Filtern
Dokumenttyp
- Posterpräsentation (20) (entfernen)
Sprache
- Englisch (20)
Schlagworte
- Concrete (20) (entfernen)
Organisationseinheit der BAM
- 8 Zerstörungsfreie Prüfung (8)
- 8.2 Zerstörungsfreie Prüfmethoden für das Bauwesen (7)
- 7 Bauwerkssicherheit (2)
- 7.1 Baustoffe (2)
- 1 Analytische Chemie; Referenzmaterialien (1)
- 1.9 Chemische und optische Sensorik (1)
- 4 Material und Umwelt (1)
- 4.0 Abteilungsleitung und andere (1)
- 8.1 Sensorik, mess- und prüftechnische Verfahren (1)
Algal biofilm façades are an alternative to traditional green façades which can help to improve biodiversity and air quality within cities. They present a low maintenance approach in which subaerial algae are grown directly on concrete substrates. The intrinsic bioreceptivity of the substrate is a critical factor in successful facade colonisation. Existing research has identified several environmental and material properties which influence concrete bioreceptivity, however a consensus has yet to be made on which properties are most influential and how the interaction between properties may promote algal biofilm growth under specific conditions.
Understanding the fundamentals of bioreceptivity enables the developement of functionalized materials. Concrete as the most used building material worldwide is of special interest as microbially greened panels may represent an alternative to classic façade greening with plants. This project includes extensive outdoor experiments, in which eight differently structured concrete panels are weathered under different conditions, aiming to grow a stable biofilm of photosynthetic eukaryotic organisms. Documentation and data analysis of this experiment will be demonstrated using an example of one of the surfaces.
The analysis of the chemical composition of cement-based materials like concrete is a crucial task in civil engineering. Concrete is a multi-phase material made of cement, water, aggregates, additives and admixtures. During the damage assessment of concrete structures, the external ingress of harmful species like chlorine, alkalis or sulfates needs to be determined. In order to provide a fast and precise analysis of concrete the application of LIBS offers unique possibilities as the technique can detect all elements at air atmosphere.
To determine the condition of concrete, the information about the chemical composition, the ingress of harmful species as well as the evaluation of characteristic values like the used cement type or the type of aggregates are needed. This work presents the two-dimensional evaluation of concrete samples using LIBS and multivariate data analysis of atomic and molecular emission. For the evaluation of the main components different classification methods will be applied to identify the heterogeneity of the samples. With respect to their specific phase, different species will be quantified using multivariate regression (PLS) and important figures of merit will be presented. All results will be verified using Standard procedure of wet chemistry (XRF, potentiometric titration and ICP-OES).
The relevance of chloride measurements in practice for durability condition assessment and a description of the working principle of LIBS will be given. A comparison of chloride profiles obtained by the common wet chemical analysis and results from LIBS measurements are shown to demonstrate the accuracy of the LIBS-technique. In addition, an example on the extra information resulting from measurements performed with LIBS for improvement of condition assessment and prediction will be shown.
In civil engineering, the laser-induced breakdown spectroscopy has been applied as a fast and reliable method for a quantitative evaluation of concrete cores. Due to a two-dimensional scanning, the heterogeneity of concrete can be evaluated and elements like Cl, Na, and S are related to the cement matrix only. This study deals with the temporal evaluation and imaging of laser-induced plasmas on cement-based materials, in order to investigate the impact of aggregates with diffrent grain size on the spectral response in LIBS.
Quantitative on-site analysis of harmful elements in building structures with a mobile LIBS-System
(2018)
Environmental influences and damage processes drastically reduce the durability of concrete and reinforced concrete structures. Much of this damage can be traced back to the penetration of harmful elements into the concrete. These elements cause damage processes such as the chlorine-induced corrosion, the alkali-silica reaction or the carbonization. For the maintenance the knowledge of the element concentration and the penetration depth of these harmful elements is essential. Based on this data, a maintenance concept can be developed and an estimation of the remaining service life-time can be carried out.
Typically, chemical analyzes are used to determine harmful elements in concrete, which are costly and time consuming. As an alternative method LIBS is used. On-site measurements were carried out with a mobile LIBS-System to determine harmful elements in a parking garage. A scanner is used to obtain a two-dimensional element mapping. For the quantitative analysis, a calibration of the system is carried out with 15 reference samples based on cement with NaCl with a concentration range of chlorine of 0.05 to 2.5 wt.%. To determine the penetration profile of the harmful element chlorine, concrete cores were drilled, split and analyzed directly on-site.
Detection of ion ingress by LIBS for Evaluation of the remaining lifetime of a concrete structure
(2018)
The majority of the built infrastructure is made of concrete, which is a multiphase system made of cement, aggregates, water and pores. Concrete is often used in combination with steel as reinforced concrete. Environmental influences, especially the ingress of harmful ions in combination with the ingress of water, trigger different damage processes which reduce the designed lifetime of a structure. The ingress of chlorides from de-icing salt or sea water leads to corrosion of the reinforcement. Also the carbonation of the concrete may trigger the corrosion of the reinforcement. The ingress of alkalis from de-icing salts may cause the expansion of the amorphous silica aggregates (alkali-silica reaction) through formation of a swelling gel of calcium silicate hydrate if water is present. The ingress of sulfates may cause spalling of the concrete surface due to ettringite formation.
For the standard procedure in civil engineering cores are taken, cut in slices, grinded and the obtained homogenized powder is solved in acid and investigated by standard procedures.
BAM has developed the LIBS technique for the 2D evaluation of the chemical composition of concrete [1-11]. The technique is established for automated laboratory use with high numbers of samples to investigate transport processes of harmful species (Cl-, CO2, SO42- and alkalis) in concrete. Information about ingress depth and the quantitative values are important to estimate the remaining lifetime of the infrastructure. LIBS is a surface technique. To get information about the ingress depth, a core has to be taken and cut in the middle. The measurements are carried out at the cross section. The main advantages of LIBS are the direct measurement on the surface of the concrete, fast analysis (sample rate 100 Hz) with a spatial resolution of up to 100 µm, the consideration of the heterogeneity of the concrete and the possibility of automated measurements which save a lot of manpower and time. As an example the investigation of ingress profiles for standard diffusion and migration tests in civil engineering takes hours in comparison to just a few minutes using LIBS. At the same time a 2D-evaluation provides information about hot spots of elemental concentration which may not be found by standard methods.
Ingress of chlorides due to a crack in a repair mortar. Left: Photo of the cross section of a concrete core and the surface investigated by LIBS (area 70 mm x 70 mm). Right: Color coded chlorine intensity on the cross section of a concrete core, dark red represents high chlorine content.
The state of the art of LIBS technique for applications in civil engineering will be presented, including typical results of 2D investigation of concrete in laboratory. The performance is also demonstrated by examples for onsite applications using a mobile LIBS system. The road map to standardization is presented as well.
Structural Health Monitoring (SHM) has become very important in today's rapidly developing time. High buildings, large bridges and complex technical structures need to be monitored continuously and this over long periods.
Visual monitoring cannot evaluate the internal condition of building structures. Thus, material embedded sensors are needed. Cable connection of these sensors pose the disadvantage of weak spots and water intrusion. For concrete embedded sensors the use of batteries is not convenient, because of limited lifetime, difficult charging, and generation of electrical waste.. Hence, monitoring should be implemented preferentially with firmly embedded passive RFID sensor modules. However, since the concrete structure forms an electromagnetically reflective and absorbing barrier, only limited energy can be transmitted to the module. This project requires a highly energy-saving system, which can record different sensor parameters at critical points.
Previous work has shown that ultrasonic monitoring using externally applied or embedded transducers and imaging methods based on coda wave interferometry are able to detect subtle changes in concrete elements. In this study, a limited number of embedded transducers has been used to monitor changes in several 12 m long two-span concrete beams subjected to point or linear loads until failure.
The ultrasonic results showed the high sensitivity to stress changes and the nonlinear character of the associated effects. However, the ultrasonic features showed a very good correlation to several conventional monitoring parameters. For higher loads (significant amount of cracking), the technique had to be modified to cope with large wave velocity variations and high decorrelation compared to the reference signal.
Using a very simple imaging procedure, the 2D stress field inside the beam has been visualized including inhomogeneities and artifact at places where cracking occurred at higher loads. The technique has the potential to be included in real time monitoring systems.