Corrosion of concrete reinforcement is one of the major damage mechanisms affecting both the load-bearing capacity and the serviceability of re-inforced concrete structures significantly. When externally discernible damages are observed during visual inspections on the structure, the extent of the damage inside the concrete is often already significant. Corrosion caused by carbonation often leads to severe discoloration of the surface or even large-area spalling of the concrete cover. In contrast, chloride-induced corrosion is usually difficult to observe visually but can cause much more serious damage in less time. The effect occurs locally and can lead to weakening of the cross-section of the reinforce-ment. This, in turn, can cause sudden structural collapses without prior notice.
In the meanwhile, various non-destructive and minimally invasive testing methods are available to evaluate the resistance to penetration of corrosion-pro-moting pollutants and to detect active corrosion. In this paper, a bridge crossing the river Regen is used as a case-study to demonstrate how the information ob-tained applying different testing methods can be combined and evaluated in the context of structural reassessments. Both the results of the permeability testing and the electrical resistance measurement are considered, as well as active corro-sion areas are localized using the half-cell potential mapping combined with the concrete cover measurement with the eddy current method and ground penetrat-ing radar. The results are evaluated using drill cores and in addition laser-induced breakdown spectroscopy was applied to obtain information about possible chlo-ride ion transport into the concrete.
An important aspect with regard to the service life of zinc based galvanic anodes and the durability of the corrosion protection of steel in concrete is the “galvanic chloride extraction”. Chloride ions move in the electric field generated by the current, flowing between the galvanic anode and the cathodic steel. Migration leads to an accumulation of anions, e.g. chloride ions, at the anode and depletion of chlorides near the steel rebar surface. The ion migration was studied on steel reinforced concrete specimens admixed with 3 wt.% chloride/wt. cement and galvanically protected by a surface applied embedded zinc anode (EZA). The zinc anode was embedded and glued to the concrete surface by a geo-polymer based chloride free binder. The EZA was operated over a period of 1 year and the ion distribution between anode (EZA) and cathode (steel reinforcement) was studied by laser induced breakdown spectroscopy (LIBS) after 5 months, 7 months and 12 months. The results show that chloride ions efficiently migrate in the direction of the zinc-anode and accumulate there. Chloride distribution in the EZA correlates with the distribution of zinc ions generated by the anodic dissolution of the zinc anode in the binder matrix. The microstructure of the binder matrix and its interface to the zinc-anode are studied by REM/EDX – preliminary results will be reported.