In this paper, we demonstrate the effects of radiation exposures of polymeric materials with UV-A 340 nm lamps (ISO 4892-3, Type 1A) at -10 °C in comparison to an irradiation at +50 °C using a Global UV Test 200 fluorescent lamp device from Weiss Umwelttechnik GmbH, which incorporates an active cooling appliance. While the effects at -10 °C actually are lower than at + 50°C their extent was clearly beyond expectations.
Durch das Füllen von Polymeren mit Nanopartikeln oder Nanoröhren werden verbesserte Materialeigenschaften z.B. bezüglich mechanischer Stabilität, Witterungsbeständigkeit, elektrischer Leitfähigkeit und Flammschutz angestrebt. Mit dem vermehrten Einsatz derartiger Nanokomposite gewinnen aber auch Fragen des Umwelt- und Gesundheitsschutzes an Bedeutung. Es gilt zu klären, ob durch Herstellung, Benutzung und Witterungsbeanspruchung möglichweise nanoskalige Partikel freigesetzt werden können. Zu diesem Zweck wurden mit Kohlenstoffnanoröhren, Carbon Nanotubes (CNT), gefüllte Polymerkomposite spektral breitbandig wie auch quasimonochromatisch unter variierter klimatischer Beanspruchung bestrahlt. Die sich vor allem an der Oberfläche mit der Alterung abzeichnenden Veränderungen wurden mikroskopisch und spektroskopisch charakterisiert.
Waste disposal of carbon nanotube (CNT) containing products is expected to be the most important pathway for release of CNTs into the environment. In the present work, the use of radiolabelled CNTs (14C-CNT) for polycarbonate polymer nanocomposites with 1 wt% 14C-CNT content allowed for the first time to quantify and differentiate the CNT release according to the type of impact along the materials' ageing history. After an initial exposure of the nanocomposite by solar-like irradiation, further environmental impacts were applied to composite material. They aimed at mimicking disposal site conditions that may induce further ageing effects and CNT release. This study included shaking in water, rapid temperature changes, soaking in humic acid solution as well as waste water effluent, and, finally, gentle mechanical abrasion. All ageing impacts were applied sequentially, both on pristine (control) and on solar-irradiated nanocomposites. All experiments were accompanied by absolute quantification of radioactive release as well as chemical and morphological analyses of the nanocomposite surfaces using infra-red (IR) spectroscopy, X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM). The morphological analysis showed that spectral irradiation can uncover CNT networks on the outer nanocomposite surface layers by polymer degradation. After having subjected the solar-irradiated nanocomposite to all studied disposal site effect, the total radioactive release was quantified to amount to 64 mg CNT/m2, whereas only 0.8 mg CNT/m2 were found for the un-irradiated control sample. Solar degradation of polymers was thus found to significantly increase the propensity of the studied polymer nanocomposites to release CNTs during ageing effects at the product's end-of-life typical for disposal sites.