Filtern
Dokumenttyp
- Vortrag (348)
- Zeitschriftenartikel (74)
- Beitrag zu einem Tagungsband (53)
- Sonstiges (53)
- Posterpräsentation (13)
- Forschungsbericht (11)
- Tagungsband (Herausgeberschaft für den kompletten Band) (3)
- Beitrag zu einem Sammelband (2)
- Dissertation (2)
- Handbuch (2)
Sprache
- Deutsch (321)
- Englisch (237)
- Mehrsprachig (2)
- Französisch (1)
Schlagworte
- Korrosion (237)
- Corrosion (161)
- Nichtrostender Stahl (62)
- KorroPad (49)
- Potentialfeldmessung (44)
- Korrosionsschutz (31)
- Zink (31)
- Korrosionsprüfung (29)
- Deckschichtbildung (28)
- Geothermal (27)
Organisationseinheit der BAM
- 7.6 Korrosion und Korrosionsschutz (561) (entfernen)
In the late 1980s, a new type of corrosion appeared in drinking water installations where galvanized steel pipes failed forming a deep groove with no corrosion at the other surfaces. The reason was discussed quite fiercely between failure analysts and material suppliers. In the end the discussion lead to the solution: inductive welded pipes of a certain sulphur content were prone to selective corrosion. The history of the arguments is discussed using old communications between Wilhelm Schwenk and Wolfgang Stichel, who later published the results in a paper unfortunately only I german.
Thus the knowledge got lost and new cases based on the same material problems are observed in application of so-called C-Steel piping systems. Failure cases are shown.
Die B 1-Brücke am Altstädter Bahnhof war der wichtigste Verkehrsknotenpunkt in Brandenburg an der Havel. Im Dezember 2019 wurden die überführte Bundesstraße und die Straßenbahnlinie für den Verkehr gesperrt. Grund für die Sperrung war eine einsetzende Rissbildung in den Längsträgerstegen in Verbindung mit Hohlstellen, die letztlich auf gerissene Spanndrähte zurückgeführt werden. Um eine Sperrung der hoch frequentierten unterführten Verkehrswege zu verhindern, wurde ein umfangreiches Überwachungskonzept erforderlich. Wesentlicher Bestandteil dieses Konzepts war ein auf der Schallemissionsanalyse basierendes Monitoringsystem, mit dessen Hilfe Spanndrahtbrüche aufgezeichnet und lokalisiert werden konnten. Auf Grundlage der so gewonnenen Ergebnisse konnten Schwerpunkte für die Bauwerksprüfung abgeleitet werden. In diesem Bericht werden die gewonnenen Erkenntnisse zum messtechnisch erfassten Schadensfortschritt und den damit verbundenen visuell festgestellten Schäden beschrieben. Dabei werden die Besonderheit des verbauten konzentrierten Spannglieds (Spannblockverfahren nach TGL 173-33) und des Spannstahls in Bezug auf die Schadensbilder dargestellt. Die gewonnenen Erkenntnisse sollten bei der Beurteilung anderer Bauwerke mit vergleichbarer Bauart berücksichtigt werden.
Agar gel pads have been used for electrochemical measurements for some time. For zinc in particular, a standard method for measuring the stability of the corrosion product layer is being established. The main interpretation factor is the corrosion product layer resistance RL, as it is easy to determine and interpret. A high corrosion product layer resistance indicates a high level of protection. However, it is not yet known how low the corrosion product layer resistance is for freshly produced zinc samples. As zinc is highly active, it reacts immediately with the environment to form a corrosion product layer, which affects the corrosion product layer resistance. The addition of zinc acetate to the agar gel pads prevents the formation of a surface layer and destroys existing ones.
This makes it possible to measure an almost corrosion product-free zinc surface. This is important in defining the range of corrosion product layer resistance for a protective surface.
Aufgrund guter mechanischer und chemischer Eigenschaften sowie einer hohen Biokompatibilität sind CoCrMo-Legierungen als Implantatwerkstoffe seit Jahrzehnten fester Bestandteil medizintechnischer Anwendungen. Diese Eigenschaften resultieren bekanntermaßen aus chemischer Zusammensetzung, atomarem Aufbau und dem Gefüge. Letzteres wird durch Legierungszusammensetzung, Herstellungsprozess und Wärmebehandlungen bestimmt. In der Vergangenheit wurden bereits Erkenntnisse zum Einfluss der Mikrostruktur auf mechanische bzw. chemische Eigenschaften von CoCrMo gewonnen. Ebenso wurde in der Literatur das Korrosionsverhalten von CoCrMo im Beisein von Körperflüssigkeiten betrachtet. Bisher fehlt es jedoch an vergleichenden Untersuchung, die das Korrosionsverhalten verschiedener Phasen- bzw. Gefügezustände in verschiedenen Körpermedien betrachten. In dieser Arbeit werden bei einer ausgewählten CoCrMo Legierung verschiedene Gefügezustände durch plastische Verformung und Wärmebehandlung erzeugt und vergleichend untersucht. Das Korrosionsverhalten wird anhand elektrochemischer Untersuchungen in verschiedenen körperflüssigkeitsnahen Lösungen im Vergleich zu Titan charakterisiert und der Einfluss von bestimmten Zusätzen (HCL und H2O2) ermittelt.
Das WIPANO-Projekt Spannstahlsicherheit wurde mit aktuellen Ergebnissen im Fachgremium der Gesellschaft für Korrosionsschutz e.V. (GfKORR) im Arbeitskreis Eisen und Stahl vorgestellt. Das Projekt hat die Verbesserung der produktspezifischen Prüfnorm ISO 15630-3 als Ziel. Vorgestellt und diskutiert wurden Aspekte des Oberflächeneinflusses, der Wasserstoffaktivität, Veränderung der Messzelle und die Anpassung des Korrosionstests durch kathodische Polarisierung.