The tribological behaviour of unfilled thermoplastic polyurethane (TPU) and a polymer sphere filled (TPUG) thermoplastic polyurethane have been studied under oscillating sliding condition against cast iron as a counterpart. In the case of unfilled TPU, the wear mechanisms are dominated by particle detachment and roll formation. In principle, TPUG also showed a similar wear mechanism as that of unfilled TPU; in addition, particle pull-out and delamination are also observed. Wear volume of TPUG was significantly higher than that for the unfilled TPU and this is attributed to the different material removal processes taking place in the material during sliding. The polymer spheres as a filler material deteriorated the wear resistance of TPU because of improper adhesion and bonding of filler in the TPU matrix and therefore it contributed to more wear. In case of TPU the friction behaviour was strongly dependant on the temperature and surface roughness of the counter body. The results showed that below the glass transition temperature higher friction values are observed with higher counter body surface roughness. However, above the glass transition temperature, higher friction values are observed with a smoother surface roughness of the counter body. In case of TPUG, the friction behaviour was not significantly dependent on surface roughness of the counter body.
Laser-induced periodic surface structures (LIPSS, ripples) with ~500–700 nm period were produced on titanium alloy (Ti6Al4V) surfaces upon scan processing in air by a Ti:sapphire femtosecond laser. The tribological performance of the surfaces were qualified in linear reciprocating sliding tribological tests against balls made of different materials using different oilbased lubricants. Extending our previous work, we studied the admixture of the additive 2-ethylhexyl-zinc-dithiophosphate to a base oil containing only anti-oxidants and temperature stabilizers. The presence of this additive along with the variation of the chemical composition of the counterbodies allows us to explore the synergy of the additive with the laseroxidized nanostructures.
The performance of titanium alloy (Ti6Al4V) surfaces was investigated in lubricated reciprocating sliding tribological tests (RSTT). Special emphasis was laid on the effect of surface nanostructures in area of contact on the respective friction and wear behaviour. These so-called laser-induced periodic surface structures (LIPSS, ripples) were produced on the titanium alloy surface upon scan processing in air by an ultrashort pulsed femtosecond (fs) laser. As lubricant served two types of base oils, a pure polyalcylene-glycol, and an SAE 0W30 oil containing only antioxidants and temperature stabilizers. Tribological tests were carried out on polished as well as LIPSS covered areas using both types of base oil. A test metrics was established, combining the additive 2-ethylhexyl-zincdithiophosphate (ZDDP) or the ionic liquid [P6,6,6,14] [DEHP] (98% purity) with the respective base oils. The test metrics also considered the orientation of motion with respect to the orientation of the structures formed on the surface. Results are presented which show that the interplay between LIPSS and the local chemistry formed by the respective additives is beneficial for the tribological behaviour of the titanium alloy. Certain combinations of base oil, additive and LIPSS reduced friction and wear significantly in the tribological contact.