Filtern
Erscheinungsjahr
Dokumenttyp
Referierte Publikation
- ja (56) (entfernen)
Schlagworte
- Hydrogen (11)
- ToF-SIMS (7)
- Microstructure (5)
- Cold cracking (4)
- Duplex stainless steel (4)
- Hydrogen assisted cracking (4)
- Hydrogen embrittlement (4)
- Restraint (4)
- AISI 304L (3)
- Cracking (3)
Organisationseinheit der BAM
- 9 Komponentensicherheit (15)
- 9.0 Abteilungsleitung und andere (15)
- 5 Werkstofftechnik (4)
- 5.1 Mikrostruktur Design und Degradation (4)
- 6 Materialchemie (3)
- 6.1 Oberflächen- und Dünnschichtanalyse (3)
- 9.4 Integrität von Schweißverbindungen (2)
- 9.2 Versuchsanlagen und Prüftechnik (1)
- P Präsident (1)
- P.0 Präsident und andere (1)
Paper des Monats
- ja (2)
As consequence for increasing threats by IEDs (Improvised Explosive Devices) on vehicles, the blast resistance of the welded frames and bodies becomes increasingly important. Considering vehicle welds subjected to blasting, the real configurations of the joints in the structure and the position of the blast loads have to be considered. The present contribution thus focuses on a weld joint at the explosion endangered wheel well of a tactical truck. The high-strength steel welds were subsequently impacted by explosion loads within the upper range from those experienced in practical military operation to cause not only deformation, but also to investigate the ultimate fracture behaviour of the high-strength weld. The interaction between cooling time t8/5 and displacement, crack path as well as fracture surface was analysed. The analyses of the fracture surfaces revealed ductile overload failure and also the size of the dimples was influenced by the cooling time t8/5. As a prominent feature, these investigations showed that the crack path of such high-strength steel welds under blasting is less influenced by the final hardness level in the respective weld microstructures but much more affected by the hardness gradient at the fusion line and inside the Heat Affected Zone (HAZ).
This study provides an in-depth survey of current technologies and applications for assessing the cold cracking susceptibility of welded joints. From the large variety of existent cold cracking test procedures, the most important and internationally established tests are presented and evaluated in terms of their usefulness and application limits. According to the type of loading, the test procedures are classified into self-restraint and externally loaded tests. Apart from the merely metallurgical weldability tests for determining the cracking susceptibility of base materials, filler materials and weld metals, advanced test methods are presented for evaluating the cold cracking susceptibility of welded components. A salient point brought out in this respect is the fact that the level of external loading in such component weld tests can be applied independently of the welding parameters, reproducing as realistically as possible the practical application case, i.e. the level of the restraint intensity. This study includes a summarized comparison of the cold cracking procedures. It is emphasized that highly accurate consideration and reproduction of the design-specific stiffness conditions is essential in the tests for assessing the cold cracking behaviour of welded joints. Therefore, various numerical analyses are presented in a final chapter for calculating the restraint intensity as a definitive factor affecting cold cracking.
The damaging impact of hydrogen on the austenitic stainless steel AISI 304 L was analysed.
To this aim, samples were charged electrochemically with the hydrogen isotope deuterium (2H, D) and examined with time-of-flight secondary ion mass spectrometry (ToF-SIMS) and electron backscatter diffraction (EBSD). The fusion of the obtained chemical and structural information revealed local enrichment of deuterium in austenite, transformation into martensite, crack formation and severe roughening of the specimen surface. The results indicated that martensite was not only formed during charging but also during Desorption and ToF-SIMS examinations. Furthermore, cross-sections of deuterium-charged samples revealed that in preferred deformation bands a g/ε/a 0 evolution is taking place.
By means of microscopic analyses and carrier gas hot extraction (CGHE), it was found that the use of NaAsO2 as recombination poison decreased the uptake of hydrogen significantly and resulted in severe precipitation on the specimen surfaces. This is in contrast to the popular presumption that NaAsO2 enhances the uptake of hydrogen (and
deuterium) during electrochemical charging by hampering its recombination from Atoms to molecules.
The Tsumeb Mine in Namibia represents one of the best-preserved mining sites in the world and is rapidly gaining cross-disciplinary interest among cultural and engineering scientists. Most of the open pit and the shaft mining equipment are still in place, including the ore processing units and the local power plant. The mining area thus deserves recognition as an industrial world heritage site, especially due to the rarity of such locations on the African continent. The Shaft #1 headgear, built in 1924, represents one of the oldest known riveted steel headgears of the Promnitz design worldwide. In contrast to similar steel structures located in the northern hemisphere, it has been exposed to a different rural semi-arid climate since it is located in the Otavi Mountain Land, characterized by semi-annual change of rainy and dry seasons. Parts of the Shaft #1 headgear have remained largely untouched for more than 70 years. Besides its outstanding heritage value, it thus also represents an interesting object for studying the composition of corrosion layers formed on mild steel surfaces when exposed to continental and industrial mining atmospheres. To find a suitable transparent corrosion prevention coating, various on-site coating samples were evaluated after 11 months of outdoor exposure, including Owatrol Oil®, which is based on natural oil and alkyd resin with strong wicking potential. The substance is frequently applied for the conservation of single components but is not yet widely used on large steel structures in the field of industrial heritage conservation. However, it represented the most stable anti-corrosion coating under the local atmospheric conditions in the on-site tests. Thus, the suitability of Owatrol Oil® as a transparent coating for corrosion protection of riveted mild steel structures in such climates was further investigated as a more recent approach for the conservation of large steel structures. Since the protective coatings are exposed to strong UV radiation in the local climate, the addition of a specific UV stabilizer mixture was also tested. For such laboratory tests, two mild steel samples were taken. The first one originated from a diagonal strut of the 1920s and the second one from a handrail mounted in the early 1960s. Using corresponding high-resolution scanning electron microscopy (HR-SEM) and energy-dispersive X-ray spectroscopy (EDX) it was found that the corrosion layers are predominantly composed of lepidocrocite and goethite. A weathering program simulating the specific environmental conditions at Tsumeb in a UV climate chamber was developed and the corrosion resistance of the mild steel surface was subsequently evaluated by potentiodynamic measurements. Such tests proved to be a fast and reliable procedure for ranking the corrosion resistance of the old mild steels. It was found that the long-term corrosion layers already provide significant protection against further corrosion in the simulated environment. However, the study also showed that this can be further improved by the application of the Owatrol Oil® as a protective coating that also seals crevices. The addition of the UV stabilizers, however, led to a significant deterioration in corrosion protection, even in comparison to that of the uncoated long-term corrosion layers on the surface. Regular overcoating seems more advisable for the long-term preservation of the Shaft #1 headgear than modifying the Owatrol Oil® Coating with the tested UV-stabilizing additives.
X5CrNiCuNb16-4 has been proven to be sufficient resistant in corrosive environments, but shows rather unusual corrosion behaviour in CCS environment. Therefore a series of 30 specimens was tested at stress amplitudes between 150 MPa and 500 MPa (sinusoidal dynamic test loads, R=-1; resonant frequency ∼ 30 Hz). Due to the rather heterogeneous fine machined surfaces (Rz=4) the specimens are comparable with prefabricated parts. X5CrNiCuNb16-4 reached the maximum number of cycles (10 x 106) at a stress amplitude of 150 MPa and lies 60% below the stress amplitude measured in air. The scatter range TN = 1:34 is disproportionately large. Although the fracture surface exhibited the typical striations and corroded surface areas no significant differences were found. The hardness was found to be homogeneous in all specimens tested at 335 HV10. Non-metallic inclusions were found within the microstructure, but no correlation could be found between the inclusions and early rupture. Still specimens that showed inclusions at the fracture surface and its cross section endured lower number of cycles. Additionally Aluminium was analysed in specimens with low number of cycles and may be cause for early rupture during corrosion fatigue tests. These findings reveal a very high sensitivity on a homogeneous microstructure upon the corrosion and corrosion fatigue behaviour of X5CrNiCuNb16-4 and needs to be taken into account when regarding this steel as pipe steel during injection of CO2 into saline aquifers.
Materials used in military applications have to withstand multiple threats like ballistics and explosions. Thus, high-strength low alloyed (HSLA) steels are used. The main joining technique for metals is welding. Therefore, analysing the dynamic impact behaviour of high-strength welds is very important to fulfil these demands.
Investigation of welds at high strain rates has rarely been conducted in the past. To determine the dynamic impact behaviour of hybrid laser-arc welds, the Split Hopkinson Pressure Bar (SHPB) technique was used. The base material was a quenched and tempered fine-grained armour steel with yield strength of 1100 MPa.
First, a full hybrid laser-arc weld was investigated by extracting specimens consisting of weld metal and heat affected base material. The influence of two variables, the cooling time between 800 °C and 500 °C (t8/5) and strength of filler material, on the impact behaviour was studied. The cooling time t8/5 was varied by preheating to influence the microstructure in the HAZ and to analyse the effect on the hardness and dynamic compressive strength.
Subsequent analysis to detail the original Investigation was carried out by dilatometer heat treatment of specimens to create homogenous subzones of the weld. These specimens have a homogenous microstructure of HAZ and were tested by SHPB to determine the stress-strain characteristics for the different microstructures of HAZ.
The results of the weld specimen showed the effect of preheating and filler material strength on the dynamic compressive behaviour. The analysis of the different microstructures of the HAZ indicated that especially the tempered microstructure caused a reduction in dynamic compressive strength.