Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (23)
- Vortrag (18)
- Posterpräsentation (6)
- Beitrag zu einem Tagungsband (4)
- Forschungsdatensatz (1)
Schlagworte
- Dislocation (9)
- Transmission electron microscopy (9)
- Creep (6)
- Microstructure (6)
- TEM (5)
- Microstructural characterization (4)
- Scanning transmission electron microscopy (STEM) (4)
- Additive manufacturing (3)
- Diffraction contrast (3)
- EBSD (3)
Organisationseinheit der BAM
- 5 Werkstofftechnik (30)
- 5.1 Materialographie, Fraktographie und Alterung technischer Werkstoffe (29)
- 5.5 Materialmodellierung (7)
- 5.2 Metallische Hochtemperaturwerkstoffe (5)
- 6 Materialchemie (3)
- 6.6 Physik und chemische Analytik der Polymere (3)
- 9 Komponentensicherheit (2)
- 9.6 Additive Fertigung metallischer Komponenten (2)
- 1 Analytische Chemie; Referenzmaterialien (1)
- 1.6 Anorganische Referenzmaterialien (1)
Paper des Monats
- ja (2)
Oxidation of a Fe-13Cr alloy under water vapor at 600 °C produced a zone of nano-sized precipitation underneath the outside scale formed by iron oxides and Fe‒Cr spinel. The majority of the spinel layer shows a mixed orientation relationship to the ferritic matrix {100}α || {100}sp & <011>α || <001>sp. However, also the discovered precipitated particles are characterized by the same crystallographic orientation relationship to the respective ferritic parent grain. The habit of the precipitates is best described by a lath morphology with their main axis parallel to <100> of ferrite.
Energy dispersive X-ray spectroscopy (EDX) and electron backscatter diffraction (EBSD) in an scanning electron microscope (SEM) have been applied to characterize the oxide layer in the micrometer scale. The clearly smaller precipitates were subsequently investigated by transmission electron microscopy (TEM). Specimens have been prepared by focused ion-beam (FIB) milling at an area previously characterized by EBSD. They cover the ferritic base material, but mainly the precipitation zone and the Fe‒Cr spinel layer. Energy filtered selected area diffraction (SAD) in the conventional (C)TEM and high-angle annular darkfield (HAADF) imaging in the scanning (S)TEM mode were employed in the characterization of the specimens.
Dislocations, as carriers of plastic deformation, affect important properties in technical materials, e. g., plasticity. The realistic description of plastic deformation caused by dislocations demands the representative measurement of their features, e.g., line direction, slip plane, Burgers vector and density. Bulk deformation of structural and functional alloys requires reliable data from large regions. The filiform nature of dislocations interacting with complex microstructures additionally demands observation and analysis techniques that allow resolving the details of their interactions in space. The use of electron tomography for this purpose is bound to difficult and time consuming experimental setups, which are not always applicable to any material. In this contribution a new tool is presented, which enables the three-dimensional reconstruction, visualization and quantification of dislocation densities and directions from manual tracing of scanning transmission electron microscopy (STEM) stereo-pairs. Examples are shown from samples of a creep-deformed monocrystalline Ni-base superalloy.
The realistic description of plastic deformation caused by dislocations demands the representative measurement of their features, e.g., Burgers vector, slip plane, line direction and density. In the case of bulk deformation of technical alloys, reliable data must be ensured for large regions. Nonetheless, the (thin) filiform nature of dislocations and also the heterogeneity in some microstructures additionally require flexible analysis techniques that resolve the details of their interactions. Strong and clear channeling contrasts, faint extinction contours and the absence of chromatic aberration make scanning transmission electron microscopy (STEM) an ideal imaging mode in wide and thick regions of TEM foils, as opposed to conventional (C)TEM. It is the purpose of this contribution to show how STEM can be applied for quantitative measurement of dislocation features. Furthermore, a new tool will be presented, which enables the three-dimensional (3D) reconstruction, visualization and quantification of dislocation densities and directions from stereo-pairs. The application of these techniques will be shown on a monocrystalline Ni-base superalloy, an important class of structural materials that has been implemented in the first row blades of gas turbines. The examples are extracted from specimens subjected to creep deformation at high temperature and low stress under various macroscopic deformation geometries. The spacial and angular accuracy are discussed as well as possible sources of error.
The demand for improved castability and low angle grain boundary (LAGB) resistance has led to the addition of low contents of e.g., B, Hf, Zr or C, into large industrial gas turbine components made of Ni-base superalloy single crystals (SXs). Due to the long-term application of Ni-base superalloy SX components in the temperature regime > 1000 °C, the formation of carbides is highly probable, which could jeopardize mechanical properties, such as high cycle fatigue. In the present contribution, the effect of internal and external stresses on the nucleation and growth characteristics of M23C6 carbides is investigated. Creep experiments are performed on the Ni-base superalloy SX LEK 94, which shows a low C concentration (= 0.1 at. %), at 1020 °C under parallel and circularly notched tensile specimens at a nominal stress of 160 MPa in the crystallographic direction [001]. The carbides are then characterized via scanning (S) and transmission (T) electron microscopy (EM). Nucleation is enhanced in the dendritic cores, often as coalesced colonies, extending over micrometers within M-rich (M: Cr, Re, W, Mo) γ channels. Lath shapes with facets on {100} (parallel to growth direction) and {111} are common. These facets exist since early stages (Fig.1a) and later develop misfit dislocations (Fig.1b), preserving the orientation relationship {100}γ || {100}M23C6. Fig. 1c shows a region from the creep gage, where carbides interact with superdislocations in the γ’ phase. Possible mechanisms are discussed.
The LEK94 is a Ni-base superalloy single crystal (SX) of the second generation, a materials class which is important for its high temperature creep resistance (>1000°C) in first stage blades of low-to-medium pressure gas turbines. Monocrystalline Ni-base superalloy SXs have a two-phase microstructure consisting of small cubes (' phase with the ordered L12 crystal structure, cube edge length: 500 nm), separated by thin channels (γ phase with fcc solid solution structure, channel width: 20 nm). The microstructural evolution during high temperature and low stress tensile creep has been thoroughly investigated previously, mainly for [001] loading, both in terms of dislocation activity (filling of γ channels, formation of dislocation networks, cutting of the γ’ phase) as well as phase coarsening (rafting, topological inversion). Other loading geometries have received less attention.
The present work studies high temperature and low stress creep deformation of the superalloy LEK 94 at temperatures around 1000°C, where rafting occurs. Differences between loading under different uniaxial, biaxial and triaxial stress states are discussed. Stereo-microscopy and g∙b analysis in the scanning transmission electron microscopy mode (STEM) are combined for microstructural analysis. The focus is set on the role of dislocation interactions with the aging microstructure. Both development in STEM characterization methods, as well as the roles of phase coarsening, γ channel filling, microstructural heterogeneity and γ’ phase cutting are discussed.
The present work describes the shear creep behavior of the superalloy LEK 94 at temperatures between 980 and 1050 °C and shear stresses between 50 and 140 MPa for loading on the macroscopic crystallographic shear system (MCSS) (011)[01-1]. The strain rate versus strain curves show short primary and extended secondary creep regimes. We find an apparent activation energy for creep of Qapp = 466 kJ/mol and a Norton-law stress exponent of n = 6. With scanning transmission electron microscopy, we characterize three material states that differ in temperature, applied stress, and accumulated strain/time. Rafting develops perpendicular to the maximum principal stress direction, gamma channels fill with dislocations, superdislocations cut gamma' particles, and dislocation networks form at gamma/gamma' interfaces. Our findings are in agreement with previous results for high-temperature and low-stress [001] and [110] tensile creep testing, and for shear creep testing of the superalloys CMSX-4 and CMSX-6 on the MCSSs (111)[01-1] and (001)[100]. The parameters that characterize the evolving gamma/gamma' microstructure and the evolving dislocation substructures depend on creep temperature, stress, strain, and time.
Shear testing can contribute to a better understanding of the plastic deformation of Ni-base superalloy single crystals. In the present study, shear testing is discussed with special emphasis placed on its strengths and weaknesses. Key mechanical and microstructural results which were obtained for the high-temperature (T ≈ 1000 °C) and low-stress (τ ≈ 200 MPa) creep regime are briefly reviewed. New 3D stereo STEM images of dislocation substructures which form during shear creep deformation in this regime are presented. It is then shown which new aspects need to be considered when performing double shear creep testing at lower temperatures (T < 800 °C) and higher stresses (τ > 600 MPa). In this creep regime, the macroscopic crystallographic [11−2](111) shear system deforms significantly faster than the [01−1](111) system. This represents direct mechanical evidence for a new planar fault nucleation scenario, which was recently suggested (Wu et al. in Acta Mater 144:642–655, 2018). The double shear creep specimen geometry inspired a micro-mechanical in-situ shear test specimen. Moreover, the in-situ SEM shear specimen can be FIB micro-machined from prior dendritic and interdendritic regions. Dendritic regions, which have a lower γ′ volume fraction, show a lower critical resolved shear stress.
Ni-base superalloy single crystals have been used in turbine blades for hot sections of gas turbines for over four decades. In order to increase the efficiency of the turbines, a continuous increase in the inlet temperature of combustion gases into the turbine has driven the design of turbine blades to complicated shapes and the presence of a complex pattern of cooling channels. These three-dimensional shapes, together with the inhomogeneous distribution of stresses along the blade, induce an also complicated triaxial stress state, which does not compare to uniaxial tests that are performed to characterize high temperature properties such as creep. A round notch on a test piece represents a simple configuration that generates a quasi-isostatic stress state across the notch. In the present contribution, the effect of a sharp round notch on the microstructural micromechanisms within the notched region cylindrical bars, loaded along [001] at 1020 °C and 160 MPa net stress, is studied. To this end, a series of interrupted creep tests is conducted on plain and notched bars and the microstructure is compared. Results are discussed in terms of degree microstructural coarsening, and dislocation activity. The effect of notch generation via grinding is also discussed in these terms. The presence of carbides evolving in from residual carbon is also shown and discussed. .Funding by the German Research Association (DFG) [grant number AG 191/1] is acknowledge
Subsurface characterization of high-strength high-interstitial austenitic steels after impact wear
(2018)
The microstructure of the subsurface after impact wear of three high-strength high interstitial austenitic steels has been analysed using transmission electron microscopy (TEM) in alloys with C and N as interstitial elements. In all cases, a nanocrystalline region followed by a transition zone and a cold-worked area are present. Additionally, microhardness and nano-scratching tests were conducted to study the wear-related properties of the impact subsurface and the base material. The results of the microstructural analysis reveal that the following mechanisms are involved during impact wear: abrasion (ploughing), microcrack formation associated with contact fatigue, entrapment and adhesion of SiO2 particles. The analysis of the wear-related properties indicates that the subsurface acts as a self-protective layer that prevents the deterioration of the substrate.
The presentation shows how the three-dimensional quantification of dislocations and their characteristic features, e.g. Burgers vector, line direction, dislocation density, is carried out at the transmission electron microscope in scanning mode (STEM) at Division 5.1 at BAM. Exemplarily, the methods are shown for Ni-base superalloy single crystals, for which a short introduction is given using further TEM techniques. Additional examples on low angle grain boundaries, nucleation of oxides at dislocations and interaction of dislocations and carbides are shown.
The content of the presentation was addapted, aiming at scientists who work within the DFG Priority Programme 1713 "Strong coupling of thermo-chemical and thermo-mechanical states in applied materials".