calorimeter, oscillatory shear rheology, and dynamic mechanical analysis. The flammability is addressed using LOI and UL 94; the fire behavior, with a cone calorimeter using different irradiation. With increasing MWNT content the storage modulus is increased (10-20%) and melt viscosity increases by several orders of magnitude, particularly for low shear rates. The melt flow, dripping, and deformation during fire are hindered, which influences UL 94 and cone calorimeter results. The peak heat release rate is reduced up to 40-50% due to an improved barrier for small amounts (2 wt%) of MWNT and for low irradiation, whereas the effect is reduced for increasing irradiation and nearly vanishes for increasing filling. Adjuvant but also deleterious mechanisms result in the complex dependency on the MWNT content. Significant flame retardancy effects are specific and limited to only some fire properties. This study allows the materials' potential for implementation in different fire scenarios and tests to be assessed and provides insight into active mechanisms.