This publication summarizes the work carried out during an IAEA coordinated research project (CRP) on safe and reliabe management of spent nuclear fuel. This work contributes to the overall goal of demonstrating the performance of spent nuclear fuel and related storage systems components over long durations, and facilitates the transfer of this knowledge to Member States. The technical areas addressed by the CRP participants were related to potential degradation mechanisms in metal casks and concrete overpacks, such as stress corrosion cracking; long term integrity and performance of the fuel cladding; thermo-mechanical behaviour of the metal seals; and long term gamma and neutron shielding capability. The participants also considered past and ongoing demonstration programmes. For each technical topic addressed the main conclusions have been drawn, including information on the development of specific monitoring and inspection techniques as well as future opportunities for closing relevant data gaps. A major achievement is also the establishment of a worldwide network of experts working on current research projects to demonstrate the long term performance of spent fuel in dry storage systems.
After restarting the site selection process for a final repository for spent nuclear fuel (SNF) and heat-generating radioactive waste, all areas with one of the three potential host rock formations considered in Germany – salt, clay and crystalline rock – are under review. The project “KoBrA“, run by BGE TECHNOLOGY and BAM, collects and reviews requirements, criteria and proposals for final disposal container concepts complying with the current safety standards, taking into consideration international experience in the field of high-level nuclear waste (HLW) management.
German packages for the transport of spent nuclear fuel are assessed with respect to specific transport conditions which are defined in the safety regulations of the International Atomic Energy Agency. In general, gastight fuel rods constitute the first barrier of the containment system. The physical state of the spent fuel and the fuel rod cladding as well as the geometric configuration of the fuel assemblies are important inputs for the evaluation of the package safety under transport conditions. The objective of this paper is to discuss the methodologies accepted by German authority BAM for the evaluation of spent fuel behavior within the package design approval procedure. Specific test conditions will be analyzed with regard to assumptions to be used in the activity release and criticality safety analysis. In particular the different failure modes of the fuel rods, which can cause release of gas, volatiles, fuel particles or fragments, have to be properly considered in these assumptions. The package as a mechanical system is characterized by a complex set of interactions, e.g. between the fuel rods within the assembly as well as between the fuel assemblies, the basket, and the cask containment. This complexity together with the limited knowledge about the material properties and the variation of the fuel assemblies regarding cladding material, burn-up and the operation history makes an exact mechanical analysis of the fuel rods nearly impossible. The application of sophisticated numerical models requires extensive experimental data for model verification, which are in general not available. The gaps in information concerning the material properties of cladding and pellets, especially for the high burn-up fuel, make the analysis more complicated additionally, and require a conservative approach. In this context some practical approaches based on experiences by BAM within safety assessment of packages for transport of spent fuel will be discussed. Ongoing research activities to investigate SNF mechanical behavior in view of gas and fissile material release under transport loads are presented.
The containment systems of transport casks for spent fuel and high radioactive waste usually include bolted lids with metallic or elastomeric seals.
The mechanical and thermal loadings associated with the routine, normal and accident conditions of transport can have a significant effect on the leak tightness of such containment system.
Scaled cask models are often used for providing the required mechanical and thermal tests series. Leak tests have been conducted on those models.
It is also common practice to use scaled component tests to investigate the influence of deformations or displacements of the lids and the seals on the standard leakage rate as well as to study the temperature and time depending alteration of the seals.
In this paper questions of the transferability of scaled test results to the full size design of the containment system will be discussed.
The presentation provides an overview about the understanding of fuel cladding failure mechanisms dominated by hydride embrittlement during long term dry storage. A currently launched research project focuses on the development of a fracture mechanics approach to describe brittle failure of fuel cladding during long term interim storage (BRUZL)“. Finally, the BAM contribution to the current European Joint Program (EJP) on radioactive waste management is illustrated.
The German nuclear waste management strategy consists of dry interim storage of spent fuel inside dual purpose casks and its subsequent direct final disposal in a deep geological repository. Interim storage is limited to 40 years so far, but will have to be extended until repository site selection and operation is concluded, potentially up to 100 years. In this context, research on the long term performance of safety relevant cask components and fuel rod integrity during such extended periods of time is of outmost importance. The barrier function of the fuel cladding depends on its integrity under operational and accidental conditions along with storage and subsequent transportation and is mainly affected over time by altering of the cladding microstructure and by thermo-mechanical conditions during reactor operation and subsequent wet and dry storage.
This paper focuses on failure mechanisms regarding cladding embrittlement caused by physical phenomena concerning hydrogen dissolution and precipitation of hydrides in the zirconium matrix. Within this context, potential cladding integrity issues under extended interim storage conditions followed by transportation are emphasized.
Delayed hydride cracking (DHC) is a well-known time-dependent temperature-activated phenomenon failure mechanism of the fuel cladding during reactor operation. The phenomenon consists of hydrogen diffusion and hydride precipitation at the tip of an initial crack and the propagation of the crack to an approximate distance equal to the length of the hydride. This failure mechanism is temperature-activated phenomenon and enhances along with thermal cycling of the fuel cladding, e. g. during reactor shutdowns. DHC shows limited relevance under quasi static storage conditions with continuously lowering temperatures. However, the literature points that DHC may occur when the temperature during storage decreases to a certain level after some decades and in combination with stress concentrations in the cladding material.
When spent fuel is transferred to dry storage by vacuum drying, the cladding temperature raises up to peak temperatures of ~370°C. Under these conditions, hydrides dissolute into the zirconium matrix up to the solubility limit defined by the peak temperature and this amount of hydrogen can precipitate in a radial re-oriented fashion due to the temperature decrease during storage. Cladding materials with radially precipitated hydrides show significant embrittlement. Radially oriented hydrides are perpendicularly oriented to hoop stresses representing the most critical configuration. Brittle failure of the cladding then occurs by crack propagation through radially oriented hydrides and finally through the zirconium matrix. The susceptibility to radial hydride precipitation depends on cladding material type and microstructure, hydrogen content, pre-drying hydride distribution, irradiation conditions, and temperature and stress histories during drying and storage operations.
This paper addresses major considerations concerning spent fuel cladding embrittlement due to hydride precipitation with regard to the boundary conditions of dry spent fuel storage in Germany. Analytical, numerical, and experimental approaches are to be discussed by BAM in order to identify the specific needs for future R&D work in that area with the purpose to provide the necessary data base for proper safety demonstration and evaluation along with future extended storage licensing procedures.
The presentation focuses on the latest developments of the German nuclear waste management policy including restructering of responsible organizations and the restart of the repository site selection process for high level radioactive waste.
The second part illustrates latest results of long term investigations of metal seals at BAM with regard to extended interim storage periods.
The presentation explains recent administrative developments in Germany concerning nuclear waste management and adresses national and European R&D funding concepts. National and international collaboration is explained followed by the latest update on long term metal seal investigations at BAM. Finally, fuel cladding failure mechanisms during long term dry storage and related R&D initiatives at BAM are explained.
The German nuclear waste management strategy consists of dry interim storage of spent fuel inside dual purpose casks and its subsequent direct final disposal in a deep geological repository. Interim storage is limited to 40 years so far, but will have to be extended until repository site selection and operation is concluded, potentially up to 100 years. In this context, research on the long term performance of safety relevant cask components and fuel rod integrity during such extended periods of time is of outmost importance. The barrier function of the fuel cladding depends on its integrity under operational and accidental conditions along with storage and subsequent transportation and is mainly affected over time by altering of the cladding microstructure and by thermo-mechanical conditions during reactor operation and subsequent wet and dry storage.
This paper focuses on failure mechanisms regarding cladding embrittlement caused by physical phenomena concerning hydrogen dissolution and precipitation of hydrides in the zirconium matrix. Within this context, potential cladding integrity issues under extended interim storage conditions followed by transportation are emphasized.
Delayed hydride cracking (DHC) is a well-known time-dependent temperature-activated phenomenon failure mechanism of the fuel cladding during reactor operation. The phenomenon consists of hydrogen diffusion and hydride precipitation at the tip of an initial crack and the propagation of the crack to an approximate distance equal to the length of the hydride. This failure mechanism is temperature-activated phenomenon and enhances along with thermal cycling of the fuel cladding, e. g. during reactor shutdowns. DHC shows limited relevance under quasi static storage conditions with continuously lowering temperatures. However, the literature points that DHC may occur when the temperature during storage decreases to a certain level after some decades and in combination with stress concentrations in the cladding material.
When spent fuel is transferred to dry storage by vacuum drying, the cladding temperature raises up to peak temperatures of ~370°C. Under these conditions, hydrides dissolute into the zirconium matrix up to the solubility limit defined by the peak temperature and this amount of hydrogen can precipitate in a radial re-oriented fashion due to the temperature decrease during storage. Cladding materials with radially precipitated hydrides show significant embrittlement. Radially oriented hydrides are perpendicularly oriented to hoop stresses representing the most critical configuration. Brittle failure of the cladding then occurs by crack propagation through radially oriented hydrides and finally through the zirconium matrix. The susceptibility to radial hydride precipitation depends on cladding material type and microstructure, hydrogen content, pre-drying hydride distribution, irradiation conditions, and temperature and stress histories during drying and storage operations.
This paper addresses major considerations concerning spent fuel cladding embrittlement due to hydride precipitation with regard to the boundary conditions of dry spent fuel storage in Germany. Analytical, numerical, and experimental approaches are to be discussed by BAM in order to identify the specific needs for future R&D work in that area with the purpose to provide the necessary data base for proper safety demonstration and evaluation along with future extended storage licensing procedures.