PET-P-DOPO is a phosphorus-containing polyester prepared from the glycol ether of the hydroquinone derivative of 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO) and dimethyl terephthalate. PET-P-DOPO and a blend of PBT with PET-PDOPO were investigated with respect to pyrolysis and fire behavior. PET-P-DOPO achieves a V-0 rating in the UL 94 test and exhibits a high LOI of 39.3%. The outstanding flame-retardant properties of PET-P-DOPO are the result of three different mechanisms (flame inhibition, charring and a protection effect of the intumescent char) that are active in PET-P-DOPO. The fire load and the peak of heat release rate (pHRR) are reduced to 34% and 17%, respectively. The char exhibits an intumescent multicellular structure enabling it to act as an efficient protection layer. As PET-P-DOPO is immiscible with PBT, the blend shows a lower breaking elongation than pure PBT. Compared to pure PET-P-DOPO, the flame retardancy of the blend is decreased according to the fraction of PET-P-DOPO used. Nevertheless, the flame-retardancy of PET-P-DOPO in the blend was good enough to compete with PBT flame-retarded by AlPi-Et (aluminum diethylphosphinate) that was used as a Benchmark.
New low-melting organic–inorganic glassy polymers containing phosphorus and silicon are synthesized by the reaction between phenylphosphonic acid and methyltrichlorosilane or methyltriethoxysilane. They possess both low-softening points and high onset decomposition temperatures, which are favorable for preparing flame retardant composites. Although the glass by itself is sensitive to water, the composites are not significantly affected in that way. For glass/clay/epoxy composites glass transition temperature (Tg) as well as storage modulus increase with the glass amount. The glasses improve flame retardancy significantly due to flame inhibition and the formation of fire residue working as protection layer during burning. The total heat evolved is reduced by 23–28% for using 5–15 wt.% glass and the maximum HRR even by 5848%. The latter effect decreases with increasing glass amount due to an adulterate residue deformation. The combination of glass and clay is proposed as a possible route to enhance flame retardancy.
Due to optimised processing of epoxy based composite materials containing a low-melting organic–inorganic glass together with an organo clay, the size of the glass particles could be successfully reduced. Thus truly nano-dispersed composites were obtained, with glass particles in the range of 10 nm to 200 nm. The small particle size allowed efficient interaction of glass particles and organo clay layers. The flame retardancy as well as the thermo-mechanical properties were tested, and the results showed that the low-melting glass led to a remarkable reduction of peak heat release rate by forming an enhanced barrier layer. Nevertheless no further improvement could be achieved by lowering the particle size to the nanometre region. For good flame retardancy a microdispersion of the low-melting glass was already sufficient.
The known flame-retardant synergism between phosphorus-based additives and metal oxides, already used for petroleum-based plastics, has been extended to bio-based materials. The pyrolysis and the flame-retardancy properties of aluminium phosphinate (AlPi) in combination with nanometric iron oxide and antimony oxide on a poly(3-hydroxy-butyrate-co-3-hydroxyvalerate)/poly(butylene adipate-co-terephthalate) (PHBV/PBAT) blend were investigated. Better fire retardancy, ascribed to increases in intermediate char, favoured improvements in the UL 94 classification. Both the phosphorus and the nanofiller components participate simultaneously in the flame-retardancy mechanism: the first acting as flame inhibition in the gas phase, and the second promoting cross-linking in the solid phase. Redox reactions between iron oxide and the phosphinate additive were confirmed by XRD analysis and provided further evidence of the activity of metal compounds.
The fire behaviour of composites clearly differs in comparison to polymers. Even though fibres and inorganic particles may be inert with respect to pyrolysis, they are clearly not with respect to fire behaviour. They change heat absorption and transfer within the Condensed phase, the melt flow/dripping behaviour of pyrolysing melts, the amount and properties of the fire residue and so on. Flame retardancy concepts tailored to composites are needed. Furthermore tasks that are specific for composites such as the structural integrity in fire get into the focus. Thus understanding of fire behaviour and flame retardancy mechanisms in composites is a key for target-oriented future development. The field is illuminated by Spotlights on different length scales. The examples are taken from different projects carried out in the group of the authors in the recent years. Flame retardancy mechanisms in nanocomposites are discussed, advanced halogen-free flame retardants for carbon and glass fibre composites presented as well as an approach to mechanical intermediate scale testing of carbon fibre composites under fire.
Novel DOPO-based flame retardants in high-performance carbon fibre epoxy composites for aviation
(2011)
Two novel, halogen-free, phosphorus-based oligomeric flame retardants are investigated in the commercial epoxy resin RTM6 and ~70 wt.% carbon fibre RTM6 composites (RTM6-CF) with respect to pyrolysis and fire behaviour. The flame retardants are based on 9,10-dihydro-9-oxy-10-phosphaphenanthrene-10-oxide (DOPO) units linked to the star-shaped aliphatic ground body tetra-[(acryloyloxy)ethyl] pentarythrit (DOPP), or heterocyclic tris-[(acryloyloxy)ethyl] isocyanurate (DOPI), respectively. The glass transition temperature is reduced by adding DOPP and DOPI, but the mechanical properties of the composites (e.g. interlaminar shear strength (ILSS) and Gc in mode I and II) remain unchanged. Decomposition models are proposed based on mass loss, evolved gas analysis (TGFTIR) and condensed product analysis (hot stage cell within FTIR). The fire behaviour is investigated comprehensively (UL 94, limiting oxygen index (LOI) and cone calorimeter). Both flame retardants act in the gas phase through flame inhibition and in the condensed phase through charring. The UL 94 of RTM6 is improved from HB to V-1 and V-0; the LOI from 25% to 3438%. Peak heat release rate (PHRR) and total heat evolved (THE) are lowered by 31-49% and 4044%, respectively. Adding CF increases the residue, reduces the THE, but suppresses the charring due to RTM6 and flame retardants. Thus the THE of RTM6-CF is reduced by about 25% when DOPI and DOPP are added. However, UL 94: V-0 and LOI of 45% and 48% are achieved with ~0.6 wt.% phosphorus.
The pyrolysis and fire behavior of halogen-free flame-retarded DGEBA/DMC, RTM6 and their corresponding 60 vol.-% carbon fibers (CF) composites were investigated. A novel phosphorous compound (DOPI) was used. Its action is dependent on the epoxy matrix. DGEBA/DMC and DOPI decompose independently of each other. Only flame inhibition occurs in the gas phase. RTM6 shows flame inhibition and a condensed phase interaction increasing charring. Both mechanisms decrease with increasing irradiance, whereas in RTM6-CF charring is suppressed at low ones. RTM6+DOPI shows a higher LOI (34.2%) than DGEBA/DMC+DOPI and a V-0 classification in UL 94. Adding CF only enhances the LOI, DOPI+CF leads to a superposition in LOI for DGEBA/DMC-CF+DOPI (31.8%, V-0) and a synergism for RTM6-CF+DOPI (47.7%, V-0).
The motivation of this study was to pursue effective eco-friendly and economical flame retarded polymer materials. With wide-ranging advantages such as improved fire and physical properties, halogen-free and relatively low cost, layered silicate / epoxy nanocomposite (EP_LS) was targeted for high efficiency of flame retardancy. One main goal of this study was to increase the understanding of the flame retardancy phenomenon in EP_LS by assessing the shielding effect of the protection layer experimentally and quantitatively. Another main goal of this study was to optimize the flame retardancy by the shielding effect in EP_LS.