Porous materials are of a great interest due to their ability to interact with ions and molecules not only on their surface but throughout their bulk. Porous materials are conventionally used in applications; such as ion exchange, adsorption/separation and in catalysis, exploiting the huge internal surface area of highly ordered porous materials. [1, 2] The ability for these materials to succeed, in a particular field, is dependent greatly upon the uniformity of the shape and size of the pores within the material. However, despite how well we are able to understand the stability of 3-D frameworks in crystalline or polycrystalline zeolites and ZIFs, there still remains major limitations in fully understanding the synthetic mechanisms occurring prior to their formation. [3, 4] Though the syntheses of a wide variety of porous solids are already well established, their formation mechanisms continue to be of great interest to both academic and industrial communities, with the thought that with greater understanding of the formation of these solids can lead to their rational design. By obtaining a better knowledge of the underlying nucleation mechanisms, it can allow for increased predictability of new structures and in addition can reveal valuable information regarding the particle dimensions aiding in controlling particle morphology and size.
Small-angle and wide-angle X-ray scattering (SAXS/WAXS) are ideal techniques for determining morphological changes in-situ, where the shape, size and crystallinity can be followed at a high temporal resolution, and when these techniques are deployed alongside complimentary techniques, such as ex-situ microscopy, a great deal of information on the formation of materials can be obtained. The above-mentioned methodologies were utilised to study the formation of Silicalite-1 from multiple silica sources to obtain a detailed picture of the formation as a whole, including the formation of intermediate species (Image 1 show the in-situ SAXS data collected from the formation of Silicalite-1 from tetraethyl orthosilicate).
In-situ SAXS/WAXS studies were also utilized to observe the formation of ZIF-8 alongside in-situ X-ray absorption spectroscopy (XAS) experiments to probe both the morphological changes, as well as any changes occurring to the local structure during synthesis (Image 2 show the in-situ SAXS data collected from the formation of ZIF-8). These timeresolved in-situ studies have been utilised to follow changes in crystallinity and crystallite size, whilst also providing valuable information on the formation of intermediate species, the nucleation of crystalline ZIFs, and their subsequent growth.
References:
[1] M E Davis. Nature, 417(6891):813–21, 2002
[2] S T Meek, J A Greathouse, M D Allendorf, Advanced Materials, 23 (2): 249-267, 2011
[3] J Grand, H Awala, CrystEngComm,18 (5): 650–664, 2016
[4] M J V Vleet, T Weng, X Li, J R Schmidt. Chem.Rev.,118 (7): 3681–3721, 2018
Surface self-assembly of spherical nanoparticles of sizes below 10 nm into hierarchical heterostructures is under arising development despite the inherent difficulties of obtaining complex ordering patterns on a larger scale. Due to template-mediated interactions between oil-dispersible superparamagnetic nanoparticles (MNPs) and polyethylenimine-stabilized gold nanoparticles (Au(PEI)NPs) at the water–oil interface of microemulsions, complex nanostructured films can be formed. Characterization of the reverse microemulsion phase by UV–vis absorption revealed the formation of heteroclusters from Winsor type II phases (WPII) using Aerosol-OT (AOT) as the surfactant. SAXS measurements verify the mechanism of initial nanoparticle clustering in defined dimensions. XPS suggested an influence of AOT at the MNP surface. Further, cryo-SEM and TEM visualization demonstrated the elongation of the reverse microemulsions into cylindrical, wormlike structures, which subsequently build up larger nanoparticle superstructure arrangements. Such WPII phases are thus proven to be a new form of soft template, mediating the self-assembly of different nanoparticles in hierarchical network-like filaments over a substrate during solvent evaporation.
The influence of zeolite support materials and their impact on CH4 oxidation activity was studied utilizing Pd supported on H-beta and H-SSZ-13. A correlation between CH4 oxidation activity, Si/Al ratio (SAR), the type of zeolite framework, reduction-oxidation behaviour, and Pd species present was found by combining catalytic activity measurements with a variety of characterization methods (operando XAS, NH3-TPD, SAXS, STEM and NaCl titration). Operando XAS analysis indicated that catalysts with high CH4 oxidation activity experienced rapid transitions between metallic- and oxidized-Pd states when switching between rich and lean conditions. This behaviour was exhibited by catalysts with dispersed Pd particles. By contrast, the formation of ion-exchanged Pd2+ and large Pd particles appeared to have a detrimental effect on the oxidation-reduction behaviour and the conversion of CH4. The formation of ion-exchanged Pd2+ and large Pd particles was limited by using a highly siliceous beta zeolite support with a low capacity for cation exchange. The same effect was also found using a small-pore SSZ-13 zeolite due to the lower mobility of Pd species. It was found that the zeolite support material should be carefully selected so that the well-dispersed Pd particles remain, and the formation of ion-exchanged Pd2+ is minimized.
The behaviour of microemulsion (ME) droplets in mesoporous systems is highly important for understanding the immobilisation of drugs or chemical formulations, cleaning processes or enhanced oil recovery. The loading of pores as well as the structural organisation of MEs within the pores is a relevant parameter, especially for immobilisation applications. For this reason, the uptake of microemulsions in cylindrical pores of SBA-15 was investigated via adsorption and small-angle neutron scattering (SANS). Adsorption isotherms revealed an adsorption of the microemulsion droplets based on the adsorption of surfactant as a driving force. The adapted scattering model is based on the analysis of bare SBA-15 in full contrast conditions and employs microemulsions inside of SBA-15 measured at the silica contrast matching point. Accordingly, the structural arrangement of microemulsion droplets in the pores of SBA-15 was determined in good detail. Microemulsion droplets smaller than the pore size access the pores while retaining their spherical shape and become increasingly ordered for higher loading, where the droplets arrange in a dense packing of spherical droplets in a cylindrical pore. Interestingly, microemulsion droplets larger than the pore size can easily be incorporated, but become deformed upon entering and are present as elongated rod-like structures.
Herein, we provide a "systems architecture"-like overview and detailed discussions of the methodological and instrumental components that, together, comprise the "MOUSE" project (Methodology Optimization for UltrafineStructure Exploration). The MOUSE project provides scattering information on a wide variety of samples, with traceable dimensions for both the scattering vector (q) and the absolute scattering cross-section (I). The measurable scattering vector-range of 0.012≤ q (nm-1) ≤ 92, allows information across a hierarchy of structures with dimensions ranging from ca. 0.1 to 400 nm. In addition to details that comprise the MOUSE project, such as the organisation and traceable aspects, several representative examples are provided to demonstrate its flexibility. These include measurements on alumina membranes, the tobacco mosaic virus, and dual-source information that overcomes fluorescence limitations on ZIF-8 and iron-oxide-containing carbon catalyst materials.
SnOct2 (Sn(II) 2-ethylhexanoate) catalyzed ROPs of L-lactide were performed in bulk with eight different alcohols as initiators. The time was varied between 1 h and 24 h for all initiators. For two initiators the temperature was also lowered to 115 ◦C. Even-numbered chains were predominantly formed in all polymerizations at short times, but the rate of transesterification (e.g. even/odd equilibration) and the molecular weight distribution were found to depend significantly on the nature of the initiator. Observed transesterification reactions also continued in solid poly (L-lactide), and with the most active initiator, almost total equilibration was achieved even at 130 ◦C. This means that all chains including those of the crystallites were involved in transesterification reactions proceeding across the flat surfaces of the crystallites. The more or less equilibrated crystalline polylactides were characterized by DSC and SAXS measurements with regard to their melting temperature (Tm), crystallinity and crystal thickness.
Ultra-SAXS can enhance the capabilities of existing synchrotron SAXS/WAXS beamlines. A compact ultra-SAXS module has been developed, which extends the measurable q-range with 0.0015 ≤ q (nm−1) ≤ 0.2, allowing structural dimensions in the range 30 ≤ D (nm) ≤ 4000 to be probed in addition to the range covered by a high-end SAXS/WAXS instrument. By shifting the module components in and out on their respective motor stages, SAXS/WAXS measurements can be easily and rapidly interleaved with USAXS measurements. The use of vertical crystal rotation axes (horizontal diffraction) greatly simplifies the construction, at minimal cost to efficiency. In this paper, the design considerations, realization and synchrotron findings are presented. Measurements of silica spheres, an alumina membrane, and a porous carbon catalyst are provided as application examples.
Nachruf auf Wilhelm Ruland
(2021)
Mit Prof. Dr. Wilhelm Ruland starb am 3. Februar 2021 einer der letzten großen Wissenschaftler, welche die Streutheorie nach dem Zweiten Weltkrieg vorangetrieben haben. Sein zentrales Thema war die Streuung an weicher Materie. Hier lieferte er bis ins hohe Alter grundlegende Beiträge, die den Stellenwert seines Leitspruchs demonstrieren: Nichts ist praktischer als eine gute Theorie.
Hydrogels with a hierarchical structure were prepared from a new highly water-soluble crosslinker N,N,N′,N′-tetramethyl-N,N′-bis(2-ethylmethacrylate)-propyl-1,3-diammonium dibromide and from the sulfobetaine monomer 2-(N-3-sulfopropyl-N,N-dimethyl ammonium)ethyl methacrylate. The free radical polymerization of the two compounds is rapid and yields near-transparent hydrogels with sizes up to 5 cm in diameter. Rheology shows a clear correlation between the monomer-to-crosslinker ratio and the storage and loss moduli of the hydrogels. Cryo-scanning electron microscopy, low-field nuclear magnetic resonance (NMR) spectroscopy, and small-angle X-ray scattering show that the gels have a hierarchical structure with features spanning the nanometer to the sub-millimeter scale. The NMR study is challenged by the marked inhomogeneity of the gels and the complex chemical structure of the sulfobetaine monomer. NMR spectroscopy shows how these complications can be addressed via a novel fitting approach that considers the mobility gradient along the side chain of methacrylate-based monomers.
Nanomaterials and nanoparticles are finding applications across a wide range of technology sectors, from medicine and food to transportation and construction. In order to assess these new materials for potential risks to health and the environment, they need to be well-characterised. The measurement of constituent nanoparticle size, shape, and size distribution are important factors for the risk evaluation process.
EMPIR project Improved traceability chain of nanoparticle size measurements (17NRM04, nPSize) is working to assess a range of traceable nanoparticle measurement approaches, including Scanning Electron Microscopy (also in Transmission Mode), Atomic Force Microscopy and Small Angle X-ray Scattering, and deliver improved calibration methods to users. For the techniques under investigation, physical models of their response to a range of nanoparticle types are developed. Validated reference materials will also be used for an inter-comparison of measurement systems, with an evaluation of the associated measurement uncertainty. With project contributions to standards development work, manufacturers will be better placed to assess the human and environmental risks posed by nanomaterials across a whole range of products.