Corrosion of steel reinforcement in concrete exposed to chloride containing
environments is a serious problem in civil engineering practice. Electrochemical
methods, e.g. potential mapping, provide information whether the steel reinforcement
is still passive or depassivation has been initiated. By applying such techniques no
information on the type of corrosion, its extent and distribution of corrosion products
is available. Particular the corrosion progress is a significant problem. Especially in
the case of element corrosion in reinforced concrete structures, the development at
the anode can not be separated into corrosion damage causing by element corrosion
or self-corrosion. Until now also in laboratory tests it is impossible to collect such
information without destroying specimens after electrochemical testing was
performed place. To overcome this problem it was tried to study the steel surface
within the mortar specimens by X-ray tomography (CT). Within the scope of these
investigations it could be shown, that X-ray tomography is suitable to make corrosion
pits visible which are embedded in a mortar with a cover thickness of about 35 mm.
In this publication the corrosion damage of reinforced steel is documented timedependent
by X-ray tomography.
Although the complex changes at the steel-concrete interface due to cathodic polarisation are widely acknowledged to have a beneficial influence concerning the cathodic protection (CP) of steel in concrete, some questions concerning the repassivation of carbon steel in consequence of cathodic polarisation are still not satisfactorily clarified. In the recent literature, some indications are presented that repassivation occurs after a certain time of polarisation. Therefore, the investigations discussed in this paper aim to clarify, to what extent the re-passivation of carbon steel due to cathodic polarisation occurs, and if the ennoblement of OCP is a sufficient indication for repassivation. In a first step, the corrosion state of five nominal equal test specimens was determined by electrochemical impedance spectroscopy (EIS). After determining the initial corrosion state by evaluating the charge transfer resistance and the polarisation resistance, respectively, the specimens were polarised cathodically. Impedance data were recorded before, during and after polarisation. The impedance data were evaluated by equivalent circuit fitting with special attention to charge transfer resistances and the impact of diffusion on the corrosion and polarisation behaviour. The results indicate that the reduction of oxides and oxygen diffusion during cathodic polarisation has strong impact on the systems behaviour and that repassivation effects occur after switching off the polarisation current and during depolarisation, respectively.
Corrosion of steel reinforcement in concrete exposed to chloride containing environments is a serious problem in civil engineering practice. Electrochemical methods, e.g., potential mapping, provide information whether the steel reinforcement is still passive or depassivation has been initiated. By applying such techniques no information on the type of corrosion, its extent and distribution of corrosion products is available. Particular the corrosion progress is a significant problem. Especially in the case of macrocell corrosion in reinforced concrete structures, the development at the anode cannot be separated into corrosion damage resulting from macrocell corrosion or self-corrosion. Until now also in laboratory tests it is impossible to collect such information without destroying specimens after electrochemical testing was performed. To overcome this problem it was tried to study the steel surface within the mortar specimens by X-ray tomography (CT). Within the scope of these investigations it could be shown, that X-ray tomography is suitable to make corrosion pits and their development visible which are embedded in a mortar with a cover thickness of about 35 mm. In this publication the time-dependent corrosion damage of reinforced steel is documented by X-ray tomography.