The residual post-fire mechanical properties of fiber-reinforced epoxy composites are influenced by their fire residues after burning. This study uses intumescent/low-melting glass flame retardants to tailor fire residues in epoxy resin. Processibility of prepregs and their quality are analysed for transfer of the flame-retardant epoxy resins to layered glass-fiber reinforced composites. Minimal effects were found on the pre-fire flexural strengths of the composites due to low loading of the flame retardants. However, when transferred to glass-fiber reinforced composites, the fire residues diminish significantly. Further studies are required to improve theoretical and experimental estimations of the post-fire mechanics of the composites.
The influence of pressure sensitive adhesive (PSA) tapes as adhesive layers on the burning behaviour of bonded materials has been investigated. Single-sided tapes as an outer connection between construction materials have large influence on flammability, flame spread and fire resistance. In contrast, double sided tapes only take a small impact on the flammability but can drasticly change the burning behaviour in developing fires.
The copper alloyed stainless steel 1.4542 (X5CrNiCuNb16-4) is used in different areas due to its good mechanical properties and corrosion resistance. Strength and corrosion resistance can be adjusted by the heat treatment, which is of importance for the application of this alloy. The mechanical properties (strength and hardness) are attributed to the dispersive precipitation of the copper rich ε–Phase. The additional precipitation of chromi-um carbides can reduce the corrosion resistance. Different ageing states were produced to investigate the precipitation behaviour with various methods. Furthermore, the influence of cold-rolling on the precipitation behaviour was studied in comparison to a solution annealed state without deformation. The microstructure was studied by SEM and the variations of hardness and magnetic proportion were characterised. The electrochemical potentiodynamic reactivation (EPR) was used to determine the corrosion resistance and detect chromium depletion in all heat-treated states. The results show that a work hard-ening accelerates the precipitation rate, while ageing at 600 °C reduces the corrosion resistance due to chromium depletion.
The full-notch creep test (FNCT) is a common method to evaluate the environmental stress cracking (ESC) behavior of high-density polyethylene (PE-HD) container materials . The test procedure as specified in ISO 16770 provides a comparative measure of the resistance against ESC using the time to failure of specimens mechanically loaded in a well-defined liquid environment. Since the craze-crack damage mechanism underlying the ESC process is associated with brittle failure, the occurrence of globally brittle fracture surfaces is a prerequisite to consider an FNCT measurement as representative for ESC . Therefore, an optical evaluation of FNCT fracture surfaces concerning their brittleness is essential. Due to the experimental setup, an inevitable increase of the true mechanical stress and the associated appearance of small ductile parts on fracture surfaces is induced in any case. Hence, an FNCT experiment is considered as 'valid', if the corresponding fracture surface is predominantly brittle . Based on laser scanning microscopy (LSM) height data of FNCT fracture surfaces , a universal and easy-to-use phenomenological criterion was developed to assess the validity of distinct FNCT experiments. This criterion is supposed to facilitate a quick evaluation of FNCT results in practical routine testing.
A promising approach for the further improvement of fire detection techniques is the inclusion of fire gases in the characteristics used to detect a fire. A screening of sample materials representative for common first burning items and their gas release under different ignition conditions was performed to gain an overview of possible target gas candidates. Different fire scenarios were investigated to evaluate fire gases produced in early stages of fire development, their time of appearance and concentration development using the vitiated mass loss calorimeter and a heating plate setup in the single burning item test chamber.
Algal biofilm façades are an alternative to traditional green façades which can help to improve biodiversity and air quality within cities. They present a low maintenance approach in which subaerial algae are grown directly on concrete substrates. The intrinsic bioreceptivity of the substrate is a critical factor in successful facade colonisation. Existing research has identified several environmental and material properties which influence concrete bioreceptivity, however a consensus has yet to be made on which properties are most influential and how the interaction between properties may promote algal biofilm growth under specific conditions.
Bench-scale fire stability testing - Protective layers in carbon fibre reinforced polymer laminates
(2023)
Fire resistance testing of components made of carbon fibre reinforced polymers (CFRP) composites usually demands intermediate-scale or full-scale testing. In this study, a bench-scale test is presented as a practicable and efficient method to assess the improvement in structural integrity of CFRP with different protective interlayers during fire.
Fire resistance testing of components made of carbon fibre reinforced polymers (CFRP) composites usually demands intermediate-scale or full-scale testing. In this study a bench-scale test is presented as practicable and efficient method to assess the improvement in structural integrity of CFRP with different protective coatings during fire.
Understanding the fundamentals of bioreceptivity enables the developement of functionalized materials. Concrete as the most used building material worldwide is of special interest as microbially greened panels may represent an alternative to classic façade greening with plants. This project includes extensive outdoor experiments, in which eight differently structured concrete panels are weathered under different conditions, aiming to grow a stable biofilm of photosynthetic eukaryotic organisms. Documentation and data analysis of this experiment will be demonstrated using an example of one of the surfaces.
On 14 August 2018, the Morandi bridge in Genoa Italy collapsed, which caused 43 people to die and great losses. Here I am not going to talk about why it collapsed. But I want to say what we can do to prevent this kind of tragedy from happening. Any structures are like us, if we are sick, we go to doctors. But if structures are sick, how could we know?
Yes, through structural health monitoring-SHM! SHM is process of implementing damage detection strategy, which is like a doctor giving us indication of the structure health status. However, the SHM is not like our health insurance which can be free. Some structure owners may be hesitated on investing large money before they see the VALUE.
Although it is proved that SHM is beneficial, the existing literature doesn’t tell them: when to do the monitoring? How often to do that? Which SHM techniques to choose? After monitoring, what action to take? There are so many decisions needed to be made, that’s why here comes my research, which can help to answer all these questions by breaking the wall of value of monitoring information!
So how do we do that? Here we introduce a decision tree. A Decision tree is a decision support tool that uses a tree-like graph or model to describe decisions and their possible outcomes, including how likely it will happen, how severe the consequences will be. Based on the probabilities and their respective costs and benefits, the value of every decision can be quantified.
Based on the decision trees, different SHM strategies can be compared and the optimal strategy will be the one with highest value. After Knowing the value of SHM, we can improve the decision basis for design, operation and life-cycle integrity management of structures to reduce the risk, reduce the cost and extend service life benefits.
So that everyone in society can benefit from a safer and more reliable environment!