This paper considers an indirect measurement approach to reconstruct a defect in a two-dimensional waveguide model for a non-destructive ultrasonic inspection via derivative-based optimization. The propagation of the mechanical waves is simulated by the scaled boundary finite element method that builds on a semi-analytical approach. The simulated data are then fitted to given data associated with the reflected waves from a defect which is to be reconstructed. For this purpose, we apply an iteratively regularized Gauss-Newton method in combination with algorithmic differentiation to provide the required derivative information accurately and efficiently. We present numerical results for three kinds of defects, namely, a crack, delamination, and corrosion. The objective function and the properties of the reconstruction method are investigated. The examples show that the parameterization of the defect can be reconstructed efficiently as well as robustly in the presence of noise.
LIBS is a complementary method to XRF and can detect all elements without the need for vacuum conditions. Automated systems are already commercially available capable of scanning surfaces with a resolution of up to 0.1 mm within a few minutes. In addition to possible applications in R&D, LIBS is also used for practical applications in building materials laboratories and even on-site.
In view of ageing infrastructure facilities, a reliable assessment of the condition of concrete structures is of increasing interest. For concrete structures, the ingress of potential harmful ions is affecting the serviceability and eventually structural performance. Pitting corrosion induced by penetrating chlorides is the dominant deterioration mechanism. Condition assessment based on frequently performed chloride profiling can be useful to identify the extent and evolution of chloride ingress. This could prove to be more economical than extensive repairs, especially for important infrastructure facilities.
Currently the most common procedure for determining the chloride content is wet chemical analysis with standard resolution of 10 mm. The heterogeneity is not considered. LIBS is an economical alternative for determining the chloride content at depth intervals of 1 mm or less. It provides 2D distributions of multiple elements and can locate spots with higher concentrations. The results are directly correlated to the mass of binder and can also be performed on-site with a mobile LIBS-System.
The application of a LIBS-system is presented. Calibration is required for quantitative analysis. Concrete cores were drilled, sliced and analyzed to determine the 2D-distribution of harmful elements. By comparing the chloride ingress and the carbonation, the interaction of both processes can be visualized in a measurement that takes less than 10 minutes for a 50 mm x 100 mm drill core.
A leaflet on the use of LIBS for the chloride ingress assessment has been completed.
Galvanic corrosion protection by embedded zinc anodes is an accepted technique for the corrosion protection of reinforcing steel in concrete. Galvanic currents flow between the zinc anode and the steel reinforcement due to the potential difference that is in the range of a few hundred mV.
The ion distribution was studied on two steel reinforced concrete specimens admixed with 3 wt.% chloride/wt. cement and galvanically protected by a surface applied EZ-anode. On both specimens, a zinc anode was embedded and glued to the concrete surface by a geo-polymer-based chloride-free binder. At one specimen, the EZ-anode was operated for 2,5 years, the EZ-anode at the other specimen was not electrically connected to the reinforcement, this specimen serves as a reference. Both specimens have been stored under identical conditions. The ion distribution between the anode (EZ-ANODE) and cathode (steel reinforcement) was studied by laser-induced breakdown spectroscopy (LIBS) after 7 months, 12 months, and 2,5 years. Results of the LIBS studies on the specimen with activated EZ-anode after 7 months, 12 months, and 2,5 years and of the reference specimen after 2,5 years are reported. Results show that diffusion of ions contributes to the changes in the ion distribution but migration, especially of chlorides towards the EZ-anode is significant despite the weak electric field – several hundred millivolts - generated by the galvanic current. Results show that chloride ions accumulate near the zinc-anode as in water-insoluble zinc-hydroxy chlorides - Simonkollite.
Galvanic corrosion protection by embedded zinc anodes is an accepted technique for the corrosion protection of reinforcing steel in concrete. Galvanic currents flow between the zinc anode and the steel reinforcement due to the potential difference that is in the range of a few hundred mV. The ion distribution was studied on two steel reinforced concrete specimens admixed with 3 wt.% chloride/wt. cement and galvanically protected by a surface applied EZ-anode. On both specimens, a zinc anode was embedded and glued to the concrete surface by a geo-polymer-based chloride-free binder. At one specimen, the EZ-anode was operated for 2,5 years, the EZ-anode at the other specimen was not electrically connected to the reinforcement, this specimen serves as a reference. Both specimens have been stored under identical conditions. The ion distribution between the anode (EZ-anode) and cathode (steel reinforcement) was studied by laser-induced breakdown spectroscopy (LIBS) after 7 months, 12 months, and 2,5 years. Results of the LIBS studies on the specimen with activated EZ-anode after 7 months, 12 months, and 2,5 years and of the reference specimen after 2,5 years are reported. Results show that diffusion of ions contributes to the changes in the ion distribution but migration, especially of chlorides towards the EZ-anode is significant despite the weak electric field – several hundred millivolts - generated by the galvanic current. Results show that chloride ions accumulate near the zinc-anode as in water-insoluble zinc-hydroxy chlorides - Simonkolleit.
Corrosion of concrete reinforcement is one of the major damage mechanisms affecting both the load-bearing capacity and the serviceability of re-inforced concrete structures significantly. When externally discernible damages are observed during visual inspections on the structure, the extent of the damage inside the concrete is often already significant. Corrosion caused by carbonation often leads to severe discoloration of the surface or even large-area spalling of the concrete cover. In contrast, chloride-induced corrosion is usually difficult to observe visually but can cause much more serious damage in less time. The effect occurs locally and can lead to weakening of the cross-section of the reinforce-ment. This, in turn, can cause sudden structural collapses without prior notice.
In the meanwhile, various non-destructive and minimally invasive testing methods are available to evaluate the resistance to penetration of corrosion-pro-moting pollutants and to detect active corrosion. In this paper, a bridge crossing the river Regen is used as a case-study to demonstrate how the information ob-tained applying different testing methods can be combined and evaluated in the context of structural reassessments. Both the results of the permeability testing and the electrical resistance measurement are considered, as well as active corro-sion areas are localized using the half-cell potential mapping combined with the concrete cover measurement with the eddy current method and ground penetrat-ing radar. The results are evaluated using drill cores and in addition laser-induced breakdown spectroscopy was applied to obtain information about possible chlo-ride ion transport into the concrete.