Filtern
Dokumenttyp
- Beitrag zu einem Tagungsband (4)
- Vortrag (2)
Referierte Publikation
- nein (6)
Schlagworte
- Dynamic Fracture Toughness (3)
- Master Curve Concept (3)
- Ductile Cast Iron (2)
- ASTM E1921 (1)
- Brittle fracture (1)
- Bruchmechanik (1)
- C(T)-Proben (1)
- Cleavage Fracture (1)
- Cleavage fracture (1)
- Ductile Cast iron (1)
Organisationseinheit der BAM
- 9 Komponentensicherheit (6) (entfernen)
Eingeladener Vortrag
- nein (2)
Within fracture mechanics safety assessment for steels in nuclear technology, the probabilistic master curve (MC) concept according to ASTM E1921 is currently used for quasi-static loading conditions as a supplement to the established deterministic ASME reference curve concept. However, for ferritic ductile cast iron (DCI), a systematic review of potential modifications to the assumptions and the procedure according to ASTM E1921 and an associated validation are still lacking. For this reason, the application of the fracture mechanics MC concept to ferritic ductile cast iron is being investigated in a joint research project between MPA Stuttgart and BAM Berlin. According to IAEA SSG-26, the safety assessment of DCI containers for transport as well as storage of radioactive materials is based on the fracture mechanics criterion of general crack initiation exclusion. Within this context, the focus of the research project is on brittle fracture. The goal is the establishment of a methodology to determine and assess dynamic fracture toughness values of DCI in the ductile-to-brittle transition regime, using samples extracted from a component.
The experimental program uses a DCI material of grade GJS-400, which is generally used for transport and storage containers of radioactive materials. Firstly, a basic mechanical-technological material characterization will be performed consisting of tensile, Charpy and Pellini tests. Following the material characterization, the loading rate relevant for brittle fracture will be determined using instrumented C(T)25-fracture tests at a temperature of -40°C. To be able to transfer the relevant loading rate to other specimen geometries or sizes, the time-dependent course of the Weibull stress is assessed via numerical analyses. With this information an extensive experimental program consisting of DC(T)9, C(T)25, C(T)50, SE(B)10, SE(B)25 and SE(B)140 specimens is performed. These experimental results will be further supported by numerical and fractographic analyses. The empirical experimental database developed for DCI materials will be used to assess the applicability of the MC concept for DCI materials under dynamic loading.
At the current time manufacturing and precracking of test specimens is ongoing. The authors provide first results concerning the mechanical-technological material characterization, the relevant loading rate for brittle fracture determined via C(T)25 tests, and some early results of other specimen types. These experimental results are also supported by preliminary numerical and statistical analyses.
Im laufenden Verbundprojekt MCGUSS untersuchen dieProjektpartner MPA Stuttgart und BAM Berlin das probabilistische Master Curve (MC) Konzept nach ASTM E1921 hinsichtlich seiner Übertragbarkeit auf ferritisches Gusseisen mit Kugelgraphit (DCI).
Ziel des Projektes ist die Entwicklung einer Methode zur Bestimmung und Bewertung der dynamischen Bruchzähigkeit von DCI im Übergangsbereich. In diesem Beitrag werden die Eigenschaften des verwendeten Werkstoffs der Festigkeitsklasse GJS-400 vorgestellt und die sich daraus ergebenden Probenentnahmestellen näher erläutert.
Weiterhin werden erste Ergebnisse der C(T)25-Versuchsserien vorgestellt, die bei Belastungsraten von ca. 5∙103 MPa√ms-1, 5∙104 MPa√ms-1 und 5∙105 MPa√ms-1 und einer Temperatur von -40 °C durchgeführt wurden.
In einem laufenden Kooperationsprojekt zwischen der BAM Berlin und der MPA Stuttgart wird das probabilistische Master Curve (MC) Konzept nach ASTM E1921 hinsichtlich seiner Übertragbarkeit auf ferritisches Gusseisen mit Kugelgraphit (DCI) untersucht.
Zielsetzung ist die Bereitstellung einer Vorgehensweise zur Bestimmung und Bewertung der dynamischen Bruchzähigkeit von DCI im Übergangsbereich. In diesem Beitrag wird der Versuchswerkstoff der Festigkeitsklasse GJS-400 näher vorgestellt.
Ferner werden erste Ergebnisse von zwei bruchmechanischen Versuchsserien an SE(B)140-Großproben bei Belastungsraten von ca. 6∙104 MPa√ms-1 bei -40 °C und -60 °C präsentiert.
Within fracture mechanics safety assessment for steels in nuclear technology, the probabilistic master curve (MC) concept according to ASTM E1921 is currently used for quasi-static loading conditions as a supplement to the established deterministic ASME reference curve concept. However, for ductile cast iron (DCI), a systematic review of potential modifications to the assumptions and the procedure according to ASTM E1921 and an associated validation are still lacking. For this reason, the application of the fracture mechanics MC concept to ferritic ductile cast iron is being investigated in a joint research project between MPA Stuttgart and BAM Berlin. According to Hojo et al. (2008) the MC concept is already in use for the brittle fracture safety assessment of ferritic forged steel containers, which would suggest an extension to ductile cast iron containers. In compliance with IAEA SSG-26, the safety assessment of DCI containers for transport as well as storage of radioactive materials is based on the fracture mechanics criterion of general exclusion of crack initiation. Within this context, the focus of the current research project is on the further development of brittle fracture safety assessment methods. Therefore, a methodology shall be established to determine and assess dynamic fracture toughness values of DCI in the ductile-to-brittle transition regime, using only a low number of small fracture mechanics test specimens extracted from a component. For the experimental program, a DCI material of grade GJS-400 (GGG-40) has been produced as it is generally used for transport and storage containers for nuclear material. A basic mechanical-technological material characterization consisting of tensile, Charpy, and Pellini tests has been planned and a comprehensive fracture mechanics test program was compiled covering dynamic testing of DC(T)9, C(T)25, C(T)50, SE(B)10, SE(B)25, and SE(B)140 specimens at various loading rates and temperatures. The specimen testing is divided between the project partners based on specimen geometry. MPA Stuttgart has been tasked with the testing of the C(T), DC(T) and Pellini specimens, while BAM Berlin was assigned the SE(B), Charpy and tensile tests. These tests allow for the determination of the loading rate relevant for brittle fracture via C(T)25 specimens and an assessment of size effects by transferring the relevant loading rate to other specimen geometries and sizes. Numerical analyses of different specimen geometries and test setups are planned to investigate the influence of stress triaxiality and loading rate. Furthermore, the time-dependent course of the Weibull stress is assessed via these numerical analyses. Throughout the experimental program, the microstructure-property relationship will also be investigated based on quantitative metallographic and fractographic analyses like scanning electron microscope images and metallographic sections. With the acquired experimental database fundamental assumptions of the MC concept, like the weakest link model and the Weibull distribution, will be assessed for the application to DCI. In the end, the applicability of the MC concept will be evaluated and if necessary, modifications to the MC concept for DCI will be proposed. This paper will present the preliminary results of the GJS400 material characterization and the related selection of test specimen extraction points. First results of the C(T)25 and SE(B)140 specimen testing will also be discussed supported by first metallographic analyses.
Within fracture mechanics safety assessment for steels in nuclear technology, the probabilistic master curve (MC) concept according to ASTM E1921 is currently used for quasi-static loading conditions as a supplement to the established deterministic ASME reference curve concept. However, for ductile cast iron (DCI), a systematic review of potential modifications to the assumptions and the procedure according to ASTM E1921 and an associated validation are still lacking. For this reason, the application of the fracture mechanics MC concept to ferritic ductile cast iron is being investigated in a recently started joint research project between MPA Stuttgart and BAM Berlin. According to the IAEA guidelines SSG 26, the safety assessment of DCI containers for transport as well as storage of radioactive materials is based on the fracture mechanics criterion of general crack initiation exclusion. Within this context, the focus of the current research project is on the further development of brittle fracture safety assessment methods. Therefore, a methodology shall be established to determine and assess dynamic fracture toughness values of DCI in the ductile-to-brittle transition regime, using samples extracted from a component. For the experimental program, a DCI material will be produced as it is generally used for transport and storage containers. A basic mechanical-technological material characterization consisting of tensile, Charpy and Pellini tests is planned and a comprehensive fracture mechanics test program was compiled covering dynamic testing of DC(T)9, C(T)25, C(T)50, SE(B)10, SE(B)25, and SE(B)140 specimens. Numerical analyses of different specimen geometries and test setups are planned to investigate the influences of stress triaxiality and loading rate. Throughout the experimental program, the microstructure-property relationship will be investigated based on quantitative metallographic and fractographic analyses. Finally, different MC assessment strategies will be considered and modifications will be made if necessary.
Within fracture mechanics safety assessment for steels in nuclear technology, the probabilistic master curve (MC) concept according to ASTM E1921 is currently used for quasi-static loading conditions as a supplement to the established deterministic ASME reference curve concept. However, for ductile cast iron (DCI), a systematic review of potential modifications to the assumptions and the procedure according to ASTM E1921 and an associated validation are still lacking. For this reason, the application of the fracture mechanics MC concept to ferritic ductile cast iron is being investigated in a recently started joint research project between MPA Stuttgart and BAM Berlin. According to the IAEA guidelines SSG 26, the safety assessment of DCI containers for transport as well as storage of radioactive materials is based on the fracture mechanics criterion of general crack initiation exclusion. Within this context, the focus of the current research project is on the further development of brittle fracture safety assessment methods. Therefore, a methodology shall be established to determine and assess dynamic fracture toughness values of DCI in the ductile-to-brittle transition regime, using samples extracted from a component. For the experimental program, a DCI material will be produced as it is generally used for transport and storage containers. A basic mechanical-technological material characterization consisting of tensile, Charpy and Pellini tests is planned and a comprehensive fracture mechanics test program was compiled covering dynamic testing of DC(T)9, C(T)25, C(T)50, SE(B)10, SE(B)25, and SE(B)140 specimens. Numerical analyses of different specimen geometries and test setups are planned to investigate the influences of stress triaxiality and loading rate. Throughout the experimental program, the microstructure-property relationship will be investigated based on quantitative metallographic and fractographic analyses. Finally, different MC assessment strategies will be considered and modifications will be made if necessary.