Filtern
Erscheinungsjahr
Dokumenttyp
Referierte Publikation
- ja (46) (entfernen)
Schlagworte
- Steel (17)
- Corrosion (16)
- CCS (14)
- CO2-storage (8)
- Pipeline (8)
- High temperature corrosion (7)
- Oxidation (4)
- Supercritical CO2 (4)
- Carbon capture and storage (3)
- Carbonate layer (3)
Organisationseinheit der BAM
- 5 Werkstofftechnik (14)
- 5.1 Mikrostruktur Design und Degradation (14)
- 5.6 Glas (2)
- 4 Material und Umwelt (1)
- 4.2 Material-Mikrobiom Wechselwirkungen (1)
- 5.2 Metallische Hochtemperaturwerkstoffe (1)
- 5.4 Multimateriale Fertigungsprozesse (1)
- 7 Bauwerkssicherheit (1)
- 7.6 Korrosion und Korrosionsschutz (1)
- 8 Zerstörungsfreie Prüfung (1)
Comparative study on high temperature oxidation of T92 steel in dry and wet oxyfuel environments
(2015)
Fireside oxidation of T92 steel was studied after exposure times up to 1000 h in the temperature range of 580–650 °C in simulated dry (CO2–27 % N2–2 % O2–1 % SO2) and wet (CO2–20 % H2O–7 % N2–2 % O2–1 % SO2) oxyfuel environments. Water vapour addition to the oxyfuel gas substantially increased the oxidation rate. The oxide scales developed under wet environment contained more defects, resulting in higher access of oxidants to the substrate material and enhanced oxidation. In addition, the oxide scales had lower chromium enrichment in the inner layer as compared to that in the dry condition. The oxide scales consisted of hematite and magnetite in the outer layer and a mixture of (Fe, Cr)-spinel, sulphides and wustite in the inner layer. The sulphur distribution differed between the oxide scales developed in dry and wet oxyfuel environments. Sulphur was mainly concentrated in the inner layer and at the oxide/alloy interface. In contrast to the wet oxyfuel gas, very high sulphur concentration was measured in the inner oxide scale formed in the dry oxyfuel gas. Additionally, Fe-sulphide was formed at the interface of inner and outer oxide layer in the wet condition.
The materials in oxyfuel power plant will be subjected to CO2– and SO2–rich gases on the fireside. The oxidation behaviour of two 9–12 % Cr steels T92 and VM12 was studied under dry oxyfuel environment in the temperature range of 580–650 °C for up to 1,000 h. The oxide structure and morphology were analyzed using various experimental techniques. A complex temperature dependence of oxidation rate is observed for both T92 and VM12 whereby the oxidation rate decreased with increasing temperature. This is attributed to increased Cr-enrichment in the inner scale with increasing temperature. T92 and VM12 alloys are also susceptible to carburization in an oxyfuel environment.
In corrosive environments such as CCS bore holes or geothermal power plants the materials loaded cyclically are also exposed constantly to the highly corrosive hot thermal water. The lifetime reduction of (X46Cr13, AISI 420C) is demonstrated in in-situ-laboratory experiments (T=60 °C, geothermal brine: Stuttgart Aquifer flow rate: 9 Nl/h, CO2). S-N plots, micrographic-, phase-, fractographic- and surface analysis were applied to obtain sustainable information on the corrosion fatigue behavior. Maximum number of cycles (here 12.5 x 106 cycles to failure) is reached at σa =173 MPa. No typical fatigue strength exists and passive corrosion fatigue is most likely failure cause.
Transmission of captured CO2 in pipelines is an essential part of the carbon capture and sequestration process chain. Dependent of the fuel, the combustion process and the capture technology the resulting gas contains impurities that might cause corrosion effects in pipelines constructed of low alloyed steels. Corrosion testing under simulated conditions therefore is a prerequisite for the installation of reliable and safe CCS systems. Sulfur and nitrogen oxides together with water vapor form corrosive acids. Their behaviours and corrosive effects in static pressurized experiments were critically investigated in the present study. The results indicate that experimental limitations might influence the predictive capability of corrosion tests with sulfur dioxide. The limited supply of corrosive constituents in static test might lead to an underestimation of the corrosion risk.
The need for a more efficient coal power plant generation (e.g. oxyfuel technology) results in modified process parameters and enhanced corrosion. To reach the necessary service life of high temperature parts protective coatings may be a sufficient technical solution. A modified Yoldas sol (Al2O3 based) was used to coat X20CrMoV12-1 by spin coating. After appropriate heat treatments transition alumina coatings being about 400 nm thick were obtained. Oxidation studies were carried out in laboratory air at temperatures up to 650 °C for up to 500 h exposure time. In case of the uncoated sample a rough oxide layer formed on the surface and a remarkable weight gain (2.62 mg/cm²) were detected. The sol–gel alumina layer (mainly δ-Al2O3) demonstrated a high protection, i.e. a very low weight gain (0.05 mg/cm²). Diffusion of alloying elements into the coating was observed. No indication of spallation of the coating occurred. Local defects (2 µm–30 µm) in the coating led to the formation of iron-oxide islands.
The process chain for Carbon Capture and Sequestration (CCS) includes tubing for injection of CO2 into saline aquifers. The compressed CO2 is likely to contain specific impurities; small concentrations of SO2 and NO2 in combination with oxygen and humidity are most harmful. In addition, CO2 saturated brine is supposed to rise in the well when the injection process is interrupted. The material selection has to ensure that neither CO2 nor brine or a combination of both will leak out of the inner tubing. In this comprehensive paper the investigated materials range from low-alloy steels and 13% Cr steels up to high-alloy materials. Electrochemical tests as well as long term exposure tests were performed in CO2, in brine and combination of both; pressure was up to 100 bar, temperature up to 60 °C. Whereas the CO2 stream itself can be handled using low alloy steels, combinations of CO2 and brine require more resistant materials to control the strong tendency to pitting corrosion. The corrosion behavior of heat-treated steels depends on factors such as microstructure and carbon content. For different sections of the injection tube, appropriate materials should be used to guarantee safety and consider cost effectiveness.
Materials testing under mechanical stress, pressure and turbulent flow of impure supercritical CO2
(2013)
The climate change necessitates measures to reduce carbon dioxide (CO2) emissions in the atmosphere, one of which is carbon dioxide capture and storage (CCS). Transmission of pressurized liquid or supercritical CO2 containing residual flue gas constituents in pipelines is an important component of CCS systems. Material testing under conditions as close as possible to real conditions is a prerequisite for reliable and safe implementation of CCS. A novel pipeline corrosion test facility was developed, accounting for major mechanical, physical and chemical influencing factors: elastic deformation, pressure, temperature, gas composition and flow velocity can be independently adjusted. Radial and tangential stress distributions on a round sample were experimentally investigated, indicating a good accordance with expected theoretical values. In this contribution the idea of the novel corrosion test facility and the assembled equipment as well as first results are presented and discussed.----------------------------------------------------------------------------------------------------Die Klimaveränderung macht Maßnahmen zur Reduktion von Kohlendioxidemission (CO2) in die Atmosphäre erforderlich, Rückhalt und Speicherung in tiefen geologischen Formationen (carbon capture and storage (CCS)) stellt eine davon dar. Der Transport von verflüssigtem oder superkritischem CO2 mit Verunreinigungen in Pipelines stellt einen wichtigen Teil von CCS-Systemen dar. Die Materialprüfung unter möglichst realitätsnahen Bedingungen ist eine wichtige Voraussetzung für die Einrichtung zuverlässiger und sicherer CCS-Systeme. Hierzu wurde eine neue Versuchseinrichtung zur Korrosionsprüfung von Pipelinewerkstoffen entwickelt, die folgende wesentliche physikalische und chemische Einflussgrößen berücksichtigt: Elastische Verformung, Druck, Temperatur, Gaszusammensetzung, und Fließgeschwindigkeit können unabhängig voneinander eingestellt werden. Die Verteilung der Radial- und Tangentialspannungen wurden in einer Rundprobe untersucht, und die Ergebnisse zeigten gute Übereinstimmungen mit den theoretisch zu erwartenden Werten. In dem vorliegenden Beitrag werden die Idee zu der neuen Korrosionsprüfeinrichtung und erste Ergebnisse vorgestellt sowie diskutiert.
Carbon capture and storage (CCS) includes processing of supercritical carbon dioxide (scCO2). The carbon dioxide (CO2) stemming from flue gases contains acid forming impurities, especially in the case of coal fired power plants. In the present work, the mobility and reactivity of acids in supercritical scCO2 was investigated. The corrosive attack of low alloyed carbon steel (material 1.0484) by water (H2O) alone in scCO2 was negligible. Nitric acid (HNO3) was very mobile and corrosive towards the carbon steel while sulfuric acid did not migrate through the scCO2 to react with the steel surface. Hydrochloric acid in scCO2 was very mobile and reactive towards both carbon steel and high alloyed test equipment. Gravimetric analyses revealed a severe material loss after corrosion in the presence of HNO3. Thickness measurements showed localized material losses.
Dealing with first corrosion screening experiments to predict the reliability and safety of Germanys first Carbon Capture and Storage site in the northern Bassin of Germany, northwest of the Capital Berlin, laboratory experiments have been established to simulate the particular conditions at T=60 °C, highly saline aquifer water similar to 'Stuttgart Aquifer', but only at ambient pressure. With mounting 2 independent full 2-grade titanium autoclave systems (running up to 250 bar and 300 °C) pressures up to p=100 bar are possible. In 2010 a specific corrosion chamber of 2-grade titanium working up to 100 °C, flowing aqui fer water with different gas mixtures was designed to fit to a high cycle fatigue testing machine. Long term fatigue experiments simulating fatigue crack growth under corrosive environments will soon start. These experiments may not only help engineering a CCS site, but results can be used to improve the maintenance of geothermal energy production sites, especially moved parts such as pumps and shafts.
The CCS technique involves the compression of emission gasses in deep geological layers. To guarantee the safety of the site, CO2-corrosion of the injection pipe steels has to be given special attention when engineering CCS-sites. To get to know the corrosion behaviour samples of the heat treated steel 1.72252CrMo4, used for casing, and the stainless injection-pipe steel 1.4034 X46Cr13 were kept at T=60 °C and ambient pressure as well as p=100 bar for 700 h - 8000 h in a CC 2-saturated synthetic aquifer environment similar to possible geological on-shore CCS-sites in the northern German Basin. The isothermal corrosion behaviour obtained by mass gain of the steels in the gas phase, the liquid phase and the intermediate phase gives surface corrosion rates around 0.1 to 0.8 mm/year at ambient pressure and much lower about 0.02 to 0.2 mm/year at 100 bar where the CO 2 is in its supercritical state. Severe pit corrosion with pit heights around 4.5 mm are only located on the 42CrMo4 steel. Main phase of the continuous complicated multi-layered carbonate/oxide structure is siderite FeCO 3 in both types of steel.