Damage tolerance counts as one of the most widespread approach to fatigue assessment and surely as one of the most promising in understanding the process-structure-property-performance relationships in additively manufactured metallic materials. Manufacturing defects, surface roughness, microstructural features, short and long crack fatigue propagation, residual stresses and applied loads can be taken into consideration in a fracture mechanics-based fatigue assessment. Many aspects are crucial to the reliable component life prediction. Among those a prominent role is played by an accurate measurement and modelling of the short crack fatigue behavior, and reliable statistical characterization of defects and residual stresses.
This work aims at addressing the issues related to both experimental testing, fatigue and fatigue crack propagation, and fracture mechanics-based modelling of fatigue lives. Examples will be provided on an additively manufactured AISI 316 L.
A range of heat treatments have been developed for wrought Inconel 718 to obtain desired properties. For additively manufactured Inconel 718, the recently developed standard ASTM F3301 provides guidance for heat treatment of powder bed fusion specimens. Although this standard is based on standards developed for wrought Inconel 718, it does not include direct aging. Since direct aging reduces the number of processing steps, it can result in a post processing cost reduction if the desired properties are obtained. In this study, we characterized the microstructure and tensile behavior of Inconel 718 specimens produced by a laser powder bed fusion process. The specimens were heat treated according to two different routines after stress relieving: a full heat Treatment versus a one-step direct aging process. Differences in the resulting texture and grain morphology were observed.
The ex-situ stress-strain behavior was broadly similar. However, a slight increase in yield strength was observed for the direct aged specimen. In order to understand this behavior, investigations with in-situ synchrotron Energy dispersive X-ray diffraction tensile testing revealed differences in the load partitioning among different Crystal directions. Importantly, the elastic anisotropy expressed by the magnitude of the diffraction elastic constants showed a dependency on the microstructures.
Additive manufacturing (AM) is developing rapidly due to itsflexibility in producing complex geometries and tailored material compositions. However, AM processes are characterized by intrinsic limitations concerning their resolution and surface finish, which are related to the layer-by-layer stacking process. Herein, a self-organization process is promoted as an approach to improve surface quality and achieve optimization of 3D minimal surface lightweight structures. The self-organization is activated after the powder bed 3D printing process via local melting, thereby allowing surface tension-driven viscous flow.The surface roughness Ra (arithmetic average of the roughness profile) could bedecreased by a factor of 1000 and transparent lenses and complex gyroid structures could be produced for demonstration. The concept of self-organization is further elaborated by incorporating external magnetic fields to intentionally manipulate magnetic particles, which are mixed with the polymer before printing and self-organization. This concept can be applied to develop programmable materials with specific microtextures responding to the external physical conditions.
The relaxation of macroscopic residual stresses in laser powder bed fused stainless steel 316L
(2021)
The processing of stainless steel 316L using the additive manufacturing process Laser Powder Bed Fusion (LPBF) can widen its field of application due to a strong increase in Yield strength, without making major compromises on the ductility nor its outstanding corrosion and oxidation properties. Furthermore, improved designs that either reduce the weight or optimise the function of a part can be obtained using LPBF. These benefits are however counterbalanced by the proneness of LPBF to inducing high Residual Stresses (RS) during manufacturing. The characterisation and monitoring of these RS are of paramount importance for the wider acceptance of the LPBF process. This study focuses on the relaxation of the initial macroscopic RS present in an LPBF 316L as-built prism that undergoes various routes of manufacturing steps to achieve different specimen geometries and stress relieving treatments. The RS are determined using Angle-Dispersive (AD) and Time-of-Flight (TOF) neutron diffraction. The results reveal high tensile RS close to the surfaces and compressive RS near the centre of the as-built parts. The reduction in size and change of geometry heavily impact the stress ranges of the remaining RS, with lower stress ranges in cylindrical shaped compared to rectangular shaped specimens. Also, the application of different stress relieving heat treatments showed that heat-treating temperatures above 800 °C are necessary to obtain a strong relaxation in LPBF 316L.
The laser powder bed fusion of 316L leads to the formation of large residual stress. In this presentation, different stress relieve treatments were employed to assess their potential to relax the residual stress. The residual stress was determined by X-ray and neutron diffraction. The results give insights on the range of relaxation one can obtain by employing low and high temperature heat treatments and relates the relaxation to changes in the microstructure.
The formation of high magnitude residual stresses is inherent in laser powder bed fused processed austenitic steel 316L. Post-process heat treatments to relieve these stresses are necessary. In this study, heat treatment temperatures of 450°C, 800°C and 900°C were applied in order to avoid excessive sensitization. This temperature range thereby encompassed the upper and lower bounds for stress relieving treatment of this material. The residual stresses were determined by neutron diffraction and the evolution of the microstructure was monitored using scanning electron microscopy and electron backscattered diffraction. The results show that a full relaxation of the residual stresses is achieved when applying 900°C for 1 hour, which seems to be closely related to the dissolution of the subgrain solidification cellular structure.