Due to the corrosion resistance of carbon steel, bridge constructions are currently protected against corrosion by applied coating systems. These coating systems need to be renewed after approximately 25 50 years. Galvanized constructions without any welding areas at the construction site could be prepared as grouted joints and can be used without any renewing for about 100 years.
Exposure sites and outdoor exposure have always been a part of atmospheric corrosion research providing the “final answer”, although at the cost of long exposure times. Individual exposure programs such as ISOCORRAG, MICAT and ICP Materials have resulted in collaborative networks of exposure sites. So far, however, there has been no collective effort to put together currently active sites in a comprehensive manner and across programs and nations. The information collected in the catalogue is possible thanks to the work of all individual site managers listed as contact persons, efforts of members of Working Party 25 (WP25) Atmospheric Corrosion of the European Federation of Corrosion (EFC) and financial support of the EFC. With this Catalogue you can both get a general overview of what is available and be guided if you are looking for a particular environment with certain characteristics.
The presentation shows systematic investigations to describe the corrosion and corrosion product formation processes of pure zinc under the climatic conditions currently prevailing in the Federal Republic of Germany. The investigations in their entirety aim at questioning current and establishing new ways of looking at the formation of corrosion products of pure zinc under atmospheric corrosion conditions. Thus, they make a significant contribution in understanding corrosion protection by zinc and zinc coatings. In particular, the focus is placed on the initial stage of the corrosion product formation. A systematic investigation of this time range, which is characterized by very reactive corrosion products, is only made possible by using gel-type electrolytes. The short periods of time at the beginning of weathering is now measurable and their influence on the formation of corrosion products and the kinetics of layer formation describable. By combining the new electrochemical approach with gravimetric, microscopic and analytical methods, new insights could be gained both on a methodic and scientific level.
Novel agar-based test electrolytes are used to perform electrochemical corrosion investigations on ZnFe and ZnNi binary as well as ZnFeMo ternary zinc coatings. The objectives of the electrochemical investigations include the characterization of the corrosion behavior, the description of the protective effect of the coatings as well as the investigation of the layer formation and degradation under artificial aging. ZnFe and ZnFeMo coatings are applied with varying iron content as well as an additional passivation layer, respectively, to study the effect on corrosion resistance. The results show that the protective effect of the coatings is not negatively influenced by different iron contents or the addition of molybdenum. Additional passivation of the ZnFe-containing coatings by means of a passivating agent leads to a significant improvement in the protective effect. Artificial aging leads to slight degradation of the additional passivation layer whereas coatings without post-treatment enhance their protective effect by the formation of corrosion product layers.