Intermediate-scale testing is indispensable when investigating the fire resistance under simultaneous compressive load of components made of glass- and carbon-fibre-reinforced composites (GFRP and CFRP). BAM is successfully operating an intermediate-scale test stand, developed for a specimen size of 500 mm x 500 mm (1000 mm). The fire resistance in terms of fire stability of CFRP and GFRP sandwiches are investigated, e.g. at 20 % of their compressive failure load at room temperature. Times to failure increase by up to a factor of 4 due to intumescent coatings. For GFRP sandwiches, different core structures with and without additional flame retardants show an astonishing impact on time to failure. CFRP shell structures are investigated on the intermediate scale with and without stringer reinforcements, resulting in completely different mechanical failure behaviour in the ultimate load test as opposed to the fire resistance test. The stringers become the only load-carrying part, while the shell acts as a protective layer. Thus the design exploiting this self-protection potential, i.e. the residue of the front skin protecting the load-bearing structure, is highlighted as a most promising route to enhance the fire resistance of lightweight materials.
Characterization of multiphase metal matrix composites by means of CT and neutron diffraction
(2016)
The present study examines the relationship between the microstructure of multiphase metal matrix composites and their damage mechanisms. The matrix AlSi12CuMgNi was combined with 15% vol. Al₂O₃ (short fibers), and with 7% vol. Al₂O₃ + 15% vol. SiC (short fibers and whiskers, respectively). The experimental approach encompasses 3D microstructure characterization by means of computed tomography of samples (a) as-cast, (b) after heat treatment, and (c) after compression tests at room temperature. The volume fraction of different phases, their distribution, their orientation, and the presence of defects and damage are studied.
The influence of the addition of SiC particles on mechanical properties of composite was investigated. Phase-specific load partition analysis for samples with fiber plane parallel to load was performed by using neutron diffraction (ND) during in-situ compression. ND results show damage in the Si phase, while Al₂O₃ short fibers carry load without damage until failure. The computed tomography observations confirm the load partition analysis.
Applications of fibre reinforced plastic (FRP) composites in modern industries are increasing due to their considerable advantages such as light weight and excellent mechanical properties. Accordingly, importance of operational safety of modern structures made of advanced composites by ensuring the material quality has led to increasing demands for development of non-destructive evaluation (NDE) systems. In the context of a European project entitled “Validated Inspection Techniques for Composites in Energy Applications” (VITCEA), the aim is to develop and validate traceable procedures for novel NDE techniques with contrasting damage detection capabilities in energy related applications such as wind and marine turbine blades, nacelles, oil and gas flexible risers. Accordingly, VITCEA focuses on optimization of ultrasonic tests (UTs) for quantitative defect detection and quality characterization of FRP structures. In this context, the present study describes the ultrasound field in heterogeneous composite materials. The theoretical predictions are compared with simulation results obtained from CIVA a software package dedicated to NDT simulations based on the asymptotic ray theory.
There have been several studies regarding the tribological behaviour of ceramics such as SiC and alumina mated against steels or self-mated. Nevertheless, only Little is known about possible tribochemical reactions when ceramics are mated against steels. In the present study, ceramic pins made of SiC (EKasicF) or alumina (F99.7) respectively were tested under dry sliding conditions against different steel disc counter bodies using a pin-ondisc tribometer. The different ceramics showed significant differences in their tribological behaviour, i.e., coefficient of friction and wear amount. Especially, the SiC couples showed significant differences in the wear amounts while these were quite similar for the alumina couples. The wear behaviour of the SiC couples is discussed in more detail. A correlation between chromium content of the steel discs
was found for the SiC couples. The surfaces of selected specimens were analysed by Auger-Electron-Spectroscopy (AES). Wear for the SiC couples was mainly attributed to tribochemical reactions as far as the steel disc was containing the alloying element chromium in considerable amount. Furthermore, a simple wear schematic is proposed.