Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (19) (entfernen)
Sprache
- Englisch (19)
Referierte Publikation
- ja (19)
Schlagworte
- Polypropylene (19) (entfernen)
Organisationseinheit der BAM
- 1 Analytische Chemie; Referenzmaterialien (2)
- 7 Bauwerkssicherheit (2)
- 7.5 Technische Eigenschaften von Polymerwerkstoffen (2)
- 1.5 Proteinanalytik (1)
- 1.7 Organische Spuren- und Lebensmittelanalytik (1)
- 4 Material und Umwelt (1)
- 4.3 Schadstofftransfer und Umwelttechnologien (1)
- 5 Werkstofftechnik (1)
- 5.3 Polymere Verbundwerkstoffe (1)
- 6 Materialchemie (1)
- 6.7 Materialsynthese und Design (1)
The peel strength of aluminium to polypropylene and poly(tetrafluoroethylene) was determined in dependence on the type and the concentration of functional groups on the polymer surface. For this purpose the polymer surface was equipped with monotype functional groups. The first method to produce monotype functionalized surfaces was an introduction of O functional groups using an oxygen plasma treatment and converting these groups to OH groups applying a wet chemical reduction. In result of this two-step treatment the hydroxyl group concentration at the polymer surface could be increased from 34 to 1014 OH groups/100 C atoms. The second method consists in the deposition of a 150 nm adhesion-promoting layer of plasmapolymers or copolymers onto the polymer surface using the pulsed plasma technique. For that purpose functional groups carrying monomers as allyl alcohol, allylamine and acrylic acid were used. Applying the plasma-initiated copolymerization and using neutral monomers like ethylene or butadiene the concentration of the functional groups was varied.
A correlation of peel strength with the ability of forming chemical interactions between Al atoms and functional groups was found: COOH > OH >> NH2 > H(CH2CH2).
Herein, we examine the influence of adding functionalized graphene (FG), distinct expanded graphites and carbon nanofillers such as carbon black and multiwall carbon nanotubes on mechanical properties, morphology, pyrolysis, response to small flame and burning behavior of a V-2 classified flame-retarded polypropylene (PP). Among carbon fillers, FG and multilayer graphene (MLG) containing fewer than 10 layers are very effectively dispersed during twin-screw extrusion and account for enhanced matrix reinforcement. In contrast to the other fillers, no large agglomerates are detected for PP-FR/FG and PP-FR/MLG, as verified by electron microscopy. Adding FG to flame-retardant PP prevents dripping due to reduced flow at low shear rates and shifts the onset of thermal decomposition to temperatures 40°C higher. The increase in the onset temperature correlates with the increasing specific surface areas (BET) of the layered carbon fillers. The reduction of the peak heat release rate by 76% is attributed to the formation of effective protection layers during combustion. The addition of layered carbon nanoparticles lowers the time to ignition. The presence of carbon does not change the composition of the evolved pyrolysis gases, as determined by thermogravimetric analysis combined with online Fourier-transformed infrared measurements. FG and well-exfoliated MLG are superior additives with respect to spherical and tubular carbon nanomaterials.
Phage display biopanning with Illumina next-generation sequencing (NGS) is applied to reveal insights into peptide-based adhesion domains for polypropylene (PP). One biopanning round followed by NGS selects robust PP-binding peptides that are not evident by Sanger sequencing. NGS provides a significant statistical base that enables motif analysis, statistics on positional residue depletion/enrichment, and data analysis to suppress false-positive sequences from amplification bias. The selected sequences are employed as water-based primers for PP-metal adhesion to condition PP surfaces and increase adhesive strength by 100% relative to nonprimed PP.
Polymer based nanocomposites by melt blending of synthesized ZnAl-Layered Double Hydroxide (ZnAl-LDH) and polypropylene (PP) were investigated by temperature modulated differential scanning calorimetry (TMDSC). The LDH was organically modified by using a surfactant, sodium dodecylbenzene sulfonate (SDBS) to increase the interlayer spacing of the LDH, so that polymer segments can intercalate the inter layer galleries. The glass transition temperature (Tg) and the thermal relaxation strength (Δcp) were determined. The Tg remains constant for concentration till 12 wt% of LDH and a slight reduction of 3 K might be observed for 16 wt% LDH but within the experimental error. The thermal relaxation strength decreases indicating reduction in the amount of mobile polymer segments from amorphous fraction. This finding is supported by the increase in the rigid amorphous fraction (RAF) which is attributed to the polymer molecules which are in close proximity to the crystals and the LDH sheets, as they hinder their mobility. This is analyzed in detail and related to the dielectric relaxation spectroscopy (BDS) results.
The aim of this study is to investigate and compare three different factors, temperature, pretreatment and exposure media, on the oxidation and aging behavior of polypropylene (PP) bulk samples in the autoclave test under increased oxygen pressure. The aging of polypropylene, in this case syringe material, was accelerated under different conditions. The samples were aged at 75°, 80° and 85 °C under pure oxygen and at 75 °C under ultrapure water. Further samples treated with 15 kGy (e-beam) were aged at 75 °C under pure oxygen. All experiments were carried out at an oxygen partial pressure of 50 bar. The different courses of aging were evaluated and compared. Color and transparency were used to assess the visual changes; weight, geometry and tensile test for the changes in technical properties; and DSC, FTIR and TDS-GC-MS to improve our physico-chemical understanding of the aging processes.
The investigations showed that all factors tested influence oxidation/aging behaviour. Dry or wet exposure has no effect on aging during the induction time. However, after the point of maximum service time the degradation process of polymer changes significantly in the presence of water. The increase of aging temperature decreases the maximum service time; however a temperature higher than 80 °C changes the relative ratio of surface and bulk oxidation. The pretreatment with irradiation decreases the maximum service time further, because the irradiation partly damages the antioxidant, and the mobility of antioxidant fragments inside the polymer changes. These diffusion effects influence the relative ratio of bulk and surface oxidation of the polymer sample.
Herein we investigate the influence of carbon additives with different particle sizes and shapes on the flame retardancy and mechanical properties of isotactic polypropylene. Thermally reduced graphite oxide (TRGO) and multi-layer graphene (MLG250), consisting of few graphene layers, are compared with spherical, tubular and platelet-like carbon fillers such as carbon black (CB), multiwall nanotubes (MWNT) and expanded graphite (EG). The different morphologies control the dispersion of the carbon particles in PP and play a key role in structure–property relationships. Uniformly dispersed CB, MLG250 and TRGO shift the onset temperature of PP decomposition to temperatures around 30 °C higher, induce a flow limit in the composites' melt viscosity and change drastically their fire behaviour. The prevented dripping and significantly increased heat absorption result in decreased time to ignition and hardly any change in the reaction to a small flame. Under forced-flaming conditions reductions in the peak heat release rate of up to 74% are achieved due to the formation of a protective layer of residue during combustion. The described effects of carbon nanomaterials on the properties of PP composites are most pronounced for well-exfoliated graphenes, making them preferable to less exfoliated, micron-sized expanded graphite or conventional spherical and tubular carbon nanoparticles.
Thermally reduced graphite oxide (TRGO), containing only four single carbon layers on average, was combined with ammonium polyphosphate (APP) and magnesium hydroxide (MH), respectively, in polypropylene (PP). The nanoparticle's influence on different flame-retarding systems and possible synergisms in pyrolysis, reaction to small flame, fire behavior and mechanical properties were determined. TRGO has a positive effect on the yield stress, which is decreased by both flame-retardants and acts as a synergist with regard to Young's modulus. The applicability and effects of TRGO as an adjuvant in combination with conventional flame-retardants depends strongly on the particular flame-retardancy mechanism. In the intumescent system, even small concentrations of TRGO change the viscosity of the pyrolysing melt crucially. In case of oxygen index (OI) and UL 94 test, the addition of increasing amounts of TRGO to PP/APP had a negative impact on the oxygen index and the UL 94 classification. Nevertheless, systems with only low amounts (≤1 wt%) of TRGO achieved V-0 classification in the UL 94 test and high oxygen indices (>31 vol%). TRGO strengthens the residue structure of MH and therefore functions as a strong synergist in terms of OI and UL 94 classification (from HB to V-0).
Functionalized graphene nanosheets TRGO and MLG 250, prepared from thermally reduced graphite oxide, represent attractive carbon additives for improving the performance of flame retardant polypropylene (PP-FR). The influence of carbon nanofiller type and content on morphology, thermal, mechanical, and electrical properties as well as the fire behavior of melt-extruded PP-FR is investigated. In contrast to conventional nano- and micron-sized carbon fillers such as expanded graphite (EG 40), nano-scaled carbon black (CB), and multiwall carbon nanotubes (CNT), only TRGO and MLG 250 afford uniform dispersion combined with simultaneously improved stiffness (+80%), electrical conductivity (3 × 10-5 S · cm-1) and enhanced flame retardancy of PP-FR, as expressed by lower peak heat release rate (-76%).
Polar groups were introduced on polypropylene surfaces for increasing the surface energy and the peel strength to evaporated aluminium layers. Three kinds of plasma processes were used for introducing such functional groups to polyolefin surfaces: low-pressure radio-frequency (RF) O2 plasma exposure, atmospheric-pressure dielectric-barrier discharge (DBD) treatment in air, and the deposition of allylamine plasma polymer. The amino groups of the allylamine plasma polymer were also used as anchoring points for chemical introduction of covalently bonded spacer molecules equipped with reactive endgroups. Thus, silanol endgroups of a covalently bonded spacer were able to interact with the evaporated metal layer. The Al-PP composites achieved a maximal peel strength of 470 N/m by exposing the polymer to the lowpressure O2 plasma and 500 N/m on exposure to the atmospheric DBD plasma. After allylamine plasma polymerization and grafting of spacers, the peel strength was usually higher than 1500 N/m and the composites could not be peeled.