Hydrogen might be introduced during fabrication welding or might be taken up from an environment during sour service or cathodic protection. Thus, hydrogen assisted stress corrosion and cold cracking is still a major topic regarding the reliability of welded steel components, as for instance offshore platforms and pipelines. In order to support conclusive testing and life time evaluation of welded steel components, a numerical model for hydrogen assisted cracking has been developed, particularly taking into consideration the geometrical effects of crack propagation on the respective hydrogen distribution alongside and ahead of the crack. Numerical calculations were based on finite element analysis of the hydrogen and stress-strain distribution by using a commercially available program. The model has been verified experimentally by slow strain rate experiments of supermartensitic stainless steels which are intended to be used more extensively as materials for welded flowlines in North Sea oil and gas production. As first results of such simulations the influence of the subsurface concentration provided by different H2S saturation levels in the NACE TM 0177-96 standard solution on crack propagation and the effect of crack shape on the hydrogen distribution profile are presented in this contribution.
Hydrogen might cause severe degradation of supermartensitic stainless steels, if they are activated during exposure to sour environments. Consistent and comprehensive data for hydrogen transport in these materials are thus required to support, in particular, modelling of hydrogen assisted cracking as a part of life time assessment of welded steel components. In addition to previously published diffusion coefficients and subsurface concentrations of a supermartensitic stainless steel further data dependent on heat treatment are provided by this contribution. Furthermore, a higher alloyed material has been investigated in the state as received and also in the quenched condition, in order to approach the influences of chemical composition on hydrogen transport in supermartensitic stainless steels. With respect to welding it turned out that the diffusion coefficient and the subsurface concentration are markedly dependent on heat treatment of the materials.