First results of an inter-laboratory comparison (27 participants in Europe, Japan and USA) of XPS data obtained with non-conducting samples are presented. Binding energies of Al 2s for alumina, N 1s and imide C 1s for Kapton and Sr 3p3/2 for a strontium titanate film on glass were obtained after static charge referencing with the help of 15 nm gold particles deposited at the surface of the test samples. For the alumina sample C 1s static charge referenced data are also presented. Repeat standard deviations (sr), between standard deviations (sb), reproducibility standard deviations (sR) and total means are evaluated from the experimental data. It can be stated that although the repeat standard deviation is as small as 0.05 eV in the best case, the standard deviation characterizing the reproducibility of the method is obviously not better than 0.15 eV in the best case at the present time. The knowledge of these standard deviations is important for metrology, validations of analytical procedures relying on qualitative photoelectron spectroscopy and XPS databanking.
The dismutation of CHClF2 to CHF3 and CHCl3 was used to probe the effect of γ-Al2O3 fluorination on fluorine-against-chlorine (Cl/F) exchange reactions. X-ray photoelectron spectroscopy (XPS), X-ray excited Auger electron spectroscopy (XAES) and X-ray absorption near edge structure (XANES) spectroscopy were employed to probe the modifications at the surface of γ-Al2O3 accompanying the initial stages of fluorination. The results suggest that fluorine uptake by γ-Al2O3 starts initially at the surface of the oxide particles, with the formation of a fluorine species that is characterised by a single bond and a high effective charge q. Catalytic Cl/F-exchange is only observed after accumulation of higher fluorine concentrations, for which insertion of fluorine into the sub-surface region of the oxide crystallites has commenced. Quantitative XPS shows that the fluorination level must exceed approximately 10 atom% of the anions to achieve catalytic activity. The spectroscopic evidence suggests that the formation of aluminium oxofluorides is sufficient to provide catalytic activity. The presence of an AlF3 phase is not a condition for the observation of catalytic activity, even though defect-rich AlF3 is ultimately the endpoint of the fluorination process and is itself a Cl/F exchange catalyst.