Solidification cracking is still a serious problem in laser beam welding, especially in the welding of thick-walled plates. The influence of weld pool geometry on solidification cracking in partial penetration welding of thick plates is investigated within scope of this study. Therefore, a specific experimental setup of steel and quartz glass in butt configuration and on the side with high-speed camera were used to record the weld pool shape. In addition, the influence of laser inclination angle on the weld pool geometry and on solidification crack formation was investigated. The results show a bulge in the weld pool root, which is separated from an upper region by a necking region. This leads to a case where there are three different longitudinal region lengths with different solidification zones. This temporal sequence of solidification strongly promotes the formation of solidification cracks in the weld root.
The study deals with the determination of the influence of an externally applied oscillating magnetic field on the melt pool dynamics in high power laser beam and hybrid laser arc welding processes. An AC magnet was positioned under the workpiece which is generating an upward directed electromagnetic force to counteract the formation of the droplets. To visualise the melt flow characteristics, several experiments were carried out using a special technique with mild steel from S355J2 with a plate thickness of up to 20 mm and a quartz glass in butt configuration. The profile of the keyhole and the melt flow were recorded with a highspeed camera from the glass side. Additionally, the influence of the magnetic field orientation to the welding direction on the filler material dilution on laser hybrid welding was studied with variating oscillation frequency. The element distribution over the whole seam thickness was measured with X-ray fluorescence (XRF). The oscillation frequency demonstrated a great influence on the melt pool dynamics and the mixing of the elements of the filler wire. The highspeed recordings showed, under the influence of the magnetic field, that the melt is affected under strong vortex at the weld root, which also avoids the formation of droplets.
In this study, steel-glass experiments were conducted to observe the melt pool geometry using a high-speed camera. The high-speed recordings and optical flow analysis show that two main flows take place in form of vortices. The lower vortex drives the melt backwards from the front keyhole wall and thus causes an extension of the melt pool, which is called bulging. This bulging promotes solidification cracking by forming a closed area filled with melt and the accumulation of impurities in the final solidification phase, resulting in low-melting phases which are under tensile stress at the end of solidification.
Solidification cracking phenomena taking place under Controlled Tensile Weldability (CTW) test conditions have already been investigated both experimentally and numerically via FEA in order to get a better understanding of the mechanisms of hot crack formation during laser beam welding of austenitic steel grades. This paper develops a three dimensional finite element model employing the contact elements technique to simulate the formation and propagation of solidification cracks during laser full penetration welding of fully austenitic stainless steel 1.4376. During the experimental procedure the resulting strain and displacement directed to the laser beam in the Close vicinity of the weld pool was measured at the surface of the workpiece using a Digital Image Correlation (DIC) technique with an external diode laser as an illuminating source. Local strain fields, global loads and crack lengths predicted by the model are in good Agreement with those observed in experiments.
Laser welding is a widely established manufacturing process in many industry sectors. Solidification cracking represents one of the most inadequately solved problems in welding and has major economic implications. The avoidance of hot crack forms for most fusion welding processes poses a key challenge for an important range of metallic construction materials and affects not only the manufacturers of welding equipment and material manufacturers, but also a large number of customers using welding technologies, as well as welding technical standardization and research. Solidification cracking susceptibility was examined with the help of the Controlled Tensile Weldability Test (CTW) developed by Federal Institute for Materials Research and Testing (BAM), Berlin. The test is based on the fact that hot crack formation depends on a critical strain that emerges within a critical temperature range, the so called brittle temperature range (BTR). Using this test and defined investigation programme a centreline solidification crack was generated. By controlling the applied strain during the laser beam welding process, it was possible to determine the critical strain and strain rate that led to solidification cracking formation. The hot cracking susceptibility of the tested stainless steels was qualified and quantified. The results demonstrate that the crack length increases with increasing applied strain. Furthermore, the strain rate has a significant influence on the formation of the solidification crack.
Laser welding is a widely established manufacturing process in many industry sectors. Solidification cracking represents one of the most inadequately solved problems in welding and has major economic implications. The avoidance of hot crack is for most fusion welding processes a key challenge for an important range of metallic construction materials and affects not only the manufacturers of welding equipment and material manufacturers, but also a large number of customers using welding technologies, as well as welding standardization and research. In this study a new investigation programme has been developed to qualify the hot cracking susceptibility of a variety of austenitic stainless steels. The results show the possibility of using this technique to determinate the critical values that occur with initiation of solidification cracking during laser beam welding
Experimental study and numerical simulation of hot crack formation for novel laser weldability test.
(2015)
Laser beam welding is a widely established manufacturing process in several industries. The solidification cracking seriously effecting the safety of welded joints could arise during the beam welding of stainless steels caused by high solidification rates. In this study the controlled tensile weldability test (CTW) was used to investigate the solidification cracking susceptibility the fully austenitic stainless steels CrMnNi (1.4376), CrNi (1.4301), CrNiMo (1.4404) and CrNiSi (1.4828) during laser beam welding. The test facility allows welding of specimens with simultaneous application of tensile load along or cross to the welding direction while the speed of tensile force application is either constant or increases linearly. The tensile force increment and/or the displacement are set by means of a CNC controller. Trials were conducted by varying the ultimate tensile strain and cross-head speed while keeping the welding parameters constant. By observing the crack-no crack behaviour and estimating the generated crack length for each trail using a new optimized experimental procedure the influence of the two important conditions (the strain and the strain rate) for the formation of solidification cracks can be investigated, the critical values of strain and strain rate that are responsible for solidification cracking formation have been determined. In the present study a three-dimensional FEM using the contact element technique was developed to simulate the solidification cracking during laser full penetration welding under external load conditions for the steel 1.4376 in order to get a better understanding of the mechanisms of hot crack initiation and the theoretical results were compared to the experimental ones. By comparing the resulting solidification crack with simulated crack, it is possible to determine the critical condition of solidification crack formation in the region where the strains and the strain rates cannot be measured due to the high temperature. The results show a good agreement between numerical calculation and experiment. It is proposed that the solidification cracking susceptibility may be predicted by FEM analysis by using the correct mechanical and thermo-physical constants of the materials.
One of the main factors affecting the use of lasers in the industry for welding thick structures is the process accompanying solidification cracks. These cracks mostly occurring along the welding direction in the welding center, and strongly affect the safety of the welded components. In the present study, to obtain a better understanding of the relation between the weld pool geometry, the stress distribution and the solidification cracking, a three-dimensional computational fluid dynamic (CFD) model was combined with a thermo-mechanical model. The CFD model was employed to analyze the flow of the molten metal in the weld pool during the laser beam welding process. The weld pool geometry estimated from the CFD model was used as a heat source in the thermal model to calculate the temperature field and the stress development and distributions. The CFD results showed a bulging region in the middle depth of the weld and two narrowing areas separating the bulging region from the top and bottom surface. The thermo-mechanical simulations showed a concentration of tension stresses, transversally and vertically, directly after the solidification during cooling in the region of the solidification cracking.
A self-restraint hot cracking test (free edge test) was used in combination with a novel optical measurement technique to determine the critical straining conditions for solidification cracking for the stainless steel grade 1.4828 (AISI 309). The Lucas-Kanade algorithm for the optical flow (OF) calculation was implemented to obtain the full-field displacement and then the full-field strain.
The use of external laser illumination with appropriate filters allows to obtain good image quality with good contrast. The critical straining conditions required for solidification cracking can be obtained by means the proposed technique in the immediate vicinity of the solidification front. A very good repeatability was demonstrated for the used measurement technique. The critical straining conditions for solidification cracking for the tested steel und under this welding conditions has been detected
The stability of the keyhole decreases for deep penetrated high-power laser beam welding. The keyhole tends to collapse with increasing laser power and e.g. keyhole induced porosity can occur. This study deals with the observation of the keyhole during high-power laser beam welding in partial penetration mode by means of a high-speed camera. A butt configuration of 25 mm thick structural steel and transparent quartz glass was used for the experiments. An oscillating magnetic field was applied perpendicular to the welding direction on the root side of the steel plate. The keyhole was highlighted with a coaxial diode laser. It was ascertained that the stability of the keyhole and the weld penetration depth were increased by applying an oscillating magnetic field with an oscillating frequency of 1.2 kHz and a magnetic flux density of 50 mT.