Filtern
Erscheinungsjahr
Dokumenttyp
- Beitrag zu einem Tagungsband (31)
- Zeitschriftenartikel (22)
- Vortrag (21)
- Sonstiges (11)
- Beitrag zu einem Sammelband (1)
Sprache
- Englisch (85)
- Französisch (1)
Schlagworte
- Corrosion (86) (entfernen)
Organisationseinheit der BAM
- 7 Bauwerkssicherheit (59)
- 7.6 Korrosion und Korrosionsschutz (59)
- 5 Werkstofftechnik (27)
- 5.1 Mikrostruktur Design und Degradation (26)
- 5.6 Glas (3)
- 1 Analytische Chemie; Referenzmaterialien (1)
- 1.4 Prozessanalytik (1)
- 3 Gefahrgutumschließungen; Energiespeicher (1)
- 3.2 Gefahrguttanks und Unfallmechanik (1)
- 5.4 Multimateriale Fertigungsprozesse (1)
Eingeladener Vortrag
- nein (21)
In Germany the “BAM-List - Requirements for Tanks for the Transport of Dangerous Goods” is the basis for substance-related prototype approvals for tank Containers undertaken by the BAM1 - Federal Institute for Materials Research and Testing. Compatibility evaluations of selected metallic materials as well as of polymeric gasket and lining materials under the influence of approximately 7200 dangerous goods have been published in the BAM-List since 1989.
The ferritic Steel UNS S44400 (X2CrMoTil8-10, 1.4521) was originally developed as alternative for the austenitic grade AISI316L (X2CrNiMo 17-12-2, 1.4404). Due to its characteristic profile this Steel was qualified for applications requiring high strength values at concomitant adequate corrosion resistance. Because of the lack of Nickel this Steel is a cost-efficient alternative to the Ni-containing austenites. No corrosion test results of UNS S44400 under the influence of dangerous goods were published in the BAM-List so far. Only data on the behavior of AISI 316L are listed. Therefore test specimens of this Steel were exposed to selected corrosive substances in order to compare both steels.
Due to the reduced alloy content a reduced corrosion resistance of the Steel UNS S44400 in acidic substances, such as formic acid, acetic acid and sulfuric acid, in comparison to the austenitic CrNiMosteels was expected but not observed. Tests in an alkaline medium showed sufficient resistance.
Within the project COORAL (German acronym for ''C02 purity for capture and storage") studies on pipeline steels exposed to circulating supercritical impure C02 have been carried out. For this purpose, a loop consisting of compressors, flow meter and two autoclaves was constructed. In order to simulate the real conditions in pipelines, impurities such as H20, CO, S02, N02 and 02 were added to the C02 stream before compression. Exposure experiments were carried out with Steel specimens placed in the autoclaves. Carbon Steel L360NB, pure iron X20Cr13, X46Cr13, X2CrMnNiN22-5-2 and alloy 31 have been exposed to circulating (flow rate 4 L/min) supercritical impure C02 for one week at 60 °C and 10 MPa Surface analysis and weight loss experiments in order to determine the corrosion products and the corrosion rates showed that the impurities cause corrosion problems. Slight general corrosion by L360NB and soft iron was observed. The initiation of pitting corrosion was observed at the surfaces of the materials X20Cr13, X46Cr13, X2CrMnNiN22-5-2. No visible signs of corrosion have been observed on alloy 31.
The process chain for Carbon Capture and Sequestration (CCS) includes tubing for injection of CO2 into saline aquifers. The compressed CO2 is likely to contain specific impurities; small concentrations of SO2 and NO2 in combination with oxygen and humidity are most harmful. In addition, CO2 saturated brine is supposed to rise in the well when the injection process is interrupted. The material selection has to ensure that neither CO2 nor brine or a combination of both will leak out of the inner tubing. In this comprehensive paper the investigated materials range from low-alloy steels and 13% Cr steels up to high-alloy materials. Electrochemical tests as well as long term exposure tests were performed in CO2, in brine and combination of both; pressure was up to 100 bar, temperature up to 60 °C. Whereas the CO2 stream itself can be handled using low alloy steels, combinations of CO2 and brine require more resistant materials to control the strong tendency to pitting corrosion. The corrosion behavior of heat-treated steels depends on factors such as microstructure and carbon content. For different sections of the injection tube, appropriate materials should be used to guarantee safety and consider cost effectiveness.
Condensates from the gas stream in simulated CO2 transport pipelines have been identified during the experiments in the laboratory. Because of their acidic origin the corrosion resistance of pipeline steels used for CCS (carbon capture and storage) technology might be limited. Over the last years it has become clear that the amount of water and acid building constituents in the CO2 stream has to be controlled very well. In this work, condensates formed in experiments using gaseous CO2 containing high amounts of water, NO2 and SO2 were analyzed, replicated, and used for extensive electrochemical experiments. These highly acidic condensates were enriched with CO2 and then applied to characteristic steels planned to use in the CCS transport chain. Even high alloy steels are susceptible to localized corrosion under these conditions. The results implicate that condensation of aggressive acid droplets has to be avoided or the locations where condensation takes place have to be controlled extensively.
The screening of coatings shows that the modification by adding individual pigment was not sufficient to protect carbon steel even during a short-term exposure, indicated by the discoloration after only seven days of exposure.
Electrochemical tests indicated that the coating cathodically protects carbon steel or slows down the corrosion reaction.
A long-term exposure test confirmed that the PANI/SiO2 modified coating successfully protects the carbon steel in the Sibayak artificial geothermal water at 150 °C for 6 months.