Blast furnace cements (CEM III) and alkali-activated slags are binders for concretes with several advantageous engineering properties, and their increased adoption in construction industry could contribute to reducing the CO2 emissions associated with cement production and use. However, the current knowledge about how these cements protect steel reinforcement in concretes against corrosion is very incomplete, which impedes their large-scale application. This knowledge gap is mainly due to the fact that these cements release sulfide and other reduced sulfur species into the concrete pore solution, the consequences of which for the state of the reinforcement and electrochemical measurements are not fully understood.
The present contribution first describes peculiarities of electrochemical measurements of steel in sulfide-containing cementitious materials and related solutions as reported in the literature and a recent report by EFC Working Party 11. It is demonstrated that the high sulfide concentrations in these systems lead to low open circuit potentials and low polarisation resistances, which may be incorrectly interpreted as indicating active corrosion of the steel.
Second, preliminary results of an ongoing project [funded by the Deutsche Forschungsgemeinschaft (DFG, German Research Foundation) – 458297195] related to the passivation and corrosion initiation of steel in sulfide-containing solutions and mortars are presented. Eight mortars based on one alkali-activated blast furnace slag (BFS), three alkali-activated BFS/fly ash blends, one sodium sulfate-activated CEM III/C (‘hybrid cement’), one CEM III/C, one CEM III/B, and one CEM I (ordinary Portland cement, OPC) were produced, and their pore solutions expressed and analysed after 7, 14, 28, and 56 days of curing. The pH values of the solutions differed systematically, with the highest pH values recorded for the CEM I and the alkali-activated BFS/fly ash blends with a high proportion of fly ash, and the lowest pH recorded for the CEM III/B. The redox potentials of the solutions were between −500 mV and −340 mV vs. Ag/AgCl for the alkali-activated binders, approx. +10 mV vs. Ag/AgCl for the CEM I, and in between for the CEM III/B and the CEM III/C. As expected, the electrical conductivity was highest for the alkali-activated binders. These results are explained by the chemical compositions of the pore solutions of the mortars.
Finally, a test set-up to investigate the behaviour of steel in sulfide-containing solutions and the changes on subsequent oxygen and/or chloride addition is introduced. Preliminary electrochemical measurements of steel in sulfide-containing solutions are presented and discussed in the context of the above-mentioned data from the literature and the compositions of the pore solutions of the studied mortars.
The reduction of the chromate contents in cements affects the electrochemical reactions of galvanized reinforcing steels in fresh concrete. By means of electrochemical measurements and bar pull-out tests the effect of chromates on the formation of protective coatings at the zinc and the bond behaviour have been investigated using chromate-containing and chromate-reduced cements. The results have shown that the bond zone was affected as a result of chromate reduction for cement types CEM I and CEM II. The disturbance to the bond zone should be considered as long-term in relation to the pore structure which is formed. The effects on the bond are largely compensated for as the concrete ages. The results of the related bond strength with displacement paths of 0.1 and 0.5?mm, respectively, are still within the range of expected figures for non-galvanized reinforcing steel despite the structural disturbance. Under practical aspects it is not necessary that the existing structural disturbance with respect to bond strength is taken into consideration.
Monitoring accelerated corrosion in chloride contaminated concrete with ground penetrating radar
(2012)
Die Streuung der Agt-Werte von Betonstahl bleibt durch die Variation der Prüfbedingungen (Temperatur, Geschwindigkeit) innerhalb der prüfnormseitig zulässigen Grenzen weitgehend unbeeinflusst. Gleichzeitig führt die Variation der Prüfbedingungen zu einer signifikanten, für die Produktabnahme relevanten Änderung des Niveaus von Agt. Die Auswertemethodik des Zugversuches (Festlegung der Höchstkraft, Wahl des Verfahrens zur Agt-Bestimmung) hat einen signifikanten Einfluss auf Niveau und Streuung von Agt. Es werden Empfehlungen zur Minimierung der Streuung von Agt gegeben.
Chloride-induced damage of reinforcing steel is especially for parking garages and bridges often very severe as large amounts of chlorides act on horizontal surfaces which could lead to fast ingress of these detrimental ions up to the level of the reinforcement and subsequently to high rates of corrosion.
In order to avoid the disadvantages of conventional rehabilitation (unreliable prognosis with patch repair or high costs and regular maintenance with cathodic protection using impressed current) a new combined protection system was developed where the principle of drying out the concrete (by means of a surface protection system) is combined with a temporary cathodic protection (by means of a sprayed zinc layer) during the transitional period of the drying out process.
This new system was tested both in the laboratory and on-site at a pilot application. Based on the results obtained the possibilities and limitations of the new system are discussed in this paper.