Filtern
Dokumenttyp
- Vortrag (35)
- Zeitschriftenartikel (14)
- Beitrag zu einem Tagungsband (9)
- Forschungsbericht (2)
- Sonstiges (1)
Schlagworte
- Korrosion (35)
- Nichtrostender Stahl (13)
- Corrosion (10)
- Deckschichtbildung (7)
- Zink (6)
- Atmosphärische Korrosion (5)
- KorroPad (5)
- Korrosionsschutz (5)
- Corrosion testing (4)
- Dauerhaftigkeit (4)
Organisationseinheit der BAM
- 7 Bauwerkssicherheit (61) (entfernen)
Eingeladener Vortrag
- nein (35)
Agar gel pads have been used for electrochemical measurements for some time. For zinc in particular, a standard method for measuring the stability of the corrosion product layer is being established. The main interpretation factor is the corrosion product layer resistance RL, as it is easy to determine and interpret. A high corrosion product layer resistance indicates a high level of protection. However, it is not yet known how low the corrosion product layer resistance is for freshly produced zinc samples. As zinc is highly active, it reacts immediately with the environment to form a corrosion product layer, which affects the corrosion product layer resistance. The addition of zinc acetate to the agar gel pads prevents the formation of a surface layer and destroys existing ones.
This makes it possible to measure an almost corrosion product-free zinc surface. This is important in defining the range of corrosion product layer resistance for a protective surface.
Die Versalzung und Verunreinigung von Metalloberflächen durch chloridhaltige Aerosole hat eine große Bedeutung für das Korrosionsverhalten von beschichteten Metalloberflächen im maritimen Bereich und bei Offshore-Anwendungen. So ist z. B. zu klären, ob und in welchem Maße eine Versalzung der Oberfläche Einfluss auf die Haftung und Dauerhaftigkeit von Beschichtungen hat. Dafür sind Detailfragen zu klären, etwa mit welcher Versalzung nach welchem Zeitraum zu rechnen ist oder wie für systematische Untersuchungen eine definierte und reproduzierbare Versalzung im Labor nachgestellt werden kann. Der Beitrag widmet sich diesen Fragestellungen. Es werden Ergebnisse eines Feldversuches auf Helgoland gezeigt und ein einfaches Verfahren zur definierten Beladung von Metalloberflächen mit Chloriden im Labormaßstab vorgestellt.
Der maßgebliche Korrosionsschutz von nicht rostendem Stahl in Beton basiert, anders als bei unlegiertem Betonstahl, auf der Ausbildung einer Chromoxidschicht. Die Chromoxidschicht ist in alkalischem und in carbonatisiertem Beton beständig, sodass nicht rostende Stähle in einem passiven Zustand vorliegen.
Die Initiierung von Lochkorrosionserscheinungen ist dagegen auch an nicht rostenden Stählen in Beton möglich. Der korrosionsauslösende Chloridgehalt ist neben dem Gehalt an Legierungselementen (insbesondere dem Chromgehalt) und der Oberflächenbeschaffenheit auch vom Konzentrationsverhältnis von OH“ zu CI“ im Elektrolyten abhängig. Daher ist prinzipiell zu erwarten, dass in karbonatisierten Betonen geringere Chloridgehalte Korrosion initiieren können als in Betonen mit höheren pH-Werten. Dies gilt in besonderem Maße für nicht rostende Betonstähle mit geringen Chromgehalten, wie z. B. Produkte aus dem Werkstoff 1.4003 (X2CrNi12) mit seiner im Vergleich zu den Standardausteniten geringen Beständigkeit. Um den kritischen korrosionsauslösenden Chloridgehalt am Beispiel eines am Markt verfügbaren ferritischen Chromstahls zu bestimmen, wurden an der Bundesanstalt für Materialforschung und -prüfung (BAM) umfangreiche Untersuchungen zu beschleunigten Korrosionsversuchen in alkalischen und karbonatisierten Mörteln durchgeführt. Mittels Laser-induced Breakdown Spectroscopy (LIBS) konnten die korrosionsauslösenden Chloridgehalte im Phasengrenzbereich Betonstahl-Mörtel ermittelt werden.
The present work describes the combination of electrochemical investigations by using a gel‐type electrolyte with Fourier‐transformed infrared spectroscopy to investigate partially extremely thin corrosion product films on titanium‐zinc. The gel pad method enables the determination of corrosion relevant parameters such as the potential and the linear polarization resistance without altering the corrosion product layers, which are extremely prone to re‐dissolution when freshly formed. Complementary infrared spectroscopy enables the determination of main compounds of even very thin surface layers of few tenth of nanometers with a certain lateral resolution. It was found that zinc forms mostly zinc carboxy‐hydroxides such as hydrozincite, under various exposure conditions. The protective properties of these hydrozincite layers depend on the structure of the corrosion product film rather than on its thickness. In mid‐term exposure tests, shallow corrosion pits were found even in the absence of corrosive agents such as chloride.
In maritimer Exposition können Zinkbauteile Nutzungsdauern von 50 Jahren erreichen. Dabei werden Expositionen mit Spritzwasserbelastung durch Meerwasser nicht betrachtet. Normative Betrachtungen und Korrosionsprognosen basierend auf Einjahreswerten liefern hier grundlegend falsche Ergbnisse, da sie eine signifikant höhere Belastung der Atmosphäre mit SO2 voraussetzen.
In maritimer Exposition können Zinkbauteile Nutzungsdauern von 50 Jahren erreichen. Dabei werden Expositionen mit Spritzwasserbelastung durch Meerwasser nicht betrachtet. Normative Betrachtungen und Korrosionsprognosen basierend auf Einjahreswerten liefern hier grundlegend falsche Ergbnisse, da sie eine signifikant höhere Belastung der Atmosphäre mit SO2 voraussetzen.
In maritimer Exposition können Zinkbauteile Nutzungsdauern von 50 Jahren erreichen. Dabei werden Expositionen mit Spritzwasserbelastung durch Meerwasser nicht betrachtet. Normative Betrachtungen und Korrosionsprognosen basierend auf Einjahreswerten liefern hier grundlegend falsche Ergebnisse, da sie eine signifikant höhere Belastung der Atmosphäre mit SO2 voraussetzen.
Die grundlegenden Korrosionsprozesse sind mit wenigen chemischen Formeln beschrieben, aber Korrosion ist immer eine Systemeigenschaft zwischen dem Werkstoff, dem Medium in dem er eingesetzt wird und den konstruktiven Bedingungen. Das macht es zu einem komplexen System, indem alle Einflussfaktoren ganzheitlich berücksichtigt werden müssen.
Anhand der Wirksumme ist eine Abschätzung des legierungsabhängigen Einflusses auf den Korrosionswiderstand gegen chloridhaltige Medien möglich. Die berechneten Werte sind nur bei optimaler Wärmebehandlung und Verarbeitung zutreffend.
Die Anwendung einer einfachen Formel unter Berücksichtigung von Chrom, Molybdän und Stickstoff ist in der Regel völlig ausreichend. Das daraus abgeleitete Ranking von Werkstoffen ist für diverse technische Regelwerke und zur Unterstützung der Werkstoffauswahl geeignet.
Für die Warenein-/Ausgangskontrolle ist die alleinige Feststellung der Wirksumme unzureichend. Ergänzende Korrosionsuntersuchungen/-prüfungen zur Beschreibung des Korrosionswiderstandes sind dafür notwendig. Gleiches gilt für die Beurteilung von Schadensfällen. Hier sind Verarbeitung, Einsatzbedingungen und die Konstruktion von ausschlaggebender Bedeutung.
Due to the large number of stainless steels with different chemical composition and different microstructure the selection of the suitable material represents a huge challenge. In order to facilitate the appropriate grade selection, in the current European standard EN 1993-1-4 a procedure is defined based on the use of a look-up table considering the key variables that influence the selection of stainless steels. The table uses descriptions that competent designers should be able to readily understand or define without prior knowledge. The output from the look-up table is used to select alloys based on a Corrosion Resistance Class (CRC) from I to V. The advantage of this approach is that the designer simply specifies the relevant CRC and does not need to consider in detail which of the many (very similar) alloys to specify.
Risiko der Wasserstoffentwicklung an martensitischen Schraubankern unter baupraktischen Bedingungen
(2020)
Die vorliegende Untersuchung beschäftigt sich mit der Fragestellung, ob unter praxisrelevanten Bedingungen die Entstehung von Wasserstoff an vollmartensitischen Schraubankern möglich ist. Im Gegensatz zu austenitischen Werkstoffen besteht bei martensitischen Werkstoffen bei Gegenwart von Wasserstoff stets die Möglichkeit einer wasserstoffinduzierten Versprödung des Materials. Hierfür wurde ein in der Praxis häufig anzutreffendes Szenario gewählt, das ein galvanisches Element, bestehend aus nichtrostenden Schraubankern (in diesem Fall martensitischen) und einer verzinkten Ankerplatte an einem Betonkörper, umfasst. Zum Nachweis einer Wasserstoffentwicklung werden der Elementstrom zwischen den Bauteilen sowie das Korrosionspotential erfasst. Die Ergebnisse der Versuche zeigen, dass über eine zeitlich begrenzte Dauer eine starke kathodische Polarisation der martensitischen Schraubanker durch die korrosive Auflösung des Zinks erfolgt. Als Folge kommt es zur Wasserzersetzung im Phasengrenzbereich der Schraubanker und zur Entstehung von atomarem Wasserstoff. Das berechnete Gasvolumen des entstandenen Wasserstoffs an den Stahlankern wurde bestimmt und lag im Mittel bei 11,14 ± 1,94 ml. Eine Diffusion des an der Stahloberfläche adsorbierten Wasserstoffs in den martensitischen Werkstoff ist somit theoretisch möglich und impliziert eine mögliche Gefährdung durch wasserstoffinduzierte Rissbildung und spontanes Versagen unter Belastung.
Hydrogen-induced stress corrosion cracking (HSCC) is well known, and highly sensitive pre-stressing steels are normally not available on the market. But in the case of existing structures, it could be necessary to ensure their safety through special kinds of investigations. Those kinds of investigations are often not applicable in a non-destructive way.
Therefore, a once in a lifetime project was initiated.
In the course of the deconstruction of the "Bridge of the 20th anniversary of the GDR" at the Altstädter Bahnhof in Brandenburg a. d. Havel, new information on the initiation of hydrogen-induced stress cracks could obtained. The initial observation to do several investigations at this bridge are several meters long longitudinal cracks in the concrete web of the box girder above and below the tension duct. The BAM was commissioned by the Brandenburg State Road Administration to participate in a corresponding joint project which is financed by the Federal Ministry for Digital and Transport. The added value of the new information gained in this project goes beyond the specific structure. It describes unexpected new damage patterns that can be transferred to other structures with concentrated tendons (tendon block method and Baur-Leonhardt method) and were previously unknown in this form. These should be made known to other developers to enable them to initiate any necessary actions.
One of the major results is, the wire breaks observed at this bridge can be attributed to cracking as a result of HSCC and subsequent crack growth until breakage, due to cyclic loading from traffic and alternating restraint stresses. The probable trigger here was crevice corrosion processes at the contact points of the wires to the spacer plates in superposition with high tensile stresses due to prestressing after or with in grouting the duct. Tension wire breaks, which may have occurred before grouting and during prestressing, were not detected. The unfavorable gap situation at the spacer plates occurs over the entire cross-section of the prestressing channel and can thus affect each individual prestressing wire. Losses in the load-bearing capacity of the prestressed concrete structure can then be the result. A disadvantage of the prestressing block method in this respect is that a large number of individual wires can be affected at the same time (theoretically all wires), which can reduce the prestressing effect of the concentrated tendon accordingly. With the usual use of only one tendon per web, the possibility of load transfer to other tendons is thus not given (lack of redundancy).
Im Vortrag werden Ergebnisse des gleichnamigen AiF Forschungsvorhabens gezeigt, die den Einfluss verschiedener Schleifmittel auf die Korrosionsbeständigkeit geschliffener Oberflächen nichtrostender Stähle belegen. Es konnte ein signifikanter Einfluss durch die Verwendung von Granulatschleifbändern nachgewiesen werden, der die Korrosionsbeständigkeit der Oberflächen reduziert. Grund sind auf der Oberfläche zurückbleibende Materialaufplattungen von Eigenmaterial aus dem Schleifprozess. Es wurden unterschiedliche Korrosionsuntersuchungen durchgeführt und mittels Oberflächenanalytik untermauert.
Durch eine breite Beteiligung von Schleifmittelherstellern, -anwendern und wissenschaftlichen Einrichtungen im projektbegleitenden Ausschuss (PA) konnte der vielschichtige Themenkomplex „Schleifen“ im Kontext zu den Projektzielen umfassend untersucht werden. Es wurden praxisrelevante Parameterfelder definiert, die eine erfolgreiche Aufklärung der Projektfragestellung ermöglichten.
Im Zuge der Untersuchungen wurde ein signifikanter Einfluss beim Einsatz von Granulatschleifbändern auf das Korrosionsverhalten geschliffener Oberflächen festgestellt. Damit zeigten geschliffene Oberflächen regelmäßig eine schlechtere Korrosionsbeständigkeit als Oberflächen, die mit sonst gleichen Parametern mit einlagig gestreuten Bändern bearbeitet wurden.
Die durch einige Untersuchungsergebnisse aus vorangegangenen AiF-Vorhaben ursprünglich verfolgte These, dass Unterschiede in der Korrosionsbeständigkeit auf die Kornart der Schleifmittel Korund bzw. SiC zurückzuführen ist, konnte nur bedingt bestätigt werden. Bei den systematischen Untersuchungen innerhalb dieses Projektes erwies sich der Einfluss der Kornart im Vergleich zum Einfluss des Schleifbandtyps (Granulat bzw. einlagig gestreutes Korn) als weniger relevant.
Durch weiterführende Untersuchungen konnten auf Oberflächen, die mit Granulatschleifbändern bearbeitet wurden, große Materialaufplattungen aus Eigenmaterial festgestellt werden. Das Eigenmaterial wird dabei im Schleifprozess zunächst abgetragen und aufgrund der Topografie des Schleifbandes zeitweise auf den Bändern festgehalten. Später lösen sich diese Materialanhäufungen vom Band ab und können prozessbedingt durch Wärme- und Krafteinwirkung auf den bearbeiteten Oberflächen aufgeplattet werden. Durch REM und KorroPad Untersuchungen ließen sich Bereiche mit solchen Eigenmaterialaufplattungen eindeutig als wesentliche Ausgangspunkte für Korrosionsprozesse identifizieren. Das aufgeplattete Material ist stark verformt, thermisch beeinflusst und bildet eine Spaltgeometrie zur Bauteiloberfläche aus. Diese Veränderungen führen zur Störung der Passivschichtausbildung in diesen Bereichen und verursachen damit eine erhöhte Korrosionsanfälligkeit der Oberflächen.
Durch gezielte Nachbearbeitungsprozesse ist es möglich, die Eigenmaterialaufplattungen von den Oberflächen zu entfernen. Im Rahmen des Vorhabens wurde dazu eine Nachbearbeitung mittels Schleifvlies geprüft, die zu einer Entfernung der Eigenmaterialaufplattungen und damit zu einer Wiederherstellung der erwarteten Korrosionsbeständigkeit führte. Wird der Endschliff von Oberflächen mit einlagig gestreutem Korn ausgeführt, sind ebenfalls keine korrosionsrelevanten Materialaufplattungen zu erwarten.
Die in einem vorhergehenden AiF Vorhaben IGF 17136 N/1 entwickelte Methode der KorroPad-Prüfung konnte auch hier erfolgreich für die Untersuchung der Auswirkung unterschiedlicher Prozessparameter auf die Korrosionsbeständigkeit der Oberflächen eingesetzt werden. Zudem erwies sich das EPR-SL-Verfahren als ein weiterer Ansatz, um die Passivschichtstabilität verschieden geschliffener Oberflächen vergleichend untersuchen zu können.
Mit den nun vorliegenden Erkenntnissen können kmU künftig durch Anpassungen und Optimierung von Schleifprozessen eine gute Korrosionsbeständigkeit der bearbeiteten Oberflächen sicherstellen. Die Optimierung der Prozessparameter und -schritte kann durch den Einsatz der KorroPad-Prüfung Inhouse erfolgen und somit die laufende Fertigung im Rahmen der Qualitätsprüfung überwacht und dokumentiert werden.
In diesem Vortrag werden Ergebnisse des gleichnamigen AiF Forschungsvorhabens gezeigt, die einen deutlichen Einfluss verschiedener Schleifmittel auf die Korrosionsbeständigkeit von damit geschliffenen nichtrostender Stahloberflächen belegen. Es konnten ein signifikanter Einfluss durch die Verwendung von Granulatschleifbändern festgestellt werden, der die Korrosionsbeständigkeit der Oberflächen drastisch reduziert. Grund sind auf der Oberfläche zurückbleibende Materialaufplattungen von Eigenmaterial aus dem Schleifprozess. Es wurden unterschiedliche Korrosionsuntersuchungen durchgeführt und mittels Oberflächenanalytik untermauert.
Das Grundproblem der heute verfügbaren und normativ geregelten Prüfverfahren für Zinküberzüge besteht neben den realitätsfernen Prüfbedingungen vor allem in der subjektiv geprägten Auswertung der Prüfergebnisse. Die systematische Betrachtung der Entwicklungen der letzten Jahre zeigt, dass die üblichen Verfahren den aktuellen Anforderungen damit schon vom Ansatz her nicht gerecht werden können und auch die bisher betriebene, fortlaufende Variation und Anpassung von Prüfbedingungen keinen grundlegend neuen Lösungsansatz bieten können. Ein solcher ergibt sich nur, wenn die Zinküberzüge hinsichtlich der kinetischen Eigenschaften der Deckschichtbildung und -auflösung umfassend beschrieben werden können, was nur durch den Einsatz elektrochemischer Untersuchungsmethoden mittels Gelelektrolyten möglich ist.
Aus diesem Grund wurde im Verbundforschungsvorhaben GELELEK auf der Basis elektrochemischer Methoden unter Verwendung eines Gelelektrolyten ein Normenvorschlag für eine Prüfnorm erarbeitet und zur Normungsreife geführt, welcher den Anforderungen an ein Messsystem für Feldanwendungen entspricht.
Im Verbundforschungsvorhaben GELELEK wurde eine gezielte Kombination von Laboruntersuchungen mit Untersuchungen im Feld und Bauteilen unter realen Einsatzbedingungen angestrebt. Randbedingungen für eine gesicherte Messung von atmosphärisch bewitterten Zinküberzügen unter Einsatz von Gelelektrolyten wurden erarbeitet und im Normenvorschlag festgeschrieben. Darüber hinaus wurde ein mobiles Messgerät für Messungen mit Gelelektrolyten an realen Bauteilen entwickelt. Nach Abschluss des Forschungsvorhabens steht Industrievertretern und Prüfinstituten ein wissenschaftlich gesichertes Messverfahren basierend auf Kennwerten zur Verfügung, um Zinküberzüge und deren momentane Schutzwirkung unter praxisrelevanten Bedingungen einschätzen und normativ geregelt prüfen zu können.
Der vorliegende Forschungsbericht gibt einen Überblick über die Motivation zur Durchführung des Forschungsvorhabens, wichtige Arbeitsschritte, Details zur entwickelten Prüfmethode sowie Einsatzmöglichkeiten für Prüfinstitute und Unternehmen.
Brückenbauwerke, die im Spannblockverfahren hergestellt wurden, können bauartbedingt wasserstoffinduzierte Spannungsrisse über den gesamten Querschnitt eines Spannkanals aufweisen. Das Risswachstum kann infolge dynamischer Beanspruchung über die Nutzungsdauer fortschreiten und zu Spanndrahtbrüchen führen.