Filtern
Dokumenttyp
Sprache
- Englisch (15)
Schlagworte
- Texture (15) (entfernen)
Organisationseinheit der BAM
- 5 Werkstofftechnik (5)
- 8 Zerstörungsfreie Prüfung (4)
- 8.5 Röntgenbildgebung (4)
- 9 Komponentensicherheit (4)
- 5.4 Multimateriale Fertigungsprozesse (3)
- 9.4 Integrität von Schweißverbindungen (3)
- 5.1 Mikrostruktur Design und Degradation (2)
- 5.2 Metallische Hochtemperaturwerkstoffe (1)
- 9.3 Schweißtechnische Fertigungsverfahren (1)
- 9.6 Additive Fertigung metallischer Komponenten (1)
Eingeladener Vortrag
- nein (3)
The elastic anisotropy caused by the texture in the Nb3Sn filaments of PIT and RRP wires has been calculated by averaging the estimates of Voigt and Reuss, using published Nb3Sn single crystal elastic constants and the Nb3Sn grain orientation distribution determined in both wire types by Electron Backscatter Diffraction. At ambient temperature the calculated Nb3Sn E-moduli in axial direction in the PIT and the RRP wire are 130 GPa and 140 GPa, respectively. The calculated E-moduli are compared with tensile test results obtained for the corresponding wires and extracted filament bundles.
Pre-Inca civilizations like the coastal cultures Moche and Nazca (Early Intermediate) and the inland culture Wari (Middle Horizon) were agrarian societies which supported indigenous elites of impressive wealth, power, and organization. With the expansion of the Wari Empire, the polychrome style and technique of Nazca propagated to the other cultures. High status burials, most of the Late Moche Fine Line ceramics and a large corpus of ceramics with Wari-derived decoration have been recovered in San José de Moro since 1991. The degree of transfer of procedures in this highly interactive scenario is of special interest: is there a limitation to decoration or is it adopted by the local potters also regarding the formulation of the ceramic bodies? In this context the relative amount, size and type of incorporated non-plastic inclusions as temper are important.
Texture formation in amorphous Al86Ni6Y4.5La1.5Co2 splats by thermal and mechanical treatment
(2016)
The crystallization behavior of amorphous Al86Ni6Y4.5La1.5Co2 splats was analyzed by differential scanning calorimetry (DSC) and X-ray diffraction (XRD). Rietveld refinement was used to analyze the preferred orientation of fcc aluminum nanocrystals in the residual amorphous matrix after annealing. Fiber textures in [200] and [220] directions were found after heating to 360 C. The influence of cold rolling on the preferred crystal orientation was studied as a function of the thickness reduction of the specimen. It was found that cold rolling significantly increases the (220) texture, while the (200) texture remains unchanged. Based on the experimental results the formation of (220) and (200) texture during the crystallization of the amorphous splats was ascribed to two different processes, internal stresses induced during splat formation or cold-rolling.
Additive Manufacturing (AM) offers the opportunity to produce easier geometrically complex parts compared to traditional production technologies. An important AM technology for metals is selective laser melting (SLM) where a part is produced by melting and solidifying powder in layers. This technique is known to cause a pronounced texture in the produced AM products due to the specific heat flow and the associated solidification of the material during SLM deposition. In order to evaluate the influence of the deposition hatch length during SLM of nickel based superalloy Inconel 718 samples on the texture and in order to identify any preferred crystallographic direction, we performed monochromatic neutron radiography scans (using wavelength from 1.6 Å to 4.4 Å, step size 0.05 Å) to image the samples while rotating it through 90°. Samples produced with short hatch length showed fine textured columnar grains oriented along the sample building direction in high-resolution radiographs. Whereas processing the sample using a ten-fold longer hatch length reduced the texture. The neutron radiographic experiments were accompanied by scanning electron microscopy including electron back-scattered diffraction to visualize and verify the microstructure and texture.
Connecting Diffraction-Based Strain with Macroscopic Stresses in Laser Powder Bed Fused Ti-6Al-4V
(2020)
The laser powder bed fusion (LPBF) production process often results in large residual stress (RS) in the parts. Nondestructive techniques to determine RS are badly needed. However, a reliable quantification of macro-RS (i.e., stress at the component level) by means of diffraction-based techniques is still a great challenge, because the link between diffraction-based strain and macro-RS is not trivial. In this study, we experimentally determine (by means of in-situ synchrotron radiation diffraction) this link for LPBF Ti-6Al-4V. We compare our results with commonly used models to determine the so-called diffraction elastic constants (DECs). We show that LPBF materials possess different DECs than wrought alloys, simply because their microstructural and mechanical properties are different. We also show that the existing models can be used to calculate DECs only if high accuracy of the RS values is not required. If the peculiarities of the microstructure have to be taken into account (as is the case of additively manufactured materials), a radically new approach is desirable.
Calcium cobaltite Ca3Co4O9, abbreviated Co349, is a promising thermoelectric material for high‐temperature applications in air. Its anisotropic properties can be assigned to polycrystalline parts by texturing. Tape casting and pressure‐assisted sintering (PAS) are a possible future way for a cost‐effective mass‐production of thermoelectric generators. This study examines the influence of pressure and dwell time during PAS at 900°C of tape‐cast Co349 on texture and thermoelectric properties. Tape casting aligns lentoid Co349. PAS results in a textured Co349 microstructure with the thermoelectrically favorable ab‐direction perpendicular to the pressing direction. By pressure variation during sintering, the microstructure of Co349 can be tailored either toward a maximum figure of merit as required for energy harvesting or toward a maximum power factor as required for energy harvesting. Moderate pressure of 2.5 MPa results in 25% porosity and a textured microstructure with a figure of merit of 0.13 at 700°C, two times higher than the dry‐pressed, pressureless‐sintered reference. A pressure of 7.5 MPa leads to 94% density and a high power factor of 326 µW/mK2 at 800°C, which is 11 times higher than the dry‐pressed reference (30 MPa) from the same powder.
The effect of two types of scanning strategies on the grain structure and build-up of Residual Stress (RS) has been investigated in an as-built IN718 alloy produced by Laser Powder Bed Fusion (LPBF). The RS state has been investigated by X-ray diffraction techniques. The microstructural characterization was performed principally by Electron Backscatter Diffraction (EBSD), where the application of a post-measurement refinement technique enables small misorientations (< 2°) to be resolved. Kernel average misorientation (KAM) distributions indicate that preferably oriented columnar grains contain higher levels of misorientation, when compared to elongated grains with lower texture. The KAM distributions combined with X-ray diffraction stress maps infer that the increased misorientation is induced via plastic deformation driven by the thermal stresses, acting to self-relieve stress. The possibility of obtaining lower RS states in the build direction as a consequence of the influence of the microstructure should be considered when envisaging scanning strategies aimed at the mitigation of RS.