Active thermography is sensitive to inhomogeneities at and below the surface of objects investigated. Thus, it should be useful for detecting plaster delaminations on concrete. In this paper, the results of field and laboratory investigations into plaster-covered concrete were compared. For evaluating the bonding state of the plaster it is not sufficient to study only the thermal contrasts at the surface of the investigated objects. The experimental results suggest that the overall thermal behaviour has to be considered.
Impulse thermography is an active method for quantitative investigations of the near
surface region of various structures. It has recently been applied and optimized to applications in civil
engineering. For quantitative analysis of data recorded on the building site, the problems are manifold.
Here, the influence of the different surface properties on the detection and characterization of voids
and honeycombing simulated by polystyrene cubes and cubes prepared of porous concrete are
demonstrated.
Influence of concret properties on the calibration of radar, ultrasonics and active thermography
(2008)
The active approach for non-destructive-testing in Civil Engineering (NDT-CE) with infraredthermography (IR), developed at the Federal Institute for Materials Research and Testing (BAM), is described in part one of this contribution. The active IR-approach is based on the principles of impulse- (IT) and pulse-phase-thermography (PPT). The concept is a direct result of a research project at the BAM in cooperation with the Technical University of Berlin (TUB) and was funded by the Deutsche Forschungsgemeinschaft (DFG). In the second part results of the new thermography-scanning system (thermo-scanner) of BAM on debonding of multi-layered structures, especially carbon fibre reinforced plates (CFRP) on concrete are presented. Both, the thermo-scanner developed at BAM, and the investigations carried out, are part of the
EU-Project Sustainable Bridges. In the third part of the paper the characteristic frequency of the optimum phase-contrast as a means for the characterization of defects depth in CE by means of PPT is introduced. A new quantitative approach is tested and discussed on concrete structures with defects of polystyrene and gas concrete.
An advanced quantitative approach of pulse-phase-thermography for nondestructive
testing in civil engineering is described in this contribution. The
characteristic frequency of the maximum phase-contrast between defects and sound
areas is used as a means for the characterization of its depth.
The new approach is tested in the laboratory on concrete structures with defects of
polystyrene. The surfaces of the structures were heated with IR-radiators for varying
time periods.
The presented investigations were funded by the Deutsche Forschungsgemeinschaft
(DFG) and were carried out in co-operation with the Technical University of Berlin
(TUB).
Impulse-thermography is an active method for quantitative investigations of the near surface region of various structures. It has recently been applied and optimised to applications in civil engineering. By using either an internal or external heat source, parts of the structure under investigation are heated up and the transient heat flux is observed by recording the temperature change at the surface as a function of time. This method is very well suited for the detection of voids and honeycombing in concrete, up to concrete covers of 10 cm as well as for the location of delaminations in multi-layered systems (e.g. plaster on concrete, CFRP-laminates on concrete, asphalt on concrete). Also safety relevant defects like voids in tendon ducts and cracks in concrete could be recognised.
The applicability of pulse phase thermography (PPT) for the investigation of structures is studied systematically on concrete test specimens and on a plastered sandstone column. In the test specimens, voids and delaminations are implemented in different depths and with different sizes, modelling real voids, honeycombing and debonding. Delaminations of plaster in concrete and masonry and behind tiles on concrete are investigated. PPT is based on the frequency analysis of the cooling down process of actively heated surfaces. Therefore, it is contactless and thus completely non-destructive (if overheating of the surface is prevented), fast and allows the inspection of large surface areas. The interpretation of amplitude and phase images gives semi-quantitative information about the observed defects. The phase images provide a deeper probing up to 1015 cm in relation to the interpretation of the thermograms and to the amplitude images. In addition, the influence of surface inhomogeneities and non-uniform heating is reduced.
New thermography systems enable the application of active investigation techniques, i.e. the observation of the cooling down process after heating the surface of a structure under investigation. Defects like voids in concrete having a different thermal diffusivity in comparison to the bulk material are visualised by different surface temperatures. The differences between temperature transient curves above sound regions and above inhomogeneities are expected to include information about the defect parameters.
Experimental investigations with impulse thermography and radar on a concrete test specimen containing voids were analysed. Radar was used to determine the depth of the voids. The influence of size and depth of the voids on the temperature transient curves was studied for different heating times. The transient curves were also fitted with a simple semi-empirical model.
Impulse-thermography has been established as a fast and reliable tool in many areas of non-destructive testing. In recent years several investigations have been done to apply active thermography to civil engineering. For quantitative investigations in this area of application, finite difference calculations have been performed for systematic studies on the influence of environmental conditions, heating power and time, defect depth and size and thermal properties of the bulk material (concrete). The comparison of simulated and experimental data enables the quantitative analysis of defects.