Filtern
Erscheinungsjahr
Dokumenttyp
- Vortrag (51)
- Zeitschriftenartikel (39)
- Beitrag zu einem Tagungsband (30)
- Beitrag zu einem Sammelband (12)
- Forschungsbericht (3)
- Buchkapitel (2)
- Posterpräsentation (2)
Sprache
- Englisch (88)
- Deutsch (50)
- Mehrsprachig (1)
Schlagworte
- Creep (20)
- Nickel-base superalloys (12)
- LCF (9)
- Superalloy (9)
- Rafting (7)
- Low cycle fatigue (6)
- Single crystal (6)
- Superalloys (6)
- TMF (6)
- Constitutive law (5)
Organisationseinheit der BAM
Paper des Monats
- ja (1)
Eingeladener Vortrag
- nein (51)
Aero-engine turbine disks are safety-relevant components which are operated under high thermal and mechanical stress conditions. The actual part qualification and certification procedures make use of spin-tests conducted on production-similar disks. While these tests provide, on the one hand, a reliable definition of the critical conditions for real components, on the other hand they represent a relevant cost item for engine manufacturers. The aim of this work is to present two alternative burst speed assessment methods under development based on the Failure Assessment Diagram (FAD) and a global stability criterion, respectively. In the scope of the fracture mechanics assessment, the failure modes hoop-burst and rim-peeling are investigated with semicircular surface cracks modelled at the critical regions on the turbine disk. The comparison of the predicted critical rotational speed shows good agreement between the assessment methods.
Aero-engine turbine disks are safety-relevant components which are operated under high thermal and mechanical stress conditions. The actual part qualification and certification procedures make use of spin-tests conducted on production-similar disks. The aim of this work is to present part of a fracture mechanics-based procedure under development which aims at replacing the tests on production-similar disks with lab tests on fracture mechanics specimens. The finite element simulation of the cracked disk considers the real thermal and mechanical loading conditions. In order to design a lab representative specimen, beside the crack driving force, expressed in terms of 𝐽-integral, also the constraint to plastic deformation e.g., stress triaxiality, at the crack-tip must be similar for the same crack in the specimen and in the disk. This has been achieved and as expected, both the highest 𝐽 -integral and constraint factor are calculated at the same location along the crack front for both disk and specimen. The results of the structural integrity assessment in the form of a Failure Assessment Diagram (FAD) show good agreement between designed specimen and disk both in terms of expected failure mode and value of the critical speed. In addition, probabilistic aspects are also considered in the calculations.
Micromechanical investigations and modelling of a copper-antimony-alloy under creep conditions
(2014)
In many practical applications, creep damage is the limiting factor of a components lifetime. A micromechanical model of creep induced grain boundary damage is proposed, which allows for the simulation of creep damage in a polycrystal within the framework of finite element analysis. The model considers grain boundary cavitation and sliding according to a micromechanically motivated cohesive zone model while creep deformation of the grains is described following the slip system theory. The model can be applied to idealised polycrystalline structures, such as a Voronoi tessellation or, like demonstrated here, to real grain structures of miniature creep specimens. Creep tests with pure Cu single crystals and with a coarse-grained polycrystalline Cu-1 wt.% Sb alloy at 823 K have been performed and used to calibrate the polycrystal model. The grain structure of the polycrystalline CuSb specimens has been revealed by the EBSD method. Extensive grain boundary sliding and cavitation has been observed in the crept specimens. Grain boundary sliding has been found to promote wedge-type damage at grain boundary triple junctions and to contribute significantly to the total creep strain. Furthermore, the assumed stress sensitivity of the models grain boundary cavity nucleation rate strongly influences the development of wedge-type damage.
Simulations of cavitation processes on a grain boundary under creep conditions have been carried out, taking into account nucleation, growth, coalescence and sintering of multiple cavities. Cavity growth rates have been calculated through a resolution procedure based on the use of holomorphic complex functions. Three dimensionless parameters have been identified that are responsible for the cavitation development. Parameter studies have been carried out in order to characterise the mechanisms that are responsible for the cavitation development. These studies have been used to develop a physically motivated, simplified model in order to describe the cavitation development of the simulations in terms of global state variables. The simplified model is able to reproduce the cavitation development for all considered combinations of the dimensionless parameters and allows the description of the thickening behaviour of a cavitating grain boundary.
A micromechanical model of creep induced grain boundary damage is proposed, which allows for the simulation of creep damage in a polycrystal with the finite element method. Grain boundary cavitation and sliding are considered via a micromechanically motivated cohesive zone model, while the grains creep following the slip system theory. The model has been calibrated with creep test data from pure Cu single crystals and a coarse-grained polycrystalline Cu-Sb alloy. The test data includes porosity measurements and estimates of grain boundary sliding. Finally, the model has been applied to Voronoi models of polycrystalline structures. In particular the influence of grain boundary sliding on the overall creep rate is demonstrated.
The stress States of components under Service conditions differ in general from the loading conditions that are routinely applied during material testing. When data that results, e.g., from uniaxial testing should be used for lifetime assessment, a good understanding of the failure behaviour in dependence of the stress state is necessary. For polycrystalline materials under high temperature loading, the development of creep damage is one important factor that limits a component’s lifetime. For cases where creep damage is related to the nucleation and growth of grain boundary cavities, the local normal stress acting on a grain boundary has been found to have a strong influence on the damage development. Hence, creep damage is usually localized along planes that lie perpendicular to the maximum principal tensile stress.
The present work focuses on the cubic slip phenomenon in single crystal superalloys with a high fraction of γ' precipitates at high temperature.
The macroscopically apparent cubic slip mechanism is known to significantly reduce the tensile and creep strength of <1 1 1> oriented specimens. However, recent results obtained by 3D dislocation dynamics (Vattré et al., 2009) suggest a new interpretation of the so-called pseudo-cubic slip related to the nature of the dislocation network formation at the interfaces. These results are taken into account in a micromechanical model to improve the estimation of the strain hardening anisotropy. In accordance with the discrete simulations, it is shown that a key role is played by the combination of the activated octahedral slip systems as a function of the crystal orientation. In the <1 1 1> case, the contribution of the activated systems to kinematical hardening compensate, whereas strain hardening remains high for the <0 0 1> case. The experimental dependence of plastic flow on the orientation is also explained at the dislocation-scale mechanisms.
Results are presented for the alloy CMSX-4 in several orientations.
In diesem Forschungsvorhaben erfolgte eine Überprüfung der Übertragbarkeit der Werkstoff- und Rechenmodelle für die Lebensdauervorhersage von ATL-Heißteilen unter TMF-Beanspruchung auf eine andere Werkstoffklasse als im Vorgängervorhaben, d.h. auf das austenitische Gusseisen EN-GJSA-XNiSiCr35-5-2 (Ni-Resist D-5S). Zunächst wurde dafür eine experimentelle Datenbasis geschaffen, da diese vor Beginn des Vorhabens nicht ausreichend war. Dazu wurden Zug-, Kriech-, LCF- und TMF-Versuche durchgeführt, die der Kalibrierung der Modelle dienten. Das Spannungs-Verformungs-Verhalten und die Lebensdauer in den LCF- und TMF-Versuchen werden durch das Modell auch für den neuen Werkstoff überwiegend gut beschrieben. LCF-Versuche mit Haltezeit bei 900 °C sowie IP-TMFVersuche mit einer Obertemperatur von 900 °C werden weniger gut vorhergesagt, da sich der Schädigungsmechanismus ändert. Eine Verifikation des Modells erfolgte mit Hilfe eines Bauteilversuchs an einem Abgassammler. Die überwiegende Anzahl der experimentell ermittelten Rissorte wurden von dem Modell vorhergesagt.
Ein wesentliches Ziel des Vorhabens war, den Einfluss von HCF-Schwingungen auf die TMF-Lebensdauer vertieft experimentell zu untersuchen und das bereits bestehende Lebensdauermodell auf HCF-Überlagerung zu erweitern. Es wurde ein bruchmechanisch motivierter Ansatz entwickelt, in dem die Lebensdauerminderung durch die im TMF-Zyklus überlagerten HCF-Schwingungen abgebildet wird. Mit diesem Ansatz lassen sich die Lebensdauern sowohl für den Werkstoff SiMo 4.05 als auch für den Ni-Resist in guter Übereinstimmung mit dem Experiment Vorhersagen.
Das Ziel des Forschungsvorhabens ist erreicht worden.
In diesem Forschungsvorhaben erfolgte eine Überprüfung der Übertragbarkeit der Werkstoff- und Rechenmodelle für die Lebensdauervorhersage von ATL-Heißteilen unter TMF-Beanspruchung auf eine andere Werkstoffklasse, d. h. auf eine austenitische Gusseisenlegierung mit Kugelgraphit. Dafür wurde die Legierung EN-GJSA-XNiSiCr35-5-2 (Ni-Resist D-5S) ausgewählt. Zunächst wurde für diesen Werkstoff eine experimentelle Datenbasis geschaffen, da diese vor Beginn des Vorhabens nicht ausreichend war. Dazu wurden Zug-, Kriech-, LCF- und TMF-Versuche durchgeführt, die der Kalibrierung der Modelle dienten. Unter TMF-Belastung zeigte der untersuchte Werkstoff ein stark abweichendes Verhalten von den im vorangegangenen Vorhaben untersuchten ferritischen SiMo-Legierungen: Der Werkstoff Ni-Resist zeigte insgesamt eine vergleichbare Festigkeit unter OP- und IP-Bedingungen, während die ferritischen Legierungen unter IP-Beanspruchung eine deutlich höhere Festigkeit aufweisen. Mit zunehmenden Temperaturen und Haltezeiten unter Zugspannungen wurden dagegen beim Werkstoff Ni-Resist Hinweise auf Kriechschädigung gefunden, die schädigungsrelevant sind. Auch dies ist ein deutlicher Unterschied zu den SiMo-Legierungen. Das Spannungs-Verformungs-Verhalten in den LCF- und TMF-Versuchen wird durch das Modell auch für den neuen Werkstoff überwiegend gut beschrieben. Das Gleiche gilt für die Lebensdauervorhersage, die mit Ausnahme der Prüftemperatur 900 °C innerhalb eines Fak-tors zwei liegt. Eine Verifikation des Modells erfolgte mit Hilfe eines Bauteilversuchs an einem Abgassammler, der abwechselnd mit heißem und kaltem Gas durchströmt wurde. Ziel der Bauteilsimulation war insbesondere die Vorhersage der Rissbildungsorte. Eine Vorhersage der exakten Lebensdauer wurde nicht erwartet, da das Bauteil mit einer Gusshaut behaftet war, während die für die Kalibrierung des Lebensdauermodells verwendeten Versuche an bearbeiteten, glatten Proben ohne Gusshaut durchgeführt wurden. Die überwiegende Anzahl der experimentell ermittelten Rissorte wurden vorhergesagt. Schließlich war ein wesentliches Ziel des Vorhabens, den Einfluss von HCF-Schwingungen auf die TMF-Lebensdauer vertieft experimentell zu untersuchen und das bereits bestehende Lebensdauermodell auf HCF-Überlagerung zu erweitern. Dazu wurde zunächst die Daten-basis aus dem Vorgängervorhaben am Bespiel von SiMo 4.05 deutlich ausgebaut, um die verschiedenen Einflussparameter zu erfassen. Es wurde ein Ansatz entwickelt, in dem die Lebensdauerminderung durch die überlagerten HCF-Schwingungen abgebildet wird. Dabei wird davon ausgegangen, dass ab einer bestimmten Risstiefe die Überlagerung der HCF-Schwingungen die Rissausbreitung stark beschleunigt. Der Zeitpunkt, wann diese Beschleunigung eintritt, wird als maßgeblich für die Lebensdauerminderung angesehen. Mit diesem Ansatz lassen sich die Lebensdauern für beide Werkstoffe in guter Übereinstimmung mit dem Experiment vorhersagen.
Für viskoplastische Stoffgesetze wird das prinzipielle Verfahren der Identifikation von Materialmodell-Parametern für das Spannungs-Verformungs- und Versagens-Verhalten metallischer Werkstoffe am Beispiel von Hochtemperatur-Ermüdung aufgezeigt. Dies betrifft zum Einen die Verwendung geeigneter und auch möglichst weniger Experimente zur Hervorbringung der zu beschreibenden Phänomene des Werkstoffverhaltens und deren gezielte Auswertung sowie zum Anderen die physikalisch kontrollierte Führung einer numerischen Optimierung zur Ermittlung vertrauenswürdiger Materialparameterwerte. Diese Vorgehensweise wurde erfolgreich auf Warmarbeitsstähle sowie poly- und einkristalline Superlegierungen angewendet.
The elastic anisotropy caused by the texture in the Nb3Sn filaments of PIT and RRP wires has been calculated by averaging the estimates of Voigt and Reuss, using published Nb3Sn single crystal elastic constants and the Nb3Sn grain orientation distribution determined in both wire types by Electron Backscatter Diffraction. At ambient temperature the calculated Nb3Sn E-moduli in axial direction in the PIT and the RRP wire are 130 GPa and 140 GPa, respectively. The calculated E-moduli are compared with tensile test results obtained for the corresponding wires and extracted filament bundles.
The formation of pores in CMSX-4 nickel based superalloys is detrimental to the service life of the material. A way to avoid the problem is to treat the superalloys under Hot Isostatic Pressing (HIP), which enables a large volume fraction of pores to be annihilated. This paper aims to understand the contribution of plastic activity related to the gliding of dislocations on the pore annihilation. Simulations based on a phase-field model of dislocation are performed and make it possible to consider the strong anisotropy of the CMSX-4 under HIP conditions in conjunction to the strong elastic heterogeneity introduced by the pore. For pores with a radius of few micrometers, it is shown that edge parts of dislocation lines that present an extra half atomic plane oriented towards the pore are stacked above and under it in the direction which is perpendicular to their slip-planes, causing an increase of the number of dislocation along the four octahedral directions of the FCC single crystal which intersect the pore center. Results are streamlined within the isotropic elastic theory of dislocations. Effects of elastic anisotropy and dislocation reactions are also investigated in order to specify what would be the dislocation configuration around a pore in CMSX-4 under HIP conditions. Notably, the elastic anisotropy is shown to significantly modify the arrangement of dislocations close to the pore equator. Simulations also allow for the characterization of pore/dislocation interactions when dislocations are involved in Low Angle Boundaries as experimentally observed.
The oxidation behaviour of single crystal PWA 1483 at 950 °C was investigated by means of XRD, SEM and EDS. The parabolic oxidation behaviour, as defined by mass gain and the respective oxide layer thicknesses, is characterized by a parabolic rate constant of about 4 × 10-6 mg²/(cm4 × s) and the formation of a multi-layered oxide scale. An outer scale contains a Ti-bearing thin film composed of TiO2 and NiTiO3 but mostly Cr in Cr2O3 and (Ni/Co)Cr2O4 besides NiTaO4. This outer scale is connected to a discontinuous layer of Al2O3 and an area of γ?'-depletion within the base material.
The current competitive situation on electricity markets forces power plants into cyclic operation regimes with frequent load shifts and starts/shutdowns. In the present work, the cyclic mechanical behavior of ferritic-martensitic 9-12 % Cr steels under isothermal and thermomechanical loading was investigated for the example of grade P92 material. A continuous softening was observed under all loading conditions. The introduction of hold periods to the applied cycles reduced material lifetime, with most prominent effects at technologically relevant small strain levels. The microstructural characterization reveals a coarsening of the original “martensitic” lath-type microstructure to a structure with polygonal subgrains and reduced dislocation density. The microstructural data forms the input for a physically-based modelling approach.
Simulation of fatigue crack growth by crack tip plastic blunting using cohesive zone elements
(2010)
The propagation of a fatigue crack in 2D specimens by crack tip plastic blunting is simulated by using a Finite Element implementation of the strip-yield model. At each cycle, the crack growth is assumed to result from the variation of the Crack Tip Opening Displacement (ΔCTOD). The implementation is based on cohesive elements with an elastic perfectly plastic behavior, which allows to simulate, the crack closure phenomena due to the plastic wake behind the crack tip. A mesh sensitivity analysis provides the minimum number of elements requested in the crack tip plastic zone for a given accuracy. Then, the advance scheme based on crack tip blunting is described. Finally, the variation of the opening load with respect to the load ratio R, and to the maximum load is investigated and compared with analytical results.
It is shown experimentally that, during annealing and creep under low applied stresses, matrix dislocation loops frequently cross-glide. The periodic length of the zigzag dislocations deposited in the interfaces is equal to that of the γ/γ'-microstructure. Initially, the zigzag dislocations move in the (001) interface by a combination of glide and climb but then they stop near the γ'-edges and align along (100). Reactions of such dislocations lead to the formation of square interfacial networks consisting of (100) oriented edge dislocations. The complex dislocation movement is explained by the inhomogeneity of the misfit stresses between γ- and γ'-lattices. The tensile components of the stress tensor drive the dislocations through the channel, whereas the shear components near the γ'-edges cause the zigzag movement and the (100) alignment. The total effect is the most efficient relaxation of the misfit stresses. The results are relevant, especially for single-crystal superalloys of the newest generations, which have an increased γ/γ'-misfit due to the high level of refractory elements.
Crack growth tests have been performed at 950 °C with Single Edge Notch specimens of the Ni-based single crystal superalloy PWA1483. In particular, several orientations and frequencies have been investigated, thus allowing the assessment of the influence of these parameters on the crack growth rate. In addition, oxidation experiments have been carried out to characterize the kinetics of the outer oxide scale growth at the same temperature.
On the other side, crack growth has been simulated with the Finite Element program ABAQUS in real test conditions by the node release technique. The nodes are released according to the measured crack growth rate.
The simulation results are compared with the test results on the basis of the computed Crack Tip Opening Displacement (CTOD). For this purpose, the crack is propagated until a stabilized value of the CTOD is obtained. This is usually the case when the crack has crossed the initial plastic zone. The procedure provides an evaluation of the effects of cycle frequency, crystal orientation, plasticity and oxide induced crack closure.
Components in the Aerospace, Power and Automotive engineering sectors are frequently subjected to cyclic stresses induced by thermal fluctuations and mechanical loads. For the design of such components, reliable material property data are required which need to be acquired using well accepted and reproducible test procedures for thermo-mechanical fatigue (TMF) loading. There is limited availability of proven TMF data indicating there is need for further research and testing. The TMF behaviour of materials is often desired to be simulated in models which describe the cyclic stress-strain behaviour, the fatigue life and the cyclic crack growth behaviour. There is a continuous need for the development and amendment of such models. Models can be validated by using materials in industrial applications which are subjected to TMF loading.
The 3rd Workshop on Thermo-Mechanical Fatigue was held on 27–29 April 2016 at BAM, Berlin, Germany. The workshop was attended by 90 attendees coming from 17 countries in the world. 38 presentations including five poster presentations were held.
The following topics were covered by the workshop:
– TMF of materials coated with Thermal Barrier Coatings.
– Thermal Gradient Mechanical Fatigue.
– TMF crack growth.
– TMF + High Cycle Fatigue.
– TMF Modelling and Lifetime Prediction.
– TMF Properties of steels, cast iron, Al-, Mg- and Ni-alloys
– Advanced TMF Testing Techniques.
– Industrial Applications.
A panel discussion was held regarding the present state of TMF testing standards (ISO and ASTM) and their potential for improvement. The discussion and contributions were summarized and forwarded to the standard committees. The 3rd TMF-Workshop ensured the continuation of international exchange of knowledge providing a forum to present and discuss all recent developments in the field of thermo-mechanical fatigue.
The current special issue publishes eleven selected papers of the 3rd TMF-Workshop 2016. The papers were peer reviewed by a number of experts in the Thermo-Mechanical Fatigue sector. I hope you will enjoy reading papers of this special issue.
Computational methods for lifetime prediction of metallic components under high-temperature fatigue
(2019)
The issue of service life prediction of hot metallic components subjected to cyclic loadings is addressed. Two classes of lifetime models are considered, namely, the incremental lifetime rules and the parametric models governed by the fracture mechanics concept. Examples of application to an austenitic cast iron are presented. In addition, computational techniques to accelerate the time integration of the incremental models throughout the fatigue loading history are discussed. They efficiently solve problems where a stabilized response of a component is not observed, for example due to the plastic strain which is no longer completely reversed and accumulates throughout the fatigue history. The performance of such an accelerated Integration technique is demonstrated for a finite element simulation of a viscoplastic solid under repeating loading–unloading cycles.
Gas turbines are widely used for a variety of purposes including power generation, compression or as jet engines in aircrafts. The critical components of a gas turbine are the high-pressure turbine blades which operate under severe conditions. These include thermo-mechanical loadings over temperatures ranging from room temperature up to 1100°C.
While a large number of constitutive models for single crystals have been proposed, most applications are restricted to special loading scenarios, temperature range and deformation mechanisms. In particular, a number of models are focused on pure creep. Only a few papers consider application of both creep and fatigue. Applications of the constitutive models to long-term stress relaxation are even scarcer. The new model assumes deformation-induced softening and can properly reproduce the viscous behavior at different time scales.
The model has been calibrated with the uniaxial tests at 800°C and 950°C in [001], [011] and [111] specimens of a nickel-basis superalloy. The predicted creep, short- and long-term relaxation and cyclic tests are in reasonable agreement with the experimental observations.
An extension of the constitutive viscoplastic model of Meric and Cailletaud is presented. The new model
accounts for coupling of plasticity and viscoplasticity to describe the rate dependence at low and moderate
temperatures. The model contains two boundaries: an elastic one and a viscoplastic one. Between the
boundaries, the only contribution to yielding is the rate dependent viscoplastic mechanism. Once the viscoplastic
boundary is reached, an additional rate independent flow mechanism becomes active. However, the extended
model is not able to predict properly both creep and long-term relaxation tests simultaneously. Therefore, a
deformation-induced softening is assumed, which is supposed to mainly affect static recovery.
The model has been calibrated with the mechanical tests on a single crystal nickel-basis superalloy. The uniaxial
tests have been carried out in the temperature interval 600°C – 1100°C in [001], [011] and [111] specimens.
The predicted creep, relaxation and non-isothermal cyclic tests exhibit reasonable agreement with the
experimental observations.
A crystallographic constitutive model is developed, which accounts for both rate-sensitive and rate-insensitive flow. Single-crystal plasticity and viscoplasticity are the limiting cases of the model, so that it properly reflects the material response over a wide temperature range. A non-linear dynamic recovery is included to properly describe ratchetting. We provide a robust integration scheme based on generalization of the return-mapping algorithm and of the procedure for active set search.
The implicit integration and consistent tangent are implemented through the UMAT subroutine in the ABAQUS finite element program. The capability of the model to account for both high and low strain rates is demonstrated in numerical examples. Finally, the stability of integration scheme and quadratic convergence of the global NewtonRaphson equilibrium iterations are demonstrated on the example of a notched bar under tension.
Experimentally informed multiscale creep modelling of additive manufactured Ni-based superalloys
(2023)
Excellent creep resistance at elevated temperatures, i.e. T / T_m> 0.5, due to γ-γ’ microstructure is one of the main properties of nickel-based superalloys. Due to its great importance for industrial applications, a remarkable amount of research has been devoted to understanding the underlying deformation mechanism in a wide spectrum of temperature and loading conditions. Additive manufactured (AM) nickel-based superalloys while being governed by similar γ-γ’ microstructure, exhibit AM-process specific microstructural characteristics, such as columnar grains, strong crystallographic texture (typically <001> fiber texture parallel to build direction) and compositional inhomogeneity, which in turn leads to anisotropic creep response in both stationary and tertiary phases.
Despite the deep insights achieved recently on the correlation between process parameters and the resulting microstructure, the anisotropic creep behavior and corresponding deformation mechanism of these materials are insufficiently understood so far. One reason for this is the lack of capable material models that can link the microstructure to the mechanical behavior. To overcome this challenge, a multiscale microstructure-based approach has been applied by coupling crystal plasticity (CP) and polycrystal model which enables the inclusion of different deformation mechanisms and microstructural characteristics such as crystallographic texture and grain morphology. The method has been applied to experimental data for AM-manufactured INCONEL-738LC (IN738). The effect of different slip systems, texture, and morphology on creep anisotropy at 850°C has been investigated. Results suggest a strong correlation between superlattice extrinsic stacking fault (SESF) and microtwinning and observed creep anisotropy.
The current lack of quantitative knowledge on processing-microstructure–property relationships is one of the major bottlenecks in today’s rapidly expanding field of additive manufacturing. This is centrally rooted in the nature of the processing, leading to complex microstructural features. Experimentally-guided modeling can offer reliable solutions for the safe application of additively manufactured materials. In this work, we combine a set of systematic experiments and modeling to address creep anisotropy and its correlation with microstructural characteristics in laser-based powder bed fusion (PBF-LB/M) additively manufactured Inconel-738LC (IN738LC). Three sample orientations (with the tensile axis parallel, perpendicular, and 45° tilted, relative to the building direction) are crept at 850 °C, accompanied by electron backscatter secondary diffraction (EBSD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM) investigations. A crystal plasticity (CP) model for Ni-base superalloys, capable of modeling different types of slip systems, is developed and combined with various polycrystalline representative volume elements (RVEs) built on the experimental measurements. Besides our experiments, we verify our modeling framework on electron beam powder bed fusion (PBF-EB/M) additively manufactured Inconel-738LC. The results of our simulations show that while the crystallographic texture alone cannot explain the observed creep anisotropy, the superlattice extrinsic stacking faults (SESF) and related microtwinning slip systems play major roles as active deformation mechanisms. We confirm this using TEM investigations, revealing evidence of SESFs in crept specimens. We also show that the elongated grain morphology can result in higher creep rates, especially in the specimens with a tilted tensile axis.
Results of an extended TMF test program on grade P92 steel in the temperature range of 620 °C - 300 °C, comprising in-phase (IP) and out-of-phase (OP) tests, partly performed with symmetric dwells at Tmax/Tmin, are presented. In contrast to previous studies, the low-strain regime is also illuminated, which approaches flexible operation in a power plant with start/stop cycles. At all strain amplitudes, the material performance is characterized by continuous cyclic softening, which is retarded in tests at lower strains but reaches similar magnitudes in the course of testing. In the investigated temperature range, the phase angle does not affect fatigue life in continuous experiments, whereas the IP condition is more detrimental in tests with dwells. Fractographic analyses indicate creep-dominated and fatigue-dominated damage for IP and OP, respectively. Analyses of the (micro)hardness distribution in the tested specimens suggest an enhanced microstructural softening in tests with dwell times for the low- but not for the high-strain regime. To rationalize the obtained fatigue data, the fracture-mechanics-based D_TMF concept, which was developed for TMF life assessment of ductile alloys, was applied. It is found that the D_TMF parameter correlates well with the measured fatigue lives, suggesting that subcritical growth of cracks (with sizes from a few microns to a few millimeters) governs failure in the investigated range of strain amplitudes.
Schnelle Lastwechsel führen v.a. in dickwandigen Kraftwerksbauteilen zu starken thermischen und mechanischen Beanspruchungen, da sich hohe Temperaturgradienten über der Wand des Bauteils einstellen. Es ergeben sich komplexe Lastkollektive aus zeitlich veränderlichen Spannungen/Dehnungen und Temperaturen, die formal einer Kombination aus Kriechbeanspruchung, Kriechermüdung und thermomechanischer Ermüdung (TMF) entsprechen.
Due to their excellent creep resistance and good oxidation resistance, 9–12% Cr ferritic–martensitic stainless steels are widely used as high temperature construction materials in power plants. However, the mutual combination of different loadings (e.g., creep and fatigue), due to a “flexible” operation of power plants, may seriously reduce the lifetimes of the respective components. In the present study, low cycle fatigue (LCF) and relaxation fatigue (RF) tests performed on grade P92 helped to understand the behavior of ferritic–martensitic steels under a combined loading. The softening and lifetime behavior strongly depend on the temperature and total strain range. Especially at small strain amplitudes, the lifetime is seriously reduced when adding a hold time which indicates the importance of considering technically relevant small strains.
Under cyclic thermomechanical loading conditions, various effects such as strain accumulation, creep damage, ageing, fatigue etc. may occur in the material of a gas turbine blade. Depending on the loading conditions, all these effects contribute to reduce the lifetime of the component. Subject of the present work is the development of a lifetime model able to discriminate between the different damage mechanisms, as well as the development of a material model to describe the mentioned effects and thus providing the input data for lifetime prediction.
Material modelling and lifetime prediction of Ni-base gas turbine blades under TMF conditions
(2014)
Under cyclic thermomechanical loading conditions, various damage mechanisms such as strain accumulation, creep cavitation, ageing, fatigue surface cracking etc. may take place in the material of a gas turbine blade. Depending on the loading conditions, all these effects can contribute to reduce the lifetime of the component. Subject of the present work is the development of a material model to describe the mechanical effects mentioned above, as well as the development of a lifetime model able to discriminate the different damage mechanisms.
Crack propagation under low cycle fatigue and thermomechanical fatigue is characterized by high plastic and creep strains that extend over large regions around the crack, so that concepts of linear-elastic fracture mechanics cannot be applied. In these cases, the cyclic crack tip opening displacement 𝛥CTOD is a promising loading parameter to quantify crack growth. In this work, suitable definitions and Finite Element techniques are investigated and compared for an accurate calculation of 𝛥CTOD under cyclic mechanical and/or thermal loading. A viscoplastic temperature dependent material model of Chaboche-type is used along with large strain settings, specified for the austenitic cast iron Ni-resist. Extensive two-dimensional analyses of Single Edge Notch Tension specimens revealed that collapsed special crack tip elements are superior compared with commonly used regular quadrilateral 8-node elements. At the same level of accuracy of 𝛥CTOD, they require an about ten times coarser mesh and show less sensitivity
w.r.t. element size for both stationary and propagating cracks. In order to simulate fatigue crack growth, an efficient, fully automated FE-technique is developed for an incremental crack propagation by successive remeshing, whereby the deformations and internal state variables are mapped from the old mesh onto the new one. Recommendations are made regarding important numerical control parameters like optimal size of crack tip elements, length of crack growth increment in relation to plastic zone size and 𝛥CTOD value.
Die Steigerung der Leistung und des thermodynamischen Wirkungsgrades von Verbrennungsmotoren führt zu erhöhten Anforderungen an die Festigkeit abgasführender Komponenten wie z. Bsp. Abgasturbolader. Als Folge erhöhter thermomechanischer Wechselbeanspruchungen (TMF) im Betrieb kommt es an den mechanisch und/oder thermisch höchst beanspruchten Stellen der Bauteile zur Bildung von Rissen, wodurch die Lebensdauer der Komponenten begrenzt wird. Derzeit werden bei Turboladern heißgehende Bauteile mit detektierten Rissen zumeist prophylaktisch ersetzt, da die weitere Ausbreitung der Risse während des Betriebs nicht vorhergesagt werden kann. Um diese aufwändige und un- ökonomische Praxis zu vermeiden, wurde im vorliegenden Forschungsvorhaben eine rechnerische Bewertungsmethode auf Basis der experimentellen und numerischen Bruchmechanik erarbeitet, mit deren Hilfe bereits in der Auslegungsphase oder während des Betriebs die (restliche) Lebensdauer der abgasführenden Komponenten vorhergesagt werden kann. Damit wird erstmalig die quantitative Vorhersage der Rissentwicklung bei TMF-Beanspruchungsbedingungen unter Berücksichtigung großer zyklischer viskoplastischer Verformungen ermöglicht.
Zentrales Ergebnis des Vorhabens ist eine automatisierte Berechnungsprozedur auf der Basis spezieller Finite-Elemente-Techniken (FEM), womit sowohl der Pfad als auch die Größe eines Risses als Funktion der Anzahl der Lastwechsel in Bauteilen unter TMF-Bedingungen berechnet werden kann. Als geeigneter Beanspruchungsparameter zur Bewertung des Rissfortschritts unter TMF wurde die zyklische Rissöffnungsverschiebung ΔCTOD verwendet. Das Werkstoffverhalten des betrachteten austenitischen Gusseisens Ni-Resist D-5S wurde mit einem validierten viskoplastischen, temperaturabhängigen Materialmodell modelliert, das zur Berücksichtigung große Verzerrungen und Rotationen am Riss erweitert wurde. Für die genaue Berechnung des ΔCTOD bei TMF wurden effiziente FEM-Techniken erarbeitet. Zur Simulation der Rissausbreitung wurde ein automatischer FEM-Algorithmus mit inkrementeller adaptiver Neuvernetzung entwickelt, bei dem die Verformungen und inelastischen Zustandsvariablen jeweils vom alten auf das neue Netz übertragen werden. Dieser Algorithmus wurde im Software-Paket ProCrackPlast implementiert, das in Verbindung mit dem kommerziellen FEM-Code Abaqus zur Lösung dreidimensionaler Rissprobleme zur Verfügung steht. Ziel der umfangreichen experimentellen Arbeiten war es, an isothermen LCF und anisothermen TMF-Versuchen mit gekerbten Flachzugproben (SENT) das Risswachstum im Temperaturbereich von 20 °C bis 700 °C zu ermitteln. Mit Hilfe begleitender 2D FEM Simulationen wurden anhand dieser Datenbasis die Rissfortschrittskurven des Werkstoffs unter Anwendung des ΔCTOD-Konzepts bestimmt und in geeigneter, parametrisierter Form den Nutzern zur Verfügung gestellt. Die Versuche an SENT-Proben wurden mit der entwickelten Software ProCrackPlast als 3D Modell simuliert. Der Vergleich der 2D und 3D Simulationen ergab einen systematischen Unterschied im CTOD und CTOD, der mit Hilfe eines Übertragungsfaktors korrigiert wurde. Der Vergleich der 3D Berechnungen mit den Experimenten zeigte eine zufriedenstellende Übereinstimmung der er- reichten Risslänge mit der Zahl der Lastzyklen im gesamten Temperaturbereich, wobei die numerische Prognose meist auf der konservativen / sicheren Seite lag. Die Übertragbarkeit der Ergebnisse der 2D Parameteridentifikation auf 3D Risskonfigurationen mit Mixed-Mode Beanspruchung ist mit zusätzlichen Versagenshypothesen verbunden, die aufgrund fehlender Versuchsdaten im Vorhaben nicht endgültig geklärt werden konnten. Zur Validierung des Gesamtkonzeptes wurden LCF-Proben mit einem bauteil- typischen Oberflächenriss experimentell und numerisch untersucht. In der Simulation konnte die komplexe Form und Größe der Rissentwicklung zufriedenstellend (richtig) vorhergesagt werden. Die Leis- tungsfähigkeit der erarbeiteten rechnerische Bewertungsmethode wurde an weiteren TMF-Beispielen vorgestellt und diskutiert. Die Software ProCrackPlast und die viskoplastische Materialroutine wurden dem Anwenderkreis des Vorhabens zusammen mit einem Nutzer-Handbuch und Verifikationsbeispielen zur Verfügung gestellt.
Das Ziel des Forschungsvorhabens ist erreicht worden.
The cyclic crack tip opening displacement ΔCTOD is a promising loading Parameter to quantify the crack propagation under thermomechanical fatigue (TMF). In this work, suitable techniques are investigated and compared for an accurate calculation of ΔCTOD under TMF loading using a viscoplastic temperature dependent material model.
It turned out that collapsed special crack tip elements give the best results. An efficient FEM-technique is developed to simulate the incremental crack growth by successive remeshing, whereby the deformations and internal state variables are mapped from the old mesh onto the new one. The developed techniques are demonstrated and discussed for two-dimensional examples like TMF-specimens. Recommendations are made regarding important numerical control parameters like optimal size of crack tip elements, length of crack growth increment in relation to plastic zone size and ΔCTOD value.
The finite element software ProCrackPlast is developed for the automated simulation of fatigue crack growth in arbitrarily loaded three-dimensional components with large scale plastic deformations, in particular under cyclic thermomechanical (TMF) loading.
ProCrackPlast is developed by extending the software Procrack, created at TU Freiberg for linear-elastic crack growth simulations. The pre-processing, FEM analysis, and the post-processing in ProCrackPlast are done by the commercial software ABAQUS. ProCrackPlast resorts to a crack growth procedure which adaptively updates the crack in finite increments based on the fracture-mechanical parameter, cyclic crack tip opening displacement ΔCTOD . Features of this software along with two application examples of fatigue crack growth in a typical cast steel, Ni-Resist, are presented in this paper to show its capability and performance.
Single-crystal components made of nickel base superalloys contain pores after casting and homogenization heat treatment. Hot isostatic pressing (HIP), which is carried above the γ' -solvus temperature of the alloy, is industrially applied to reduce porosity. A modeling of HIP based on continuously distributed dislocations is developed in a 2D setting. Glide and climb of straight-edge dislocations, as well as vacancy diffusion, are the deformation mechanisms taken into account.
Thereby, dislocation glide is controlled by dragging a cloud of large atoms, and climb is controlled by vacancy diffusion. Relying on previous investigations of the creep behavior at HIP temperatures, it is assumed that new dislocations are nucleated at low-angle boundaries (LAB) and move through subgrains until they either reach the opposite LABs or react with other dislocations and annihilate.
Vacancies are created at the pore surface and diffuse through the alloy until they are either consumed by climbing dislocations or disappear at the LABs. The field equations are solved by finite elements. It is shown that pore shrinking is mostly controlled by vacancy diffusion as the shear stresses at the LABs are too low to
nucleate a sufficient amount of dislocations.
Constitutive modelling of creep degradation due to rafting in single-crystalline Ni-base superalloys
(2009)
A constitutive model for the mechanical behaviour of single-crystalline superalloys at high temperatures has been developed. The model relies on the slip system theory and is able to predict rafting and its influence on plastic flow. The kinetics of rafting are assumed to be driven by the reduction of the internal stresses represented by the macroscopic back-stress. The rafting effect is incorporated in the model through the dependence of the Orowan stress on the channel width. The model has been validated for the alloy CMSX-4 at 950 °C. The rafting part of the model has been calibrated by measurements of the channel widths after several levels of creep strains and for several loads.
Experimental and analytical investigation of the TMF-HCF lifetime behavior of two cast iron alloys
(2017)
The combined loading Thermomechanical Fatigue (TMF) with High Cycle Fatigue (HCF) has been experimentally investigated for two cast iron alloys. Both alloys contain globular graphite nodules but the first one has a ferritic structure while the second one has an austenitic crystal structure. In particular, the influences of the HCF frequency, of the HCF loading amplitude and of the location of the superposed HCF cycles have been investigated. It was observed that the HCF frequency has a limited impact on the fatigue life. On the other side, the HCF-strain amplitude has a highly non-linear influence on the fatigue life. The experimental results can be understood in terms of a fracture mechanics based damage mechanism: Cracks quickly initiate due to the TMF loading and the growth of the cracks up to a few mm controls the fatigue life. If HCF-loading cycles are superposed, cyclic crack propagation dramatically accelerates after a threshold has been reached. This threshold is regarded as controlling the fatigue life reduction. The previous ideas have been expressed in a model that can be very simply applied to estimate the fatigue life reduction ratio due to the superposed HCF cycles. It only contains two adjustable parameters and can be combined with any TMF life assessment model.
Modeling the lifetime reduction due to the superposition of TMF and HCF loadings in cast iron alloys
(2016)
The superposition of small amplitude, high frequency loading cycles (HCF) to slow, large amplitude loading cycles (TMF) can significantly reduce the fatigue life. In this work, the combined TMF+HCF loading has been experimentally investigated for a cast iron alloy. In particular, the influence of the HCF frequency of the HCF amplitude and of the location of the superposed HCF cycles has been assessed. It was observed that the HCF frequency has a limited impact on the TMF fatigue life. On the other side, the HCF-strain amplitude has a highly non-linear influence on the TMF fatigue life. A simple estimate for the fatigue life reduction due to the superposed HCF cycles has been derived from fracture mechanics considerations. It is assumed that the number of propagation cycles up to failure can be neglected after a threshold for the HCF loading has been reached. The model contains only two adjustable parameters and can be combined with any TMF life prediction model. The model predictions are compared with the test results for a large range of TMF+HCF loading conditions.
Die Analyse der Lebensdauer von Bauteilen unter thermomechanischer Ermüdung (TMF) erfordert ein geeignetes Stoffgesetz, welches in der Lage ist, zyklische Plastizität die Abhängigkeit der Spannungsantwort nach der Dehnrate, Kriechen und Spannungsrelaxation temperaturabhängig zu beschreiben und ein Lebensdauermodell, welches in Abhängigkeit von der örtlich aufgelösten Spannungs- und Verformungsgeschichten eine Schätzung der Anzahl der Zyklen bis zum Anriss liefern kann.
Interrupted LCF-tests at 850 deg C for Inconel 738LC have been carried out and the specimens have been intensively examined by REM to quantify the evolution of fatigue damage. Surface crack nucleation at oxidatized grain boundaries and coalescence of neighboring flaws occurred during the whole experiment. An anomalous fast single crack growth is observed just after nucleation, followed by a relative stagnation of the propagation in absence of coalescence. A statistical model is proposed that describes these pheonmena. It leads to an integro-differential equation for the crack density f(c,n) after n cycles, similar to the Bolzmann equation which describes the collision of molecules in a dilute gas.
Mit Hilfe des HIP-Verfahrens („Hot Isostatic Pressing“) werden Poren in der einkristallinen Nickel-Basis Superlegierung CMSX-4 kontinuierlich geschrumpft und dadurch die nach der Erstarrung und der Wärmebehandlung vorhandene Porosität stark reduziert. In diesem Beitrag werden experimentelle und numerische Untersuchungen zu den Mechanismen der Porenschrumpfung zusammengefasst. Es zeigt sich, dass das Verformungsverhalten während Kriechversuchen bei der HIP-Temperatur durch Versetzungsgleitung auf oktaedrischen Ebenen dominiert wird.
Dagegen zeigen Messungen der Porositätsabnahme und Simulationen des Porenschließens, dass die Kinetik der Porenschrumpfung durch das Phänomen der Leerstellendiffusion zwischen Poren und Kleinwinkelkorngrenzen („Low Angle Boundary“, LAB) bestimmt wird. Im Gegensatz führt die klassische Kristallviskoplastizität zu einer systematischen Überschätzung dieser Kinetik. Der scheinbare Widerspruch lässt sich auflösen, wenn man bedenkt, dass auf der Skala der Poren Versetzungsquellen nicht gleichmäßig verteilt sind, wie in der konventionellen Kristallplastizität implizit angenommen wird. Stattdessen wird in einem weiterführenden Modell davon ausgegangen, das Kleinwinkelkorngrenzen (LABs) als Versetzungsquellen fungieren, während die Scherspannungen sehr stark in der Nähe der Poren lokalisiert sind, was die Emission von Versetzungen deutlich reduziert.
Rafting during high temperature deformation in a single crystal superalloy: experiments and modeling
(2012)
Experimental characterization and mechanical modeling of creep induced rafting in superalloys
(2012)
A constitutive model has been developed for the high temperature mechanical behavior of single crystal superalloys, including rafting and its consequences. The flow stress depends on the γ channel width via the Orowan stress. An evolution equation for channel widening during high temperature straining has been derived and calibrated with measurements. Therein, rafting is assumed to be driven by the relaxation of internal stresses. The model is able to represent the mechanical softening at high stresses consecutive to rafting. The model has been applied to simulate rafting during uniaxial creep in several crystal orientations, in notched specimens as well as in cyclically loaded specimens.
A constitutive model for the mechanical behavior at high temperatures of superalloys with a high volume fraction of the ? ? phase is derived from an analysis of the main deformation mechanisms. The model assumes periodically distributed cubic ? ? particles and an homogeneous slip distribution perpendicular to the slip planes inside the matrix channels and the particles. It accounts for octahedral and cubic slip in the ? channels, recovery by climb of loops around the precipitates until complete annihilation, shear of both matrix and precipitates by complete matrix dislocations and partial slip reversal during unloading. The back-stresses of the constitutive law are identified with the long-range internal stresses in the microstructure which are explicitly calculated by Fourier series for a simplified distribution of the plastic strains in the microstructure. In particular the three types of channels are distinguished. The internal variables of the model are the plastic strains produced by each mechanism, the number of mobile loops in the ? channels and the scalar dislocation density in the ?/? ? interfaces for each slip system.
On the Connection between Continuum Crystal Plasticity and the Mechanics of Discrete Dislocations
(2003)
Experimentshow that the strength of Ni-base superalloystrongly depends on the actual morphology of the microstructure. This makes a multiphase micro-mechanical modelling indispensable for a reliable safety analysis. Unfortunately, the classical crystal plasticity theory leads to erroneous predictions, when applied to the scale of the microstructure. This paper suggests that this failure is related to a breakdown of the meaning of plastic strain at the scale of the size of dislocation loops. We propose a global modelling of the compound that overcomes the deficiencies of local crystal plasticity at this description level.
The calculation of the glide force on a dislocation in finite elasticity requires a suitable description of the variation of the deformation due to dislocation motion. This is achieved in this paper by extending the linear Somigliana-type dislocation model to finite strains. The core is modeled by a strip of finite width where the displacement jump continuously decreases with the distance to the dislocation tip. In the case of finite transformations, this distance can be defined in the deformed or in the undeformed state. By defining it in the undeformed natural state of the crystal, we show that the work dissipated by friction in the core region only depends on the dislocation motion. Using the principle of virtual work, the equation of the dislocation motion and several alternative expressions for the glide force are derived. The obtained force may be interpreted as a generalization of Eshelby's configurational forces for a noncoherent singular surface. In the linear case, the glide force of Peach and Koehler as well as the well-known expression of the self-force due to De Wit and Koehler are retrieved.
A stochastic model for fatigue short crack growth is presented. It takes into account the interaction between the crack-tip plastic zone and grain boundaries. The process is Markovian. It is completely described by the crack length and the size of the plastic zone. The integro-differential equation giving the evolution of the transition probability distribution is derived.
Das zyklische mechanische Verhalten der einkristallinen Superlegierungen und deine Modellierung
(2002)
Modeling the reinforcement of alloys by hard precipitates: The example of Nibase of superalloy
(2002)
Numerical simulation of fatigue crack growth in a single crystal superalloy at high temperature
(2013)
The elastic constants are the most basic mechanical properties of a material and are needed for any structural analysis of a component. For example, they have a major influence on the eigenfrequencies of vibrating parts. Single crystals of Ni-base superalloys are strongly anisotropic, which means that the observed properties are orientation dependent. Tensor algebra is then required to mathematically formulate the elastic properties and their relations to the crystal orientation. Hence, this chapter first summarizes some basic definitions and calculation rules for Rotation matrices, including the definition of the Euler angles, which are most commonly used to define the relative orientations of the crystal and the component. Parts of this chapter closely follow the lines of the excellent exposition of the topic by Olschewski.
The large number of TEM investigations and the regular microstructure
of single-crystal nickel-base superalloys has boosted the development of a number of physically motivated constitutive laws. In contrast to the more phenomenological models discussed in the next chapter, these models use dislocation densities as internal variables. Obvious advantages are that the computed densities can be compared to TEM observations and the Deformation mechanisms can be easier translated into mathematical equations.