Nanocomposites based on poly(ʟ-lactide) (PLA) and organically modified MgAl Layered Double Hydroxides (MgAl-LDH) were prepared by melt blending and investigated by a combination of Differential Scanning Calorimetry (DSC), Small- and Wide-Angle X-ray Scattering (SAXS, WAXS), and dielectric spectroscopy (BDS). Scanning microfocus SAXS investigations show that the MgAl-LDH is homogeneously distributed in the matrix as stacks of 6 layers and/or partly exfoliated layers. DSC and WAXS show that the degree of crystallinity decreases linearly with the content of LDH. The extrapolation of the dependencies (DSC and WAXS) to zero estimates a limiting concentration of LDH CCri of ca. 21 wt% where the crystallization of PLA is completely suppressed by the nanofiller. The dielectric behavior of neat PLA show two relaxation regions, a β-relaxation at low temperatures related to localized fluctuations and the α-relaxation at higher temperatures due to the dynamic glass transition. The dielectric spectra of the nanocomposites show several additional relaxation processes compared to neat PLA which are discussed in detail. For the nanocomposites around 260 K (ƒ = 1 kHz) an additional process is observed which intensity increases with increasing concentration of LDH. This process is mainly attributed to the exchanged dodecylbenzene sulfonate (SDBS) molecules which are adsorbed at the LDH layers and form a mixed phase with the polymer close to the layers and stacks. An analysis of this process provides information about the molecular dynamics in the interfacial region between the LDH layers and the PLA matrix which reveal glassy dynamics in this region. In the temperature range around 310 K (ƒ = 1 kHz) a further process is observed. Its relaxation rate has an unusual saddle-like temperature dependence. It was assigned to rotational fluctuations of water molecules in a nanoporous environment provided by the LDH filler. Above the glass transition temperature a further process is observed at temperatures above. It is related to Maxwell/Wagner/Sillars polarization due to the blocking of charges at the nanofiller.
The unusually fast crystallization of the organic compound nifedipine has been investigated in detail using different solutions as precursors for the formation of the initial glassy nifedipine films. Starting from these amorphous films the crystallization process was investigated by time-resolved light microscopy at different temperatures around Tg of nifedipine. In all studied cases (acetone, acetonitrile, ethyl acetate, dichloromethane, tetrahydrofuran) the measured mean crystallization rates are, on average, 10000 times higher than rates reported in previous studies. Such high rates cannot be explained by a classical diffusional crystal growth mechanism of nifedipine. Instead, nifedipine shows a strong propensity for diffusionless growth. Solvent assisted or solvent induced preordering of the glassy modification is suggested to be the most probable driving force behind these fast crystallization processes. The nifedipine crystallization rates can be controlled not only by specific solvent–molecule interactions but also by temperature. Below 40 °C, the temperature dependence of the rates is generally small. Above 40 °C, a slowing down of the crystallization rates with increasing temperatures indicates a kinetic competition between different polymorphs. The molecular dynamics of nifedipine molecules in the amorphous phase as well as the relaxation times are studied by dielectric measurements. The dielectric data corroborate the inherently strong propensity of nifedipine to crystallize diffusionlessly under all conditions.
Organically modified ZnAl Layered Double Hydroxides (ZnAl-LDH) was synthesized and melt blended with polyethylene to obtain nanocomposites. The resulting morphology was investigated by a combination of Differential Scanning Calorimetry (DSC), Small and Wide-angle X-ray scattering (SAXS and WAXS) and dielectric relaxation spectroscopy (DRS). The arrangement (intercalation) of polyethylene chains between LDH stacks was investigated employing SAXS. The homogeneity of the nanocomposites and average number of stack size (4–6 layers) were determined using scanning microfocus SAXS (BESSY II). DSC and WAXS results show that the degree of crystallinity decreases linearly with the increasing content of LDH. The extrapolation of this dependence to zero estimates a limiting concentration of ca. 45% LDH where the crystallization of PE is completely suppressed by the nanofiller. The dielectric spectra of the nanocomposites show several relaxation processes which are discussed in detail. The intensity of the dynamic glass transition (β-relaxation) increases with the concentration of LDH. This is attributed to the increasing concentration of the exchanged anion sodium dodecylbenzene sulfonate (SDBS) which is adsorbed at the LDH layers. Therefore, a detailed analysis of the β-relaxation provides information about the structure and the molecular dynamics in the interfacial region between the LDH layers and the polyethylene matrix which is otherwise dielectrically invisible (low dipole moment).
Nanocomposites based on polypropylene (PP) and organically modified ZnAl layered double hydroxides (ZnAl-LDH) were prepared by melt blending and investigated by a combination of differential scanning calorimetry (DSC), small- and wide-angle X-ray scattering (SAXS and WAXS), and dielectric relaxation spectroscopy (DRS). An average number of stack size of LDH layers is calculated by analyzing the SAXS data which is close to that of pure organically modified ZnAl-LDH. Scanning microfocus SAXS investigations show that the ZnAl-LDH is homogeneously distributed in the PP matrix as stacks of 4–5 layers with an intercalated morphology. DSC and WAXS results show that the degree of crystallinity decreases linearly with the increasing content of LDH. The extrapolation of this dependence to zero estimates a limiting concentration of ca. 40% LDH where the crystallization of PP is completely suppressed by the nanofiller. The dielectric spectra of the nanocomposites show several relaxation processes which are discussed in detail. The intensity of the dynamic glass transition (β-relaxation) increases with the concentration of LDH. This is attributed to the increasing concentration of the exchanged anion dodecylbenzenesulfonate (SDBS) which is adsorbed at the LDH layers. Therefore, a detailed analysis of the β-relaxation provides information about the structure and the molecular dynamics in the interfacial region between the LDH layers and the polypropylene matrix which is otherwise dielectrically invisible (low dipole moment). As a main result, it is found that the glass transition temperature in this interfacial region is by 30 K lower than that of pure polypropylene. This is accompanied by a drastic change of the fragility parameter deduced from the relaxation map.