Hybrid laser-arc welding (HLAW) was applied for butt welding of 14.5 mm thick plates of ferritic cryogenic steel X8Ni9 containing 9% Ni, which is used for manufacturing storage and transport facilities of liquefied natural gas (LNG). The weld seam formation and the achievable metallurgical and mechanical properties of the hybrid welds were investigated experimentally for two types of filler wire, an austenitic wire dissimilar to the base metal (BM) and an experimentally produced matching ferritic wire. Safe penetration and uniform distribution of the austenitic filler metal in the narrow hybrid weld could only be achieved in the upper, arcdominated part of the weld. The pronounced heterogeneous distribution of the austenitic filler metal in the middle part and in the root area of the weld could not ensure sufficient notched impact toughness of the weld metal (WM). As a result, a decrease in the impact energy down to 17±3 J was observed, which is below the acceptance level of ≥34 J for cryogenic applications. In contrast, the use of a matching ferritic filler wire resulted in satisfactory impact energy of the hybrid welds of up to 134±52 J at the concerned cryogenic temperature of -196 °C. The obtained results contribute to an important and remarkable conversion in automated manufacturing of LNG facilities. In other words, the results will help to develop a new laser-based welding technology, where both quality and productivity are considered.The efficiency of the developed welding process has been demonstrated by manufacturing a prototype where a segment of the inner wall of large size LNG storage tank was constructed. In this concern, hybrid laser arc welding was conducted in both horizontal (2G) and vertical (3G) positions as a simulation to the actual onsite manufacturing. The prototype was fabricated twice where its quality was confirmed based on non-destructive and destructive examinations.
With an availability of the modern high power fibre lasers the application range of laser and laser hybrid welding can be significantly increased. For the implementation of this new technology in the economically extremely interesting application of pipeline construction it is necessary to fulfil a series of systematic research studies. As it has been shown in the past the fibre laser hybrid wielding of pipeline Steel X65 up to 32 mm thickness is possible with appropriate quality. For the use of laser-hybrid welding in pipe laying insensibility towards tolerances and the possibility of girth welding are very important factors in addition to the weld seam quality. The aim of a Research project carried out in the Federal Institute for Materials Research and Testing (BAM) was the development of a welding procedure using high power fibre laser in combination with GMAWProcess which could be applied for welding of pipelines. For tests segments of linepipes with an outer diameter of 914 mm and a wall thickness of 16 mm have been welded using specially designed equipment for girth welding of pipes. First promising results for the use of laser-hybrid welding of thick materials could be demonstrated. The gap-bridgeability and misalignement was studied.
The aim of the present work was to investigate the possibilities of hybrid laser arc welding regarding reliable production of longitudinal welds of high strength pipe steels X80 and X120 and to evaluate achievable mechanical properties of laser hybrid welds. The study focused on weld toughness examination in low temperature range up to –60°C. Suitable filler materials were identified in the context of this task. It could be shown that metal cored electrodes guaranteed sufficient Charpy impact toughness at low temperature for both investigated materials. Modern arc welding technologies such as modified pulsed spray arc were used to promote deeper penetration of the filler material into the narrow laser welding gap. Edge preparation with a 14 mm deep root face was considered as optimum, because no penetration of the filler material could be detected beyond this depth limit, and therefore, any metallurgical influences on the weld metal properties through the welding wire could be excluded.
New brilliant high-power lasers such as disc laser and fibre laser open up new fields of applications for laser-hybrid welding, e.g. power generation, shipbuilding and pipeline construction. For the use of laser-hybrid welding in pipe laying, insensibility towards tolerances and the possibility of orbital welding are very important factors in addition to the weld seam quality.
Within the scope of a basic research project, first promising results for laser-hybrid welding of thick materials could be demonstrated. As base material, the typical pipeline steel API 5L X65 was selected. With the help of a 20 kW fibre laser in combination with an arc-welding process it was possible to produce high-quality welds in plates of up to 20 mm thickness in a single pass and of up to 32 mm in three to five passes, both welded in position PA. Various joint preparations were examined to weld 20 mm thick plates in one pass. Besides different welding positions, gap bridgeability and misalignment were studied. Results for microhardness and Charpy toughness are presented to proof the applicability of laser-hybrid welding for joining in pipe laying.
This paper presents investigation results of a process for defect-free hybrid laser arc welding (HLAW) of closed circumferential welds. The process aims to avoid weld imperfections in the overlap area of a HLAW circumferential weld. A process control strategy for closing the circumferential weld was developed to achieve a defect-free overlap region by controlling the solidification conditions at the end of the weld. The controlled heat flow is achieved by adjusting the parameters of both welding processes involved, the laser beam as well as gas metal arc welding (GMAW) process. Experimental investigations were carried out on 12 mm to 15 mm thick tube sections. The influence of process parameters such as the laser ramp time, the change in magnification scale and the defocusing of the laser beam on the solidifi-cation conditions at the end of the circumferential weld was investigated to find an optimum strategy for ramping out the process energy. Within the framework of the experimental studies, it was demonstrated that defocusing the laser beam in the range between 60 mm and 100 mm over a short run-out area of the weld of approximately 15 mm led to a significantly better weld formation in the overlap area. A favourable cup-shaped weld shape could be achieved without a tendency to crack. The laser optics with a motor-driven lens system made it possible to increase the laser beam diameter without changing the position of the GMAW arc relative to the component surface.
Notch impact toughness of laser beam welded thick sheets of cryogenic nickel alloyed steel X8Ni9
(2020)
This research work deals with the investigations of the impact toughness of laser beam welded 14.5 mm thick sheets made of cryogenic steel X8Ni9 as a function of preheating. This 9% nickel alloyed steel is widely used in the liquefied natural gas (LNG) industry. An application of highly efficient welding processes such as high-power laser beam welding (LBW) in LNG sector requires an understanding of the interactions between the LBW process parameters and weld properties, in particular the impact toughness. The results show that the original fine-grained martensitic microstructure of the base metal (BM) is significantly changed by melting and crystallization during the LBW, what can lead to a decrease in the impact toughness of the weld metal (WM) below the required level. An optimal preheating temperature range leads to the favorable thermal welding cycle and is of remarkable importance for maintaining the notch impact toughness of laser beam welded joints of these thick steel sheets. A parameter window was identified in which V-notch impact toughness comparable to that of the BM at -196 °C was achieved.