Spalling of concrete due to fire exposure can lead to severe damage of building components. It is a much discussed subject in structural engineering and not yet completely understood. Generally, it is assumed that thermohydraulic and thermomechanical processes induce tensile stresses in the concrete. Furthermore, the tensile strength of concrete is reduced due to increasing temperatures. The combination of an increasing tensile stress and a decreasing tensile strength result in the occurrence of explosive spalling. The spalling behaviour of concrete is influenced by many parameters, for instance the water cement ratio, porosity, permeability of concrete as well, the presence of steel reinforcement and polypropylene fibres, also the size and geometry of the fire exposed area. Within the current research project at Bundesanstalt für Materialforschung und prüfung (BAM), the susceptibility to spalling of six different concrete mixtures is analysed to quantify the size effect using small scale, intermediate scale and full scale tests. A special fire test setup was built to test specimens simultaneously to enable a better comparability. All specimens are tested without additional mechanical load and unrestraint to prevent external induced cracking at the fire exposed site. Thermocouples are used to measure in situ the temperature distribution as an indication on the thermal degradation of the concrete during the fire tests. Afterwards the maximum spalling depth and the damaged area of the specimen are illustrated by a photogrammetric measurement system. The contribution to the spalling workshop presents the results of four concrete mixtures tested in intermediate-scale and full-scale fire tests. The comparisons are based on the concrete temperature as well as the obtained photogrammetric data. The results show that the spalling depth and the spalling area are significantly affected by the size of the fire exposed area.
Construction methods, environmental stressors, and aging factors are the main causes for defects of reinforced concrete in nuclear power plants (NPP). These defects are typically occurred as corrosion of reinforcement steel, delamination, cracks, malfunction of post-tensioning or steel composite systems etc. Some of the challenges for assessing the performance of these structures by nondestructive testing methods (NDT) are that the assessment could be performed only during the annual overhauls when testing is time-limited and uncertainty of the accuracy and reliability of the available NDT testing devices combined with the lack of the international uniformity of the methods used for NDT tests. To overcome these challenges, a mock-up wall representing a section of the concrete containment of the NPP was built. The mock-up wall included simulated defects, which mimic the most common types of defects in NPP concrete structures such as dimensional errors, honeycombing, delamination, defects adjacent to the steel liner and voids in grouted tendon ducts for the post-tensioned structures. This paper introduces the design and construction of the wall including the concrete properties, reinforcement, tendon ducts and the types of the simulated defects. The paper also introduces the NDT methods and techniques that are suitable for assessing the condition of the mock-up wall under the real environmental conditions. These techniques include mechanical methods as rebound hammer, ultrasonic and electromagnetic methods. This mock-up wall will enable to investigate reliably available NDT methods and experts’ skills providing also an important and very much need educational platform for future NDE experts.
The propagation of ultrasonic waves in concrete is affected by its micro- and macro-structure, geometry and properties as well as external influences as stress, temperature or moisture. In addition, age and degradation have a strong influence. Therefore, Ultrasound has been used to monitor concrete samples and structures since decades. However, early applications using conventional techniques as time-of flight or changes in amplitudes have been limited to detect changes in a late stage close to serviceability or ultimate load states.
Around 2000, several new, more sensitive techniques adopted from geophysics or other field of material sciences have been introduced to research in ultrasonic monitoring of concrete. The most discussed methodologies are coda wave interferometry, a technique which allows to detect very subtle changes from repeated ultrasonic measurements. Nonlinear acoustic techniques help to identify e. g. cracks even in an inhomogeneous background. Both techniques can be combined.
This paper reviews methods and results achieved so far on the laboratory scale and with full scale models the directions for future research and application is given as well.
Sustainability means meeting the needs of today without compromising the needs of the next generations. How can we meet the needs of the next generations, if we do not even know what these needs are? If we do not listen to the next generation and learn from them? Do we even meet the needs of today for everyone on earth?
In earthquake-prone regions such as the Pacific Northwest, damage assessment tools are needed to enable safety evaluations to support recovery. Currently, damage assessment is performed primarily by visual inspection and is often impossible for structural members that are inaccessible, such as deep foundations or interior members hidden by cladding. This study explores the possibility of using embedded ultrasonic transducers to monitor reinforced concrete members for damage progression under earthquake loading. A novel methodology is proposed where changes in the member condition due to an increase in the earthquake-type loading of a full-scale column-foundation specimen are correlated with changes in the recorded ultrasonic waveforms. The discussed preliminary analysis of the ultrasonic signals is based on wave propagation velocity, changes in the coda wave portion, and maximum amplitude of the signals. Three embedded transducers were used to continuously monitor the laboratory specimen during destructive testing. This paper provides an overview of the proposed methodology, outlines the laboratory experiment, and discusses some preliminary observations.
Ultrasonic transmission measurements are used to monitor concrete elements mostly on a laboratory scale since decades. Recently, coda wave interferometry, a technique adapted from seismology, has been introduced to civil engineering experiments. It can be used to reveal subtle changes in concrete samples and even large construction elements without having a transducer directly at the location where the change is taking place. The methodology works best with embedded transducers to avoid coupling issues or excessive environmental influence. These transducers can be used for newly built and existing structures. Recently, large concrete beams have been equipped with a network of transducers and loaded until failure. Using code wave interferometry, it was possible to visualize stress fields and damaged areas. This paper gives an overview of the state of the art, recent results achieved at BAM and a task list for further results and development.
The LAUS: First Applications of a New System for Ultrasonic Imaging of Very Concrete Structures
(2019)
The LAUS (Large Aperture Ultrasonic System) has been developed to image very thick concrete structures, which are not accessible for commercial systems. The device and the corresponding software is the result of joint Research of BAM, an ultrasonic instrument manufacturer and University of Kassel, Germany. It consists of 12 separate Arrays of 32 point-contact shear wave transducers each, which can be deployed in flexible configurations. Each array is combined with battery and transmitter, receiver and wireless communication electronics.
Three case histories are presented. First the system was deployed on a 5-m thick heavily reinforced foundation slab.
The reflection of the slab’s bottom was imaged clearly. In addition, a multiple reflection was registered, thus giving hope that even thicker elements might be imaged by the instrument. Second, the LAUS was used to investigate a massive bridge girder where a heavy rainstorm during concreting had led to imperfections that were visible after removing the formwork was removed. The LAUS could image tendon ducts in 1.8m depth and the backwall closely behind them. Some limited areas showed blurred reflections and were checked by drill holes; these areas were affected by diffuse damage which could be repaired by injections. Third, a large retaining wall was checked for thickness.
Meanwhile, the LAUS has been used in underground waste deposits (nuclear and other) for quality assurance of sealing plugs. A confirmed penetration depth of about 7 m has been reached.
Fatigue is one of the most prevalent issues, which directly influences the service life expectancy of concrete structures. Fatigue has been investigated for years for steel structures. However, recent findings suggest that concrete structures may also be significantly subjected to fatigue phenomena that could lead to premature failure of certain structural elements. To date, fatigue of reinforced concrete has been given little focus. Knowledge on the influence factors and durability/capacity effects on this material should be improved. Current technological means to measure fatigue in civil structures like bridges and wind turbines (both onshore and offshore) are outdated, imprecise and inappropriate.
Meanwhile, this topic has got much more attention as time-variant loading on concrete structures plays an increasing role, e.g. in bridges with increasing traffic and heavier trucks, and for wind turbines for renewable energy production, e.g. for offshore wind turbine support structures affected by wind and waves.
The European Innovative Training Networks (ITN) Marie Skłodowska-Curie Actions project INFRASTAR (Innovation and Networking for Fatigue and Reliability Analysis of Structures - Training for Assessment of Risk) provides research training for 12 PhD students. The project aims to improve knowledge for optimizing the design of new structures as well as for more realistic verification of structural safety and more accurate prediction of the remaining fatigue lifetime of existing concrete structures.
First, the INFRASTAR research framework is detailed. Then it will be exemplified through the presentation of the major results of the four PhD students involved in the work package dealing with auscultation and monitoring. This includes the development and improvement of Fiber Optics (FO) and Coda Wave Interferometry (CWI) for crack sizing and imagery, new sensor technologies and integration, information management, monitoring strategy for fatigue damage investigation and lifetime prediction.