Filtern
Dokumenttyp
- Zeitschriftenartikel (5)
- Beitrag zu einem Tagungsband (4)
- Vortrag (2)
- Posterpräsentation (1)
- Forschungsdatensatz (1)
Sprache
- Englisch (13) (entfernen)
Schlagworte
- Alloy 2618A (5)
- Coarsening (5)
- Aging (4)
- Creep (4)
- Aluminium (3)
- Degradation (3)
- Microstructure (3)
- Aluminum alloy (2)
- Aluminum alloys (2)
- Dark-field transmission electron microscopy (DFTEM) (2)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (2)
The studied aluminium alloy is EN AW-2618A (2618A). It is very widely used for exhaust gas turbo-charger compressor wheels. Due to long operating times, high cycle fatigue (HCF) and material aging under the influence of temperatures up to 230 °C is particularly relevant for the wheels. The wheels are typically milled from round wrought blanks. From such round blanks, different testpieces are extracted and a comprehensive series of HCF tests is conducted at room temperature. The tests investigate the materials fatigue performance in the T61 state for two load-ratios, namely R = -1 and R = 0.1. Additionally, two overaged material states are tested, accounting for the aging process the material undergoes during long operating times at high temperatures. The experimental results are evaluated and compared to each other.
Furthermore, the design process of notched specimens is presented. With the notched specimens, it is aimed to quantify the notch sensitivity of the material. Relating thereto, two potential model parameters for the fatigue lifetime model are introduced. Finally, the extended research data management in this project is highlighted and its advantages for sustainable use in material science and engineering applications are shown.
The article covers data on the Brinell hardness of the forged precipitation-hardened aluminum alloy EN AW-2618A in the initial T61 condition (i. e. slightly underaged) and after isothermal aging for up to 25,0 0 0 h at aging temperatures between 160 °C and 350 °C. In addition, the hardness was determined on specimens after creep testing at 190 °C and various stresses. The hardness decreases with increasing ag- ing time due to the microstructural evolution of the harden- ing precipitates. The drop occurs faster the higher the aging temperature. Aging under creep load additionally accelerates the hardness decrease.
A study was made on the effect of creep loading on the precipitate radii evolution of the aluminum alloy 2618A.
The overageing process of the alloy was investigated under load at a temperature of 190 °C with stresses between 79 and 181 MPa and compared to stress free isothermal ageing. The precipitates responsible for strength were characterized using dark-field transmission electron microscopy (DFTEM). This allows the experimental Determination of radii distributions of the rod-shaped Al2CuMg precipitates and the evaluation regarding their mean precipitate radius. It was found that the mean precipitate radius enables the comparison of the different microstructural conditions of crept and uncrept samples. The mean precipitate radii of the samples experiencing creep are significantly higher than those of undeformed samples. It was shown that the acquired radii distributions are viable to determine averaged particle radii for comparison of the aged samples. A ripening process including pipe diffusion along dislocations describes the data on coarsening very well for the creep samples.
Fatigue tests were performed on the forged aluminum alloy EN AW-2618A in the T61 state. Different stress ratios (R = -1, R = 0.1) were selected to study the influence of mean stress on fatigue life. Two overaged states (10 h/230 ◦C, 1000 h/230 ◦C) were also tested to investigate the influence of overaging on fatigue life. Transmission electron microscopy (TEM) was used to characterize the precipitates (S-phase), which are mainly responsible for the strength of the alloy. A fractographic analysis was also performed to determine the failure mode. Overaging reduces the fatigue life compared to the T61 state. The longer the aging time, the lower the fatigue resistance. The reason is the decrease in (yield) strength, which correlates with the radius of the S-phase: the precipitate radius increases by a factor of approximately two for the overaged states compared to the initial state. The analysis of the fracture surfaces showed crack initiation occurs predominantly on the outer surface and is
associated with the primary phases.