The application of composite pressure vessels is of great interest due to tremendous weight saving. Nevertheless, ageing of CFRP (carbon fiber reinforced plastic) composites pressure vessels underlies complex interactions between metallic liner and composite and is not fully understood yet. One main challenge is the application of appropriate testing methods for detecting the influences of pressure cycles and creep behavior on the material. This contribution presents results achieved by using conventional eddy current testing (ET) and high frequency ET. Here, we could show that also conventional ET with low frequencies are useable to investigate pressure vessels of different material combinations like aluminum-CFRP and synthetics-CFRP.
Composite pressure vessels for transporting dangerous goods and for hydrogen and natural gas vehicles consist of a load-bearing composite and a gas-tight, metallic or polymeric barrier layer (liner). To investigate the aging behavior of such composite pressure vessels, BAM carried out the interdisciplinary project COD-AGE. The aim of the project was the development of methods and models for the description and determination of the aging behavior of carbon fiber composites using the example of pressure vessels in order to better predict aging and safe working life. One focus of this project was the provision of suitable NDT methods. These included both test-related tests and the possible development of test equipment for later practical use.
In the lecture, test results of the age-related eddy current test on composite pressure vessels are presented.
In aging tests, pressure vessels made of an approximately 4 mm thick aluminum liner and approx. 8 mm thick CFRP layer were examined. Typical application of such pressure vessels are respiratory protective devices of the fire department. The pressure vessels were tested using conventional eddy current technology from the outer and inner side as well as with high-frequency eddy current technology. Both damage to the metallic liner and structures of the CFRP could be detected. A particular mechanical challenge was the inspection of the inside of the liners, since a cylindrical surface with an inside diameter of 150 mm has to be tested with an access of only 15 mm diameter.
Non-destructive testing for surface crack detection and head check depth quantification at the gauge corner of railway tracks can be achieved using eddy current methods. With the extension of the tested zone to the running surface, rail defect signal types other than head checks can be measured. Due to their mostly irregular shape, a quantitation based on a calibration against regular test cracks of varying depth may not be linear. Estimates of the expected influence of more complex crack patterns may be obtained by a finite element simulation of sufficiently simple limiting cases, like two displaced or intersecting cracks or a simply branched or flexed crack. As a first step, a 3D finite element model of the HC10 eddy current probe distributed by Prüftechnik Linke und Rühe (PLR), Germany was built and verified against measured results from an (easily fabricated) reference block with isolated long cracks.