Early detection of fatigue cracks and accurate measurements of the crack growth play an important role in the maintenance and repair strategies of steel structures exposed to cyclic loads during their service life. Observation of welded connections is especially of high relevance due to their higher susceptibility to fatigue damage. The aim of this contribution was to monitor fatigue crack growth in thick welded specimens during fatigue tests as holistically as possible, by implementing multiple NDT methods simultaneously in order to record the crack initiation and propagation until the final fracture. In addition to well-known methods such as strain gauges, thermography, and ultrasound, the crack luminescence method developed at the Bundesanstalt für Materialforschung und -prüfung (BAM), which makes cracks on the surface particularly visible, was also used. For data acquisition, a first data fusion concept was developed and applied in order to synchronize the data of the different methods and to evaluate them to a large extent automatically. The resulting database can ultimately also be used to access, view, and analyze the experimental data for various NDT methods. During the conducted fatigue tests, the simultaneous measurements of the same cracking process enabled a comprehensive comparison of the methods, highlighting their individual strengths and limitations. More importantly, they showed how a synergetic combination of different NDT methods can be beneficial for implementation in large-scale fatigue testing but also in monitoring and inspection programs of in-service structures - such as the support structures of offshore wind turbines.
Ultrasonic coda wave interferometry can detect small changes in scattering materials like concrete. We embedded ultrasonic transducers in the Gänstorbrücke Ulm, a monitored road bridge in Germany, to test the methodology. Since fall 2020, we've been monitoring parts of the bridge and comparing the results to commercial monitoring systems. We calculate signal and volumetric velocity changes using coda waves, and long-term measurements show that the influence of temperature on strains and ultrasound velocity changes can be monitored. Velocity change maps indicate that different parts of the bridge react differently to environmental temperature changes, revealing local material property differences. A load experiment with trucks allows calibration to improve detectability of possibly damaging events. Our work focuses on measurement reliability, potential use of and distinction from temperature effects, combination with complementary sensing systems, and converting measured values to information for damage and life cycle assessment.
In this work, we report on our progress for investigating a new experimental approach for thermographic detection of internal defects by performing 2D photothermal super resolution reconstruction. We use modern high-power laser projector technology to repeatedly excite the sample surface photothermally with varying spatially structured 2D pixel patterns. In the subsequent (blind) numerical reconstruction, multiple measurements are combined by exploiting the joint-sparse nature of the defects within the specimen using nonlinear convex optimization methods. As a result, a 2D-sparse defect/inhomogeneity map can be obtained. Using such spatially structured heating combined with compressed sensing and computational imaging methods allows to significantly reduce the experimental complexity and to study larger test surfaces as compared to the one-dimensional approach reported earlier.
Klebeverbindungen sind aus vielen Anwendungen wie dem Leichtbau nicht mehr wegzudenken. Durch die Verklebung gleicher oder ungleicher Materialien entstehen viele Vorteile gegenüber konservativen Fügeverfahren. Jedoch stellen schwache Haftfestigkeiten eine sehr unbeliebte Fehlerart dar, die schlecht zu detektieren sind und zu einem frühzeitigen Versagen der Verklebung bei vergleichsweise geringen Belastungen führen können. Aufgrund hoher Sicherheits- und Qualitätsansprüche wird die Haftfestigkeit dieser Verbindungen jedoch noch immer zerstörend geprüft. Zufriedenstellende zerstörungsfreie Verfahren, um Haftfestigkeiten zu prüfen, sind nicht vorhanden und Thema gegenwärtiger Forschung. Ein Ansatz, der in diesem Projekt verfolgt wird, liegt in der Verwendung geführter Ultraschallwellen.
Hierzu wird anhand von Simulationen mittels der Scaled Boundary Finite Element Methode gezeigt, dass die gezielte Auswertung bestimmter Bereiche des Dispersionsdiagrams, den sogenannten vermiedenen Kreuzungen (engl. mode repulsion regions), eine Charakterisierung der Haftfestigkeiten zulassen könnten. Dies liegt darin begründet, dass die mittleren mechanischen Belastungen der Kleberschicht in diesen Bereichen ein lokales Maximum aufweisen und daher eine erhöhte Sensitivität auf Materialänderungen haben. Es wird gezeigt, wie sensitiv diese Bereiche auf Materialänderungen in der Klebergrenzschicht sind und welche potenziellen Fehlergrößen existieren.
In a joint project of partners from industry and research, the automated recycling of construction and demolition waste (CDW) is investigated and tested by combing laser-induced breakdown spectroscopy (LIBS) and near-infrared (NIR) spectroscopy. Joint processing of information (data fusion) is expected to significantly improve the sorting quality of various materials like concrete, main masonry building materials, organic components, etc., and may enable the detection and separation of impurities such as SO3-cotaining building materials (gypsum, aerated concrete, etc.). The project focuses primarily on the Berlin site to analyze the entire value chain, minimize economic/technological barriers and obstacles at the cluster level, and sustainably increase recovery and recycling rates. First measurements with LIBS and NIR spectroscopy show promising results in distinguishing various material types and indicate the potential for a successful combination. In addition, X-ray fluorescence (XRF) spectroscopy is being performed to obtain more information about the quantitative elemental composition of the different building materials. Future work will apply the developed sorting methodology in a fully automated measurement setup with CDW on a conveyor belt.
Due to the diffusive nature of heat propagation in solids, the detection and resolution of internal defects with active thermography based non-destructive testing is commonly limited to a defect-depth-to-defect-size ratio greater than or equal to one. In the more recent past, we have already demonstrated that this limitation can be overcome by using a spatially modulated illumination source and photothermal super resolution-based reconstruction. Furthermore, by relying on compressed sensing and computational imaging methods we were able to significantly reduce the experimental complexity to make the method viable for investigating larger regions of interest. In this work we share our progress on improving the defect/inhomogeneity characterization using fully 2D spatially structured illumination patterns instead of scanning with a single laser spot. The experimental approach is based on the repeated blind pseudo-random illumination using modern projector technology and a high-power laser. In the subsequent post-processing, several measurements are then combined by taking advantage of the joint sparsity of the defects within the sample applying 2D-photothermal super resolution reconstruction. Here, enhanced nonlinear convex optimization techniques are utilized for solving the underlying ill-determined inverse problem for typical simple defect geometries. As a result, a higher resolution defect/inhomogeneity map can be obtained at a fraction of the measurement time previously needed.
Für die aktive Thermografie als zerstörungsfreie Prüfmethode galt lange Zeit die Faustformel, dass die Auflösung interner Defekte/Inhomogenitäten auf ein Verhältnis von Defekttiefe/Defektgröße ≤ 1 beschränkt ist. Die Ursache hierfür liegt in der diffusiven Natur der Wärmeleitung in Festkörpern. Sogenannte Super-Resolution-Ansätze erlauben seit Kurzem die Überwindung dieser physikalischen Grenze um ein Vielfaches. Damit ergibt sich die attraktive Möglichkeit die Thermografie von einem rein oberflächensensitiven Prüfverfahren hin zu einem Verfahren mit verbesserter Tiefenreichweite zu entwickeln. Wie weit diese Entwicklung getrieben werden kann, ist Gegenstand aktueller Forschung.
Wir konnten bereits zeigen, dass diese klassische Grenze für 1D- und 2D Defektgeometrien mit Hilfe des Abscannens des Prüfkörpers mittels einzelner Laserspots und der anschließenden Anwendung von photothermischer Super-Resolution-Rekonstruktion überwunden werden kann. Bei dieser Methode wird eine Kombination aus sequenzieller räumlich strukturierter Beleuchtung und numerischen Optimierungsmethoden eingesetzt. Dies geschieht allerdings auf Kosten der experimentellen Komplexität, die zu einer langen Messdauer, großen Datensätzen und langwieriger numerischer Auswertung führt.
In dieser Arbeit berichten wir über einen neuen experimentellen Ansatz, bei dem räumlich strukturierte 2D-Beleuchtungsmuster in Verbindung mit Compressed-Sensing und Computational-Imaging-Methoden verwendet werden, um die experimentelle Komplexität deutlich zu verringern und die Methode für die Untersuchung größerer Prüfflächen nutzbar zu machen.
Der experimentelle Ansatz basiert dabei auf der wiederholten (blinden) photothermischen Anregung mit räumlich strukturierten 2D-Mustern unter Verwendung moderner Projektortechnik und eines Hochleistungslasers. In der anschließenden numerischen Rekonstruktion werden mehrere Messungen unter Ausnutzung der Joint-Sparsity der Defekte innerhalb des Prüfkörpers mittels nichtlinearer konvexer Optimierungsmethoden kombiniert. Als Ergebnis kann eine 2D-sparse Defekt-/Inhomogenitätskarte erstellt werden.
Active thermography as a nondestructive testing modality suffers greatly from the limitations imposed by the diffusive nature of heat conduction in solids. As a rule of thumb, the detection and resolution of internal defects/inhomogeneities is limited to a defect depth to defect size ratio greater than or equal to one. Earlier, we demonstrated that this classical limit can be overcome for 1D and 2D defect geometries by using photothermal laser-scanning super resolution. In this work we report a new experimental approach using 2D spatially structured illumination patterns in conjunction with compressed sensing and computational imaging methods to significantly decrease the experimental complexity and make the method viable for investigating larger regions of interest.
Eine zentrale Aufgabe der zerstörungsfreien Prüfung und der Strukturüberwachung (engl. Structural Health Monitoring - SHM) mit Ultraschallwellen ist die Bewertung von Schäden in Bauteilen. In vielen Bauteilen, wie zum Beispiel platten- und schalenförmigen Strukturen, Rohrleitungen oder Laminaten, breitet sich der Ultraschall in Form geführter Wellen aus. Zwar haben geführte Wellen eine relativ große Reichweite innerhalb des Bauteils und ermöglichen so eine großflächige Prüfung, ihre multimodalen und dispersiven Eigenschaften erschweren jedoch die Analyse der vom Schaden kommenden Reflexionen. Eine Möglichkeit, die Messsignale zu interpretieren und die Schäden zu charakterisieren, ist deren Vergleich mit der Wellenausbreitung in einem digitalen Modell. Hierbei stellt sich die Aufgabe, den Schaden im digitalen Modell anhand der Messdaten zu rekonstruieren. Diese Rekonstruktion beschreibt ein inverses Problem, das mehrere Vorwärtsrechnungen braucht, um das Schadensmodell an die Messdaten anzupassen. Durch die kleine Wellenlänge von Ultraschallwellen sind klassische Vorwärtsmethoden wie die Finte Elemente Methode rechenintensiv, weshalb die Autoren die semi-analytische Scaled Boundary Finite Element Method (SBFEM) benutzen, um den Rechenaufwand zu verringern. Im Beitrag wird ein inverses Verfahren basierend auf dem Automatischen Differenzieren in Kombination mit der SBFEM vorgestellt und an verschiedenen Schadenstypen in 2D-Querschnittmodellen von Wellenleitern getestet. In der präsentierten Vorstudie werden dafür „Messdaten“ aus unabhängigen Simulationen verwendet.
Thermographic super resolution techniques allow the spatial resolution of defects/inhomogeneities below the classical limit, which is governed by the diffusion properties of thermal wave propagation. In this work, we report on the extension of this approach towards a full frame 2D super resolution technique. The approach is based on a repeated spatially structured heating using high power lasers. In a second post-processing step, several measurements are coherently combined using mathematical optimization and taking advantage of the (joint) sparsity of the defects in the sample
Thermographic super-resolution techniques allow the resolution of defects/inhomogeneities beyond the classical limit, which is governed by the diffusion properties of thermal wave propagation. Photothermal super-resolution is based on a combination of an experimental scanning strategy and a numerical optimization which has been proven to be superior to standard thermographic methods in the case of 1D linear defects. In this contribution, we report on the extension of this approach towards a full frame 2D photothermal super-resolution technique. The experimental approach is based on a repeated spatially structured heating using high power lasers. In a second post-processing step, several measurements are coherently combined using mathematical optimization and taking advantage of the (joint) sparsity of the defects in the sample. In our work we extend the possibilities of the method to efficiently detect and resolve defect cross sections with a fully 2D-structured blind illumination.
The detection of cracks before the failure is highly significant when it comes to safety-relevant structures. Crack detection in metallic samples at high surface temperature is one of the challenging situation in manufacturing industries.
Laser thermography has already proved its detection capability of surface cracks in metallic samples at room temperature. In this work a continuous wave (CW) laser use to generate a laser, which is using to scan the metal surface with notch.
The corresponding heat distribution on the surface monitored using infrared thermal (IR) camera. A simplified 3D model for laser thermography is developed and validated with experimental results. A dedicated image processing algorithm developed to improve the detectability of the cracks. To understand the dependency of surface temperature, laser power, laser scanning speed etc. in defect detection, we carried out parametric studies with our validated model. Here we Report the capability of laser thermography in crack detection at elevated temperature.
Non-destructive testing (NDT) is a major contributor to the safe railway operation. Even though NDT reliability in railway maintenance is affected by human factors, there are only just a few studies published in this field so far. Education and training of the NDT personnel are some of the most important drivers of safe and reliable NDT. Continuously improving current practices and tools used for educational purposes can be achieved not only through technical con¬tent, but also through the attention to human factors. The aim of this study was to deepen the understanding of possible human-related risks in the manual ultrasonic inspection of the hollow railway axles and to suggest measures to improve the education and training of the NDT person¬nel. This was achieved by means of Failure Modes and Effects Analysis (FMEA) carried out with eight NDT experts and by a survey of 27 experienced inspectors. The results show that failures can happen throughout the entire NDT process. Prevention of those failures could be improved through the optimization of the organization, technology, documentation and regulations, working conditions and the general process, and through the optimization of the formal education and training. Specialized training of the executives, extended training of the supervisors and the inspectors and improvement of the inspection documentation have been suggested. The study also showed potential for the improvements of the inspection in the field.
Increasing requirements on the infrastructure caused by more and heavier traffic coincide with both the aging and the progressive degradation of bridge constructions. These exemplary issues lead to a non-negligible need for reassessments of existing bridges. Compared to the new building design, safety reserves can be used in the evaluation of such existing structures, since uncertainties that may arise during the design, construction and previous Service time are better known or no longer present. Uncertainties can be evaiuated more precisely by measurements. In the meantime, the application of advanced NDT-methods on concrete structures have become so capable, that crucial structure Parameters like certain material properties or geometrical dimensions can be quantified without significant destructive interventions. The measured data can be explicitly incorporated into the probabilistic computation models used for the bridge reassessment in form of random variables. Therewith, a previously insufficient model can be refined to achieve a higher level of approximation. This contribution emphasises two fundamental steps of the measured data based probabilistic reassessment: The sensitivity analyses to identify the cruciai Parameters and the needed accuracy of the related information as well as the comparison with expected uncertainties of non-destructively measured Parameters.
Ultrasonic methods are used in concrete investigations since decades. While being limited to transmission testing in the laboratory for a while, in-situ echo measurements for structural investigations and condition assessment have made their way into practical application in the past 20 years. However, several challenges remain. On one side, there are technical issues as limitations in depth of penetration, resolution and imaging capabilities. On the other side there are still gaps in validation, standardization and certification, which are limiting the applicability in condition/load capacity assessment.
This review reports a couple of developments which will help to overcome these issues. This includes technical developments as new devices which are easier to handle on site or giving a much deeper penetration depth (e.g. the LAUS device at BAM) as well as improvements in imaging by hardware update (e. g. air coupled ultrasound or coded signals) or new software (e. g. RTM imaging). To foster the application in real world projects we are as well working on standardization by developing new reference specimen with international partners which will ensure world-wide comparability of ultrasonic and other methods and quality assurance codes. Further, non-destructive methods are being used to update probabilistic models used for the reassessment of existing structures to support the structural engineer’s decisions.
Entwicklung eines luftgekoppelten Ultraschall-Echo-Prüfverfahrens mittels fluidischer Anregung
(2019)
In vielen technischen Bereichen werden Ultraschallverfahren zur zer-störungsfreien Werkstoffprüfung eingesetzt. Dabei wird ein Schallpuls von einem Prüfkopf in ein Prüfobjekt eingebracht. Der Puls kann unter anderem durch Membra-nen oder Piezoelemente erzeugt werden und wird in der Regel durch direkten Kontakt oder über ein Koppelmittel an das Objekt übertragen. Luftgekoppelter Ultraschall spielt in kommerziellen Anwendungen bisher eine untergeordnete Rolle, da die Dif-ferenz der akustischen Impedanzen von Luft und Festkörpern immense Verluste beim Übergang des Schallsignals hervorruft.
In diesem Beitrag soll ein neuartiges Anregungsprinzip vorgestellt werden, mit dem ein Großteil dieser Verluste vermieden wird. Anstelle eines Festkörpers soll mit Hilfe einer fluidischen Düse Druckluft zur Signalerzeugung eingesetzt werden. In die-ser Düse wird eine selbsterhaltende Strömungsinstabilität erzeugt, die einen Schall-puls von bis zu 100 kHz hervorruft, sodass der Impedanzverlust in die Umgebungsluft entfällt. Da die charakteristische Frequenz eines fluidisch generierten Pulses maßgeb-lich von der Bauform der Düse und dem anliegenden Druck abhängt, lässt sich mittels einer geeigneten Strömungsregelung ein breiter Frequenzbereich zur Abtastung nut-zen. Die so emittierten Pulse werden auf das Prüfobjekt gerichtet und die reflektierten Signale mit einem Laservibrometer an der Oberfläche des Objekts im Echo-Verfahren abgetastet. Von drei signalmindernden Materialübergängen bei gewöhnlichem luftge-koppeltem Ultraschall bleibt in dem hier vorgeschlagenen Messystem lediglich die Grenzfläche von Luft zu Prüfkörper, sodass eine höhere Signalausbeute als bisher er-wartet werden kann.
The reassessment of bridges is becoming increasingly important. The basic requirement for analyses of structural safety is reliable knowledge about individual structures. This paper introduces the new approach to evaluate the quality of measured data gained from non-destructive testing (NDT) to provide reliable, objective, and relevant information about existing bridges. The purpose is to relate this validated knowledge to probabilistic analyses. Bridging the gap between NDT and numerical reassessments indicates reduced numerical uncertainties and residual service time extensions. This paper deals with an application of this approach using measurement data collected by ultrasonic technique at a prestressed concrete bridge.
Reliability assessment of existing bridge constructions based on results of non-destructive testing
(2018)
The non-destructive testing methods available for civil engineering (NDT-CE) enable the measurements of quantitative parameters, which realistically describe the characteristics of existing buildings. In the past, methods for quality evaluation and concepts for validation expanded into NDT-CE to improve the objectivity of measured data. Thereby, a metrological foundation was developed to collect statistically sound and structurally relevant information about the inner construction of structures without destructive interventions. More recently, the demand for recalculations of structural safety was identified. This paper summarizes a basic research study on structural analyses of bridges in combination with NDT. The aim is to use measurement data of nondestructive testing methods as stochastic quantities in static calculations. Therefore, a methodical interface between the guide to the expression of uncertainty in measurement and probabilistic approximation procedures (e.g. FORM) has been proven to be suitable. The motivation is to relate the scientific approach of the structural analysis with real information coming from existing structures and not with those found in the literature. A case study about the probabilistic bending proof of a reinforced concrete bridge with statistically verified data from ultrasonic measurements shows that the measuring results fulfil the requirements concerning precision, trueness, objectivity and reliability.
Systematic errors in the evaluation of uncorrected data from thermographic lock-in measurements
(2018)
Lock-in thermography (LT) is based on the correct evaluation of phase differences between the temperature oscillations at different surface regions of the object under test during periodic heating. Since the usual heating procedures contain a DC component, the actual heating pattern achieved is not harmonic. This causes systematic deviations when phase differences are determined by means of harmonic analysis, e.g. with FFT analysis. The resulting errors depend clearly on the ratio between DC and AC amplitude, which is demonstrated at simulated and experimentally recorded temperature transients. Further experimental LT data obtained by different oscillating energy inputs showed a variety of possible shapes of transients with different DC components.
It is known that the spalling risk of dense, high-strength concretes (HSC) can be reduced by the addition of polypropylene (PP) fibres and, in particular, PP-fibres that have been pre-treated using electron irradiation. It is presumed that the enhanced reduction in spalling resulting from electron irradiation pre-treatment of the fibres can be attributed to enhanced penetration of the molten fibre material into the micro-cracks around the fibres, due to their significantly decreased viscosity. So far there has been no experimental evidence for this. Against this background, this paper gives a com-parative analysis of the mode of action of PP-fibres with and without pre-treatment using multi-scale test methodology.
Initially, fire tests on small-scale building components with accompanying damage monitoring veri-fied that the amount of PP-fibres can be halved by using pre-treated PP-fibres without reducing the fire performance of HSC. Detailed investigations of PP-fibres carried out in a completed research project funded by DFG (the German Research Foundation) using digital scanning calorimetry and thermogravimetry measurements (DSC/TG) as well as viscometer measurements showed that the pre-treatment has no significant influence on the melting temperature of the PP-fibres. However, a drastic reduction of the melt viscosity due to the electron irradiation was detectable. Additional dila-tation tests showed that the expansion behaviour of both fibre types and their melts do not differ significantly [1]. Rather, both fibre types generate high pressures when their thermal expansion is hindered. Further detailed investigations by means of continuous heating tests with a low heating rate were carried out on separately produced concrete cylinders. These tests showed that the pre-treatment of the PP-fibres causes earlier dehydration in conjunction with stagnation of thermal expansion of the concrete cylinders (temperature reduction from 180 °C to 170 °C). This is accompanied by in-creased acoustic emission activity during the thermal expansion tests. This leads to the assumption that the pre-treatment of PP-fibres results in earlier micro-crack development. However, it was not possible to confirm this assumption by microscopic examination of drilling cores with a diameter of 30 mm exposed to defined temperatures in the range between 150°C and 300°C. Microscopic obser-vations and additional X-ray 3D computed tomography (3D-CT) scans on miniaturised drilling cores exposed to temperature cycles showed a similar networking of fibre beds by means of micro-cracks in HSC for both fibre types. However, energy dispersive X-ray spectroscopy and wavelength disper-sive X-ray spectroscopy revealed fundamental differences in the penetration capacity of the fibre melts of the two fibre types. The increased penetration of the pre-treated PP-fibre melt revealed in these tests, confirms the initial working hypothesis.