- Corrosion (8)
- CO2 (3)
- Carbon steel (3)
- Steel (3)
- CCS (2)
- Geothermal (2)
- Utilization (2)
- Alkali-activated materials (1)
- CCU (1)
- CCUS (1)
Organisationseinheit der BAM
- 7.6 Korrosion und Korrosionsschutz (15) (entfernen)
Recent studies have shown that even at a very low concentration of impurities (less than 100 ppmv of SO2, NO2, O2 and H2O) the droplet formation and condensation of sulfuric and nitric acids in dense phase CO2 are possible and observable. To reveal the mechanism of droplet corrosion in dense phase CO2 at high pressure and low temperature, further studies on factors that affect wettability and resulting corrosion behaviors of transport pipeline steels are needed. In this study, effects of surface morphology were investigated by varying surface roughness of carbon steel coupons exposed to CO2 stream containing impurities to measure the wettability by contact angle and to observe the condensation as well as possible droplet corrosion that followed. Other considered factors were: pH of the droplet, temperature, droplet volume, and exposure time.
According to the results of the experiments carried out, the following points can be concluded:
1. Exposure tests showed that specimens with the addition of SiO2 particles and polyaniline particles exhibit better corrosion resistance than specimens with the addition of only polyaniline particles or binder only.
2. Open circuit potential measurements showed that in the beginning of the experiments, both coatings had an open circuit potential 100 mV higher than carbon steel. Within one day of immersion, the potential of carbon steel increased significantly, indicating the formation of oxide layer. After extended exposure the carbon steel potential sat between PS1 (which had higher potential) and PS2 (which had a lower potential) and all three were in the range –600 mV to –500 mV vs Ag/AgCl.
3. Both coatings PS-1 and PS-2 were degraded with increasing exposure time, shown by the decrease of absolute impedance value at low frequency range after 2, 4, and 6 days exposure.
4. Potentiodynamic test was performed after 3 hours and 6 days exposure, and it was shown that the coating in the initial stage exhibited more passive behavior than the specimens exposed for 6 days.
By exposure and electrochemical tests in the laboratory the Cu-effect on corrosion behavior of carbon steel, high-alloyed steels and Ti-alloy can be assessed.
Critical materials specific properties were determined by static exposure and electrochemical tests in an artificial geothermal water with high salinity and low pH, containing Cu. Conclusions were drawn using characteristic potential values.
It could be shown that significant Cu-deposition and -precipitation only occurred in combination with carbon steel. High-alloyed materials (S31603, S31653, S31700, S31703, S31803 and N08904) prevent the disturbing Cu-agglomeration. Therefore, they are suitable to be chosen for future design of the piping system, either in massive or in cladded form, if formation of crevices with non-metallic materials can be excluded.
From the interactions and pitting corrosion point of view, R50400 seems to be most favorable.
Corrosion of steel reinforcement in concrete is one of the major deterioration mechanisms limiting the service life of reinforced concrete structures. While for conventional (Portland cement-based) concretes a great amount of experience exists in this regard, the factors that determine the onset of reinforcement corrosion in alkali-activated materials are incompletely understood yet. One aspect of corrosion protection is leaching and the accompanying changes of the concrete pore solution. In the present study, alkali-activated fly ash mortars with embedded carbon steel rebars were exposed to de-ionised water for periods up to 330 days, and the electrochemical response of the steel (free corrosion potential, polarisation resistance), the alteration of the mortar (ohmic resistance, mechanical strength, pore size distribution) as well as the pore solution composition were monitored. Although substantial alkali leaching was observed, the pH of the pore solution remained at values sufficient to protect the embedded steel from depassivation. The mortar did not exhibit indications of significant deterioration. Thus, the present results suggest that leaching is not critical for protection of steel reinforcement in alkali-activated fly ash mortars and concretes.
Metallene Konstruktionswerkstoffe reagieren infolge ihres thermodynamisch instabilen Zustandes mehr oder weniger stark mit Stoffen aus der Umgebung. Eine große Rolle bei diesen Reaktionen spielt das Feuchtigkeitsangebot an der Metalloberfläche, welches nicht zwingend mit einem sichtbaren Wasserfilm einhergehen muss. An der Atmosphäre bilden sich an sauberen Metalloberflächen bei etwa 80 % relativer Luftfeuchte, bei versalzten Oberflächen auch schon ab etwa 25 % r. F., Feuchtfilme aus. Im Feuchtfilm laufen grundsätzlich die gleichen elektrochemischen Reaktionen ab, wie diese von wässrigen Medien bekannt sind. Dabei geht das Metall zunächst in Ionenform und in nachgelagerten Reaktionen in einen thermodynamisch stabilen Zustand in Form unterschiedlichster Oxid- und Hydroxidverbindungen über. Die so entstehenden Korrosionsprodukte können im Feuchtigkeitsfilm begrenzt löslich oder unlöslich sein und lagern sich auf den Oberflächen der Konstruktionswerkstoffe häufig als feste Korrosionsprodukte ab bzw. wachsen dort auf. Je nachdem wie die Korrosionsprodukte strukturell zum Untergrund passen, können sich dichte, sehr gut haftende Schichten ausbilden oder poröse, dicke Schichten ohne nennenswerte Haftung aufwachsen. Wachsen dichte, porenfreie Schichten mit guter Haftung auf, die im umgebenden Medium unlöslich sind, wird die weitere Auflösung des Metalls stark gehemmt. Man spricht dann von der Ausbildung schützender Deckschichten bzw. von Passivschichten auf welcher der Korrosionsschutz und damit die Dauerhaftigkeit vieler Konstruktionswerkstoffe beruhen. Kaesche bezeichnete die Passivität sehr treffend als „optimalen Grenzfall des Korrosionsschutzes durch Schichten von Korrosionsprodukten“. Aus technischer Sicht hält Kaesche eine Unterscheidung von Deckschichten bzw. Passivschichten für nicht zwingend erforderlich, da beide die Korrosionsgeschwindigkeit in gleichem Maß herabsetzen können. Die Übergänge zwischen den meist dickeren und dadurch sichtbaren Deckschichten und den meist dünnen, nicht sichtbaren Passivschichten sind fließend.