The laser-induced breakdown spectroscopy (LIBS) is a fast method to provide multi-elemental analysis of any sample. At the Federal Institute for Materials Research and Testing (BAM) the LIBS technique is applied on building materials to measure ingress profiles of harmful species like chloride and alkalis. The ingress depth and the quantitative amount is important for the evaluation of the potential for damage processes like the alkali-silica reaction or chloride-induced corrosion. Concrete as an example is a highly heterogeneous material with 1/7 cement (major component CaO) and 6/7 aggregates (SiO2) with different grain sizes. Due to a scanning procedure a two dimensional element distribution of a concrete surface can be measured. In order to have an automated Separation method to evaluate heterogeneous materials, different cluster algorithm have been tested. Best results have been achieved with the Expectation-Maximization-Algorithm (EM-Algorithm).
Carbon-based conductive coatings are complex composites, consisting of an organic or inorganic binder and conductive carbon components, for application as anodes in impressed current cathodic protection systems of reinforced concrete structures. The electrochemical properties of three coatings at different humidity and in saturated calcium hydroxide solution were studied by electrochemical methods, such as electrochemical impedance measurement, measuring of open circuit potential over time and galvanostatic polarization.
Carbon-based conductive coatings are complex composites, consisting of an organic or inorganic binder and conductive carbon components, for application as anodes in impressed current cathodic protection systems of reinforced concrete structures. The electrochemical properties of three coatings at different humidity and in saturated calcium hydroxide solution were studied by electrochemical methods, such as electrochemical impedance measurement, measuring of open circuit potential over time and galvanostatic polarization.
Welcome to the 2nd International Conference on Advances in Cement and Concrete Technology in Africa (ACCTA 2016), January 27– 29, 2016, held at White Sands Hotel, Dar es Salaam, Tanzania.
The first ACCTA conference that took place in January 2013 in Johannesburg was a result of an African-European collaborative research project. Due to the success of this conference, it was announced that a triennial international conference is necessary, with the next conference scheduled to take place once again in Johannesburg. Within the organisation of the conference, unfortunately some unforeseeable events arose, which would lead to either a delay of the conference in Johannesburg until 2018 or a change of venue. The great response from the international scientific community supported the option to maintain the originally scheduled date. With the support of the local organisation committee from the University of Dar es Salaam and the contributions from the University of the Witwatersrand and the University of Zagreb the conference was shifted to Dar es Salaam.
Despite the new boundary framework, we are extremely happy that it was possible to arrange an outstanding and excellent scientific programme. Therefore we would like to thank in particular the keynote speakers and all members of the international scientific community, as well as other delegates that supported the conference by their contributions and attendance. This shows us how significantly important the African cement and concrete market is for the entire global community.
Africa can become a spearhead for the future of construction with cement and concrete. The continent exhibits an enormous construction potential and due to the relatively short history of building with these materials, innovations can be adopted and adapted unbiased and without influence of stakeholders, traditions, and complicated networks of regulations. This is a fertile ground for the existing promising generation of engineers and decision makers for re-inventing cement and concrete in the best possible way.
There is no global optimum solution for concrete. The best solution in Africa is not the best solution in Europe or another part of the world, and the best solution in one particular African country is diverging from the best solution in another African country depending upon resources, supply chains, infrastructure, construction needs, traditions, available manpower, skills and technologies. Nevertheless, we can globally support our objectives to build future oriented and sustainable construction solutions by mutually learning from each other. In order to tackle the future challenges and build more sustainably and innovatively with concrete, we need to enhance interdisciplinary and cross-national skills and create networks between experts and decision makers globally.
ACCTA offers this kind of platform, and we are happy to announce that the conference reaches a high impact in the world. Delegates and speakers come from more than 40 countries in the world originating from all continents. Besides the technical content there will be plenary discussions on the most relevant topics of future binder technologies and standards and product safety with outstanding expert panellists.
We want to wish all delegates a successful conference and hope that this book can be a significant contribution for a future oriented and better concrete technology; in Africa and the entire world. Welcome to Dar es Salaam, Tanzania.
The current knowledge about fatigue behavior of concrete is still incomplete. This concerns especially the progress of fatigue which precedes the fatigue failure. Therefore, the process of fatigue itself under cyclic compressive loading was investigated in a systematic and comprehensive way. The aim of this investigation was to obtain a deeper insight and to provide a better understanding of the damage process occurring within the material during fatigue loading. Concrete cylinders were tested with a number of cycles to failure between 106 and 107. To investigate macroscopic and microscopic changes in the material, various methods of non-destructive and destructive testing were used. One main result was, in contrast to other authors, that the investigated changes in macroscopic material behavior could not be explained only by a development of micro-cracks. The results indicated rather, that the related changes in the fatigue behavior are mainly a result of viscous processes in the hardened cement paste, similar to the processes of creep. Based on the experimental results a description of the possible processes was derived which take place in the material structure during fatigue loading and also leads to the observed macroscopic changes in the material behavior. In this context, the results have shown that in case of isotropic material behavior a stiffness reduction related to a scalar value could not capture the damage effect on the stress-strain-relationship caused by fatigue.
The use of starch and its derivatives in concrete as an admixture to modify relevant properties of concrete is on the increase in recent times. It is known to modify the rheology, to affect the hydration kinetics of cement, and influence on initial and final setting time of cement. This paper examines the effect of cassava starch on concrete. shrinkage properties of concrete, with and without starch addition, were studied. Various percentages (0, 0.5, 1.0, 1.5 and 2 %) of starches by weight of cement were added to concrete mixes prepared in the laboratory. Shrinkage tests were conducted for duration of up to one year. The result show that concretes with starch additions exhibit lower shrinkage, which is an indication the addition of starch as admixture in concrete improves the ability of the concrete reduce shrinkage problems.
Investigation of chloride-induced pitting corrosion of steel in concrete with innovative methods
(2016)
The combination of electrochemical and 3D computed tomography (CT) investigations offers the possibility of verifying electrochemical measurements non-destructively. Determining the steel surfaces damaged by pitting corrosion allows developing specimens having damage pattern corresponding to practice. Corrosion phenomena like decoupled pitting corrosion cannot be verified by electrochemical measurements only, but with the combination of those two kinds of investigations it is possible. Another advantage is the minimization of the number of samples. The classical experimental procedure requires the destruction of samples after each damage step.This can be avoided by the use of 3D computed tomography. As long as the corrosion phenomena are completely within the examination zone shown by the 3D computed tomography, the electrochemical measurements can be calculated on an area basis to get the specific corrosion rate or polarization resistance.
Two fly ash-based geopolymer concretes with quartz aggregates or with expanded clay (lightweight) aggregates were exposed to the ISO 834-1 standard fire curve in a small-scale fire test set-up. Acoustic emission measurements during fire exposure and subsequent cooling were employed to study spalling events and cracking during the tests. Optical microscopy and additional acoustic measurements were conducted after the testing to better understand the crack propagation in the samples. The testing revealed that neither of the concretes were susceptible to spalling, which is particularly notable for the concrete with quartz aggregates, as it is a high-strength concrete. This behavior is attributed to the relatively high permeability of the concretes and their low amount of chemically bound water. Significant crack formation was detected only around the temperature of the alpha–beta quartz transition (573 °C) and on cooling. Because of aggregate deformations at the quartz transition temperature, deterioration after heating was more significant in the geopolymer concrete with quartz aggregates. Crack formation also occurred in the concrete with expanded clay aggregates, caused by shrinkage of the geopolymer paste on cooling. Acoustic emission measurements proved to be a valuable tool to investigate processes during high temperature exposure.
Thermo-mechanical and spalling behavior of normal weight and lightweight geopolymer concretes
(2016)
The mechanical and microstructural properties of two geopolymer concretes, produced with either quartz aggregate or expanded clay aggregate, were assessed before, during and after high-temperature exposure up to 750 °C in order to better understand the engineering properties of the material. SEM investigations were also undertaken to better understand the observed changes in the mechanical properties. It was found that dehydration of capillary water caused micro-cracking and strength losses at temperatures ≤ 300 °C. At higher temperatures (T ≥ 500 °C) sintering promoted strength increases, leading significant strength advantages over conventional concretes. Stress-mechanical strain curves, which are the basis of the fire design of concrete structures, were determined. In addition, the two geopolymer concretes where exposed to the ISO 834-1 standard fire curve in a small-scale spalling test set-up. Acoustic emission measurements during, and acoustic measurements and optical microscopy after heat exposure were employed to investigate crack formation during the tests. Both concretes did not spall, which is attributed to their comparatively high permeability and their low amount of chemically bound water. Significant crack formation was detected only around the temperature of the α–β quartz transition (573 °C) and on cooling. Because of aggregate deformations at the quartz transition temperature, deterioration after heating was more significant in the geopolymer concrete with quartz aggregates. Crack formation occurred also in the concrete with expanded clay aggregates, presumably caused by shrinkage of the geopolymer paste on cooling.