Hard coated steel components are used in a wide application range, mostly for protective, wear resistant and decorative purposes. Despite of these coatings being regarded as relatively dense, there is always a high risk of localized corrosion when a coated low alloyed steel component encounters a surrounding high humidity atmosphere or even an aqueous medium. An approach to enhance the corrosion properties is the addition of magnesium to physical vapor deposited hard coatings, like TiN. It has been found that there is a remarkable increase in corrosion resistance in dependence of magnesium content of the TiMgN coating and its surface properties. In this work the authors will explain the underlying corrosion protection mechanisms by means of electrochemical and analytical studies. The positive impact of magnesium in the coating relates on its preferred dissolution vs. steel. This causes the potential to shift to more negative direction with respect to the steel substrate and additionally leads to a temporarily passivation of the steel due to alkalization of the surrounding electrolyte by formation of magnesium hydroxide.
. Hard coated steel components are used in a wide application range, mostly for protective, wear resistant and decorative purposes. Despite of these coatings being regarded as relatively dense, there is always a high risk of localized corrosion when a coated low alloyed steel component encounters a surrounding high humidity atmosphere or even an aqueous medium. An approach to enhance the corrosion properties is the addition of magnesium to physical vapor deposited hard coatings, like TiN. It has been found that there is a remarkable increase in corrosion resistance in dependence of magnesium content of the TiMgN coating and its surface properties. In this work the authors will explain the underlying corrosion protection mechanisms by means of electrochemical and analytical studies. The positive impact of magnesium in the coating relates on its preferred dissolution vs. steel. This causes the potential to shift to more negative direction with respect to the steel substrate and additionally leads to a temporarily passivation of the steel due to alkalization of the surrounding electrolyte by formation of magnesium hydroxide.
Laser-induced periodic surface structures (LIPSS) were generated on titanium nitride (TiN) hardcoating surfaces (deposited on metallic substrates) upon irradiation with multiple linearly polarized femtosecond laser pulses in air (30 fs duration, 790 nm wavelength, 1 kHz pulse repetition rate). The conditions were optimized in a sample-scanning geometry for the processing of large surface areas (5 mm x 5 mm) covered homogeneously by nanostructures with sub-wavelength periods ranging between ~200 nm and 700 nm. For these nanostructures the coefficient of friction was characterized under reciprocating sliding condition against a ball of hardened steel at 1 Hz using different lubricants (regime of mixed friction). After 1000 cycles, the corresponding wear tracks were characterized by optical and scanning electron microscopy. High-resolution energy dispersive X-ray analyzes (EDX) allowed the visualization of chemical alterations within the wear tracks. For specific conditions, the nanostructures endured the tribological treatment. Our experiments provide a qualification of the tribological performance of the fs-LIPSS on TiN surfaces.
A new approach is presented to quantify the so-called "heat affected zone" (HAZ) during
femtosecond laser pulse processing. Ablation of titanium nitride (TiN) thin films (~3 μm
thickness) by multiple femtosecond laser pulses (τ=130 fs, λ=800 nm) in air environment was
studied by means of two different surface analytical methods both being sensitive to chemical
alterations at the surface. Scanning Auger electron microscopy was applied for a visualization of the
spatial distribution of specific elements (Ti, O) within the laser-modified areas. The chemical state
of the irradiated surface was revealed by complementary x-ray photoelectron spectroscopy. Both
methods were used for a depth-profiling chemical analysis (tracking the elements Ti, N, O, and C)
using an Ar-ion beam for surface sputtering. In a narrow laser fluence range slightly below the
ablation threshold of TiN significant superficial oxidation can be observed leading to the formation
of substoichiometric TiO2-x. At fluences above the ablation threshold, an increased titanium
concentration is observed within the entire ablation craters. Following upon sputter removal the
elemental distribution into the depth of the nonablated material, the results allow an estimation of
the heat-affected zone for femtosecond laser ablation in air environment. According to our analyses,
the HAZ extends up to a few hundreds of nanometers into the nonablated material.
The results of an interlaboratory comparison of energy dispersive X-ray microanalysis of TiN0.84 and ZrN were presented. The microprobe group of the German Physical Society (DPG) and the Federal Institute for Materials Research and Testing (BAM) had initiated the interlaboratory comparison. The primary aim was to test modern EDX systems equipped with ultrathin windows concerning the accuracy and reliability of the analysis of compounds containing light elements. The participants from 23 laboratories performed the analysis at different primary energies, in the standard-less mode as well as on the base of own standards, and considering Ti-K or Ti-L in case of TiN0.84. The results show a slight overestimation of the nitrogen content and a large standard deviation from the mean value. Reasons for the scattering of the results are discussed.
Micromachining experiments were performed with Ti:sapphire laser pulses (130 fs - 150 fs, 800 nm, approximately 10 Hz) in air. Employing the direct focusing technique, highly absorbing titanium nitride (TiN) and weakly absorbing polyimide (PI) and polymethylmethacrylate (PMMA) served as target materials. The lateral and vertical precision of the laser ablation and morphological features were characterized by scanning force (SFM), scanning electron (SEM) and optical microscopy. For TiN, incubation can be observed, i.e. the single-pulse surface damage threshold (0.26 J/cm2) is by a factor of two greater than the threshold for 100 pulses. Ablation rates below 10 nm per pulse can be achieved. The evolution of sub-wavelength ripples is presented in dependence on pulse number and laser fluence, respectively. The incubation behavior of the polymers can be described by an accumulation model as for TiN. Experiments on PI with varying focal lengths result in the same modification thresholds. Different polarization states of light (linear, circular) lead to a variation of the ablation rate and to various morphological patterns in the ablation craters (wavelength ripples, cones). Swelling of PMMA occurred at fluences below the ablation threshold.
Ultrashort pulse laser microstructuring (pulse duration 130 fs, wavelength 800 nm, repetition rate 2 Hz) of titanium nitride (TiN) films on silicon substrates was performed in air using the direct focusing technique. The lateral and vertical precision of laser ablation was evaluated. The TiN ablation threshold changed with the number of pulses applied to the surface due to an incubation effect. An ablation depth per pulse below the penetration depth of light was observed. Columnar structures were formed in the silicon substrate after drilling through the TiN layer.