The LEK94 is a Ni-base superalloy single crystal (SX) of the second generation, a materials class which is important for its high temperature creep resistance (>1000°C) in first stage blades of low-to-medium pressure gas turbines. Monocrystalline Ni-base superalloy SXs have a two-phase microstructure consisting of small cubes (' phase with the ordered L12 crystal structure, cube edge length: 500 nm), separated by thin channels (γ phase with fcc solid solution structure, channel width: 20 nm). The microstructural evolution during high temperature and low stress tensile creep has been thoroughly investigated previously, mainly for [001] loading, both in terms of dislocation activity (filling of γ channels, formation of dislocation networks, cutting of the γ’ phase) as well as phase coarsening (rafting, topological inversion). Other loading geometries have received less attention.
The present work studies high temperature and low stress creep deformation of the superalloy LEK 94 at temperatures around 1000°C, where rafting occurs. Differences between loading under different uniaxial, biaxial and triaxial stress states are discussed. Stereo-microscopy and g∙b analysis in the scanning transmission electron microscopy mode (STEM) are combined for microstructural analysis. The focus is set on the role of dislocation interactions with the aging microstructure. Both development in STEM characterization methods, as well as the roles of phase coarsening, γ channel filling, microstructural heterogeneity and γ’ phase cutting are discussed.
The realistic description of plastic deformation caused by dislocations demands the representative measurement of their features, e.g., Burgers vector, slip plane, line direction and density. In the case of bulk deformation of technical alloys, reliable data must be ensured for large regions. Nonetheless, the (thin) filiform nature of dislocations and also the heterogeneity in some microstructures additionally require flexible analysis techniques that resolve the details of their interactions. Strong and clear channeling contrasts, faint extinction contours and the absence of chromatic aberration make scanning transmission electron microscopy (STEM) an ideal imaging mode in wide and thick regions of TEM foils, as opposed to conventional (C)TEM. It is the purpose of this contribution to show how STEM can be applied for quantitative measurement of dislocation features. Furthermore, a new tool will be presented, which enables the three-dimensional (3D) reconstruction, visualization and quantification of dislocation densities and directions from stereo-pairs. The application of these techniques will be shown on a monocrystalline Ni-base superalloy, an important class of structural materials that has been implemented in the first row blades of gas turbines. The examples are extracted from specimens subjected to creep deformation at high temperature and low stress under various macroscopic deformation geometries. The spacial and angular accuracy are discussed as well as possible sources of error.
Oxidation of a Fe-13Cr alloy under water vapor at 600 °C produced a zone of nano-sized precipitation underneath the outside scale formed by iron oxides and Fe‒Cr spinel. The majority of the spinel layer shows a mixed orientation relationship to the ferritic matrix {100}α || {100}sp & <011>α || <001>sp. However, also the discovered precipitated particles are characterized by the same crystallographic orientation relationship to the respective ferritic parent grain. The habit of the precipitates is best described by a lath morphology with their main axis parallel to <100> of ferrite.
Energy dispersive X-ray spectroscopy (EDX) and electron backscatter diffraction (EBSD) in an scanning electron microscope (SEM) have been applied to characterize the oxide layer in the micrometer scale. The clearly smaller precipitates were subsequently investigated by transmission electron microscopy (TEM). Specimens have been prepared by focused ion-beam (FIB) milling at an area previously characterized by EBSD. They cover the ferritic base material, but mainly the precipitation zone and the Fe‒Cr spinel layer. Energy filtered selected area diffraction (SAD) in the conventional (C)TEM and high-angle annular darkfield (HAADF) imaging in the scanning (S)TEM mode were employed in the characterization of the specimens.