Electron microscopy investigation of the structure of a compact extruded from nanopowder of nickel
(2007)
Synthesis of Molybdenum and Niobium Mono- and Binary Silicides by the Method of SHS-Metallurgy
(2016)
The process of self-propagating high-temperature synthesis of the Mo–Nb–Si silicides from the powder mixtures has been investigated. Based on performed experiments, the composition of powder mixtures as well as technological parameters are proposed which provide the synthesis of monosilicides MoSi₂, NbSi₂, and binary silicides Mo₁-хNbxSi₂ with different ratios of Nb/Mo by adding different contents of MoO₃ and Nb₂O₅. Microstructure and phase compositions of the obtained silicide ingots are characterized by scanning electron microscopy, electron probe microanalysis, X-ray diffraction, and backscatter electron diffraction.
The morphology of pores partially shrunk during a half-hour HIP at temperature of 1288 °C and pressure of 103 MPa has been investigated in nickel-based superalloy CMSX-4. The investigation resulted in the following findings: surrounding the shrinking pores by a c¢-shell (Ni3Al), faceting of the pores surface by {023} and {011} planes, and formation the submicroscopic satellite pores connected by channels with the neighboring larger pores. It is assumed that the formation of the c¢-shell around the pores and the faceting of the pore surface is due to diffusion processes occurring during pore shrinkage, and therefore these findings can be considered as arguments supporting the vacancy model of pore annihilation. The submicroscopic satellite pores are expected to be the result of dividing the casting pores of a complex initial shape during their shrinking. The connecting channels are probably required for the gas to escape from the rapidly shrinking small satellite pores into the slowly shrinking large pore. Thus, it is reasonable to assume that the casting pores may contain some amount of gas.