Filtern
Erscheinungsjahr
Dokumenttyp
- Vortrag (35)
- Zeitschriftenartikel (32)
- Posterpräsentation (3)
- Beitrag zu einem Tagungsband (2)
- Dissertation (1)
- Sonstiges (1)
- Forschungsbericht (1)
Schlagworte
- TED-GC/MS (24)
- Microplastics (21)
- Mikroplastik (20)
- Microplastic (15)
- Reference materials (6)
- Mikroplastik-Analytik (5)
- Polymer 3R (5)
- CUSP (4)
- Referenzmaterial (4)
- TED-GC-MS (4)
Organisationseinheit der BAM
- 6 Materialchemie (66)
- 6.6 Physik und chemische Analytik der Polymere (66)
- 6.1 Oberflächen- und Dünnschichtanalyse (7)
- 6.5 Synthese und Streuverfahren nanostrukturierter Materialien (3)
- 5 Werkstofftechnik (2)
- 6.3 Strukturanalytik (2)
- 1 Analytische Chemie; Referenzmaterialien (1)
- 1.7 Organische Spuren- und Lebensmittelanalytik (1)
- 5.1 Mikrostruktur Design und Degradation (1)
- 5.3 Polymere Verbundwerkstoffe (1)
Paper des Monats
- ja (1)
Eingeladener Vortrag
- nein (35)
Funktionalisierte Oberflächen sind in vielen Bereichen, z. B. als Haftvermittler in Polymerkompositen, für katalytische Anwendungen oder als Sensoren von Interesse. Für viele solcher Anwendungen ist es ausreichend, den verwendeten Werkstoff mit einem ultradünnen Polymerfilm zu überziehen. Dazu gibt es bislang einige Verfahren, wie z. B. Chemical Vapour Deposition, Layer-by-Layer-Technik, Langmuir-Blodgett-Technik oder Spin-Coating, die alle bestimmte Nachteile haben.
In der vorliegenden Arbeit wurden wenige Nanometer dicke Polymerschichten auf metallischen und nicht-metallischen Substraten mittels Elektrospray Ionisation abgeschieden.
So wurden typischerweise etwa 10 nm dicke Schichten von Polyacrylsäure (PAA) hergestellt. Die analytische Charakterisierung der produzierten Schichten erfolgte mit der Röntgen-Photoelektronenspektroskopie. Die Atomkraft- bzw. Rasterelektronenmikroskopie gaben Auskunft über den Bedeckungsgrad und die Schichtmorphologie. Die Infrarot-Reflexions-Absorptions-Spektroskopie wurde zur Bestimmung des Restlösemittelgehaltes verwendet.
Zur Optimierung der Schichtabscheidung und -struktur wurden verschiedene Parameter variiert, wie z. B. der Kapillaren-Proben-Abstand, die Beschichtungszeit oder die Beschichtungstemperatur, wobei sich herausstellte, dass die Schichtbildungsparameter für jedes Polymer individuell angepasst werden müssen.
Es konnte gezeigt werden, dass Beschichtungen, bei denen sich das Substrat senkrecht zur Kapillare befindet, bei Raumtemperatur mit einem Kapillaren-Proben-Abstand von mindestens 100 mm zu lösemittelfreien PAA-Schichten führen. Dabei war die Ausbildung der Filmtopographie unabhängig sowohl von der Konzentration der Lösung als auch von der Oberflächenenergie des Substrates.
Water treatment with activated carbon (AC) is an established method for the removal of organic micropollutants and natu ral organic matter. However, it is not yet possible to predict the removal of individual pollutants. An appropriate material characterization, matching adsorption processes in water, might be the missing piece in the puzzle. To this end, this study examined 25 diferent commercially available ACs to evaluate their material properties. Frequently reported analyses, including N2 adsorption/desorption, CHNS(O), point of zero charge (PZC) analysis, and X-ray photoelectron spectroscopy, were conducted on a selected subset of powdered ACs. Inorganic elements examined using X-ray fuorescence and X-ray difraction spectroscopy revealed that relative elemental contents were distinctive to the individual AC’s raw material and activation procedure. This study also is the frst to use thermogravimetric analysis (TGA) coupled to Fourier-transform infrared spectroscopy (FTIR) to conduct quantitative analyses of functional surface oxygen groups (SOGs: carboxylic acid, anhydride, lactone, phenol, carbonyl, and pyrone groups) on such a large number of ACs. The comparably economical TGA method was found to provide good surrogates for the PZC by pyrolytic mass loss up to 600 ◦C (ML600), for the oxygen content by ML1000 and for the carbon content by oxidation. Mass loss profles depict the AC’s chemistry like fngerprints. Furthermore, we found that SOG contents determined by TGA-FTIR covered a wide individual range and depended on the raw material and production process of the AC. TGA and TGA-FTIR might therefore be used to identify the suitability of a particular AC for a variety of target substances in diferent target waters. This can help practitioners to control AC use in waterworks or wastewater treatment plants.
Inputs of plastic impurities into the environment via the application of fertilizers are regulated in Germany and the EU by means of ordinances. Robust and fast analytical methods are the basis of legal regulations. Currently, only macro- and large microplastic contents (>1 mm) are measured. Microplastics (1–1,000 µm), are not yet monitored. Thermal analytical methods are suitable for this purpose, which can determine the mass content and can also be operated fully automatically in routine mode. Thermal extraction desorption-gas chromatography/mass spectrometry (TED-GC/MS) allows the identification of polymers and the determination of mass contents in solid samples from natural environments. In accordance with the German or European Commission (EC) Fertiliser Ordinance, composting plants should be monitored for microplastic particles with this method in the future. In this context a compost plant was sampled. At the end of the rotting process, the compost was sieved and separated in a coarse (>1 mm) and a fine fraction (<1 mm). The fine fraction was processed using density separation comparing NaCl and NaI as possible salt alternative and screened for microplastic masses by TED-GC/MS with additional validation and quality assurance experiments. With TED-GC/MS total microplastics mass contents of 1.1–3.0 μg/mg in finished compost could be detected with polyethylene mainly. What differs much to the total mass of plastics in the coarse fraction with up to 60 μg/mg, which were visually searched, identified via ATR-FTIR and gravimetrically weighted.
AbstractMicroplastics (MP) can be detected in all environmental systems. Marine and terrestrial aquatic systems, especially the transported suspended solids, have often been the focus of scientific investigations in the past. Sediments of aquatic river systems, on the other hand, were often ignored due to the time‐consuming sample preparation and analysis procedures. Spectroscopic measurement methods counting particle numbers are hardly suitable as detection methods, because there are plenty of natural particles next to a small number of MP particles. Integral methods, such as thermoanalytical methods are determining the particle mass independently of the inorganic components.In this study, a workflow for sample preparation via density separation and subsequent analysis by thermal extraction desorption‐gas chromatography/mass spectrometry is presented, which leads to representative and homogeneous samples and allows fast and robust MP mass content measurements suitable for routine analysis. Polymers were identified and quantified in all samples. Polyethylene and styrene‐butadiene rubber are the dominant polymers, besides polypropylene and polystyrene. Overall, total polymer masses between 1.18 and 337.0 µg/g could be determined. Highest MP concentrations in riverbed sediment are found in sites characterized by low flow velocities in harbors and reservoirs, while MP concentrations in sandy/gravelly bed sediments with higher flow velocities are small.
An investigation of microplastic (MP) occurrence in a municipal wastewater treatment plant (WWTP) effluent with tertiary treatment was carried out. Representative sample volumes of 1 m3 were taken by applying a fractionated filtration method (500, 100, and 50 µm mesh sizes). The detection of MP mass fractions by thermal extraction desorption–gas chromatography/mass spectrometry (TED-GC/MS) was achieved without the previously required additional sample pretreatment for the first time. Different types of quantification methods for the evaluation of TED-GC/MS data were tested, and their accuracy and feasibility have been proven for real samples. Polyethylene, polystyrene, and polypropylene were identified in effluent samples. The polymer mass content varied significantly between 5 and 50 mg m−3. A correlation between the MP load and the quantity of suspended matter in the WWTP effluents, particle size distribution, particle type, and operation day (i.e., weekday, season, and capacity) was not found. It can be concluded that a meaningful assessment of WWTPs requires a comprehensive sampling campaign with varying operation conditions.
Long-time behavior of surface properties of microstructures fabricated by multiphoton lithography
(2021)
The multiphoton lithography (MPL) technique represents the future of 3D microprinting, enabling the production of complex microscale objects with high precision. Although the MPL fabrication parameters are widely evaluated and discussed, not much attention has been given to the microscopic properties of 3D objects with respect to their surface properties and time-dependent stability. These properties are of crucial importance when it comes to the safe and durable use of these structures in biomedical applications. In this work, we investigate the surface properties of the MPL-produced SZ2080 polymeric microstructures with regard to the physical aging processes during the post-production stage. The influence of aging on the polymeric microstructures was investigated by means of Atomic Force Microscopy (AFM) and X-ray Photoelectron Spectroscopy (XPS). As a result, a time-dependent change in Young’s Modulus, plastic deformation, and adhesion and their correlation to the development in chemical composition of the surface of MPL-microstructures are evaluated. The results presented here are valuable for the application of MPL-fabricated 3D objects in general, but especially in medical technology as they give detailed information of the physical and chemical time-dependent dynamic behavior of MPL-printed surfaces and thus their suitability and performance in biological systems.
Tracking waterborne microplastic (MP) in urban areas is a challenging task because of the various sources and transport pathways involved. Since MP occurs in low concentrations in most wastewater and stormwater streams, large sample volumes need to be captured, prepared, and carefully analyzed. The recent research in urban areas focused mainly on MP emissions at wastewater treatment plants (WWTPs), as obvious entry points into receiving waters. However, important transport pathways under wet-weather conditions are yet not been investigated thoroughly. In addition, the lack of comprehensive and comparable sampling strategies complicated the attempts for a deeper understanding of occurrence and sources. The goal of this paper is to (i) introduce and describe sampling strategies for MP at different locations in a municipal catchment area under dry and wet-weather conditions, (ii) quantify MP emissions from the entire catchment and two other smaller ones within the bigger catchment, and (iii) compare the emissions under dry and wet-weather conditions. WWTP has a high removal rate of MP (>96%), with an estimated emission rate of 189 kg/a or 0.94 g/[population equivalents (PEQ · a)], and polyethylene (PE) as the most abundant MP. The specific dry-weather emissions at a subcatchment were ≈30 g/(PEQ · a) higher than in the influent of WWTP with 23 g/(PEQ · a). Specific wet-weather emissions from large sub-catchment with higher traffic and population densities were 1952 g/(ha · a) higher than the emissions from smaller catchment (796 g/[ha · a]) with less population and traffic. The results suggest that wet-weather transport pathways are likely responsible for 2–4 times more MP emissions into receiving waters compared to dry-weather ones due to tire abrasion entered from streets through gullies. However, more investigations of wet-weather MP need to be carried out considering additional catchment attributes and storm event characteristics.
Tire wear (TW) constitutes a significant source of microplastic in terrestrial ecosystems. It is known that particles emitted by roads can have an effect up to 100 m into adjacent areas. Here, we apply for the first-time thermal extraction desorption gas chromatography-mass spectrometry (TED-GC/MS) to determine TW in soil samples by detection of thermal decomposition products of styrene-butadiene rubber (SBR), without additional enrichment. Additionally, zinc contents were determined as an elemental marker for TW. Mixed soil samples were taken along three transects along a German motorway in 0.3, 2.0, and 5.0 m distance from the road. Sampling depths were 0–2, 2–5, 5–10, and 10–20 cm. Four fine fractions, 1 000–500, 500–100, 100–50, and <50 μm, were analyzed.
TW contents based on SBR ranged from 155 to 15 898 mg kg−1. TW contents based on zinc were between 413 and 44 812 mg kg−1. Comparison of individual values of SBR and zinc reveals SBR as a more specific marker. Results confirm that most TW ends up in the topsoil within a 2 m distance.
The sampling strategy resulted in representative data for a larger area. Standard deviations of quadruple TED-GC/MS determination of SBR were <10% for all grain size fractions. TED-GC/MS is a suitable analytical tool for determining TW in soil samples without the use of toxic chemicals, enrichment, or special sample preparation.
Microplastic (MP) contamination in natural water circulation is a concern for environmental issues and human health. Various types of polymer materials have been identified and were detected in MP analytic test procedures. Beyond MP polymer type, particle size and form play a major role in water analysis due to possible negative toxicologic effects on flora and fauna. However, the correct quantitative measurement of MP size distribution over several orders of magnitude is strongly influenced by sample preparation, filtration materials and processes, and microanalytical techniques, as well as data acquisition and analysis. In this paper, a reference methodology is presented aiming at an improved quantitative analysis of MP particles. An MP analysis workflow is demonstrated including all steps from reference materials to sample preparation, filtration handling, and MP particle size distribution analysis. Background-corrected particle size distributions (1–1000 µm) have been determined for defined polyethylene (PE) and polyethylene terephthalate (PET) reference samples. Microscopically measured particle numbers and errors have been cross-checked with the total initial mass. In particular, defined reference MP samples (PE, PET) are initially characterized and applied to filtration experiments. Optical microscopy imaging on full-area Si filters with subsequent image analysis algorithms is used for statistical particle size distribution analysis. To quantify the effects of handling and filtration, several blind tests with distilled water are carried out to determine the particle background for data evaluation. Particle size distributions of PE and PET reference samples are qualitatively and quantitatively reproduced with respect to symmetry, and maximum and cut-off diameter of the distribution. It is shown that especially MP particles with a radius of >50 µm can be detected and retrieved with high reliability. For particle sizes <50 µm, a significant interference with background contamination is observed. Data from blank samples allows a correction of background contaminations. Furthermore, for enhanced sampling statistics, the recovery of the initial amount of MP will be qualitatively shown. The results are intended as an initial benchmark for MP analytics quality. This quality is based on statistical MP particle distributions and covers the complete analytic workflow starting from sample preparation to filtration and detection. Microscopic particle analysis provides an important supplement for the evaluation of established spectroscopic methods such as Fourier-transform infrared spectroscopy or Raman spectroscopy.
Stainless steel AISI 304 surfaces were studied after a mild anodic polarization for oxide growth in the presence and absence of two derivatives of vitamin B2 (riboflavin and flavin mononucleotide) that can be secreted by metal‐reducing bacteria and act as a chelating agent for iron species. The alterations in oxide chemistry were studied by means of surface‐sensitive techniques such as X‐ray photoelectron spectroscopy and time‐of‐flight secondary ion mass spectrometry analysis. The complementary electrochemical characterization revealed a preferential growth of an oxide/hydroxide iron‐rich film that is responsible for an altered pit initiation and nucleation behavior. These findings suggest that as the corrosion behavior is determined by the interplay of the chemical and electronic properties, only a mild anodic polarization in the presence of redox‐active molecules is able to alter the chemical and electronic structure of the passive film formed on stainless steel AISI 304. This helps to achieve a profound understanding of the mechanisms of microbially influenced corrosion (MIC) and especially the possible effects of the redox‐active biomolecules, as they may play an important role in the corrosion susceptibility of stainless steel surfaces.
There is growing interest in quantifying microplastics in environmental samples. This application note presents a thermal extraction desorption-gas chromatography/mass spectrometry (TED-GC/MS) method that is well suited to automation and increased sample throughput. The method is also able to detect all particle sizes in the sample as long as the limit of detection (LOD) is reached and allows analysis of larger samples of 15 to 25 mg or more. Samples were decomposed by thermogravimetric analysis (TGA), and the gaseous decomposition products were trapped on a solid-phase sorbent, followed by thermal desorption‑gas chromatography/mass spectrometry (TD-GC/MS) using an Agilent 5977B GC/MSD coupled to an Agilent 7890B GC. Target microplastic particle (MP) polymers were identified in environmental samples including surface water, finished compost, house dust, and drinking water. Quantification of MP polymers in environmental samples provided LODs of 0.06 to 2.2 μg, allowing the detection of MPs in trace amounts with sample weights of up to 1 g. Method repeatability was adequate for reliable quantification with RSDs of approximately 6 to 12%.
A new concept for the ecotoxicological assessment of plastics under consideration of aging processes
(2023)
Microplastics are widely distributed in aquatic and terrestrial environments, but up to now less is known about (eco)toxicological impacts under realistic conditions. Research so far has focused mainly on impacts on organisms by fresh, single‐origin plastic fragments or beads. However, plastics found in the environment are complex in composition, this means different polymer types and sources, with and without additives and in all stages of age, and therefore, in a more or less advanced stage of degradation. For oxidized degradation products that might be released from plastic materials during aging, there is a lack of information on potentially adverse effects on aquatic biota. The latter is of particular interest as oxidized degradation products might become more water soluble due to higher polarity and are more bioavailable, therefore. The present study focused on plastic leachates of polystyrene (PS) and polylactic acid (PLA), which were derived from alternating stress by hydrolysis and ultraviolet (UV) radiation—representing a realistic scenario in the environment. Test specimens of PS, PLA, or a PLA/PS layer (each 50%) were alternately exposed to UV radiation for 5 days followed by hydrolysis for 2 days, for several weeks alternating. Ecotoxicological effects of the storage water (artificial freshwater) of the test specimens and additionally, in a second experimental setup, the effects of five potential polymer degradation products were detected by 72 h algae growth inhibition tests with Desmodesmus subspicatus. Results clearly indicate inhibitory effects on algae growth by contaminants in the storage water of stressed plastics with increasing growth inhibition of proceeding hydrolysis and UV stress times. Different polymers caused variable inhibitions of algae growth with stronger inhibitions by PS and less effects by PLA and the mixed layer of both. Moreover, not microplastic particles but the resulting dissolved degradation products after aging caused the ecotoxicological effects—with strong effects by the oxidized degradation products. The existing data highlight the relevance of plastic aging as a framework for microplastic ecotoxicity evaluation and allow a proof of concept.
Zielsetzung des vom Bundesministerium für Bildung und Forschung geförderten Projektes RUSEKU war es, repräsentative Untersuchungsstrategien für die Detektion von Mikroplastik mittels TED GC/MS in wässerigen Medien zu ermitteln. Dabei wurden verschiedene Probenahmekonzepte und – verfahren für unterschiedliche Fallgestaltungen und Fragestellungen untersucht, sowie neue Filtersysteme entwickelt. Bei der Detektion der Partikel lag der Fokus auf der Anwendung und Weiterentwicklung der ThermoExtraktion/Desorption-Gaschromatographie-Massenspektrometrie (TED-GC/MS) zur Bestimmung von Mikroplastikgehalten. Anwendung fanden die Methoden bei der Beprobung von Flaschenwasser, Waschmaschinenabläufen, dem urbanen Abwassersystem der Stadt Kaiserslautern, sowie in Oberflächengewässer.
Im Verbundprojekt RUSEKU wurde die Probenahme von Wasserproben entscheidend weiterentwickelt. Wichtig ist hierbei zu gewährleisten, dass genügend Merkmalsträger in jeder Probe untersucht werden. Es muss daher eine für den Probenahmeort repräsentative Beprobung hinsichtlich des Wasservolumens in Abhängigkeit der Partikelanzahl gewährleistet sein.
Das Hauptaugenmerk lag im vorliegenden Projekt auf einer praxisnahen Beprobungsstrategie. Es wurden verschiedene Konzepte ausprobiert.
• Grundsätzlich hat sich gezeigt, dass eine Stichprobe eine Momentaufnahme des MP-Massengehaltes zeigt. Es wird eine hohe Statistik, also eine Vielzahl an Messungen am gleichen Probenahmeort, benötigt, um eine valide Aussage über den MP-Gehalt zu machen.
• Es zeigt sich, dass eine integrale Probenahme über mehrere Wochen mit dem SK routinemäßig möglich ist. Die erfassten MP-Massen sind reproduzierbar und robust.
• Die DFZ ist für Stichproben geeignet. Partikel < 50 µm werden eventuell unterschätzt
• Die fraktionierte Filtration kann für Stich- und Mischproben direkt im Feld genutzt werden. Fraktionen von 10 und 5 µm werden später im Labor Vakuum filtriert. Es erfolgt eine Fraktionierung der Probe mit Siebmaschenweiten von 1000, 500, 100, 50, 10 und 5 µm.
• Die fraktionierte Filtration kann auch anschließend an die Beprobung mit dem SK zur Anwendung kommen. Wird die mit dem SK gewonnene Wasserprobe fraktioniert filtriert, kann neben einem MP-Gesamtgehalt auch eine Einschätzung über die Partikelgrößen gewonnen werden.
• Für Wässer mit geringen Partikelzahlen wurde ein Messfiltertiegel entwickelt. Dieser hat eine Maschenweite von 6 µm. Seine Anwendung kann mögliche Verluste beim Transferieren vom Probenahmetool zum Messgefäß und mögliche Kontaminationen reduzieren.
Die Optimierung der Probenahmestrategie wurde durch Modellversuche und Simulationen unterstützt. Modellversuche zum Sinkverhalten und Simulationen von MP in realen Gewässern verdeutlichten das komplexe Verhalten der Partikel. Es konnte gezeigt werden, dass Partikel ab einer bestimmten Größe (und kleiner) bei genügend starker Turbulenz sich in der Wassersäule unabhängig von ihrer Dichte verhalten und so auch MP mit kleiner Dichte (z.B. PE) in der gesamten Wassersäule zu finden sind. Es konnte mit dem TEM die Existenz von NP gezeigt werden.
Ein wesentlicher Aspekt des RUSEKU Projektes war die Beprobung realer Kompartimente. Beprobt wurde neben Oberflächengewässern, das urbane Abwassersystem der Stadt Kaiserslautern, Waschmaschinenabwasser und Flaschenwasser.
• In Oberflächengewässern wurde hauptsächlich PE gefunden. Je nach Probe und Gewässer konnten auch PP, PS, PET, PA, SBR und Acrylate nachgewiesen werden.
• Im urbanen Abwassersystem der Stadt Kaiserslautern konnte an allen Probenahmestandorten MP nachgewiesen werden. Es wurde hauptsächlich PE, neben geringeren Mengen an PP, PS und SBR gefunden. Nach einem Regenereignis war der SBR Anteil deutlich erhöht.
• Die Beprobung eines realen Wäschepostens, bestehend aus T-Shirts und Hemden mit PA/CO oder PES/CO Mischgewebe, zeigte einen PA- und PES-Austrag im Waschwasser. Der überwiegende Teil der detektierten Fasern ist aber auf Baumwolle zurückzuführen. Reine gravimetrische Messungen zur Detektion von MP führen zu einer starken Überschätzung.
• In Flaschenwasser (PET-Flaschen) konnte MP detektiert werden. PET wurde nur im stillen Mineralwasser, nicht in Mineralwasser mit Kohlensäure gefunden werden. Teilweise wurde auch das MP-Material des Verschlusses im Wasser detektiert.
• Für Luftproben konnte ein Aufbau zur größenselektiven Beprobung getestet werden.
Neben der Probenahme hat das Projekt auch gezeigt, dass die TED-GC/MS geeignet für die MP-Detektion im Routinebetrieb ist. Die TED-GC/MS konnte weiter optimiert werden. Es wurden MP-Massen bestimmt.
Im Projekt wurden erste realitätsnahe Referenzmaterialien für die MP Detektion hergestellt. Die Herstellung von realitätsnahen Polymeren in ausreichender Homogenität und Menge hat sich als große Herausforderung herausgestellt.
There is only sparse empirical data on the settling velocity of small, non-buoyant microplastics thus far, although it is an important parameter governing their vertical transport within aquatic environments. This study reports the settling velocities of 4031 exemplary microplastic particles. Focusing on the environmentally most prevalent particle shapes, irregular microplastic fragments of four different polymer types (9–289 µm) as well as five discrete length fractions (50–600 µm) of common nylon and polyester fibers were investigated, respectively. All settling experiments were carried out in quiescent water using a specialized optical imaging setup. The method has been previously validated in order to minimize disruptive factors, e.g. thermal convection or particle interactions, and thus enable the precise measurements of the velocities of individual microplastic particles (0.003–9.094 mm/s). Based on the obtained data, ten existing models for predicting a particle’s terminal settling velocity were assessed. It is concluded that models, which were specifically deduced from empirical data on larger microplastics, fail to provide accurate predictions for small microplastics. Instead, a different approach is highlighted as a viable option for computing settling velocities across the microplastics continuum in terms of size, density and shape.
Despite the increasing concern about the harmful effects of micro- and
nanoplastics (MNPs), there are no harmonized guidelines or protocols yet available for MNP ecotoxicity testing. Current ecotoxicity studies often use commercial spherical particles as models for MNPs, but in nature, MNPs occur in variable shapes, sizes and chemical compositions. Moreover, protocols developed for chemicals that dissolve or form stable dispersions are currently used for assessing the ecotoxicity of MNPs. Plastic particles, however, do not dissolve and also show dynamic behavior in the exposure medium, depending on, for example, MNP physicochemical properties and the medium’s conditions such as pH and ionic strength. Here we describe an exposure protocol that considers the particle-specific properties of MNPs and their dynamic behavior in exposure systems. Procedure 1 describes the top-down production of more realistic MNPs as representative of MNPs in nature and particle characterization (e.g., using thermal extraction desorption-gas chromatography/mass spectrometry). Then, we describe exposure system development for short- and long-term toxicity tests for soil (Procedure 2) and aquatic (Procedure 3) organisms. Procedures 2 and 3 explain how to modify existing ecotoxicity guidelines for chemicals to target testing MNPs in selected exposure systems. We show some examples that were used to develop the protocol to test, for example, MNP toxicity in marine rotifers, freshwater mussels, daphnids and earthworms. The present protocol takes between 24 h and 2 months, depending on the test of interest and can be applied by students, academics, environmental risk assessors and industries.
The scientific and practical challenge of detecting microplastics (MPs) in the environment in a targeted and rapid manner is solved by innovative coupling of thermogravimetric analysis with mass spectrometric methods.
Fast identification and quantitative determination of most thermoplastic polymers and elastomers is possible by using thermal extraction Desorption gas chromatography–mass spectrometry (TED-GC–MS).
Zur Ermittlung von Mikroplastik-Gehalten in verschiedenen Umweltmatrices ist ein schnelles Detektionsverfahren für die Routineanalytik notwendig. Ein solches Verfahren wird hier in Form der ThermoExtraktion/Desorption-GasChromatographie/ MassenSpektroskopie (TED-GC/MS) vorgestellt. Neben grundlegenden verfahrensspezifischen Erläuterungen zur Identifizierung und Quantifizierung von Mikroplastik werden auch exemplarische Beispiele aus unterschiedlichen Umweltkompartimenten und Produkten dargestellt. Neu vorgestellt wird ein neues Verfahren zur Analytik von Flaschenwasser. Dazu wurde ein Messfiltertiegel entwickelt, der besonders für Proben mit geringen Gehalten an abfiltrierbaren Stoffen geeignet ist
In this breakout session first, an introduction is given on the planning and organisation of an inter-laboratory comparison (ILC) under the pre-standardisation plattform VAMAS within the newly formed technical working area TWA 45 Micro and Nano Plastics in the Environment. An update with the ILCs on micro- and nanoplastic performed so far is also given. In the third part, the requirements for a reference materials are presented. The needs from the different H2020 micro- and nanoplastic projects are collected and compiled in an ILC matrix for joint activities as the next steps.
Materials
(2022)
The occurrence of microplastic (MP) in food products, such as beverages in plastic bottles, is of high public concern. Existing analytical methods focus on the determination of particle numbers, requiring elaborate sampling tools, laboratory infrastructure and generally time-consuming imaging detection methods. A comprehensive routine analysis of MP in food products is still not possible. In the present work, we present the development of a smart filter crucible as sampling and detection tool. After filtration and drying of the filtered-off solids, a direct determination of the MP mass content from the crucible sample can be done by thermal extraction desorption gas chromatography mass spectroscopy (TED-GC/MS). The new filter crucible allows a filtration of MP down to particle sizes of 5 µm. We determined MP contents below 0.01 µg/L up to 2 µg/L, depending on beverages bottle type. This may be directly related to the bottle type, especially the quality of the plastic material of the screw cap. Dependent on the plastic material, particle formation increases due to opening and closing operations during the use phase. However, we have also found that some individual determinations of samples were subjected to high errors due to random events. A conclusive quantitative evaluation of the products is therefore not possible at present.
A harmonization of sampling, sample preparation and detection is pivotal in order to obtain comparable data on microplastics (MP) in the environment. This paper develops and proposes a suitable sampling concept for waterbodies that considers different plastic specific properties and influencing factors in the environment.
Both artificial water including defined MP fractions and the discharge of a wastewater treatment plant were used to verify the derived sampling procedure, sample preparation and the subsequent analysis of MP using thermal extraction-desorption gas chromatography - mass spectrometry (TED-GC-MS).
A major finding of this paper is that an application of various particle size classes greatly improves the practical handling of the sampling equipment. Size classes also enable the TED-GC-MS to provide any data on the MP size distribution, a substantial sampling property affecting both the necessary sampling volume and the optimal sampling depth.
In the artificial water with defined MP fractions, the recovery rates ranged from 80 to 110%, depending on the different MP types and MP size classes. In the treated wastewater, we found both Polyethylene and polystyrene in different size classes and quantities.
Nebulizing of polymer solutions, in a high-voltage field under atmospheric conditions by electrospray ionization (ESI), is a comfortable way to deposit ultra-thin layers of polar or ionic polymers onto any conductive substrate materials. The substrate is grounded and the polymer solution is sprayed through a powered capillary. The formed charged droplets shrink by solvent evaporation during their way to the grounded substrate, the charges close ranks and the droplets collapse consecutively by charge repulsion, thus forming finally charged single macromolecules. After their discharging at the grounded substrate, an ultrathin ‘quasi-monomolecular’ polymer layer is formed. It could be shown by imaging of scratches through the polymer layer by atomic force microscopy that the deposited polymer layers are dense at a thickness of about 10 nm. Carbon fibre bundles were coated with poly (allylamine) (PAAm) or poly(acrylic acid) (PAA) as potential adhesion-promoting layers in fibre–polymer composites. The polymer deposition is self-inhibiting after formation of a continuous coverage of about 200 nm for PAAm and 30 nm for PAA as result of surface charging. Continuous deposition onto such isolating layers or polymers without charging can be achieved by using current of alternating polarity. The film formation is self-healing because of the electrophoretic effect, i.e. the ion discharging occurs preferentially at noncoated areas. This electrophoretic effect of ESI was demonstrated by completely enwrapping all the carbon fibres of the roving within a distance of about 100 μm far from its outside and also at the backside of the fibre bundle with about 80% of the topside coverage, as measured by X-ray photoelectron spectroscopy and visualized using scanning electron microscopy.
Microplastic detection in water samples becomes important for tracing microplastic sources. Microplastic may harm desalination facilities by blocking filters and disturbing the marine food chain. Thermo analytical methods such as pyrolysis gas chromatography mass spectroscopy, and spectroscopic methods like (micro) Raman spectroscopy or (micro) Fouriertransform infrared spectroscopy in combination with appropriate filters and sample preparation are suitable for analyzing microplastics on a scale from 1 µm to 1000 µm fast and unambiguous. While the thermo analytical methods are suitable for larger sample volumes, Raman spectroscopy and Fouriertransform infrared spectroscopy are able to detect and analyze single microplastic particles for instance in bottled water. Machine learning algorithms ensure a reliable classification of different plastic materials.
This presentation summarizes outcomes of the CUSP projects POLYRISK and PlasticsFatE according to thermoanalytical methods.It highlights the importants of analytical methods to measure physical and chemical properties of the test materials. These informations are neccessary for interpretation of the toxicological test results.
Understanding the interaction between boehmite and epoxy and the formation of their interphases with different mechanical and chemical structures is crucial to predict and optimize the properties of epoxy-boehmite nanocomposites. Probing the interfacial properties with atomic force microscopy (AFM)-based methods, especially particle-matrix long-range interactions, is challenging. This is due to size limitations of various analytical methods in resolving nanoparticles and their interphases, the overlap of interphases, and the effect of buried particles that prevent the accurate interphase property measurement. Here, we develop a layered model system in which the epoxy is cured in contact with a thin layer of hydrothermally synthesized boehmite. Different microscopy methods are employed to evaluate the interfacial properties. With intermodulation atomic force microscopy (ImAFM) and amplitude dependence force spectroscopy (ADFS), which contain information about stiffness, electrostatic, and van der Waals forces, a soft interphase was detected between the epoxy and boehmite. Surface potential maps obtained by scanning Kelvin probe microscopy (SKPM) revealed another interphase about one order of magnitude larger than the mechanical interphase. The AFM-infrared spectroscopy (AFM-IR) technique reveals that the soft interphase consists of unreacted curing agent. The long-range electrical interphase is attributed to the chemical alteration of the bulk epoxy and the formation of new absorption bands.
In recent years, thermoextraction/desorption-gas chromatography/mass spectrometry (TED-GC/MS) has been developed as a rapid detection method for the determination of microplastics (MP) mass contents in numerous environmentally relevant matrices and, in particular, for the measurement of polymers in water samples without time-consuming sample preparation. The TED-GC/MS method was applied to investigate a typical European municipal wastewater system for possible MP masses. Such investigations are important in view of the recent revision of the Urban Wastewater Treatment Directive. Four different representative sampling sites were selected: greywater (domestic wastewater without toilet), combined sewer, and influent and effluent of a wastewater treatment plant (WWTP). All samples were collected by fractional filtration. Filtration was carried out over mesh sizes of 500, 100, 50, and in some cases, 5 µm. Polyethylene (PE), polypropylene (PP), and polystyrene (PS) were detected in all samples, with the PE fraction dominating in all cases. Styrene-butadiene rubber which serves as an indication of tire abrasion, was only found in the influent of the WWTP. The highest MP mass contents were found in the combined sewer, so MP can become a source of pollution during heavy rain events when the capacity limits of the effluent are reached, and the polluted effluent is released uncontrolled into the environment. Based on the studies, MP retention from the WWTP could be estimated to be approximately 96%. Few trends in polymer type or mass contents were detected within the different fractions of the samples or when comparing samples to each other.
The occurrence of small particles consisting of organic polymers, so-called microplastic (MP), in aquatic Environments attracts increasing interest in both public and science. Recent sampling campaigns in surface Waters revealed substantial numbers of particles in the size range from a few micrometers to a few millimeters. In order to validate sample preparation, identification and quantification and to investigate the behavior of MP particles and potential toxic effects on organisms, defined MP model particles are needed. Many studies use spherical compounds that probably behave differently compared to irregularly shaped MP found in environmental samples.
However, preparation and handling of MP particles are challenging tasks and have been systematically investigated in the present study. Polystyrene (PS) as a commonly found polymer with a density slightly above that of water was selected as polymer type for milling and fractionation studies. A cryogenic ball mill proved to be practical and effective to produce particles in the size range from 1 to 200 μm. The yield of small particles increased with increasing pre-cooling and milling durations. Depending on the concentration and the size, PS particles do not completely disperse in water and particles partly creep vertically up along glass walls. Stabilized MP suspensions without use of surfactants that might harm organisms are needed for toxicological studies. The stabilization of PS particle suspensions with ozone treatment reduced the wall effect and increased the number of dispersed PS particles but increased the dissolved organic carbon concentration and changed the size Distribution of the particles.
A sedimented freshwater suspended organic matter fortified with particles of polyethylene (PE), polypropylene (PP), polystyrene (PS), and polyethylene terephthalate (PET) was employed in an interlaboratory comparison of thermoanalytical methods for microplastics identification and quantification. Three laboratories performed pyrolysis gas chromatography-mass spectrometry (Py-GC-MS), three others provided results using thermal extraction desorption followed by gas chromatography coupled to mass spectrometry (TED-GC-MS). One participant performed thermogravimetry-infrared spectroscopy (TGA-FTIR) and two participants used thermogravimetry coupled to mass spectrometry (TGA-MS). Further participants used differential scanning microscopy (DSC), a procedure based on micro combustion calorimetry (MCC) and a procedure based on elemental analysis.
Each participant employed a different combination of sample treatment, calibration and instrumental Settings for polymer identification and quantification. Though there is obviously room for improvements regarding the between-laboratory reproducibility and the harmonization of procedures it was seen that the participants Performing Py-GC-MS, TED-GC-MS, and TGA-FTIR were able to correctly identify all polymers and to report reasonable quantification results in the investigated concentration range (PE: 20.0 μg/mg, PP: 5.70 μg/mg; PS: 2.20 μg/mg, PET: 18.0 μg/mg). Although for the other methods limitations exists regarding the detection of specific polymers, they showed potential as alternative approaches for polymer quantification in solid environmental matrices.
Discussions in science, politics and public media about microplastic in the Environment and its unclear effects for animals and humans are common these days.
Although microplastic findings in water, soil and even air are well known, no general estimations about the quality or quantity of microplastic particles in environment exit. Research is necessary to develop reliable and traceable, harmonized protocols for sampling, sample preparation and fast, but accurate analysis for qualitative and quantitative measurement of microplastic in various environmental matrices. For development of such reliable and traceable methods, the use of microplastic reference materials is necessary to assess various concepts. These microplastic reference particles should be an appropriate reflection of the microplastic particles found in environment.
Due to the high use in industrial products six polymers seem to be relevant in environment as microplastic particles: polyethylene (PE), polypropylene (PP), polystyrene (PS), polyethylene terephthalate (PET), polyamide (PA) and polyvinylchloride (PVC). The raw source of These thermoplastic materials are pellets or granulate with dimensions of 1 to 5 mm in diameter. Most common they own a regular cylindrical shape or are prolate sphericals. These can be bought cost-efficient by various polymer producers. But discussions in microplastic research topic lead to particle sizes down to 1 μm. Furthermore, various unregular shapes and geometries of the particles have to be considered as well as an oxidized surface. In the present work we engage the acquisition and production of
realistic reference material. Different aspects should demonstrate the complex and difficult task of generating approriate, cost-efficient and well-defined reference materials. The particle size distribution by using
different particle sizing methods as well as individual particle shapes are documented. Different material properties were addressed. PE, PS and PA were chosen as typical and relevant microplastic with opposite individual material characteristics in density and glass Transition temperature. The easiest possibility for acquisition of small microplastic particles is the purchase of polymer emulsion particles (20 to 150 μm).
An alternative possibility to produce small microplastic particles is milling under liquid nitrogen conditions in cryo mills. Particles purchased or self-made differ strongly in shape and size depending on production method.
SETAC
The plastic value chain, central part of modern living, caused environmental pollution and bioaccumulation of plastic nanoparticles (PNPs). Their ubiquitous presence in different environmental and biological compartments has become a serious threat to human health and ecosystems. Frequently used plastic materials such as polypropylene (PP), polystyrene (PS) and polyethylene (PE) have been detected in the form of PNPs in the food chain, soil, water and air, as well as in human feces and blood. In this study, we aimed to provide novel insights in endocrine disrupting properties of PNPs using in vitro estrogen receptor (ER) transactivation assay. The effects of PP-NPs, PE-NPs and PS-NPs and their mixture on T47D-KBluc cell line stably transfected with luciferase as reporter enzyme was evaluated by means of cytotoxicity, cellular uptake and ER activation. Tested dose range for PNPs was 0.001 – 10 mg/L. Both cellular uptake and cytotoxicity for all PNPs was found to be dose-dependent. Only the highest dose of PP-NPs and PE-NPs induced apoptosis and cell death, while PS-NPs were not cytotoxic in tested dose range. For tested concentrations, PP-NPs and PE-NPs showed significant agonistic activity on ER, while PS-NPs cannot be considered ER active. When, applied as mixture, PNP demonstrated additive toxicity effects compared to the effect of each individual PNPs. Additivity was also observed for ER agonistic effect of PNPs mixture according to the benchmark dose-addition modelling approach. This study provides missing science-based evidence on endocrine disrupting effects of PE-NPs, PP-NPs, PS-NPs and their mixtures and highlights the importance of considering unintentional, aggregate and combined exposure to different PNPs in risk management.
Nowadays, sensors based on polymers/nanostructured metal oxide composites have been investigated exten-sively because of their sensitivity to NO2 gas at ambient temperature. In this work, nanocomposite membranes of xanthan gum (XG) with different contents of MnO2 nanoparticles were prepared as a potential NO2 gas sensor operating at room temperature by a simple one-step oxidation-reduction reaction. The structural, morphological, thermal, and electrical properties of the composite membrane were investigated. The FT-IR results confirm the successful preparation of MnO2 through the oxidation of XG by KMnO4 and reveal further the structural changes of the XG/MnO2 nanocomposite upon its exposure to NO2 gas. The capping of the synthesized MnO2 nano-particles by XG, the surface composition of the XG/MnO2 nanocomposite membranes, and the effect of NO2 gas on the surface composition was investigated using the XPS technique. The DC conductivity and dielectric loss of nanocomposites were higher than for neat XG. The conductivities of the nanocomposites XG/MO-4, XG/MO-4/ low NO2, and XG/MO-4/high NO2 composites are half, one, and three orders of magnitude higher than that for pure XG revealing a transition from insulating to conductive properties. The results demonstrated that XG/MnO2 nanocomposite membranes are promising for potential applications in NO2 gas sensing.
Polymer deposition morphology by electrospray deposition - Modifications through distance variation
(2014)
Electrospray deposition (ESD) of highly diluted polymers was examined with regard to the deposited surface structure. Only the flight distance (flight time) onto the resulting deposited surface was varied from 20 to 200 mm.
An apparatus without any additional heating or gas flows was used. Polyacrylic acid (PAA) and polyallylamine (PAAm) in methanol were deposited on Si wafers. The polymer layers were characterized by scanning electron microscopy, X-ray photoelectron spectroscopy, derivatization reactions and Fourier transform infrared spectroscopy using a grazing incidence unit.
SEM images illustrated the changing structures of PAA and PAAm. For PAA the deposited structure changed from a smooth film (20 mm) to a film with individual droplets on the coated surface (100 mm and 200 mm), while for PAAm individual droplets can be seen at all distances. The ESD process with cascades of splitting droplets slows down for PAA after distances greater than 40 mm. In contrast, the ESD process for PAAm is nearly stopped within the first flight distance of 20 mm. Residual solvent analysis showed that most of the solvent evaporated within the first 20 mm capillary-sample distance.
Die Elektrospray-Ionisations (ESI)-Vernebelung von Polymerlösungen wird analytisch zur massenspektrometrischen Bestimmung der Molmassen von Makromolekülen genutzt. Dabei werden die Polymermoleküle nach einem speziellen Mechanismus im Hochspannungsfeld unter Normaldruckbedingungen vereinzelt und in das Massenspektrometer überführt. Dieser Prozeß kann auch zur flächigen Abscheidung einzelner Polymermoleküle genutzt werden. Die Struktur und Zusammensetzung sowie die Molmassenverteilung der Polymere bleiben dabei erhalten. Schichten polarer oder ionischer Polymere der Dicke einer Quasi-Monolage bis hin zu mehreren 100 Nanometern können abgeschieden werden. Erwähnenswert ist, daß der ESI-Prozeß zu den elektrophoretischen Verfahren gehört, was die Ausbildung lochfreier Schichten auf elektrisch leitenden Substraten nicht nur auf der der Spraydüse zugewandten Seite ermöglicht, sondern auch auf der abgeschatteten Rückseite. Dieses Verhalten wurde zur vollständigen ESI-Umhüllung von dichtgepackten Kohlenstoff-Faser-Bündeln mit haftvermittelnden Polymerschichten ausgenutzt.
Der Vortrag wurde im Rahmen der Abschlusskonferenz des Forschungsschwerpunktes "Plastik in der Umwelt" des BMBF gehalten. Er fasst die Ergebnisse des Verbundprojektes RUSEKU zusammen. Es wurde die Herstellung verschiedener Testmaterialien für die Mikroplastik (MP) Analytik beschrieben. Im weiteren geht es um verschiedene Ansätze MP kostengünstig und schnell zu detektieren, z.B. mit Nahinfrarotspektroskopie. Nanoplastik konnte mit der Transmissionselektronenmikroskopie sichtbar gemacht werden. Für die praxisnahe Beprobung von Gewässern wurde die Fraktionierte Filtration entwickelt. Integrale Beprobungen können mit dem Sedimentationskasten erfolgen. Als Beispiele für die Beprobung realer Gewässer wurde das urbane Abwassersystem Kaiserslautern, Getränkewasser und Waschmaschinenwasser gezeigt.
Mikroplastik findet sich in Ozeanen, Seen, Flüssen und Bächen. Es kann in unserem Boden, in der Luft und sogar in Organismen nachgewiesen werden. Jedes Jahr werden weltweit Millionen Tonnen freigesetzt. Doch wo und wie landet Mikroplastik in der Umwelt? Und wie können wir diese winzigen Partikel nachweisen?
Monitoring von Mikroplastik
(2021)
The pathways of plastics, especially of microplastic (MP), in environmental compartments, particularly in aquatic systems, are not well understood. The critical point is the lack of fast, harmonised methods for sampling, sample preparation and sample analysis. These three analytical steps are dependent on one another and must be optimised.
In recent years, we developed a method for representative sampling and fast detection of MP in aqueous systems. The sampling in different freshwater bodies is performed in the field with a fractionated filtration system using mesh sizes of 500, 100 and 50 µm. For water with an intermediate or high content of suspended particular matter a minimum of 1000 L has to be filtered. In the lab, mesh sizes of 10 and 5 µm are used for further filtration. Subsequently, the water filtrates of the different particle size classes are sterilised, dried, weighed and homogenised, if necessary.
Conventional methods for MP analysis are infrared and raman spectroscopy, giving information on the shapes and numbers of individually identified MP particles. Our focus is on the determination of mass contents of various polymers potentially contained in environmental samples. For qualitative and quantitative MP detection TED-GC-MS is used, a two-step method based on gas chromatography-mass spectrometry (GC-MS) with previous thermal extraction. This method not only enables us to screen the samples for characteristic marker-molecules, thus identifying single polymers, but furthermore allows the calculation of mass contents of individual polymers. In the present work, different freshwater compartments were exemplarily studied to identify containing polymers and calculate their mass content in MP particles.
The number of publications reporting the amount of microplastic (MP) all over the world increased rapidly. Methods used so far are very time consuming and not able to provide information on total contents. As harmonised sampling, sample preparation and analysis strategies are missing different studies can hardly be compared and quantitative data, including identification and mass contents of the polymers found, are missing. This leads to a lack of comprehensive understanding of MP occurrence, source and entry pathways into the environment.
We developed a method, Thermal Extraction/Desorption-Gaschromatography-Massspectrometry, as a fast screening method for MP analysis. Solid residues of water samples are heated up to 600 C under a N2 atmosphere without any sample preparation. The collected decomposition gases are separated in a gas chromatography system and detected in a mass spectrometer. Mass contents of the identified polymers can be calculated.
In this presentation we will show first results from the influent of the wastewater treatment plant Kaiserslautern (Germany) and its combined sewage system as possibly entry pathway. In order to determine the relevance of wastewater split streams analysis of grey water will be conducted. Samples are fractionally filtered by a sieve cascade with mesh sizes of 500, 100, 50 µm.
This study reflects typical consumer textile washing behaviour while taking into account existing standards in the household appliance and garment industries. Two garments were washed repeatedly with artificial dirt and detergent 30 times. The collected washing water was separated using fractional filtration. Textile physical tests were used to follow property changes of the garments, the microplastic release is determined using thermoextraction/desorbtion–gas chromatography/mass spectrometry and the total organic carbon was measured as a sum parameter for the organic bonded carbon. This article shows the importance of a reality‐based approach when investigating microplastics of textile origin in the laundry care process. Deposits of detergent and dirt on the textiles were detected. The total mass of sieve residues was much higher than the release of synthetic polymers. The cotton content of the garments causes a much higher fibre release than synthetic fibres. Both will lead to false results by purely gravimetric analysis because nonpolymer fibres will be included microplastic mass. The results cannot be generalised only by the main polymer type, knowledge of the textile construction must be included for final evaluation.
Material Selection Strategy
(2023)
The electrospray ionization (ESI) method was used for deposition of thin films of poly(acrylic acid) (PAA) onto ZSM-5, Cu/ZSM-5 and Ag-Cu/ZSM-5 zeolites. This method allowed the formation of uniform polymer films of controlled thickness on conductive substrates.
The zeolites were prepared home-made. The effect of incorporation of Cu (5 wt.%) and Ag-Cu (1+4 wt.%) onto ZSM-5 on its particle size, unit cell parameters and crystallinity was investigated.
The deposited PAA layer acts as a common dispersing agent with its ionic COOH (COO-) groups. The antibacterial activity towards the bacterial strains such as Staphylococcus pneumonia (S. Pneumonia), Bacillus subtilis (B. subtilis), Escherichia coli (E. coli) and Pseudomonas aeruginosa (P. aeruginosa) as Gram positive and Gram negative bacteria, respectively, and Aspergillus fumigatus (A. fumigatus), Candida albicans (C. albicans) as Fungi was evaluated. The chemical and physical modifications of ZSM-5, Cu/ZSM-5 and Ag-Cu/ZSM-5 surfaces were characterized by X-ray photoelectron spectroscopy, Fourier-transform infrared spectroscopy, atomic force microscopy and X-ray diffraction.
The Cu/ZSM-5 and Ag-Cu/ZSM-5 nanocomposites coated with a 10 nm thick PAA layer exhibit significant antibacterial activity. The carboxyl (¬-COOH) or the corresponding carboxylate groups (¬-COO-) interact with Cu2+ and Ag+ ions by formation of ionic bonds (¬-COO-Ag+ or 2 ¬-COO->Cu2+). Moreover, short exposure to light and temperature has reduced Cu2+ and Ag+ to Cu0 and Ag0.
Microplastic particles with sizes between 1 to 1000 μm are widely distributed worldwide. Origin, transport pathways and fate are poorly known, as sampling, sample preparation and detection methods are major challenges. In addition, reference materials that mimic environmental particles are lacking. Most challenging is the yield of MP particle production and the need for resource-intensive grinding with liquid nitrogen. In this paper, a machine is designed to produce aged microplastic particles as reference material candidates with high yield. The machine is based on ultraviolet aging of a thin foil and mechanical fragmentation using clean air. An example of aging and fragmentation of high density polyethylene with additional physical and chemical characterization of shape, size, aging state by carbonyl index and density is presented.
Die große Herausforderung in der Detektion von Mikroplastik (MP)‑Partikeln (1-1000 µm) besteht darin, sie neben Millionen von natürlichen Partikeln in Umweltproben nachzuweisen. Zum Aufspüren von Senken, Eintragspfaden und für Monitoring-Kampagnen ist ein schnelles, automatisiertes Verfahren unerlässlich. Ein solches Verfahren wurde an der Bundesanstalt für Materialforschung und -prüfung (BAM) mit der ThermoExtraktion/Desorption-Gaschromatographie-Massenspektrometrie (TED-GC/MS) in den letzten Jahren entwickelt.
All over the world, microplastic (MP) particles (particle size: 1 - 1.000 µm) are found in water, soil, air, biota and even food products. But plenty of these discussed findings are based on a very low number of real datasets, which are extrapolated to general projections. Furthermore, most data are not comparable because the strategies for sampling, sample preparation and detection methods are not harmonised/ or standardised. This would require extensive proficiancy tests. Because of the ubiquity presence and the unclear risks, which might arise from those particles, various political and environmental organisations (i.e. OECD, UNEP, WHO) identify the reduction of plastic entry in the environment as a key challenge for now and the future. This challenge includes the identification of relevant entry pathways but also the demand of harmonised, meaningful and reliable analytical procedures.
Regarding this task within the last few years, a fast practical solution for MP analysis has been developed, which includes the steps of representative sampling, adequate sample preparation and fast detection. Sampling is done by fractional filtration over sieves with mesh sizes of 500, 100, 50 and 5 µm [1]. The received samples are measured by ThermoExtraction/Desorption-Gas Chromatography-Mass Spectrometry (TED-GC-MS) [1,2]. for the most abundant polymers used in practice, which are polyethylene (PE), polypropylene (PP), polystyrene (PS), polyethylene terephthalate (PET), polyamide (PA) and acrylate as well as styrene-butadiene-rubber (SBR), a main component of tires.
The present presentation will give first-time insight in a comprehensive dataset of microplastic analysis for an exemplary urban sewage system. MP mass contents of different waters at several days, such as greywater, stormwater retention tank, influent and effluent of a wastewater treatment plant (WWTP) within an urban sewage system in Germany are determined. Furthermore, the mass of the polymers found in dry weather and rain weather flow are compared. The use of these large datasets allows first expressive conclusions regarding the contribution of urban sewage system to the MP entry sources in the environments.
We found PP and PS in all different waters. Furthermore, there is SBR in influent and also in effluent of the WWTP. Surprisingly, we could also detect hugh amounts of PE in the effluent of the WWTP.
Detektion von Mikroplastik
(2022)
Seit einigen Jahren wird in den Medien viel über das Thema Mikroplastik (MP) diskutiert. Dabei wird häufig von einer großen Anzahl an MP-Partikeln in allen Bereichen der Umwelt, wie dem Wasser, dem Boden, der Luft und in Biota sowie über mögliche Gefahren ausgehend von MP, berichtet. Jedoch sind diese Studien häufig nicht untereinander vergleichbar, da verschiedene Konzepte der Probennahme, der Aufbereitung und unterschiedliche Detektionsverfahren verwendet werden. Um diesen Mangel an vergleichbaren und aussagekräftigen Daten zu beheben, wird aktuell versucht, eine Harmonisierung der Mikroplastikanalytik voranzutreiben. Neue, schnellere Methoden zur MP Quantifizierung wurden entwickelt. Gleichzeitig werden neue Strategien zur Probenahme und Probenvorbereitung konzipiert, da hier die Fehlerquellen besonders große Auswirkungen auf das Ergebnis haben.
In diesem Vortrag werden verschiedene Verfahren bezogen auf Probennahme, -vorbereitung und Analytik gezeigt und bezüglich ihres möglichen Ergebnisses diskutiert.
Zur Validierung und Harmonisierung von verschiedenen Methoden in der Mikroplastik-Analytik werden polymere Referenzmaterialien benötigt. In diesem Vortrag wird dargestellt, was bisher an der BAM zu Referenzmaterialien für die Mikroplastik-Analytik entwickelt wurde, wo es hingehen soll und ein Überblick über bisher gelaufene Vergleichsuntersuchungen gebracht.
Plasma polymers and electrospray-ionization (ESI) polymer layers are compared for most efficient adhesion promotion in carbon fiber-epoxy resin composites. The ultra-thin ESI layers (2–30 nm) of commercial poly(acrylic acid) and poly-(hydroxyethylmethacrylate) produce an significant increase of adhesion measured by single-fiber pull out tests.
However, plasma Treatment has also advantages, such as simultaneous activation of the fiber substrate. Chemical structure and composition are rather far from the regular structure of commercial polymers as deposited by ESI processing.
In den Umweltmedien Wasser, Boden und Luft wird Mikroplastik (MP) gefunden. Mögliche Eintragspfade, besonders Einträge über den Klarlauf kommunaler Klärwerke, sind unklar. Dazu wurde das Klärwerk Ruhleben in Berlin an jeweils vier Tagen im Sommer- und Winterbetrieb beprobt. Es wurde jeweils 1 m3 Klarlauf fraktioniert filtriert (500, 100 und 50 µm Siebe). Weiterhin wurde Rohabwasser exemplarisch untersucht. Als Analyse-methoden wurden die TED-GC-MS und die FTIR Mikroskopie verwendet.
Bei der TED-GC-MS wird die Probe zunächst thermisch extrahiert, bevor die charakteristischen Zersetzungsgase mittels einer GC-Säule getrennt und im MS detektiert werden [1,2]. Es ist hier erstmals gelungen, nicht nur das MP zu identi-fizieren, sondern auch eine Massenbilanz zu erstellen und so eine quantitative Auswertung vorzunehmen. Es wurde PE, PS ganzjährig und PP im Sommer gefunden. Das Klärwerk Ruhleben hat einen Rückhalt an MP von 99%.
In diesem Beitrag wird der Einfluss des Aktivkohleprodukts auf die Adsorption von Spurenstoffen aus Kläranlagenablauf gezeigt und diskutiert. Im zweiten Teil wird das Material Aktivkohle analytisch charakterisiert und die Eigenschaften systematisiert. Die gewonnenen Erkenntnisse werden mit Bezug zu Praxislösungen zusammengefasst.
Results from different methods applied to micro- and nanoplastics (MNPs) analysis show that there are large gaps in harmonisation with respect to terminology, size classes, sample preparation protocols and, finally, to the comparability of the measurands and descriptors.
Within the European research cluster to understand the health impacts of micro- and nanoplastics (CUSP) working group WG3-Inter-Laboratory Comparisons an overview of the existing detection methods revealing advantages and disadvantages regarding the analytical tasks is being compiled. There is a clear need to develop high class characterized reference materials for MNPs in the size ranges of 100-10 µm and smaller than 10 µm, so that these can be used to validate methods and to make results comparable. Inter-laboratory comparisons (ILCs) on model samples with complex matrices regarding mass, or water samples for number-based methods, will help us to advance the process of harmonization as well as to train users early in process of developing new methods.
We plan to keep all five CUSP projects well-connected also with the 'outside' MNP projects and ILCs and to extract the optimum of needs, capabilities, and efforts in order to launch new VAMAS ILCs which should expand already available ones.
An immobilization of graphene oxide (GO) into a matrix of polyvinyl formaldehyde (PVF) foam as an eco-friendly, low cost, superior, and easily recovered sorbent of Pb ions from an aqueous solution is described. The relationships between the structure and electrochemical properties of PVF/GO composite with implanted Pb ions are discussed for the first time. The number of alcohol groups decreased by 41% and 63% for PVF/GO and the PVF/GO/Pb composite, respectively, compared to pure PVF. This means that chemical bonds are formed between the Pb ions and the PVF/GO composite based on the OH groups. This bond formation causes an increase in the Tg values attributed to the formation of a strong surface complexation between adjacent layers of PVF/GO composite. The conductivity increases by about 2.8 orders of magnitude compared to the values of the PVF/GO/Pb composite compared to the PVF. This means the presence of Pb ions is the main factor for enhancing the conductivity where the conduction mechanism is changed from ionic for PVF to electronic conduction for PVF/GO and PVF/GO/Pb.